CN103419538A - Production process for transferring and printing PET (Polyester) transfer film onto metal plate - Google Patents
Production process for transferring and printing PET (Polyester) transfer film onto metal plate Download PDFInfo
- Publication number
- CN103419538A CN103419538A CN2013103103749A CN201310310374A CN103419538A CN 103419538 A CN103419538 A CN 103419538A CN 2013103103749 A CN2013103103749 A CN 2013103103749A CN 201310310374 A CN201310310374 A CN 201310310374A CN 103419538 A CN103419538 A CN 103419538A
- Authority
- CN
- China
- Prior art keywords
- sheet metal
- transfer film
- pet polyester
- transferred
- production technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a production process for transferring and printing a PET (Polyester) transfer film onto a metal plate. The production process comprises the following steps: Step A, performing polishing, oil removal, pickling, cleaning and drying of the metal plate; Step B, placing the metal plate on a light curing transfer printer, and regulating the production speed; Step C, coating a glue as a bottom glue in a rolling manner, drying the glue via a lamp box, and enabling the glue to keep semi-dry; Step D, sticking and pressing the metal plate and the PET transfer film, and enabling a pattern layer of the PET transfer film to firmly stick to the metal plate; Step E, tearing a PET film layer from the metal plate after illumination curing of an infrared lamp, and enabling the pattern on the PET transfer film to be transferred onto the metal plate; Step F, coating a clear coating in a rolling manner, and performing the illumination curing of the clear coating with the infrared lamp; Step G, finishing transferring and printing, and obtaining the finished product. The product obtained via the production process is lifelike in layering effect of wood grain and stone grain, the operation is convenient, working efficiency is greatly improved, production cost is saved, and an industry blank is filled.
Description
Technical field
The present invention relates to hot transfer printing field, in particular a kind of production technology that PET polyester transfer film is transferred to sheet metal.
Background technology
By existing production technology, PET polyester transfer film is transferred on sheet metal, dim design, wood grain, bag pattern are true to nature not, environmental protection, can not meet instructions for use.
Therefore, prior art has yet to be improved and developed.
Summary of the invention
The object of the present invention is to provide a kind of production technology that PET polyester transfer film is transferred to sheet metal, be intended to solve and by existing production technology, PET polyester transfer film be transferred on sheet metal, dim design, wood grain, bag pattern are true to nature not, environmental protection, can not meet the problem of instructions for use.
Technical scheme of the present invention is as follows: a kind of production technology that PET polyester transfer film is transferred to sheet metal wherein, specifically comprises the following steps:
Steps A: will pass through again oil removing, pickling, cleaning, oven dry after the sheet metal polishing;
Step B: steps A is obtained sheet metal be put on the photocuring transfer interpreter, mix up speed of production;
Step C: do primer at sheet metal top roll cementing again, dry through lamp box, make glue on sheet metal in leather hard;
Step D: the sheet metal by glue in leather hard and the pressing of PET polyester transfer film make the patterned layer of PET polyester transfer film firmly stick on sheet metal;
Step e: sheet metal process infrared lamp illumination curing, the PET rete is torn again, make PET polyester transfer film design transfer to sheet metal;
Step F: at sheet metal top roll transparent painting, use the infrared lamp illumination curing again;
Step G: transfer printing completes, and obtains finished product.
The described production technology that PET polyester transfer film is transferred to sheet metal, wherein, described step B speed of production is between 5 m/mins-15 m/mins.
The described production technology that PET polyester transfer film is transferred to sheet metal, wherein, the thickness of described step C roller coat glue is between 3 μ m-8 μ m.
The described production technology that PET polyester transfer film is transferred to sheet metal, wherein, between 24 joules-50 joules of the energy of described step C lamp box.
The described production technology that PET polyester transfer film is transferred to sheet metal, wherein, the infrared lamp in described step e and step F is the UV infrared lamp.
The described production technology that PET polyester transfer film is transferred to sheet metal, wherein, between 900 joules-1300 joules of the energy of the infrared lamp in described step e and step F.
The described production technology that PET polyester transfer film is transferred to sheet metal, wherein, in described step F, the colored varnish of roller coat is the UV colored varnish.
The described production technology that PET polyester transfer film is transferred to sheet metal, wherein, between the roller coat thickness 5 μ m-15 μ m of the described step F colored varnish.
The described production technology that PET polyester transfer film is transferred to sheet metal, wherein, the sheet metal described in steps A is iron plate sheet material or stainless steel materials.
The described production technology that PET polyester transfer film is transferred to sheet metal, wherein, the sheet metal described in steps A is aluminium-plastic panel sheet material or aluminum veneer sheet material.
