CN103409014A - 一种耐热的金属涂料及其制备方法 - Google Patents
一种耐热的金属涂料及其制备方法 Download PDFInfo
- Publication number
- CN103409014A CN103409014A CN2013103099673A CN201310309967A CN103409014A CN 103409014 A CN103409014 A CN 103409014A CN 2013103099673 A CN2013103099673 A CN 2013103099673A CN 201310309967 A CN201310309967 A CN 201310309967A CN 103409014 A CN103409014 A CN 103409014A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat
- pigment
- metallic paint
- dimethyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种耐热的金属涂料及其制备方法，金属涂料包括以下重量份的原料：乙二醇20-30份、聚醋酸乙烯20-30份、颜料40-45份、分散剂10-20份、铜粉2-3份、二乙二醇丁醚12-18份、三乙醇胺24-29份、磷酸二氢锌10-15份、氟化钠7-9份、二甲基甲酚2-10份、酒石酸2-8份、氨水1-10份、水20-50份。本发明制备的金属涂料固化后表现出优良的绝缘性，耐热性好，可高达200℃；而且尺寸稳定，不易开裂，固化收缩率小，为1.2%-1.6%。冲击强度在55-68kg/cm2，附着力强。
Description
技术领域
本发明涉及一种涂料，尤其涉及一种耐热的金属涂料及其制备方法。
背景技术
涂料是一种能牢固覆盖在物体表面，起保护、装饰、标志和其他特殊用途的化学混合物涂料。中国涂料界的《涂料工艺》是这样定义的：“涂料是一种材料，这种材料可以用不同的施工工艺涂覆在物件表面，形成粘附牢固、具有一定强度、连续的固态薄膜。这样形成的膜通称涂膜，又称漆膜或涂层。”属于有机化工高分子材料，所形成的涂膜属于高分子化合物类型。按照现代通行的化工产品的分类，涂料属于精细化工产品。现代的涂料正在逐步成为一类多功能性的工程材料，是化学工业中的一个重要行业。涂料能够防腐、防水、防油、耐化学品、耐光、耐温等。物件暴露在大气之中，受到氧气、水分等的侵蚀，造成金属锈蚀、木材腐朽、水泥风化等破坏现象。在物件表面涂以涂料，形成一层保护膜，能够阻止或延迟这些破坏现象的发生和发展，使各种材料的使用寿命延长。所以，保护作用是涂料的一个主要作用。但是现有技术的金属涂料易导电,使用时存在安全隐患,而且金属涂料的粘接力普遍不高，容易掉落。
发明内容
针对现有技术的不足，本发明提供了一种绝缘性能好、附着力强的耐热的金属涂料及其制备方法。
一种耐热的金属涂料，包括以下重量份的原料：乙二醇20-30份、聚醋酸乙烯20-30份、颜料40-45份、分散剂10-20份、铜粉2-3份、二乙二醇丁醚12-18份、三乙醇胺24-29份、磷酸二氢锌10-15份、氟化钠7-9份、二甲基甲酚2-10份、酒石酸2-8份、氨水1-10份、水20-50份。
优选地，颜料是金红石型钛白粉、氧化锌、硅灰石或高龄土中的一种。
分散剂可以使颜料粒子容易分散，然后使颜料粒子带上足够的表面电荷以避免再聚集，分散剂优选三聚磷酸钾、柠檬酸、二甲基三酸酯中的一种或几种。
