CN103773044A - 一种花生壳/pp复合材料的制备方法 - Google Patents

一种花生壳/pp复合材料的制备方法 Download PDF

Info

Publication number
CN103773044A
CN103773044A CN201210410510.7A CN201210410510A CN103773044A CN 103773044 A CN103773044 A CN 103773044A CN 201210410510 A CN201210410510 A CN 201210410510A CN 103773044 A CN103773044 A CN 103773044A
Authority
CN
China
Prior art keywords
hot pressing
preparation
arachidis hypogaeae
pericarppium arachidis
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201210410510.7A
Other languages
English (en)
Inventor
涂秀芹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANJING XIRUISI CHEMICAL Co Ltd
Original Assignee
NANJING XIRUISI CHEMICAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANJING XIRUISI CHEMICAL Co Ltd filed Critical NANJING XIRUISI CHEMICAL Co Ltd
Priority to CN201210410510.7A priority Critical patent/CN103773044A/zh
Publication of CN103773044A publication Critical patent/CN103773044A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种花生壳/PP复合材料的制备方法，将花生壳洗涤烘干并制成粉末；将花生壳粉末、PP共混混炼；热压制板，热压温度为150~200℃，压力为10~15MPa，热压时间为5~8min；冷压成型；脱模。经测试，与现有技术相比，本发明的花生壳/PP复合材料，拉伸强度、冲击强度、弯曲强度有显著提高。制备方法简单，易于工业化，具有很好的实用性。

Description

一种花生壳/PP复合材料的制备方法
技术领域
本发明涉及复合材料，具体涉及一种花生壳/PP复合材料的制备方法。
背景技术
每年都有大量的花生壳成为农业废弃物，十分浪费。为其寻找合理的应用途径，提高其利用价值具有十分重要的经济效益和社会效益。
在利用花生壳制备复合材料方面，在20世纪70年代中期，美国LIGHTSEY等人最先开始研制花生壳粉/PP复合材料，并将此种复合材料用于装饰材料领域。随后相继有学者研究了以花生壳为原料生产的木塑复合材料在建筑材料、包装材料和军事材料方面的应用。
发明内容
发明目的：针对现有技术中存在的不足，本发明的目的是提供一种花生壳/PP复合材料的制备方法，以使其具有更大的经济效益和社会效益。
技术方案：为了实现上述发明目的，本发明采用的技术方案如下：
一种花生壳/PP复合材料的制备方法，包括以下步骤：
（1）花生壳洗涤烘干，制成粉末备用；
（2）将花生壳粉末与PP共混混炼；
（3）热压制板，热压温度为150~200℃，压力为10~15MPa，热压时间为5~8min；
（4）冷压成型；
（5）脱模。
花生壳粉末与PP的质量分数为20~60%。
有益效果：与现有技术相比，本发明的花生壳/PP复合材料的拉伸强度、冲击强度、弯曲强度有显著提高。具有很好的实用性。
具体实施方式
下面结合具体实施例对本发明作进一步的说明。
实施例1
花生壳洗涤烘干，并制成粉末。将花生壳粉末、PP共混混炼，质量分数35%。热压制板，热压温度为180℃，压力为12MPa，热压时间为5min；冷压成型；脱模。经检测，产品符合质量要求。
实施例2
花生壳洗涤烘干，并制成粉末。将花生壳粉末、PP共混混炼，质量分数40%。热压制板，热压温度为160℃，压力为12MPa，热压时间为5min；冷压成型；脱模。经检测，产品符合质量要求。
实施例3
花生壳洗涤烘干，并制成粉末。将花生壳粉末、PP共混混炼，质量分数45%。热压制板，热压温度为170℃，压力为12MPa，热压时间为5min；冷压成型；脱模。经检测，产品符合质量要求。

Claims (2)

1.一种花生壳/PP复合材料的制备方法，其特征在于，包括以下步骤：
（1）花生壳洗涤烘干，制成粉末备用；
（2）将花生壳粉末与PP共混混炼；
（3）热压制板，热压温度为150~200℃，压力为10~15MPa，热压时间为5~8min；
（4）冷压成型；
（5）脱模。
2.根据权利要求1所述的花生壳/PP复合材料的制备方法，其特征在于，花生壳粉末与PP的质量分数为20~60%。
CN201210410510.7A 2012-10-24 2012-10-24 一种花生壳/pp复合材料的制备方法 Pending CN103773044A (zh)