CN104960346A - Wood floor printing method - Google Patents
Wood floor printing method Download PDFInfo
- Publication number
- CN104960346A CN104960346A CN201510356498.XA CN201510356498A CN104960346A CN 104960346 A CN104960346 A CN 104960346A CN 201510356498 A CN201510356498 A CN 201510356498A CN 104960346 A CN104960346 A CN 104960346A
- Authority
- CN
- China
- Prior art keywords
- steel rider
- timber floor
- printing process
- graining roll
- process according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a wood floor printing method, and belongs to the field of wood floor production technologies. According to the technical scheme, the wood floor printing method comprises the steps that 1, covering material coating is conducted on the surface of a substrate at least one time, and a covering layer which covers the color and the contour of boils on the surface of the substrate is formed; 2, polishing leveling is conducted on the surface of the covering layer; 3, the surface of the covering layer is coated with general primer paint and wear-resisting primer paint, and a primer paint layer is formed; 4, pattern transfer is conducted on the surface of the primer paint layer through a printing roller set, non-planar transfer of patterns is conducted on the substrate, and a printed substrate is formed; 5, the printed substrate is coated with sizing paint, and a surface printed floor is formed. According to the wood floor printing method, the covering layer is additionally arranged to improve the flatness of the paint surface, and the design of the printing roller set is optimized.
Description
Technical field
The invention belongs to timber floor production technology field, particularly relate to a kind of timber floor printing process.
Background technology
Current timber floor transfer technique is that the technique of being dried by roll extrusion is realized, but this technique is very high to the requirement of various parameter, does not with great difficulty damage substrate surface and lacquer painting if grasped, and various the implementing of the step of technique own is difficult to control quality.
And for example the publication number coating process that is a kind of floor disclosed in the Chinese invention patent of CN103144396A or surfaces of wall stereo decoration, comprises the following steps: the 1. aqueous paint colouring step of base material; 2. the common priming paint of base material and wear-resistant primer application step, forms prime coat; 3. by having the steel rider of ridge design, base material prime coat is carried out to the pressing step of concave-convex effect; 4. the application step of finish paint.Coating process of the present invention, simple to operate, by carrying out the compacting in stereo concave-convex face to prime coat with steel rider, obtain the decorative effect of surface three-dimensional; But this invention suppresses recess and convex place linking portion easily occurs that paint film is cracked; Suppress out that Z-Correct bump mapping Z-correct is fuzzy, decorative pattern profile is unintelligible, repetitive rate is high, surface abrasion resistance is not good, and the stereoeffect of incrustation is not obvious.
Summary of the invention
The invention provides for the deficiencies in the prior art part and set up covering layer to promote the flatness of lacquer painting and to optimize a kind of timber floor printing process of design of graining roll group.
Technical scheme of the present invention is to provide a kind of timber floor printing process, is included in the five steps that base material completes,
Step one, the surface of described base material is at least carried out the coating of a cover material, is formed and hides the described color of substrate surface furuncle and the covering layer of profile;
Step 2, by smooth for the surface finish of described covering layer;
Step 3, is coated with common priming paint and wear-resistant primer on the surface of described covering layer, forms prime coat;
Step 4, carries out decorative pattern transfer printing by graining roll group to described primer coat surface, and the on-plane surface transfer printing described base material being carried out to pattern forms printing base material;
Step 5, on described printing element, coating sizing paint, makes surface printing floor.
The covering layer that the present invention sets up can hide wood grain on base material and furuncle, makes substrate surface be complete plane, recess and convex place linking portion would not be caused like this in transfer process because of the out-of-flatness of substrate surface to occur that paint film is cracked.
As preferably of the present invention, on the surface of described base material, in described step one, carry out the coating of twice cover material.
As preferably of the present invention, the cover material described in described step one is putty.
As preferably of the present invention, while the graining roll group described in described step 4 carries out decorative pattern transfer printing to described primer coat surface, carry out lubricant mist sprinkling at described graining roll group outer surface.
