CN103419538B - A kind of PET polyester transfer film is transferred to the production technology of sheet metal - Google Patents
A kind of PET polyester transfer film is transferred to the production technology of sheet metal Download PDFInfo
- Publication number
- CN103419538B CN103419538B CN201310310374.9A CN201310310374A CN103419538B CN 103419538 B CN103419538 B CN 103419538B CN 201310310374 A CN201310310374 A CN 201310310374A CN 103419538 B CN103419538 B CN 103419538B
- Authority
- CN
- China
- Prior art keywords
- sheet metal
- transfer film
- pet polyester
- transferred
- production technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of PET polyester transfer film and be transferred to the production technology of sheet metal, comprise the following steps: step A: after sheet metal is polished again through oil removing, pickling, clean, dry;Step B: be put on photocuring transfer interpreter, mix up speed of production;Step C: roller coat glue does primer, dries through lamp box, makes glue be in leather hard;Step D: by sheet metal and PET polyester transfer film pressing, make the patterned layer of PET polyester transfer film firmly be pasted onto on sheet metal;Step E: through infrared lamp illumination curing, PET film layer is torn, makes PET polyester transfer film pattern transfer on sheet metal;Step F: the roller coat colored varnish, uses infrared lamp illumination curing;Step G: transferred, obtains finished product.The product wood grain, the bag level effect that are obtained by the present invention are true to nature, easy to operate, substantially increase work efficiency, save production cost, have filled up the blank of industry.
Description
Technical field
The present invention relates to thermal transfer field, a kind of PET polyester transfer film is transferred to the production technology of sheet metal.
Background technology
By existing production technology, PET polyester transfer film being transferred on sheet metal, dim design, wood grain, bag pattern are the most true to nature, environmental protection, it is impossible to meet and use requirement.
Therefore, prior art has yet to be improved and developed.
Summary of the invention
It is an object of the invention to provide a kind of PET polyester transfer film and be transferred to the production technology of sheet metal, aim to solve the problem that and by existing production technology, PET polyester transfer film is transferred on sheet metal, dim design, wood grain, bag pattern are the most true to nature, environmental protection, it is impossible to meet and use the problem required.
Technical scheme is as follows: a kind of PET polyester transfer film is transferred to the production technology of sheet metal, wherein, specifically includes following steps:
Step A: after sheet metal is polished again through oil removing, pickling, clean, dry;
Step B: step A is obtained sheet metal be put on photocuring transfer interpreter, mix up speed of production;
Step C: roller coat glue does primer on sheet metal again, dries through lamp box, makes the glue on sheet metal be in leather hard;
Step D: glue is in sheet metal and the PET polyester transfer film pressing of leather hard, makes the patterned layer of PET polyester transfer film firmly be pasted onto on sheet metal;
Step E: again sheet metal through infrared lamp illumination curing, PET film layer is torn, makes PET polyester transfer film pattern transfer on sheet metal;
Step F: the roller coat colored varnish on sheet metal again, uses infrared lamp illumination curing;
Step G: transferred, obtains finished product.
Described production technology PET polyester transfer film being transferred to sheet metal, wherein, described step B speed of production is between 5 ms/min-15 ms/min.
Described production technology PET polyester transfer film being transferred to sheet metal, wherein, the thickness of described step C roller coat glue is between 3 μm-8 μm.
Described production technology PET polyester transfer film being transferred to sheet metal, wherein, between the energy of described step C lamp box 24 joules-50 joules.
Described production technology PET polyester transfer film being transferred to sheet metal, wherein, the infrared lamp in described step E and step F is UV infrared lamp.
Described production technology PET polyester transfer film being transferred to sheet metal, wherein, between the energy of the infrared lamp in described step E and step F 900 joules-1300 joules.
Described production technology PET polyester transfer film being transferred to sheet metal, wherein, in described step F, the colored varnish of roller coat is the UV colored varnish.
Described production technology PET polyester transfer film being transferred to sheet metal, wherein, between roller coat thickness 5 μm-15 μm of the described step F colored varnish.
Described production technology PET polyester transfer film being transferred to sheet metal, wherein, the sheet metal described in step A is iron plate sheet material or stainless steel materials.
Described production technology PET polyester transfer film being transferred to sheet metal, wherein, the sheet metal described in step A is aluminium-plastic panel sheet material or aluminum veneer sheet material.
