CN103450660A - 以废弃聚氨酯泡沫及废弃赛璐璐制备板材的方法 - Google Patents
以废弃聚氨酯泡沫及废弃赛璐璐制备板材的方法 Download PDFInfo
- Publication number
- CN103450660A CN103450660A CN2013104197989A CN201310419798A CN103450660A CN 103450660 A CN103450660 A CN 103450660A CN 2013104197989 A CN2013104197989 A CN 2013104197989A CN 201310419798 A CN201310419798 A CN 201310419798A CN 103450660 A CN103450660 A CN 103450660A
- Authority
- CN
- China
- Prior art keywords
- polyurethane foam
- waste
- xylonite
- discarded
- waste polyurethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
以废弃聚氨酯泡沫及废弃赛璐璐来制备板材的方法。主要工艺过程是:废弃赛璐璐溶于丙酮制得粘合剂,加入废弃聚氨酯泡沫粉,拌和均匀,在模具中成型,回收丙酮,即得板材。用本方法制备以废弃聚氨酯泡沫及废弃赛璐璐为原料的板材成本很低,可以有效利用大量废弃赛璐璐、废弃聚氨酯泡沫,合理利用了资源并减轻废弃物造成的污染,提供了一种用途广泛的新型防水板材。
Description
技术领域
本发明涉及一种板材的制备方法,特别指以废弃聚氨酯泡沫及废弃赛璐璐来制备板材的方法。
背景技术
目前板材的需求量逐年增长,而板材的价格也在逐步攀升,同时轻质及保温的板材具有广泛的用途,非常容易推广和应用。
本发明是以废弃聚氨酯泡沫及废弃赛璐璐为原料。废弃聚氨酯泡沫和废弃赛璐璐是造成环境污染的主要废弃物。目前还未见以废弃聚氨酯泡沫与废弃赛璐璐来制备板材的相关报道,而其低廉的成本使其在建筑及装修领域有广阔的应用前景。
发明内容
本发明要解决的技术问题是提供一种板材的制备方法,这种方法以废弃聚氨酯泡沫及废弃赛璐璐为原料来制备板材。
本发明要解决的技术问题是由如下方案解决的:将废弃聚氨酯泡沫粉碎得到废弃聚氨酯泡沫粉,以其作为基材,再以废弃赛璐璐和丙酮为原料制备粘合剂,然后以上述基材和粘合剂制备板材。其特征是:将废弃赛璐璐溶解在丙酮中制备粘合剂,加入废弃聚氨酯泡沫粉,拌和均匀、成型、回收丙酮,即得产品。
本发明的优点是:1、用本方法制备的板材成本很低。2、可以有效利用大量废弃聚氨酯泡沫及废弃赛璐璐。3、合理利用资源并减轻废弃物造成的污染。4.所制备的板材质量轻并可以防水。
附图说明
图1.以废弃聚氨酯泡沫及废弃赛璐璐制备板材的工艺流程图。
具体实施方式
粘合剂的制备:称取4.65g废弃赛璐璐加入到40.0ml丙酮中,搅拌使其溶解得到粘合剂。
实施例1:在7.02g粘合剂中,加入2.00g废弃聚氨酯泡沫粉,拌和均匀,在模具中成型,加热下经过冷凝回收丙酮,即得产品。
实施例2:在7.02g粘合剂中,加入1.50g废弃聚氨酯泡沫粉,拌和均匀,在模具中成型,加热下经过冷凝回收丙酮,即得产品。
实施例3:在7.02g粘合剂中,加入1.00g废弃聚氨酯泡沫粉,拌和均匀,在模具中成型,加热下经过冷凝回收丙酮,即得产品。
实施例4:在7.02g粘合剂中,加入0.50g废弃聚氨酯泡沫粉,拌和均匀,在模具中成型,加热下经过冷凝回收丙酮,即得产品。
Claims (3)
1.以废弃聚氨酯泡沫及废弃赛璐璐来制备板材的方法,其特征是:在废弃赛璐璐溶于丙酮制得粘合剂中,加入废弃聚氨酯泡沫粉,拌和均匀,在模具中成型,回收丙酮,即得产品。
2.废弃聚氨酯泡沫粉及废弃赛璐璐制备板材的原料配比范围(质量比)是:粘合剂:废弃聚氨酯泡沫粉1:0.0712-0.2849。
3.权利要求1中的废弃聚氨酯泡沫是指:废弃保温聚氨酯泡沫、废弃外包装聚氨酯泡沫,废弃赛璐璐(硝化纤维塑料)是指赛璐璐为原料做的废弃乒乓球、玩具及文具等。