This technique of the present invention not only can reduce the wearing and tearing of graining roll group, improve service life, and then improve the operating efficiency of printing, and the clean of graining roll group surface can be ensured, also can improve further by graining roll group printing texture toughness, increase abrasion resistant effect.
As preferably of the present invention, the temperature of described lubricant mist is 60-65 DEG C.
As preferably of the present invention, the outer circumference surface temperature of the graining roll group described in when the graining roll group described in described step 4 carries out decorative pattern transfer printing to described primer coat surface remains between 66-68 DEG C.
As preferably of the present invention, the pressure that described graining roll group is produced by weight own carries out compacting transfer to described prime coat.
This mode of the present invention can eliminate that machinery initiatively extrude that the pressure that causes extrudes and the lacquer painting that causes damages, this mode is different with prior art and common transfer apparatus active rotation mode, base material itself is used to move relative to graining roll group, rotating of graining roll group is driven by the frictional force of prime coat relative to graining roll group surface, the pressure of transfer printing is from the weight of graining roll group itself, such graining roll group and prime coat of making has certain adaptation space that the transferring effect of lacquer painting is promoted, and will roll surface and primer coat surface be caused to be close to all the time by the mode transfer printing of extruding as existing transfer apparatus, just easily lacquer painting is caused to rupture running into uneven place.
As preferably of the present invention, described graining roll group comprises the first steel rider, the second steel rider and the 3rd steel rider that set gradually, and the outer circumference surface of the first described steel rider, the second described steel rider and the 3rd described steel rider is provided with stamp line; The pattern of upper, middle and lower three parts of the linear trisection of the described stamp line corresponding same printed patterns of difference in the direction of motion of described graining roll of the first described steel rider, described second steel rider and described 3rd steel rider.
As preferably of the present invention, described step 4 is carried out when the prime coat described in described step 3 is solid state.
As preferably of the present invention, enamel-cover of shaping described in described step 4 draws together adhesive agent, colouring agent and mould release.
The present invention has following beneficial effect:
The present invention have technique realize simple, automaticity stereoeffect that is high, transfer printing is good, decorative pattern texture nature, repetitive rate is low and do not damage the good advantage of lacquer painting surface abrasion resistance.
Accompanying drawing explanation
Fig. 1 is graining roll group structural representation of the present invention;
Fig. 2 is the stamp line structural representation of graining roll group of the present invention;
In figure, 1-base material; 2-covering layer; 3-prime coat; 4-graining roll group; 401-first steel rider; 402-second steel rider; 403-the 3rd steel rider; 4a-central shaft; 4b-steel ring; 4c-radial bars; 4d-copper plate layer; 4e-stamp line; A-first recess; B-first protuberance; C-second recess.
Detailed description of the invention
Below method of the present invention is described in detail and by reference to the accompanying drawings the structure related in the present invention is described in further detail simultaneously.
Specific embodiments of the invention are as follows:
As shown in Figure 1 to Figure 2, the embodiment of the present invention is included in the five steps that base material 1 completes,
Step one, carries out the coating of twice cover material on the surface of the substrate 1, is formed and hides the color of the surperficial furuncle of base material 1 and the covering layer 2 of profile.Cover material is putty.
Step 2, by smooth for the surface finish of covering layer 2.
Step 3, is coated with common priming paint and wear-resistant primer on the surface of covering layer 2, forms prime coat 3.When carrying out step 4 after solidifying priming paint state, solidification can use dries and naturally dries two kinds of modes.
