CN103468186A - 竹纤维刨花板粘合剂及其制备方法 - Google Patents

竹纤维刨花板粘合剂及其制备方法 Download PDF

Info

Publication number
CN103468186A
CN103468186A CN2013104647571A CN201310464757A CN103468186A CN 103468186 A CN103468186 A CN 103468186A CN 2013104647571 A CN2013104647571 A CN 2013104647571A CN 201310464757 A CN201310464757 A CN 201310464757A CN 103468186 A CN103468186 A CN 103468186A
Authority
CN
China
Prior art keywords
urea
adhesive
solution
flakeboard
batch
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013104647571A
Other languages
English (en)
Inventor
陈显新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHISHUI XINSHENG BAMBOO FIBER Co Ltd
Original Assignee
CHISHUI XINSHENG BAMBOO FIBER Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHISHUI XINSHENG BAMBOO FIBER Co Ltd filed Critical CHISHUI XINSHENG BAMBOO FIBER Co Ltd
Priority to CN2013104647571A priority Critical patent/CN103468186A/zh
Publication of CN103468186A publication Critical patent/CN103468186A/zh
Pending legal-status Critical Current

Abstract

竹纤维刨花板粘合剂及其制备方法，粘合剂配比为：甲醛溶液32％、氢氧化钠溶液20％、尿素31％、氯化铵溶液6％、甲酸5％、防水剂溶液3％、聚乙烯醇3％；制备方法步骤为：往反应釜投入甲醛溶液，加入第一批尿素及防水剂溶液；升温至40℃时，加入聚乙烯醇，至90℃时保温10-30分钟；30分钟后加入第二批尿素，加氢氧化钠溶液并降温；80℃时加入第三批尿素；68℃时加入第四批尿素；40℃以下放料。本发明摩尔比0.3，减少了树脂中的游离尿素，提高了胶的接合度；减少表面层固化时间，捕捉树脂中的游离甲醛，减少了游离甲醛的释放量，从27mg／100g降至5.5mg／100g,制作工艺简单，粘接强度高、绿色环保。

Description

竹纤维刨花板粘合剂及其制备方法
技术领域
本发明涉及一种粘合剂，尤其涉及一种竹纤维刨花板粘合剂及其制备方法，属于竹木加工技术领域。
背景技术
目前应用非常广泛的竹制品粘合剂为脲醛树脂，传统刨花板粘合剂配方：按重量百分比为：甲醛溶液37﹪；氢氧化钠溶液20％；尿素40％；氯化铵溶液3％。但是脲醛树脂的耐水性和耐热性较 差，并且脲醛树脂会释放甲醛，而甲醛为有毒物质，长期吸入低含量的甲醛容易引发慢性呼吸道疾病、基因突变或白血病等，因此脲醛树脂不适用。
发明内容
本发明的目的是为了克服现有技术中的不足，从而提供一种竹纤维刨花板粘合剂及其制备方法。
为达到上述目的本发明采用如下技术方案：
竹纤维刨花板粘合剂，按重量百分比为：
甲醛溶液32％
氢氧化钠溶液20％
尿素31％
氯化铵溶液6％
甲酸5％
防水剂溶液3％
聚乙烯醇3％
竹纤维刨花板粘合剂制备方法，它包括以下步骤：
步骤一：往反应釜投入甲醛溶液，调pH值8.0一8.6，加入第一批尿素及防水剂溶液；
步骤二：升温至40℃时，加入聚乙烯醇，至90℃时保温10-30分钟，用甲酸调pH值到5.2；
步骤三：10-30分钟后加入第二批尿素，测粘度达到要求以后，加氢氧化钠溶液调pH值到7.8一8.0，并降温；
步骤四：80℃时加入第三批尿素；
步骤五：68℃时加入第四批尿素；
步骤六：40℃以下放料。
采用上述技术方案的有益效果是：
（1）、本发明摩尔比由原来的1.3调到1.03，并且采用碱—酸—碱的工艺路线，多次加料的制胶过程，这一工艺可以使甲醛得到充分的反应，改善了脲胶分子结构，减少了树脂中的游离尿素，同时提高了胶的接合度；同时胶水中添加了氨水，有效地延长了胶的活性能，减少表面层固化时间，捕捉树脂中的游离甲醛，减少了游离甲醛的释放量，从27mg／100g降至5.5mg／100g,达到了GB／T1178—1999标准。
（2）、本发明不仅制作工艺简单，而且粘接强度高、绿色环保。
具体实施方式
竹纤维刨花板粘合剂，按重量百分比为：
甲醛溶液32％
氢氧化钠溶液20％
尿素31％
氯化铵溶液6％
甲酸5％
防水剂溶液3％
聚乙烯醇3％
竹纤维刨花板粘合剂制备方法，它包括以下步骤：
步骤一：往反应釜投入甲醛溶液，调pH值8.0一8.6，加入第一批尿素及防水剂溶液；
步骤二：升温至40℃时，加入聚乙烯醇，至90℃时保温10-30分钟，用甲酸调pH值到5.2；
步骤三：10-30分钟后加入第二批尿素，测粘度达到要求以后，加氢氧化钠溶液调pH值到7.8一8.0，并降温；
步骤四：80℃时加入第三批尿素；
步骤五：68℃时加入第四批尿素；
步骤六：40℃以下放料。
本发明有如下特点：
⑴ 胶配比： 尿素：甲醛=1:1.03；
⑵ 体含量60％，固化时间90S，粘度32S,水溶性1.1倍，游离甲醛0.5％，PH值7.5—8.5，甲醛释放量5.5mg／100g。

Claims (2)

1.竹纤维刨花板粘合剂，其特征在于：包括按重量百分比为：
甲醛溶液32％
氢氧化钠溶液20％
尿素31％
氯化铵溶液6％
甲酸5％
防水剂溶液3％
聚乙烯醇3％。
2.竹纤维刨花板粘合剂制备方法，其特征在于：该方法包括以下步骤：
步骤一：往反应釜投入甲醛溶液，调pH值8.0一8.6，加入第一批尿素及防水剂溶液；
步骤二：升温至40℃时，加入聚乙烯醇，至90℃时保温10-30分钟，用甲酸调pH值到5.2；
步骤三：10-30分钟后加入第二批尿素，测粘度达到要求以后，加氢氧化钠溶液调pH值到7.8一8.0，并降温；
步骤四：80℃时加入第三批尿素；
步骤五：68℃时加入第四批尿素；
步骤六：40℃以下放料。
CN2013104647571A 2013-10-09 2013-10-09 竹纤维刨花板粘合剂及其制备方法 Pending CN103468186A (zh)