CN102241935A - 一种防盗门用水性丙烯酸氨基面漆及制备方法 - Google Patents
一种防盗门用水性丙烯酸氨基面漆及制备方法 Download PDFInfo
- Publication number
- CN102241935A CN102241935A CN2011101741869A CN201110174186A CN102241935A CN 102241935 A CN102241935 A CN 102241935A CN 2011101741869 A CN2011101741869 A CN 2011101741869A CN 201110174186 A CN201110174186 A CN 201110174186A CN 102241935 A CN102241935 A CN 102241935A
- Authority
- CN
- China
- Prior art keywords
- water
- aqueous transparent
- agent
- waterborne
- raw materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防盗门用水性丙烯酸氨基面漆及制备方法,属于金属防护领域。本发明提供的水性丙烯酸氨基面漆,属于绿色环保型涂料,由去离子水,水性丙烯酸树脂和水性氨基树脂作为基料,水性透明红色浆和水性透明黄色浆作为水性透明色浆,助溶剂、中和剂、消光剂、消泡剂和基材润湿剂作为助剂制成,首次将水性涂料应用到防盗门的涂装,以水为溶剂,能够降低VOC的排放,减少溶剂型涂料对环境及人身健康的危害,不改变现有防盗门的涂装工艺,施工性能较好,对材质表面适应性好,涂层附着力强,漆膜丰满,装饰性好,耐候性较溶剂型涂料好。
Description
技术领域
本发明属于金属防护领域,具体涉及一种防盗门用水性丙烯酸氨基面漆及制备方法。
背景技术
目前,我国防盗门装饰用透明面漆还全部采用传统溶剂型丙烯酸氨基涂料,这些漆中含有大量的有机溶剂,如芳香烃、卤代烃等,在喷涂和烘干过程中有大量有毒溶剂挥发,不仅对工人健康产生影响,增加了火灾隐患,还对大气造成了严重的污染。近年来,随着世界各国对VOC(volatile organic compounds,挥发性有机化合物)污染的日益重视和环保法规不断严格VOC的排放标准,水性涂料以其无毒环保、VOC含量低、不然不爆的高安全性得到市场的青睐。水性涂料的应用领域也将更加广泛,随着国家及全社会对于“低碳”理念的不断推进和深化发展,相对于溶剂型涂料更具优势的水性涂料产业其发展前景将十分可观。
发明内容
为了改善防盗门用水性丙烯酸氨基面漆对环境及人身健康的危害,本发明提供一种VOC极低的防盗门用水性丙烯酸氨基面漆,该漆属于绿色环保型漆料。
一种防盗门用水性丙烯酸氨基面漆,按重量百分比计算,它是由以下原料配比制成的:16%~25%的去离子水,所述基料:55%~65%的水性丙烯酸树脂和10%~13%的水性氨基树脂,所述水性透明色浆:0.3%~1.2%的水性透明红色浆和0.3%~1.2%的水性透明黄色浆,所述助剂:2%~4%的助溶剂、1.5%~3%的中和剂、1%~3%的消光剂、0.1%~0.4%的消泡剂和0.2%~0.4%的基材润湿剂。
具体地,所述防盗门用水性丙烯酸氨基面漆,按重量百分比计算,它是由以下原料配比制成的:25%的去离子水,所述基料:55%的水性丙烯酸树脂和12%的水性氨基树脂,所述水性透明色浆:1%的水性透明红色浆和0.8%的水性透明黄色浆,所述助剂:2%的助溶剂、1.9%的中和剂、1.8%的消光剂、0.2%的消泡剂和0.3%的基材润湿剂。
具体地,所述防盗门用水性丙烯酸氨基面漆,按重量百分比计算,它是由以下原料配比制成的:19%的去离子水,所述基料:60%的水性丙烯酸树脂和11%的水性氨基树脂,所述水性透明色浆:1.2%的水性透明红色浆和0.8%的水性透明黄色浆,所述助剂:3%的助溶剂、2.2%的中和剂、2.2%的消光剂、0.3%的消泡剂和0.3%的基材润湿剂。
具体地,所述防盗门用水性丙烯酸氨基面漆,按重量百分比计算,它是由以下原料配比制成的:16%的去离子水,所述基料:64%的水性丙烯酸树脂和10%的水性氨基树脂,所述水性透明色浆:0.6%的水性透明红色浆和1.4%的水性透明黄色浆,所述助剂:3.5%的助溶剂、2.5%的中和剂、1.2%的消光剂、0.4%的消泡剂和0.4%的基材润湿剂。
一种防盗门用水性丙烯酸氨基面漆的制备方法,具体包括以下步骤:
1)、将所述水性丙烯酸树脂、水性氨基树脂、助溶剂、中和剂、去离子水按照所述原料配比依次加入备料锅中;
2)、将所述加入到备料锅中的配料进行低速搅拌,直至搅拌均匀后,按照所述原料配比加入所述消光剂,高速分散20分钟以上,形成均匀漆浆,无明显块状物质;