Beneficial effect of the present invention: the present invention is by providing a kind of production technology that PET polyester transfer film is transferred to sheet metal, the product wood grain, the bag level effect that by this production technology, obtain are true to nature, easy to operate, greatly improved operating efficiency, save production cost, filled up the blank of industry; This production technology firmly sticks on sheet metal PET polyester transfer film forever to be difficult to come off, greatly to have improved fixture, inside and outside wallboard and ceiling decoration industry sheet metal service life.
The accompanying drawing explanation
Fig. 1 in the present invention is transferred to PET polyester transfer film the flow chart of steps of the production technology of sheet metal.
The specific embodiment
For making purpose of the present invention, technical scheme and advantage clearer, clear and definite, referring to accompanying drawing, developing simultaneously, the present invention is described in more detail for embodiment.
As shown in Figure 1, be in the present invention, PET polyester transfer film to be transferred to the flow chart of steps of the production technology of metal.The described production technology that PET polyester transfer film is transferred to sheet metal specifically comprises the following steps:
Steps A: will pass through again oil removing, pickling, cleaning, oven dry after the sheet metal polishing;
Step B: steps A is obtained sheet metal be put on the photocuring transfer interpreter, mix up speed of production;
Step C: do primer at sheet metal top roll cementing again, dry through lamp box, make glue on sheet metal in leather hard;
Step D: the sheet metal by glue in leather hard and the pressing of PET polyester transfer film make the patterned layer of PET polyester transfer film firmly stick on sheet metal;
Step e: sheet metal process infrared lamp illumination curing, the PET rete is torn again, make PET polyester transfer film design transfer to sheet metal;
Step F: at sheet metal top roll transparent painting, use the infrared lamp illumination curing again;
Step G: transfer printing completes, and obtains finished product.
The production technology that this PET polyester transfer film is transferred to metal is applicable to various metals sheet material, as iron plate, and aluminium-plastic panel, aluminum veneer, corrosion resistant plate, etc.
Through many experiments, draw, the product effect that described step B speed of production obtains between 5 m/mins-15 m/mins is best.
Through many experiments, draw, the product effect that the thickness of described step C roller coat glue obtains between 3 μ m-8 μ m is best.
Through many experiments, draw, the product effect obtained between 24 joules-50 joules of the energy of described step C lamp box is best.
In the present embodiment, the infrared lamp in described step e and step F is the UV infrared lamp.
Through many experiments, draw, the product effect obtained between 900 joules-1300 joules of the energy of described step e infrared lamp is best.
Through many experiments, draw, the product effect obtained between 900 joules-1300 joules of the energy of described step F infrared lamp is best.
In the present embodiment, in described step F, the colored varnish of roller coat is the UV colored varnish.
Through many experiments, draw, the product effect obtained between the roller coat thickness 5 μ m-15 μ m of the described step F colored varnish is best.
Embodiment 1
Steps A: will after the polishing of iron plate sheet material, pass through again oil removing, pickling, cleaning, oven dry; Step B: step 1 is obtained iron plate sheet material be put on the photocuring transfer interpreter, speed of production is 5 m/mins; Step C: on iron plate sheet material, the glue of roller coat thickness 3 μ m is done primer again, through the lamp box of 25 joules of energy, dries, and makes glue on iron plate sheet material in leather hard; Step D: the iron plate sheet material by glue in leather hard and the pressing of PET polyester transfer film firmly stick on iron plate sheet material the patterned layer of PET polyester transfer film; Step e: the UV infrared lamp illumination curing of 900 joules of iron plate sheet material process energy, the PET rete is torn again, make PET polyester transfer film design transfer to iron plate sheet material; Step F: the UV colored varnish of roller coat thickness 5 μ m on iron plate sheet material again, by the UV infrared lamp illumination curing of 900 joules of energy; Step G: transfer printing completes, and obtains finished product.
The product wood grain, the bag level effect that by this production technology, obtain are true to nature, easy to operate, have greatly improved operating efficiency, save production cost, have filled up the blank of industry; This production technology firmly sticks on sheet metal PET polyester transfer film forever to be difficult to come off, greatly to have improved fixture, inside and outside wallboard and ceiling decoration industry sheet metal service life.
Embodiment 2
Steps A: will after the polishing of aluminum veneer sheet material, pass through again oil removing, pickling, cleaning, oven dry; Step B: step 1 is obtained aluminum veneer sheet material be put on the photocuring transfer interpreter, speed of production is 10 m/mins; Step C: on aluminum veneer sheet material, the glue of roller coat thickness 5 μ m is done primer again, through the lamp box of 40 joules of energy, dries, and makes glue on aluminum veneer sheet material in leather hard; Step D: the aluminum veneer sheet material by glue in leather hard and the pressing of PET polyester transfer film firmly stick on aluminum veneer sheet material the patterned layer of PET polyester transfer film; Step e: the UV infrared lamp illumination curing of 1100 joules of aluminum veneer sheet material process energy, the PET rete is torn again, make PET polyester transfer film design transfer to aluminum veneer sheet material; Step F: the UV colored varnish of roller coat thickness 10 μ m on aluminum veneer sheet material again, by the UV infrared lamp illumination curing of 1300 joules of energy; Step G: transfer printing completes, and obtains finished product.
