CN105317185A - Technology for producing UV transfer inner wall decorative board - Google Patents
Technology for producing UV transfer inner wall decorative board Download PDFInfo
- Publication number
- CN105317185A CN105317185A CN201510888389.2A CN201510888389A CN105317185A CN 105317185 A CN105317185 A CN 105317185A CN 201510888389 A CN201510888389 A CN 201510888389A CN 105317185 A CN105317185 A CN 105317185A
- Authority
- CN
- China
- Prior art keywords
- calcium silicate
- silicate board
- sanding
- roller
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a technology for producing a UV transfer inner wall decorative board and belongs to the field of decorative board processing. The technology includes the steps that sanding and dust removing are carried out on a calcium silicate board for three times; preheating is conducted; waterproof sealing is carried out; permeable sealing is carried out; back coating is conducted; putty is coated twice in a rolling mode; primer is coated twice in a rolling and spraying mode; UV glue is coated twice in a rolling mode; UV colored paint is coated in a rolling mode; surface paint is painted in a spraying mode twice to form the UV transfer inner wall decorative board; film covering and packaging are conducted. Patterns, colors and glossiness of the UV transfer inner wall decorative board produced through the technology can be customized flexibly, surface smoothness is high, paint films are full, and the board is environmentally friendly, healthy, good in durability, waterproof and resistanct to scratching, acid, base and corrosion and does not fade.
Description
Technical field
The present invention relates to a kind of production technology of UV transfer printing inner wall decoration plate, belong to decorative panel manufacture field.
Background technology
UV transfer printing inner wall decoration plate is a kind of Novel interior wall dalle grown up in recent years, and transfer technique is applied to decorative panel by it, and can copy on substrate by any decorative pattern, similarity is high, enhances ornamental.Red long paint (Changzhou) Co., Ltd (CN201310066666.2) of history discloses a kind of production technology of UV fluorine carbon decorative panel, comprising: carry out positive and negative polishing to decorating board; The decorating board of having polished is carried out dust removal process; The mode of roller coat is adopted to carry out UV infiltration to decorating board; After having permeated, surface finish, smooth and dust removal process are carried out to decorating board; After completing above-mentioned process, decorating board applies UV putty layer; At UV putty layer top roll priming layer, and be cured; Showering priming paint again on prime coat, and be cured, form the priming paint face before transfer printing; Adopt on the priming paint face of transfer technique before transfer printing and process, form transfer decorative plate.Any decorative pattern copies on substrate by this invention, and finished product similarity is high, and manufacture craft is simple, long service life.The present invention on this basis, significant improvement has been carried out to preparation technology, the UV transfer printing inner wall decoration plate pattern of production, color, glossiness not only can arbitrarily be customized, and surface flatness is high, paint film is plentiful, good endurance, colour-fast, good waterproof performance, scratch-resistant, acid and alkali-resistance are anticorrosive, environment protection health.
Summary of the invention
The invention provides a kind of production technology of UV transfer printing inner wall decoration plate, the UV transfer printing inner wall decoration plate pattern of production, color, glossiness not only can arbitrarily be customized, and surface flatness is high, paint film is plentiful, good endurance, colour-fast, good waterproof performance, scratch-resistant, acid and alkali-resistance are anticorrosive, environment protection health.