Step 4, carries out decorative pattern transfer printing by graining roll group 4 pairs of prime coat 3 surfaces, and on-plane surface transfer printing base material 1 being carried out to pattern forms printing base material 1.The outer circumference surface that graining roll group 4 comprises the first steel rider 401, second steel rider 402 and the 3rd steel rider 403, first steel rider 401, second steel rider 402 and the 3rd steel rider 403 set gradually is provided with stamp line 4e; The pattern of upper, middle and lower three parts of the linear trisection of the stamp line 4e corresponding same printed patterns of difference in the direction of motion of graining roll of the first steel rider 401, second steel rider 402 and the 3rd steel rider 403.Concrete technique is as follows: base material 1 is with the speed charging of 5m/min on lathe, and carry out lubricant mist sprinkling at graining roll group 4 outer surface, the temperature of lubricant mist is 60-65 DEG C, and the outer circumference surface temperature of graining roll group 4 remains between 66-68 DEG C simultaneously.The pressure that graining roll group 4 is produced by weight own carries out compacting transfer to prime coat 3.Copperplate layer 4d on first steel rider 401 rotates and prints out the first recess a, copperplate layer 4d on second steel rider 402 rotates and prints out the first protuberance b, copperplate layer 4d on 3rd steel rider 403 rotates and prints out the second recess c, by the continuous rotation on the first steel rider 401, second steel rider 402, the 3rd steel rider 403, stamp line 4e on copperplate layer 4d is printed on base material 1 to version to decorative pattern rotation tri-times, is formed and there is visual stereoscopic effect of decorative patterns.
Step 5, on printing element 1, coating sizing paint, makes surface printing floor.Sizing enamel-cover draws together adhesive agent, colouring agent and mould release.
Embodiment recited above is only be described the preferred embodiment of the present invention, not limits the spirit and scope of the present invention.Under the prerequisite not departing from design concept of the present invention; the various modification that this area ordinary person makes technical scheme of the present invention and improvement; all should drop into protection scope of the present invention, the technology contents of request protection of the present invention, all records in detail in the claims.
Claims (10)
1. a timber floor printing process, is characterized in that: be included in the five steps that base material (1) completes,
Step one, the surface of described base material (1) is at least carried out the coating of a cover material, is formed and hides the color of described base material (1) surperficial furuncle and the covering layer (2) of profile;
Step 2, by smooth for the surface finish of described covering layer (2);
Step 3, is coated with common priming paint and wear-resistant primer on the surface of described covering layer (2), forms prime coat (3);
Step 4, carries out decorative pattern transfer printing by graining roll group (4) to described prime coat (3) surface, and the on-plane surface transfer printing described base material (1) being carried out to pattern forms printing base material (1);
Step 5, at described printing element (1) upper coating sizing paint, makes surface printing floor.
2. a kind of timber floor printing process according to claim 1, is characterized in that: the coating carrying out twice cover material in described step one on the surface of described base material (1).
3. a kind of timber floor printing process according to claim 1, is characterized in that: the cover material described in described step one is putty.
4. a kind of timber floor printing process according to claim 1, is characterized in that: the graining roll group (4) described in described step 4 carries out lubricant mist sprinkling at described graining roll group (4) outer surface while carrying out decorative pattern transfer printing to described prime coat (3) surface.
5. a kind of timber floor printing process according to claim 4, is characterized in that: the temperature of described lubricant mist is 60-65 DEG C.
6. a kind of timber floor printing process according to claim 1 or 4, is characterized in that: the outer circumference surface temperature of the graining roll group (4) described in when the graining roll group (4) described in described step 4 carries out decorative pattern transfer printing to described prime coat (3) surface remains between 66-68 DEG C.
7. a kind of timber floor printing process according to claim 1 or 4, is characterized in that: the pressure that described graining roll group (4) is produced by weight own carries out compacting transfer to described prime coat (3).
8. a kind of timber floor printing process according to claim 1 or 4, it is characterized in that: described graining roll group (4) comprises the first steel rider (401), the second steel rider (402) and the 3rd steel rider (403) that set gradually, the outer circumference surface of described the first steel rider (401), described the second steel rider (402) and the 3rd described steel rider (403) is provided with stamp line (4e); The pattern of upper, middle and lower three parts of the linear trisection of described stamp line (4e) the corresponding same printed patterns of difference in the direction of motion of described graining roll of described the first steel rider (401), described second steel rider (402) and described 3rd steel rider (403).
9. a kind of timber floor printing process according to claim 1, is characterized in that: described step 4 at the prime coat (3) described in described step 3 for carrying out during solid state.
10. a kind of timber floor printing process according to claim 1, is characterized in that: enamel-cover of shaping described in described step 4 draws together adhesive agent, colouring agent and mould release.