CN104830194A - 一种防锈水性金属漆 - Google Patents
一种防锈水性金属漆 Download PDFInfo
- Publication number
- CN104830194A CN104830194A CN201510259950.0A CN201510259950A CN104830194A CN 104830194 A CN104830194 A CN 104830194A CN 201510259950 A CN201510259950 A CN 201510259950A CN 104830194 A CN104830194 A CN 104830194A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- antirust
- metallic paint
- aqueous metallic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种防锈水性金属漆,按重量份数计包括下列组分:聚丙烯酰胺20~30份、硬脂基甜菜碱10~20份、硫酸钾1~8份、铝银浆2~7份、磷酸钠1~5份、醇酯十二5~15份、水性防锈剂2~6份、耐盐雾剂3~9份、流平剂3~8份、增稠剂1~6份、填料5~10份、去离子水25~35份。本发明制备的防锈水性金属漆,可在常温条件下迅速固化成膜,涂层光泽度高,丰满度好,完美的呈现了底材的金属效果。且耐候性好,对各种腐蚀性物质具有很好的抵抗力。本发明不使用有机溶剂,环保无毒,不会对环境和人体产生危害,适用于可广泛应用于各种汽车、船舶、机械制造和石化设备的涂装领域。
Description
技术领域
本发明涉及油漆领域,尤其涉及一种防锈水性金属漆。
背景技术
防锈金属漆是一种可保护金属表面免受大气、海水等的化学或电化学腐蚀的涂料。防锈金属漆包括水性和油性两种,油性防锈漆会使材料表面油腻,且含有亚硝酸盐、铬酸盐等有毒物质,对操作人员危害较大。水性金属漆金属质感好,不容易生锈,美观环保。因此,对于水性金属漆的开发也越来越受到重视。
然而,目前市场上的防锈水性金属漆大多数是通过颜料的添加起到防锈目的,遮盖了金属表面的光泽。去掉这些颜料的清漆,仅靠树脂来维持防锈性能不佳,所以存在防锈性能差、遮盖力差、易黄变等问题。另外,现有的水性金属漆大多含有苯酚等有毒物质,对人体健康造成危害。
发明内容
本发明的目的在于克服上述现有技术存在的不足,提供一种不含有机溶剂、环保无毒的防锈水性金属漆。
为达到上述目的,本发明是通过以下技术方案实现的:
一种防锈水性金属漆,按重量份数计包括下列组分:聚丙烯酰胺20~30份、硬脂基甜菜碱10~20份、硫酸钾1~8份、铝银浆2~7份、磷酸钠1~5份、醇酯十二5~15份、水性防锈剂2~6份、耐盐雾剂3~9份、流平剂3~8份、增稠剂1~6份、填料5~10份、去离子水25~35份。
优选的,所述水性防锈剂为失水山梨醇单油酸酯、肌醇六磷酸酯、季戊四醇酯、糖酯中的任意一种。
优选的,所述流平剂为氟改性丙烯酸、聚酯改性硅氧烷、聚醚改性硅氧烷中的任意一种。
优选的,所述增稠剂为聚丙烯酰胺、聚乙烯醇、聚乙烯吡咯烷酮、聚氧化乙烯中的任意一种。
优选的,所述填料为碳酸钙、云母粉、膨润土中的任意一种。
本发明的有益效果:
本发明制备的防锈水性金属漆,可在常温条件下迅速固化成膜,涂层光泽度高,丰满度好,完美的呈现了底材的金属效果。且耐候性好,对各种腐蚀性物质具有很好的抵抗力。本发明不使用有机溶剂,环保无毒,不会对环境和人体产生危害,适用于可广泛应用于各种汽车、船舶、机械制造和石化设备的涂装领域。