To achieve these goals, the technical solution used in the present invention is: the production technology providing a kind of UV transfer printing inner wall decoration plate, comprises the following steps:
(1) three sanding, dedusting: adopt two roller sander to carry out three sandings to calcium silicate board, after sanding, calcium silicate board is sent to dust removal machine by conveyor track, by the fiber roller cleaning dust rolled in dust removal machine;
(2) preheating: the calcium silicate board after dedusting is sent to levelling drying alley by conveyor track, to calcium silicate board heating, is convenient to the attachment of next procedure water-protected enclosure priming paint;
(3) water-protected enclosure: the calcium silicate board surface after sanding is coated with last layer seal coat, then through being heating and curing, form waterproofing course, heating-up temperature is no more than 55 DEG C;
(4) infiltration is closed: after the calcium silicate board sanding after water-protected enclosure, dedusting, be sent to roll coater by conveyor track, be applied to by leak-proof paint on calcium silicate board, and levelling is dry, forms impervious barrier;
(5) back of the body is coated with: calcium silicate board is sent to roll coater by conveyor track, and UV priming paint is applied to the calcium silicate board back side, UV photocuring;
(6) roller coat twice putty: calcium silicate board is sent to roll coater by conveyor track, roller coat UV putty, UV solidifies, then roller coat one deck putty, sanding after UV photocuring, dedusting;
(7) roller coat, showering twice priming paint: first roller coat prime coat in UV putty layer, uses curtain coater showering priming paint, sanding after UV photocuring, dedusting again after solidification;
(8) roller coat twice UV glue: transfer printing height emulation UV F-C paint after roller coat UV glue, then roller coat UV glue, levelling is dry, UV photocuring;
(9) roller coat UV colored paint: roller coat UV colored paint, levelling is dry, UV photocuring;
(10) showering twice UV finish paint: curtain coater showering twice UV finish paint, levelling is dry, UV photocuring, and normal temperature cools, and forms UV transfer printing inner wall decoration plate;
(11) overlay film packaging: plastic sheeting is invested on UV transfer printing inner wall decoration plate by overlay film film cutting machine, and redundance plastic sheeting is cut, completes packaging.
Above-mentioned a kind of UV transfer printing inner wall decoration plate, in step (1) three sanding, first select preliminary roller 80 object abrasive band to the back side sanding of calcium silicate board, next selects preliminary roller 80 object abrasive band to the front sanding of calcium silicate board, third time sanding is the front sanding to calcium silicate board, preliminary roller selects 120 object abrasive bands, and rear roller selects 180 object abrasive bands.
Above-mentioned a kind of UV transfer printing inner wall decoration plate, heated calcium silicate board by microwave in the described levelling drying of step (2), step (4), (8), (9), (10) described levelling drying are heated calcium silicate board by infrared light.
Above-mentioned a kind of UV transfer printing inner wall decoration plate, 240 object abrasive bands are adopted in the sanding of the described putty coating of step (6), adopt 320 object abrasive bands in the sanding of the described priming paint coating of step (7), putty and the priming paint consumption of often opening plate are respectively 0.15Kg.
Technique scheme tool has the following advantages or beneficial effect:
(1) adopt transfer technique, and strict technology controls decorative panel pattern, color, glossiness can arbitrarily be customized.
(2) adopt multiple tracks sanding, dust collecting process, twice UV putty/UV priming paint/UV glue/UV finish paint technique, make surface flatness high, paint film is plentiful, and decorative effect is strong.
(3) substrate is calcium silicate board, not containing radioactive substance; The UV F-C paint of environmental protection is as application raw material, and manufacturing process does not use solvent, not containing the material that benzene, formaldehyde etc. are harmful, and environment protection health, green safety.
(4) the UV coating structure through the formation of multiple tracks UV curing process is fine and close, hardness is high, scratch-resistant, and remain unchanged for a long period of time shape, prolonged colour-fast.
(5) unique water-protected enclosure, infiltration confining bed, add the compact curing film that UV plate paint and ultraviolet generation chemical reaction are formed, and makes this product waterproof effect strong, can resist the corrosion of various soda acid thimerosal.
Detailed description of the invention
Below preferred embodiment of the present invention is described in detail, can be easy to make advantages and features of the invention be those skilled in the art will recognize that thus make more explicit defining to protection scope of the present invention.
