CN103409036A - 一种浅灰色闪光漆的配方 - Google Patents
一种浅灰色闪光漆的配方 Download PDFInfo
- Publication number
- CN103409036A CN103409036A CN2013103012843A CN201310301284A CN103409036A CN 103409036 A CN103409036 A CN 103409036A CN 2013103012843 A CN2013103012843 A CN 2013103012843A CN 201310301284 A CN201310301284 A CN 201310301284A CN 103409036 A CN103409036 A CN 103409036A
- Authority
- CN
- China
- Prior art keywords
- resin
- pearlescence
- green
- aluminium powder
- mixing solutions
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种浅灰色闪光漆的配方,各组分的质量百分比为:37A铝粉、37S铝粉、紫珠光粉、绿珠光粉、黑浆、H-01树脂、585-1树脂、硝化棉、环氧树脂、丁酯、钛青兰、466助剂,本发明的有益效果:本发明采用3种树脂作为混合,尤其利用环氧树脂的高聚特性来增加油漆的附着力,在施工过程中更容易附着在装饰面上,提高了工作效率,节约成本,且多种颜料混合而得的浅灰色应用范围广泛。
Description
技术领域
本发明涉及到油漆涂料领域,具体涉及一种浅灰色闪光漆的配方。
背景技术
随着人们生活水平的不断提高,人们对生活质量的要求也在不断提高,市场上对高质量、高档次颜料的需求也越来越大。但是油漆本身的性能包括耐用性、施工简便与否、附着力三方面,随着人工成本的逐渐提高尤其装修师傅的施工价格的指数性增长,施工简便越来越成为人们考虑的首要问题。
发明内容
为了达到施工过程中施工简单的效果,本发明提供了一种浅灰色闪光漆的配方:具体方案如下:
一种浅灰色闪光漆的配方,由以下质量百分比的成份组成:
37A铝粉 3.5-4.5%
37S铝粉 0.3-0.4%
紫珠光粉 0.6-0.7%
绿珠光粉 1-2%
黑浆 4-6%
H-01树脂 35-40%
585-1树脂 18-23%
硝化棉 10-15%
环氧树脂 8-12%
丁酯 6-9%
钛青兰 0.3-0.5%
466助剂 0.1%。
进一步的改进在于:由以下具体质量百分比的成份组成:
37A铝粉 4%
37S铝粉 0.35%
紫珠光粉 0.65%
绿珠光粉 1.5%
黑浆 5%
H-01树脂 38%
585-1树脂 20%
硝化棉 12%
环氧树脂 10%
丁酯 8%
钛青兰 0.4%
466助剂 0.1%。
一种根据上述配方组成来制备油漆的方法,其具体步骤如下:
步骤一:将硝化棉、H-01树脂、585-1树脂、环氧树脂用丁酯溶解得到混合溶液;
步骤二:将37A铝粉、37S铝粉、钛青兰加入步骤一所得的混合溶液中,搅拌均匀得到混合溶液;
步骤三:将紫珠光粉、绿珠光粉、黑浆加入到步骤二所得的混合溶液中,搅拌均匀得到混合溶液;
步骤四:向步骤三所得的混合溶液中缓慢加入466助剂在50-55℃下搅拌5小时,静置,得到合格产品。
本发明的有益效果:本发明采用H-01树脂、585-1树脂、环氧树脂这三种树脂作为混合,尤其利用环氧树脂的高聚特性来增加油漆的附着力,在施工过程中更容易附着在装饰面上,提高了工作效率,节约成本,且多种颜料混合而得的浅灰色应用范围广泛。
具体实施方式
为了加深本发明的理解,下面将结合实施例对本发明做进一步详细描述。
实施例1:
本实施例提供一种浅灰色闪光漆的配方,由以下质量百分比的成份组成:
37A铝粉 4.5%
37S铝粉 0.3%
紫珠光粉 0.6%
绿珠光粉 2%
黑浆 4%
H-01树脂 35%
585-1树脂 23%
硝化棉 12%
环氧树脂 10%
丁酯 8%
钛青兰 0.5%
466助剂 0.1%。
根据上述配方组成来制备油漆的方法,具体步骤如下:
步骤一:将硝化棉、H-01树脂、585-1树脂、环氧树脂用丁酯溶解得到混合溶液;
步骤二:将37A铝粉、37S铝粉、钛青兰加入步骤一所得的混合溶液中,搅拌均匀得到混合溶液;
步骤三:将紫珠光粉、绿珠光粉、黑浆加入到步骤二所得的混合溶液中,搅拌均匀得到混合溶液;
步骤四:向步骤三所得的混合溶液中缓慢加入466助剂在50-55℃下搅拌5小时,静置,得到合格产品。
本实施例的有益效果:本实施例采用H-01树脂、585-1树脂、环氧树脂这三种树脂作为混合,尤其利用环氧树脂的高聚特性来增加油漆的附着力,在施工过程中更容易附着在装饰面上,提高了工作效率,节约成本,且多种颜料混合而得的浅灰色应用范围广泛。
实施例2:
本实施例提供一种浅灰色闪光漆的配方,与实施例1的不同仅在于:所述配方组份的质量含量稍有不同:
37A铝粉 3.6%
37S铝粉 0.4%
紫珠光粉 0.6%
绿珠光粉 2%
黑浆 5%
H-01树脂 40%
585-1树脂 18%
硝化棉 10%
环氧树脂 12%
丁酯 8%
钛青兰 0.3%
466助剂 0.1%。
实施例3:
本实施例提供一种浅灰色闪光漆的配方,与实施例1的不同仅在于:所述配方组份的质量含量稍有不同,也是最优选择:
37A铝粉 4%
37S铝粉 0.35%
紫珠光粉 0.65%
绿珠光粉 1.5%
黑浆 5%
H-01树脂 38%
585-1树脂 20%
硝化棉 12%
环氧树脂 10%
丁酯 8%
钛青兰 0.4%
466助剂 0.1%。
实施例1-3仅用于解释本发明,其中实施例3作为最优配方选择,并不对本发明的保护范围构成限定。
Claims (3)
1.一种浅灰色闪光漆的配方,其特征在于:由以下质量百分比的成份组成:
37A铝粉 3.5-4.5%
37S铝粉 0.3-0.4%
紫珠光粉 0.6-0.7%
绿珠光粉 1-2%
黑浆 4-6%
H-01树脂 35-40%
585-1树脂 18-23%
硝化棉 10-15%
环氧树脂 8-12%
丁酯 6-9%
钛青兰 0.3-0.5%
466助剂 0.1%。
2.根据权利要求1所述的一种浅灰色闪光漆的配方,其特征在于:由以下具体质量百分比的成份组成:
37A铝粉 4%
37S铝粉 0.35%
紫珠光粉 0.65%
绿珠光粉 1.5%
黑浆 5%
H-01树脂 38%
585-1树脂 20%
硝化棉 12%
环氧树脂 10%
丁酯 8%
钛青兰 0.4%
466助剂 0.1%。
3.一种根据权利要求1或2所述的的配方组成来制备油漆的方法,其特征在于:其具体步骤如下:
步骤一:将硝化棉、H-01树脂、585-1树脂、环氧树脂用丁酯溶解得到混合溶液;
步骤二:将37A铝粉、37S铝粉、钛青兰加入步骤一所得的混合溶液中,搅拌均匀得到混合溶液;
步骤三:将紫珠光粉、绿珠光粉、黑浆加入到步骤二所得的混合溶液中,搅拌均匀得到混合溶液;
步骤四:向步骤三所得的混合溶液中缓慢加入466助剂在50-55℃下搅拌5小时,静置,得到合格产品。