The product wood grain, the bag level effect that by this production technology, obtain are true to nature, easy to operate, have greatly improved operating efficiency, save production cost, have filled up the blank of industry; This production technology firmly sticks on sheet metal PET polyester transfer film forever to be difficult to come off, greatly to have improved fixture, inside and outside wallboard and ceiling decoration industry sheet metal service life.
Embodiment 3
Steps A: will after the polishing of corrosion resistant plate sheet material, pass through again oil removing, pickling, cleaning, oven dry; Step B: step 1 is obtained corrosion resistant plate sheet material be put on the photocuring transfer interpreter, speed of production is 15 m/mins; Step C: on corrosion resistant plate sheet material, the glue of roller coat thickness 8 μ m is done primer again, through the lamp box of 50 joules of energy, dries, and makes glue on corrosion resistant plate sheet material in leather hard; Step D: the corrosion resistant plate sheet material by glue in leather hard and the pressing of PET polyester transfer film firmly stick on corrosion resistant plate sheet material the patterned layer of PET polyester transfer film; Step e: the UV infrared lamp illumination curing of 1300 joules of corrosion resistant plate sheet material process energy, the PET rete is torn again, make PET polyester transfer film design transfer to corrosion resistant plate sheet material; Step F: the UV colored varnish of roller coat thickness 15 μ m on corrosion resistant plate sheet material again, by the UV infrared lamp illumination curing of 1100 joules of energy; Step G: transfer printing completes, and obtains finished product.
The product wood grain, the bag level effect that by this production technology, obtain are true to nature, easy to operate, have greatly improved operating efficiency, save production cost, have filled up the blank of industry; This production technology firmly sticks on sheet metal PET polyester transfer film forever to be difficult to come off, greatly to have improved fixture, inside and outside wallboard and ceiling decoration industry sheet metal service life.
Should be understood that, application of the present invention is not limited to above-mentioned giving an example, and for those of ordinary skills, can be improved according to the above description or convert, and all these improvement and conversion all should belong to the protection domain of claims of the present invention.
Claims (10)
1. a production technology that PET polyester transfer film is transferred to sheet metal, is characterized in that, specifically comprises the following steps:
Steps A: will pass through again oil removing, pickling, cleaning, oven dry after the sheet metal polishing;
Step B: steps A is obtained sheet metal be put on the photocuring transfer interpreter, mix up speed of production;
Step C: do primer at sheet metal top roll cementing again, dry through lamp box, make glue on sheet metal in leather hard;
Step D: the sheet metal by glue in leather hard and the pressing of PET polyester transfer film make the patterned layer of PET polyester transfer film firmly stick on sheet metal;
Step e: sheet metal process infrared lamp illumination curing, the PET rete is torn again, make PET polyester transfer film design transfer to sheet metal;
Step F: at sheet metal top roll transparent painting, use the infrared lamp illumination curing again;
Step G: transfer printing completes, and obtains finished product.
2. the production technology that PET polyester transfer film is transferred to sheet metal according to claim 1, is characterized in that, described step B speed of production is between 5 m/mins-15 m/mins.
3. the production technology that PET polyester transfer film is transferred to sheet metal according to claim 1, is characterized in that, the thickness of described step C roller coat glue is between 3 μ m-8 μ m.
4. the production technology that PET polyester transfer film is transferred to sheet metal according to claim 1, is characterized in that, between 24 joules-50 joules of the energy of described step C lamp box.
5. the production technology that PET polyester transfer film is transferred to sheet metal according to claim 1, is characterized in that, the infrared lamp in described step e and step F is the UV infrared lamp.
6. the production technology that PET polyester transfer film is transferred to sheet metal according to claim 1, is characterized in that, between 900 joules-1300 joules of the energy of the infrared lamp in described step e and step F.
7. the production technology that PET polyester transfer film is transferred to sheet metal according to claim 1, is characterized in that, in described step F, the colored varnish of roller coat is the UV colored varnish.
8. the production technology that PET polyester transfer film is transferred to sheet metal according to claim 1, is characterized in that, between the roller coat thickness 5 μ m-15 μ m of the described step F colored varnish.
9. according to the described production technology that PET polyester transfer film is transferred to sheet metal of claim 1-8 any one, it is characterized in that, the sheet metal described in steps A is iron plate sheet material or stainless steel materials.
10. according to the described production technology that PET polyester transfer film is transferred to sheet metal of claim 1-8 any one, it is characterized in that, the sheet metal described in steps A is aluminium-plastic panel sheet material or aluminum veneer sheet material.