Beneficial effects of the present invention: the present invention is transferred to the production technology of sheet metal by providing a kind of PET polyester transfer film, the product wood grain, the bag level effect that are obtained by this production technology are true to nature, easy to operate, substantially increase work efficiency, save production cost, fill up the blank of industry;This production technology makes PET polyester transfer film firmly be pasted onto on sheet metal to be forever difficult to come off, and substantially increases fixture, inside and outside wallboard and ceiling decoration industry sheet metal service life.
Accompanying drawing explanation
Fig. 1 is the flow chart of steps of the production technology in the present invention, PET polyester transfer film being transferred to sheet metal.
Detailed description of the invention
For making the purpose of the present invention, technical scheme and advantage clearer, clear and definite, the present invention is described in more detail for the embodiment that develops simultaneously referring to the drawings.
As it is shown in figure 1, be the flow chart of steps of the production technology in the present invention, PET polyester transfer film being transferred to metal.The production technology that described PET polyester transfer film is transferred to sheet metal specifically includes following steps:
Step A: after sheet metal is polished again through oil removing, pickling, clean, dry;
Step B: step A is obtained sheet metal be put on photocuring transfer interpreter, mix up speed of production;
Step C: roller coat glue does primer on sheet metal again, dries through lamp box, makes the glue on sheet metal be in leather hard;
Step D: glue is in sheet metal and the PET polyester transfer film pressing of leather hard, makes the patterned layer of PET polyester transfer film firmly be pasted onto on sheet metal;
Step E: again sheet metal through infrared lamp illumination curing, PET film layer is torn, makes PET polyester transfer film pattern transfer on sheet metal;
Step F: the roller coat colored varnish on sheet metal again, uses infrared lamp illumination curing;
Step G: transferred, obtains finished product.
The production technology that this PET polyester transfer film is transferred to metal is applicable to various metals sheet material, such as iron plate, and aluminium-plastic panel, aluminum veneer, corrosion resistant plate, etc..
Drawing through many experiments, the product effect that described step B speed of production obtains between 5 ms/min-15 ms/min is best.
Drawing through many experiments, the product effect that the thickness of described step C roller coat glue obtains between 3 μm-8 μm is best.
Drawing through many experiments, the product effect obtained between the energy of described step C lamp box 24 joules-50 joules is best.
In the present embodiment, the infrared lamp in described step E and step F is UV infrared lamp.
Drawing through many experiments, the product effect obtained between the energy of described step E infrared lamp 900 joules-1300 joules is best.
Drawing through many experiments, the product effect obtained between the energy of described step F infrared lamp 900 joules-1300 joules is best.
In the present embodiment, in described step F, the colored varnish of roller coat is the UV colored varnish.
Drawing through many experiments, the product effect obtained between roller coat thickness 5 μm-15 μm of the described step F colored varnish is best.
Embodiment 1
Step A: after iron plate sheet material is polished again through oil removing, pickling, clean, dry;Step B: step 1 is obtained iron plate sheet material be put on photocuring transfer interpreter, speed of production is 5 ms/min;Step C: the glue of roller coat thickness 3 μm does primer on iron plate sheet material again, the lamp box through energy 25 joules is dried, and makes the glue on iron plate sheet material be in leather hard;Step D: glue is in iron plate sheet material and the PET polyester transfer film pressing of leather hard, makes the patterned layer of PET polyester transfer film firmly be pasted onto on iron plate sheet material;Step E: again iron plate sheet material through the UV infrared lamp illumination curing of energy 900 joules, PET film layer is torn, makes PET polyester transfer film pattern transfer on iron plate sheet material;Step F: the UV colored varnish of roller coat thickness 5 μm on iron plate sheet material again, by the UV infrared lamp illumination curing of energy 900 joules;Step G: transferred, obtains finished product.
The product wood grain, the bag level effect that are obtained by this production technology are true to nature, easy to operate, substantially increase work efficiency, save production cost, have filled up the blank of industry;This production technology makes PET polyester transfer film firmly be pasted onto on sheet metal to be forever difficult to come off, and substantially increases fixture, inside and outside wallboard and ceiling decoration industry sheet metal service life.