具体实施方式
下面结合具体实施例对本发明进行详细说明。以下实施例将有助于本领域的技术人员进一步理解本发明,但不以任何形式限制本发明。应当指出的是,对本领域的普通技术人员来说,在不脱离本发明构思的前提下,还可以做出若干变形和改进。这些都属于本发明的保护范围。
一种防锈水性金属漆,按重量份数计包括下列组分:聚丙烯酰胺20~30份、硬脂基甜菜碱10~20份、硫酸钾1~8份、铝银浆2~7份、磷酸钠1~5份、醇酯十二5~15份、水性防锈剂2~6份、耐盐雾剂3~9份、流平剂3~8份、增稠剂1~6份、填料5~10份、去离子水25~35份。
本发明制备的防锈水性金属漆,具有不含有机溶剂、环保无毒、防腐蚀等优点。
实施例1
本发明的防锈水性金属漆,按重量份数计包括下列组分:聚丙烯酰胺20份、硬脂基甜菜碱10份、硫酸钾8份、铝银浆7份、磷酸钠1份、醇酯十二15份、失水山梨醇单油酸酯6份、耐盐雾剂3份、氟改性丙烯酸8份、聚丙烯酰胺1份、碳酸钙5份、去离子水35份。
实施例2
本发明的防锈水性金属漆,按重量份数计包括下列组分:聚丙烯酰胺30份、硬脂基甜菜碱20份、硫酸钾1份、铝银浆2份、磷酸钠5份、醇酯十二5份、肌醇六磷酸酯2份、耐盐雾剂9份、聚酯改性硅氧烷3份、聚乙烯醇6份、云母粉10份、去离子水25份。
实施例3
本发明的防锈水性金属漆,按重量份数计包括下列组分:聚丙烯酰胺25份、硬脂基甜菜碱15份、硫酸钾4份、铝银浆5份、磷酸钠3份、醇酯十二10份、季戊四醇酯4份、耐盐雾剂6份、聚醚改性硅氧烷6份、聚乙烯吡咯烷酮4份、膨润土8份、去离子水30份。
实施例4
本发明的防锈水性金属漆,按重量份数计包括下列组分:聚丙烯酰胺22份、硬脂基甜菜碱11份、硫酸钾2份、铝银浆3份、磷酸钠2份、醇酯十二6份、糖酯3份、耐盐雾剂4份、聚酯改性硅氧烷4份、聚氧化乙烯2份、云母粉6份、去离子水27份。
实施例5
本发明的防锈水性金属漆,按重量份数计包括下列组分:聚丙烯酰胺28份、硬脂基甜菜碱18份、硫酸钾7份、铝银浆6份、磷酸钠4份、醇酯十二13份、季戊四醇酯5份、耐盐雾剂8份、聚醚改性硅氧烷7份、聚氧化乙烯5份、膨润土8份、去离子水25~35份。
实施例6
本发明的防锈水性金属漆,按重量份数计包括下列组分:聚丙烯酰胺20份、硬脂基甜菜碱15份、硫酸钾4份、铝银浆7份、磷酸钠5份、醇酯十二7份、失水山梨醇单油酸酯3份、耐盐雾剂9份、氟改性丙烯酸7份、聚丙烯酰胺2份、碳酸钙7份、去离子水25份。
以上对本发明的具体实施例进行了描述。需要理解的是,本发明并不局限于上述特定实施方式,本领域技术人员可以在权利要求的范围内做出各种变形或修改,这并不影响本发明的实质内容。
Claims (5)
1.一种防锈水性金属漆,其特征在于,按重量份数计包括下列组分:聚丙烯酰胺20~30份、硬脂基甜菜碱10~20份、硫酸钾1~8份、铝银浆2~7份、磷酸钠1~5份、醇酯十二5~15份、水性防锈剂2~6份、耐盐雾剂3~9份、流平剂3~8份、增稠剂1~6份、填料5~10份、去离子水25~35份。
2.根据权利要求1所述的水性金属漆,其特征在于:所述水性防锈剂为失水山梨醇单油酸酯、肌醇六磷酸酯、季戊四醇酯、糖酯中的任意一种。
3.根据权利要求1所述的水性金属漆,其特征在于:所述流平剂为氟改性丙烯酸、聚酯改性硅氧烷、聚醚改性硅氧烷中的任意一种。
4.根据权利要求1所述的水性金属漆,其特征在于:所述增稠剂为聚丙烯酰胺、聚乙烯醇、聚乙烯吡咯烷酮、聚氧化乙烯中的任意一种。
5.根据权利要求1所述的水性金属漆,其特征在于:所述填料为碳酸钙、云母粉、膨润土中的任意一种。