金属涂料的制备方法，包括以下步骤：将乙二醇、聚醋酸乙烯、颜料、分散剂、铜粉、水混合均匀，然后依次加入二乙二醇丁醚、三乙醇胺、磷酸二氢锌、氟化钠、二甲基甲酚、酒石酸，混合均匀，最后加入氨水混匀。
本发明固化后表现出优良的绝缘性，其电性能为下击穿电压为35-50kV/mm，体积电阻为10Ω·cm，电绝缘性能良好；耐热性好，可高达200℃；而且尺寸稳定，不易开裂，固化收缩率小，为1.2%-1.6%。冲击强度在55-68kg/cm2，附着力强。
具体实施方式
下面通过具体实施例对本发明作进一步详细介绍。
实施例1
一种耐热的金属涂料，包括以下重量份的原料制成：乙二醇20份、聚醋酸乙烯20份、金红石型钛白粉40份、三聚磷酸钾10份、铜粉2份、二乙二醇丁醚12份、三乙醇胺24份、磷酸二氢锌10份、氟化钠7份、二甲基甲酚2份、酒石酸2份、氨水1份、水20份。
其制备方法包括以下步骤：将乙二醇、聚醋酸乙烯、颜料、分散剂、铜粉、水混合均匀，然后依次加入二乙二醇丁醚、三乙醇胺、磷酸二氢锌、氟化钠、二甲基甲酚、酒石酸，混合均匀，最后加入氨水混匀。
实施例2
一种耐热的金属涂料，包括以下重量份的原料制成：乙二醇30份、聚醋酸乙烯30份、氧化锌45份、柠檬酸和二甲基三酸酯（二者重量比为1：1）20份、铜粉3份、二乙二醇丁醚18份、三乙醇胺29份、磷酸二氢锌15份、氟化钠9份、二甲基甲酚10份、酒石酸8份、氨水10份、水50份。
其制备方法包括以下步骤：将乙二醇、聚醋酸乙烯、颜料、分散剂、铜粉、水混合均匀，然后依次加入二乙二醇丁醚、三乙醇胺、磷酸二氢锌、氟化钠、二甲基甲酚、酒石酸，混合均匀，最后加入氨水混匀。
实施例3
一种耐热的金属涂料，包括以下重量份的原料制成：乙二醇25份、聚醋酸乙烯25份、硅灰石43份、二甲基三酸酯15份、铜粉2.5份、二乙二醇丁醚15份、三乙醇胺26份、磷酸二氢锌13份、氟化钠8份、二甲基甲酚8份、酒石酸5份、氨水6份、水30份。
其制备方法包括以下步骤：将乙二醇、聚醋酸乙烯、颜料、分散剂、铜粉、水混合均匀，然后依次加入二乙二醇丁醚、三乙醇胺、磷酸二氢锌、氟化钠、二甲基甲酚、酒石酸，混合均匀，最后加入氨水混匀。
下面通过试验测试金属涂料的各项性能：
| 实施例1 | 实施例2 | 实施例3 | |
| 击穿电压kV/mm | 35 | 40 | 50 |
| 体积电阻Ω·cm | 10 | 10 | 10 |
| 耐热性℃ | 150 | 200 | 180 |
| 固化收缩率% | 1.2 | 1.3 | 1.6 |
| 柔韧性mm | 1 | 0.8 | 0.7 |
| 冲击强度kg/cm2 | 55 | 60 | 68 |
| 耐热性℃ | 220 | 250 | 260 |
另外，本发明不限于上述实施方式，只要在不超出本发明的范围内，可以采取各种方式实施本发明。
Claims (4)
1.一种耐热的金属涂料，其特征在于包括以下重量份的原料：乙二醇20-30份、聚醋酸乙烯20-30份、颜料40-45份、分散剂10-20份、铜粉2-3份、二乙二醇丁醚12-18份、三乙醇胺24-29份、磷酸二氢锌10-15份、氟化钠7-9份、二甲基甲酚2-10份、酒石酸2-8份、氨水1-10份、水20-50份。
2.根据权利要求1所述的耐热的金属涂料，其特征在于：颜料是金红石型钛白粉、氧化锌、硅灰石或高龄土中的一种。
3.根据权利要求1所述的耐热的金属涂料，其特征在于：分散剂是三聚磷酸钾、柠檬酸、二甲基三酸酯中的一种或几种。
4.权利要求1所述的耐热的金属涂料的制备方法，其特征在于包括以下步骤：将乙二醇、聚醋酸乙烯、颜料、分散剂、铜粉、水混合均匀，然后依次加入二乙二醇丁醚、三乙醇胺、磷酸二氢锌、氟化钠、二甲基甲酚、酒石酸，混合均匀，最后加入氨水混匀。