Embodiment 2
Step A: after aluminum veneer sheet material is polished again through oil removing, pickling, clean, dry;Step B: step 1 is obtained aluminum veneer sheet material be put on photocuring transfer interpreter, speed of production is 10 ms/min;Step C: the glue of roller coat thickness 5 μm does primer on aluminum veneer sheet material again, the lamp box through energy 40 joules is dried, and makes the glue on aluminum veneer sheet material be in leather hard;Step D: glue is in aluminum veneer sheet material and the PET polyester transfer film pressing of leather hard, makes the patterned layer of PET polyester transfer film firmly be pasted onto on aluminum veneer sheet material;Step E: again aluminum veneer sheet material through the UV infrared lamp illumination curing of energy 1100 joules, PET film layer is torn, makes PET polyester transfer film pattern transfer on aluminum veneer sheet material;Step F: the UV colored varnish of roller coat thickness 10 μm on aluminum veneer sheet material again, by the UV infrared lamp illumination curing of energy 1300 joules;Step G: transferred, obtains finished product.
The product wood grain, the bag level effect that are obtained by this production technology are true to nature, easy to operate, substantially increase work efficiency, save production cost, have filled up the blank of industry;This production technology makes PET polyester transfer film firmly be pasted onto on sheet metal to be forever difficult to come off, and substantially increases fixture, inside and outside wallboard and ceiling decoration industry sheet metal service life.
Embodiment 3
Step A: after corrosion resistant plate sheet material is polished again through oil removing, pickling, clean, dry;Step B: step 1 is obtained corrosion resistant plate sheet material be put on photocuring transfer interpreter, speed of production is 15 ms/min;Step C: the glue of roller coat thickness 8 μm does primer on corrosion resistant plate sheet material again, the lamp box through energy 50 joules is dried, and makes the glue on corrosion resistant plate sheet material be in leather hard;Step D: glue is in corrosion resistant plate sheet material and the PET polyester transfer film pressing of leather hard, makes the patterned layer of PET polyester transfer film firmly be pasted onto on corrosion resistant plate sheet material;Step E: again corrosion resistant plate sheet material through the UV infrared lamp illumination curing of energy 1300 joules, PET film layer is torn, makes PET polyester transfer film pattern transfer on corrosion resistant plate sheet material;Step F: the UV colored varnish of roller coat thickness 15 μm on corrosion resistant plate sheet material again, by the UV infrared lamp illumination curing of energy 1100 joules;Step G: transferred, obtains finished product.
The product wood grain, the bag level effect that are obtained by this production technology are true to nature, easy to operate, substantially increase work efficiency, save production cost, have filled up the blank of industry;This production technology makes PET polyester transfer film firmly be pasted onto on sheet metal to be forever difficult to come off, and substantially increases fixture, inside and outside wallboard and ceiling decoration industry sheet metal service life.
It should be appreciated that the application of the present invention is not limited to above-mentioned citing, for those of ordinary skills, can be improved according to the above description or convert, all these modifications and variations all should belong to the protection domain of claims of the present invention.
Claims (5)
1. production technology PET polyester transfer film being transferred to sheet metal, it is characterised in that
Specifically include following steps:
Step A: after sheet metal is polished again through oil removing, pickling, clean, dry;
Step B: step A is obtained sheet metal be put on photocuring transfer interpreter, mix up speed of production;
Step C: roller coat glue does primer on sheet metal again, dries through lamp box, makes the glue on sheet metal be in leather hard;
Step D: glue is in sheet metal and the PET polyester transfer film pressing of leather hard, makes the patterned layer of PET polyester transfer film firmly be pasted onto on sheet metal;
Step E: again sheet metal through infrared lamp illumination curing, PET film layer is torn, makes PET polyester transfer film pattern transfer on sheet metal;
Step F: the roller coat colored varnish on sheet metal again, uses infrared lamp illumination curing;
Step G: transferred, obtains finished product;
Wherein, the infrared lamp in described step E and F is UV infrared lamp, and the energy of infrared lamp is between 900 joules-1300 joules;The thickness of described step C roller coat glue is between 3 μm-8 μm;The energy of described step C lamp box 24 joule-50
Between Jiao Er;Between roller coat thickness 5 μm-15 μm of the described step F colored varnish.
The most according to claim 1 PET polyester transfer film is transferred to the production technology of sheet metal, it is characterised in that described step B speed of production is between 5 ms/min-15 ms/min.
The most according to claim 1 PET polyester transfer film is transferred to the production technology of sheet metal, it is characterised in that in described step F, the colored varnish of roller coat is the UV colored varnish.
4. according to production technology PET polyester transfer film being transferred to sheet metal described in claim 1-3 any one, it is characterised in that the sheet metal described in step A is iron plate sheet material or stainless steel materials.
5. according to production technology PET polyester transfer film being transferred to sheet metal described in claim 1-3 any one, it is characterised in that the sheet metal described in step A is aluminium-plastic panel sheet material or aluminum veneer sheet material.