Embodiment 1:
A production technology for UV transfer printing inner wall decoration plate, comprises the following steps:
(1) three sanding, dedusting: adopt two roller sander to carry out three sandings to calcium silicate board, first select preliminary roller 80 object abrasive band to the back side sanding of calcium silicate board, next selects preliminary roller 80 object abrasive band to the front sanding of calcium silicate board, third time sanding is the front sanding to calcium silicate board, preliminary roller selects 120 object abrasive bands, rear roller selects 180 object abrasive bands, after sanding, calcium silicate board is sent to dust removal machine by conveyor track, by the fiber roller cleaning dust rolled in dust removal machine;
(2) preheating: the calcium silicate board after dedusting is sent to levelling drying alley by conveyor track, to calcium silicate board heating using microwave, is convenient to the attachment of next procedure water-protected enclosure priming paint;
(3) water-protected enclosure: the calcium silicate board surface after sanding is coated with last layer seal coat, then through being heating and curing, forming waterproofing course, often opening the seal coat consumption 0.1Kg of plate, heating-up temperature 55 DEG C;
(4) infiltration is closed: after the calcium silicate board sanding after water-protected enclosure, dedusting, be sent to roll coater by conveyor track, be applied to by leak-proof paint on calcium silicate board, be sent to levelling drying alley, adopts infrared light to heat calcium silicate board, forms impervious barrier;
(5) back of the body is coated with: calcium silicate board is sent to roll coater by conveyor track, and UV priming paint is applied to the calcium silicate board back side, UV photocuring;
(6) roller coat twice putty: calcium silicate board is sent to roll coater by conveyor track, roller coat UV putty, UV photocuring, then roller coat one deck putty, adopt 240 object abrasive band sandings, dedusting after UV photocuring, the putty consumption often opening plate is 0.15Kg;
(7) roller coat, showering twice priming paint: first roller coat prime coat in UV putty layer, uses curtain coater showering priming paint again, adopts 320 object abrasive band sandings, dedusting after UV photocuring after solidification, the priming paint consumption often opening plate is 0.15Kg;
(8) roller coat twice UV glue: be solidificated on calcium silicate board by wood grain UV fluorocarbon film transfer printing process after roller coat UV glue, then roller coat UV glue, be sent to levelling drying alley, adopts infrared light heating, UV photocuring;
(9) roller coat UV colored paint: roller coat UV colored paint, is sent to levelling drying alley, adopts infrared light heating, UV photocuring;
(10) showering twice UV finish paint: curtain coater showering twice UV finish paint, is sent to levelling drying alley, adopt infrared light heating, UV photocuring, normal temperature cools, and forms UV transfer printing inner wall decoration plate;
(11) overlay film packaging: plastic sheeting is invested on UV transfer printing inner wall decoration plate by overlay film film cutting machine, and redundance plastic sheeting is cut, completes packaging.
Embodiment 2:
A production technology for UV transfer printing inner wall decoration plate, comprises the following steps:
(1) three sanding, dedusting: adopt two roller sander to carry out three sandings to calcium silicate board, first select preliminary roller 80 object abrasive band to the back side sanding of calcium silicate board, next selects preliminary roller 80 object abrasive band to the front sanding of calcium silicate board, third time sanding is the front sanding to calcium silicate board, preliminary roller selects 120 object abrasive bands, rear roller selects 180 object abrasive bands, after sanding, calcium silicate board is sent to dust removal machine by conveyor track, by the fiber roller cleaning dust rolled in dust removal machine;
(2) preheating: the calcium silicate board after dedusting is sent to levelling drying alley by conveyor track, to calcium silicate board heating using microwave, is convenient to the attachment of next procedure water-protected enclosure priming paint;
(3) water-protected enclosure: the calcium silicate board surface after sanding is coated with last layer seal coat, then through being heating and curing, forming waterproofing course, often opening the seal coat consumption 0.1Kg of plate, heating-up temperature 50 DEG C;
(4) infiltration is closed: after the calcium silicate board sanding after water-protected enclosure, dedusting, be sent to roll coater by conveyor track, be applied to by leak-proof paint on calcium silicate board, be sent to levelling drying alley, adopts infrared light to heat calcium silicate board, forms impervious barrier;
(5) back of the body is coated with: calcium silicate board is sent to roll coater by conveyor track, and UV priming paint is applied to the calcium silicate board back side, UV photocuring;
(6) roller coat twice putty: calcium silicate board is sent to roll coater by conveyor track, roller coat UV putty, UV solidifies, then roller coat one deck putty, and adopt 240 object abrasive band sandings, dedusting after UV photocuring, the putty consumption often opening plate is 0.15Kg;
(7) roller coat, showering twice priming paint: first roller coat prime coat in UV putty layer, uses curtain coater showering priming paint again, adopts 320 object abrasive band sandings, dedusting after UV photocuring after solidification, the priming paint consumption often opening plate is 0.15Kg;
(8) roller coat twice UV glue: be solidificated on calcium silicate board by imitative stone material UV fluorocarbon film transfer printing process after roller coat UV glue, then roller coat UV glue, be sent to levelling drying alley, adopts infrared light heating, UV photocuring;
(9) roller coat UV colored paint: roller coat UV colored paint, is sent to levelling drying alley, adopts infrared light heating, solidification;
(10) showering twice UV finish paint: curtain coater showering twice UV finish paint, is sent to levelling drying alley, adopt infrared light heating, solidification, normal temperature cools, and forms UV transfer printing inner wall decoration plate;
(11) overlay film packaging: plastic sheeting is invested on UV transfer printing inner wall decoration plate by overlay film film cutting machine, and redundance plastic sheeting is cut, completes packaging.
