CN103469631A - Production process of nylon cotton bound cloth fabric - Google Patents
Production process of nylon cotton bound cloth fabric Download PDFInfo
- Publication number
- CN103469631A CN103469631A CN2013104074014A CN201310407401A CN103469631A CN 103469631 A CN103469631 A CN 103469631A CN 2013104074014 A CN2013104074014 A CN 2013104074014A CN 201310407401 A CN201310407401 A CN 201310407401A CN 103469631 A CN103469631 A CN 103469631A
- Authority
- CN
- China
- Prior art keywords
- cloth
- cotton
- carry out
- washing
- access node
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production process of a nylon cotton bound cloth fabric. The production process specifically comprises the following steps of weaving, dyeing, washing, sheathing cotton, performing secondary washing and performing post-finishing and setting. The fabric produced by the production process disclosed by the invention has the characteristics of air permeability and comfort.
Description
Technical field
The present invention relates to a kind of textile production process, relate in particular to the production technology of the cotton access node cloth fabric of a kind of nylon.
Background technology
Access node cloth also is referred to as layer cloth, a kind of by independently warp thread and the weft yarn overlapped two-layer fabrics that is interwoven independently separately more than two groups separately more than two groups, generally there is abundant warming effect, yet general access node cloth gas permeability is poor, and more undesirable aspect comfort level.
Summary of the invention
The present invention is directed to the technical problem existed in prior art, a kind of production technology of the cotton access node cloth fabric of comfortable nylon of breathing freely is provided.
Technical scheme of the present invention is as follows: the production technology of the cotton access node cloth fabric of a kind of nylon specifically comprises step:
I, weave: the mixed yarn raw material of 32s is sent in two-sided small jacquard machine and knit out embryo cloth under the normal temperature state, and the rotating speed of guaranteeing two-sided small jacquard machine is 18 rev/mins;
II, dyeing: add scouring and dyeing degreaser 1g/l in the embryo cloth of above-mentioned steps I, levelling agent 0.5g/l, chelated dispersants 1g/l, acetic acid 1 ~ 1.5g/l and DISPERSE DYES are soaked it and are dyeed in 30 ~ 60 minutes under 130 ℃;
III, washing: the cloth dyeed in the step II is washed, then take a policy at the temperature of 70 ~ 80 ℃ powder 3g/l and soda ash 3g/l reduces and washes 20 minutes, after taking-up, adding hot water to carry out heat washes, then at 60 ℃ of temperature, add 0.5g/l acetic acid to carry out pickling in 30 minutes, carry out again twice washing after pickling completes;
IV, cover cotton: the cloth washed in the step III is added to chelated dispersants 1g/l, and levelling agent 1g/l and dyestuff soak dyeing in 50 minutes under 60 ℃;
V, secondary washing: the cloth completed in the step IV is carried out to the 10min washing at 60 ℃ of temperature, then add acid to carry out pickling, then carry out 1 ~ 2 time and soap, finally carry out 1 ~ 2 hot water wash until the cloth softness;
VI, rear arrangement typing: the cloth that the step V has been washed is sent into the speed of a motor vehicle with 20m/min in setting machine and is finalized the design.
In described step I, the mixed yarn of 32s is that terylene mixes with cotton, and wherein terylene and cotton ratio are 65:35.
In described step I, the pH value of acetic acid is 4-4.5.
Upper overfeeding 25 while in described step VI, sending into setting machine, lower overfeeding-3.
Beneficial effect of the present invention is: implement technical scheme of the present invention, the fabric that disclosed production technology is produced has ventilative comfortable characteristics.
The specific embodiment
Below content of the present invention is described further.
The concrete technology step of barring-on jacquard weave eyelet fabric of the present invention production roughly is divided into and weaves, dyeing, and washing, cover is cotton, secondary washing and rear arrangement several steps of finalizing the design.
Below just from the concrete technology of this access node cloth production, come step by step to introduce in detail whole production, so that technical solution of the present invention is easier to understand, grasp.
