CN103406535A - 一种粉末冶金刹车钳铁合金及其制备方法 - Google Patents
一种粉末冶金刹车钳铁合金及其制备方法 Download PDFInfo
- Publication number
- CN103406535A CN103406535A CN2013102726032A CN201310272603A CN103406535A CN 103406535 A CN103406535 A CN 103406535A CN 2013102726032 A CN2013102726032 A CN 2013102726032A CN 201310272603 A CN201310272603 A CN 201310272603A CN 103406535 A CN103406535 A CN 103406535A
- Authority
- CN
- China
- Prior art keywords
- powder
- powder metallurgy
- parts
- under
- minute
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种粉末冶金刹车钳铁合金及其制备方法，其特征在于由下列重量份的原料制成：铁粉95-99、铬粉1.4-1.8、氮化硼1.2-1.4、铋0.12-0.15、石墨0.4-0.6、Sb0.02-0.04、Bi0.9-1.2、Yb0.01-0.02、ZnO1.2-1.4、氧化硼0.4-0.6、纳米膨润土1.2-1.4、硼化铬0.2-0.4、微晶蜡3-3.6、分散剂2-3。本发明增加铬含量，性好，能满足刹车钳性能需要，本发明采用粉末冶金工艺，成本大大降低。
Description
技术领域
本发明涉及粉末冶金领域，尤其涉及一种粉末冶金刹车钳铁合金及其制备方法。
背景技术
粉末冶金技术是将材料科学和金属成形技术完善的结合起来一种新型技术，因为高效、无切削加工、节材、节能、环保而被广泛使用于各种行业。
粉末冶金结构件制品材料成分不受熔炼限制，既可以加入合金成分，也可以加入其它结构组分，并且在相当大的范围内根据要求进行调整，进而在力学性能上能达到与钢件匹配的效果。
粉末冶金机械化程度高，既能减少人员，又能提高效率，进而节约成本。粉末冶金技术能取代传统的制造工艺，为广大传统企业节约成本。
所以研究各种机械零部件的粉末冶金的配方，适应不同的需要，具有重要的意义。
现有刹车钳均是锻造或切削加工，工艺复杂，成本高。
发明内容
本发明的目的是提供一种粉末冶金刹车钳铁合金及其制备方法，工艺简单，适合大批量生产。
本发明的技术方案如下：
一种粉末冶金刹车钳铁合金，其特征在于由下列重量份的原料制成：
铁粉95-99、铬粉8.4-8.8、氮化硼1.2-1.4、铋0.12-0.15、石墨0.4-0.6、Sb0.02-0.04、Bi0.9-1.2、Yb0.01-0.02、ZnO1.2-1.4、氧化硼0.4-0.6、纳米膨润土1.2-1.4、硼化铬0.2-0.4、微晶蜡3-3.6、分散剂2-3。
所述的分散剂由下列重量份的原料制成：聚乙烯醇7、硬脂酸锌3、乙撑基双硬酯酰胺1、氮化铝粉2、丁基硫醇锡2、烷基酚聚氧乙烯醚2、硼化铬2、双十四碳醇酯1。
制备方法是：将各物料混合，研磨分散均匀即可。
所述的粉末冶金刹车钳铁合金的制备方法，其特征在于包括以下步骤：
（1）将各物料混合，在50-55℃下搅拌均匀40-50分钟后，装入模具，压制成坯；
（2）将压坯放在烧结炉中，在含氧量为3-4%的氮气氛保护下，以6-8℃/分钟速率升温至720-760℃条件下烧结2-3小时；再以9-12℃/分钟速率升温至980-1020℃条件下烧结3-4小时；再以12-15℃/分钟速率降温至550-580℃条件下保温2-3小时；再以8-10℃/分钟速率降温至320-350℃条件下保温2-3小时；
（3）将压坯放入110-125℃甘油中，2-3小时；
（4）将压坯送入蒸汽处理炉中，在炉中温度450-480℃的条件下通入蒸汽60-90分钟；取出空冷即得。
本发明增加铬含量，性好，能满足刹车钳性能需要，本发明采用粉末冶金工艺，成本大大降低。
具体实施方式
一种粉末冶金刹车钳铁合金，由下列重量份的原料（公斤）制成：
铁粉99、铬粉8.8、氮化硼1.4、铋0.12、石墨0.6、Sb0.02、Bi0.9、Yb0.02、ZnO1.4、氧化硼0.6、纳米膨润土1.2、硼化铬0.2、微晶蜡3、分散剂3。
所述的分散剂由下列重量份的原料制成：聚乙烯醇7、硬脂酸锌3、乙撑基双硬酯酰胺1、氮化铝粉2、丁基硫醇锡2、烷基酚聚氧乙烯醚2、硼化铬2、双十四碳醇酯2。制备方法是：将各物料混合，研磨分散均匀即可。
粉末冶金刹车钳铁合金的制备方法，包括以下步骤：
（1）将各物料混合，在50-55℃下搅拌均匀40-50分钟后，装入模具，压制成坯；
（2）将压坯放在烧结炉中，在含氧量为3-4%的氮气氛保护下，以6-8℃/分钟速率升温至720-760℃条件下烧结2-3小时；再以9-12℃/分钟速率升温至980-1020℃条件下烧结3-4小时；再以12-15℃/分钟速率降温至550-580℃条件下保温2-3小时；再以8-10℃/分钟速率降温至320-350℃条件下保温2-3小时；
（3）将压坯放入110-125℃甘油中，2-3小时；
（4）将压坯送入蒸汽处理炉中，在炉中温度450-480℃的条件下通入蒸汽60-90分钟；取出空冷即得。
经过检测，本发明法兰的热处理硬度：HRC65 ；抗拉强度：1380MPa 。
Claims (2)
1.一种粉末冶金刹车钳铁合金，其特征在于由下列重量份的原料制成：
铁粉95-99、铬粉8.4-81.8、氮化硼1.2-1.4、铋0.12-0.15、石墨0.4-0.6、Sb0.02-0.04、Bi0.9-1.2、Yb0.01-0.02、ZnO1.2-1.4、氧化硼0.4-0.6、纳米膨润土1.2-1.4、硼化铬0.2-0.4、微晶蜡3-3.6、分散剂2-3；
所述的分散剂由下列重量份的原料制成：聚乙烯醇6-7、硬脂酸锌2-3、乙撑基双硬酯酰胺1-2、氮化铝粉1-2、丁基硫醇锡1-2、烷基酚聚氧乙烯醚1-2、硼化铬1-2、双十四碳醇酯1-2；制备方法是：将各物料混合，研磨分散均匀即可。
2.根据权利要求1所述的粉末冶金刹车钳铁合金的制备方法，其特征在于包括以下步骤：
（1）将各物料混合，在50-55℃下搅拌均匀40-50分钟后，装入模具，压制成坯；
（2）将压坯放在烧结炉中，在含氧量为3-4%的氮气氛保护下，以6-8℃/分钟速率升温至720-760℃条件下烧结2-3小时；再以9-12℃/分钟速率升温至980-1020℃条件下烧结3-4小时；再以12-15℃/分钟速率降温至550-580℃条件下保温2-3小时；再以8-10℃/分钟速率降温至320-350℃条件下保温2-3小时；
（3）将压坯放入110-125℃甘油中，2-3小时；
（4）将压坯送入蒸汽处理炉中，在炉中温度450-480℃的条件下通入蒸汽60-90分钟；取出空冷即得。