3)、按照所述原料配比向所述均匀漆浆中依次加入所述水性透明色浆,消泡剂,基材润湿剂,并再次搅拌均匀;
其中,所述水性透明色浆包括水性透明红色浆和水性透明黄色浆。
与现有技术相比,本发明的优点在于:
本发明首次将水性涂料应用到防盗门的涂装,以水为溶剂,能够降低VOC的排放,减少溶剂型涂料对环境及人身健康的危害;不改变现有防盗门的涂装工艺,产品的施工性能较好;水性丙烯酸氨基面漆对材质表面适应性好,涂层附着力强,漆膜丰满,装饰性好,耐候性较溶剂型涂料好。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚,下面将结合具体实施方式作对本发明做进一步的详细描述。
实施例1
本实施例是由以下原料按重量份配比制成的:55%的水性丙烯酸树脂,12%的水性氨基树脂,2%的助溶剂,1.9%的中和剂,25%的去离子水,1.8%的消光剂,1%的水性透明红色浆,0.8%的水性透明黄色浆,0.2%的消泡剂,0.3%的基材润湿剂;
上述水性丙烯酸树脂使用湖南益阳LY-618,水性氨基树脂使用英力士R-747为基料;
所述上述一种防盗门用水性丙烯酸氨基面漆的制备方法,具体包括如下步骤:
1)、将上述量的水性丙烯酸树脂、水性氨基树脂、助溶剂、中和剂、去离子水依次加入备料锅中;
2)、将加入到备料锅中的配料进行低速搅拌,直至搅拌均匀后,加入上述量的消光剂,高速分散20分钟以上,形成均匀漆浆,无明显块状物质;
3)、向均匀漆浆中依次加入上述量的水性透明色浆(水性透明红色浆和水性透明黄色浆)、消泡剂、基材润湿剂,将漆浆再次搅拌均匀。
实施例2
本实施例是由以下原料按重量份配比制成的,60%的水性丙烯酸树脂,11%的水性氨基树脂,3%的助溶剂,2.2%的中和剂,19%的去离子水,2.2%的消光剂,1.2%的水性透明红色浆,0.8%的水性透明黄色浆,0.3%的消泡剂,0.3%的基材润湿剂。
其制备方法同实施例1,这里不再赘述。
实施例3
本实施例是由以下原料按重量份配比制成的,64%的水性丙烯酸树脂,10%的水性氨基树脂,3.5%的助溶剂,2.5%的中和剂,16%的去离子水,1.2%的消光剂,0.6%的水性透明红色浆,1.4%的水性透明黄色浆,0.4%的消泡剂,0.4%的基材润湿剂。
其制备方法同实施例1,这里不再赘述。
以上所述的实施例,只是本发明较优选的实施方式,本领域的技术人员在本发明技术方案范围内进行的通常变化和替换都应包含在本发明的保护范围内。
Claims (5)
1.一种防盗门用水性丙烯酸氨基面漆,其特征在于,按重量百分比计算,它是由以下原料配比制成的:16%~25%的去离子水,所述基料:55%~65%的水性丙烯酸树脂和10%~13%的水性氨基树脂,所述水性透明色浆:0.3%~1.2%的水性透明红色浆和0.3%~1.2%的水性透明黄色浆,所述助剂:2%~4%的助溶剂、1.5%~3%的中和剂、1%~3%的消光剂、0.1%~0.4%的消泡剂和0.2%~0.4%的基材润湿剂。
2.根据权利要求1所述的防盗门用水性丙烯酸氨基面漆,其特征在于,按重量百分比计算,它是由以下原料配比制成的:25%的去离子水,所述基料:55%的水性丙烯酸树脂和12%的水性氨基树脂,所述水性透明色浆:1%的水性透明红色浆和0.8%的水性透明黄色浆,所述助剂:2%的助溶剂、1.9%的中和剂、1.8%的消光剂、0.2%的消泡剂和0.3%的基材润湿剂。
3.根据权利要求1所述的防盗门用水性丙烯酸氨基面漆,其特征在于,按重量百分比计算,它是由以下原料配比制成的:19%的去离子水,所述基料:60%的水性丙烯酸树脂和11%的水性氨基树脂,所述水性透明色浆:1.2%的水性透明红色浆和0.8%的水性透明黄色浆,所述助剂:3%的助溶剂、2.2%的中和剂、2.2%的消光剂、0.3%的消泡剂和0.3%的基材润湿剂。
4.根据权利要求1所述的防盗门用水性丙烯酸氨基面漆,其特征在于,按重量百分比计算,它是由以下原料配比制成的:16%的去离子水,所述基料:64%的水性丙烯酸树脂和10%的水性氨基树脂,所述水性透明色浆:0.6%的水性透明红色浆和1.4%的水性透明黄色浆,所述助剂:3.5%的助溶剂、2.5%的中和剂、1.2%的消光剂、0.4%的消泡剂和0.4%的基材润湿剂。
5.根据权利要求1~4中的任意一项权利要求,一种防盗门用水性丙烯酸氨基面漆的制备方法,其特征在于,具体包括以下步骤:
1)、将所述水性丙烯酸树脂、水性氨基树脂、助溶剂、中和剂、去离子水按照所述原料配比依次加入备料锅中;
2)、将所述加入到备料锅中的配料进行低速搅拌,直至搅拌均匀后,按照所述原料配比加入所述消光剂,高速分散20分钟以上,形成均匀漆浆,无明显块状物质;
3)、按照所述原料配比向所述均匀漆浆中依次加入所述水性透明色浆,消泡剂,基材润湿剂,并再次搅拌均匀;
其中,所述水性透明色浆包括水性透明红色浆和水性透明黄色浆。