Weave: terylene and cotton are mixed into to the yarn raw material with ratio 65:35, under the normal temperature state, the mixed yarn raw material of 32s are sent in 30 cun two-sided small jacquard machines of 22G and woven, draw embryo cloth, the rotating speed of guaranteeing two-sided small jacquard machine in the braiding process is 18 rev/mins;
Dyeing: add scouring and dyeing degreaser 1g/l in the embryo cloth in above-mentioned steps, levelling agent 0.5g/l, chelated dispersants 1g/l, acetic acid 1.5g/l and DISPERSE DYES that pH value is 4 ~ 4.5 are soaked it and are dyeed in 30 ~ 60 minutes under 130 ℃;
Washing: the cloth completed in above-mentioned dyeing is washed, then take a policy at the temperature of 80 ℃ powder 3g/l and soda ash 3g/l reduces and washes 20 minutes, after taking-up, adding hot water to carry out heat washes, then at 60 ℃ of temperature, add 0.5g/l acetic acid to carry out pickling in 30 minutes, carry out again twice washing after pickling completes;
Cover is cotton: add chelated dispersants 1g/l in the cloth that above-mentioned washing is completed, levelling agent 1g/l and dyestuff soak dyeing in 50 minutes under 60 ℃;
Secondary washing: the cloth that above-mentioned steps is completed carries out washing in 10 minutes at 60 ℃ of temperature, then adds acid to carry out pickling, then carries out 1 ~ 2 time and soap, and finally carries out 1 ~ 2 hot water wash until the cloth softness;
Rear arrangement typing: by the above overfeeding 25 of the cloth washed in above-mentioned steps, lower overfeeding-3 is sent in setting machine and is finalized the design, and guarantees that temperature is 150 ℃, and the speed of a motor vehicle is 20m/min.
Technology contents of the present invention and technical characterictic have disclosed as above; yet those of ordinary skill in the art still may be based on teaching of the present invention and announcements and are done all replacement and modifications that does not deviate from spirit of the present invention; therefore; protection domain of the present invention should be not limited to the content that embodiment discloses; and should comprise various do not deviate from replacement of the present invention and modifications, and contained by the present patent application claim.
Claims (4)
1. the production technology of the cotton access node cloth fabric of a nylon is characterized in that comprising step:
I, weave: the mixed yarn raw material of 32s is sent in two-sided small jacquard machine and knit out embryo cloth under the normal temperature state, and the rotating speed of guaranteeing two-sided small jacquard machine is 18 rev/mins;
II, dyeing: add scouring and dyeing degreaser 1g/l in the embryo cloth of above-mentioned steps I, levelling agent 0.5g/l, chelated dispersants 1g/l, acetic acid 1 ~ 1.5g/l and DISPERSE DYES are soaked it and are dyeed in 30 ~ 60 minutes under 130 ℃;
III, washing: the cloth dyeed in the step II is washed, then take a policy at the temperature of 80 ℃ powder 3g/l and soda ash 3g/l reduces and washes 20 minutes, after taking-up, adding hot water to carry out heat washes, then at 60 ℃ of temperature, add 0.5g/l acetic acid to carry out pickling in 30 minutes, carry out again twice washing after pickling completes;
IV, cover cotton: the cloth washed in the step III is added to chelated dispersants 1g/l, and levelling agent 1g/l and dyestuff soak dyeing in 50 minutes under 60 ℃;
V, secondary washing: the cloth completed in the step IV is carried out to the 10min washing at 60 ℃ of temperature, then add acid to carry out pickling, then carry out 1 ~ 2 time and soap, finally carry out 1 ~ 2 hot water wash until the cloth softness;
VI, rear arrangement typing: the cloth that the step V has been washed is sent into the speed of a motor vehicle with 20m/min in setting machine and is finalized the design.
2. the production technology of the cotton access node cloth fabric of a kind of nylon according to claim 1, it is characterized in that: in described step I, the mixed yarn of 32s is that terylene mixes with cotton, wherein terylene and cotton ratio are 65:35.
3. the production technology of the cotton access node cloth fabric of a kind of nylon according to claim 1, it is characterized in that: in described step I, the pH value of acetic acid is 4-4.5.
4. the production technology of the cotton access node cloth fabric of a kind of nylon according to claim 1, is characterized in that: upper overfeeding 25 while in described step VI, sending into setting machine, lower overfeeding-3.