Claims (4)
1. a production technology for UV transfer printing inner wall decoration plate, is characterized in that, comprise the following steps:
(1) three sanding, dedusting: adopt two roller sander to carry out three sandings to calcium silicate board, after sanding, calcium silicate board is sent to dust removal machine by conveyor track, by the fiber roller cleaning dust rolled in dust removal machine;
(2) preheating: the calcium silicate board after dedusting is sent to levelling drying alley by conveyor track, to calcium silicate board heating, is convenient to the attachment of next procedure water-protected enclosure priming paint;
(3) water-protected enclosure: the calcium silicate board surface after sanding is coated with last layer seal coat, then through being heating and curing, form waterproofing course, heating-up temperature is no more than 55 DEG C;
(4) infiltration is closed: after the calcium silicate board sanding after water-protected enclosure, dedusting, be sent to roll coater by conveyor track, be applied to by leak-proof paint on calcium silicate board, and levelling is dry, forms impervious barrier;
(5) back of the body is coated with: calcium silicate board is sent to roll coater by conveyor track, and UV priming paint is applied to the calcium silicate board back side, UV photocuring;
(6) roller coat twice putty: calcium silicate board is sent to roll coater by conveyor track, roller coat UV putty, UV solidifies, then roller coat one deck putty, sanding after UV photocuring, dedusting;
(7) roller coat, showering twice priming paint: first roller coat prime coat in UV putty layer, uses curtain coater showering priming paint, sanding after UV photocuring, dedusting again after solidification;
(8) roller coat twice UV glue: transfer printing height emulation UV F-C paint after roller coat UV glue, then roller coat UV glue, levelling is dry, UV photocuring;
(9) roller coat UV colored paint: roller coat UV colored paint, levelling is dry, UV photocuring;
(10) showering twice UV finish paint: curtain coater showering twice UV finish paint, levelling is dry, UV photocuring, and normal temperature cools, and forms UV transfer printing inner wall decoration plate;
(11) overlay film packaging: plastic sheeting is invested on UV transfer printing inner wall decoration plate by overlay film film cutting machine, and redundance plastic sheeting is cut, completes packaging.
2. a kind of UV transfer printing inner wall decoration plate according to claim 1, it is characterized in that, in step (1) three sanding, first select preliminary roller 80 object abrasive band to the back side sanding of calcium silicate board, next selects preliminary roller 80 object abrasive band to the front sanding of calcium silicate board, third time sanding is the front sanding to calcium silicate board, preliminary roller selects 120 object abrasive bands, and rear roller selects 180 object abrasive bands.
3. a kind of UV transfer printing inner wall decoration plate according to claim 1, it is characterized in that, heated calcium silicate board by microwave in the described levelling drying of step (2), step (4), (8), (9), (10) described levelling drying are heated calcium silicate board by infrared light.
4. a kind of UV transfer printing inner wall decoration plate according to claim 1, it is characterized in that, 240 object abrasive bands are adopted in the sanding of the described putty coating of step (6), adopt 320 object abrasive bands in the sanding of the described priming paint coating of step (7), putty and the priming paint consumption of often opening calcium silicate board are respectively 0.15Kg.