CN103387786A - 一种高性能水性环保涂料的制备方法 - Google Patents
一种高性能水性环保涂料的制备方法 Download PDFInfo
- Publication number
- CN103387786A CN103387786A CN2012101463815A CN201210146381A CN103387786A CN 103387786 A CN103387786 A CN 103387786A CN 2012101463815 A CN2012101463815 A CN 2012101463815A CN 201210146381 A CN201210146381 A CN 201210146381A CN 103387786 A CN103387786 A CN 103387786A
- Authority
- CN
- China
- Prior art keywords
- epoxy resin
- preparation
- parts
- paint
- solidifying agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种高性能水性环保涂料的制备方法,该涂料由环氧树脂、三聚磷酸铝APW-1、云母粉、5A分子筛、固化剂制备得到,其中各组分的重量份数为:环氧树脂:50-70份、三聚磷酸铝APW-1为10-12份,云母粉为4-6份,5A分子筛4-8份,固化剂10-20份,将上述组分充分混合,熟化0.5-1h即可使用。本发明漆膜对金属和非金属都有很强的粘接强度。可以制得高弹性的漆膜;本发明产品耐气候性较好,户外用时漆膜较不易失光、粉化。
Description
技术领域
本发明涉及一种涂料,特别涉及一种高性能水性环保涂料的制备方法。
背景技术
以环氧树脂为主要成膜物质的涂料称为环氧树脂漆,含有两个或两个以上环氧基团的树脂属于环氧树脂,环氧基团是有一个氧原子和两个碳原子组成的环,具有高度活泼性,使环氧树脂能与多种类型固化剂发生交联反应形成三位网状结构的高聚物。
环氧树脂漆的优点很多:如1)、漆膜对金属、陶瓷、玻璃、混凝上、木材等极性底材,均有优良的附着力因为环氧树脂漆有很多羟基及醚健,能与底材吸引,而且环氧固化时体积收缩率低,不象不饱和聚酯在固化时体积收缩率高达11%,产生内应力而损及附着力。W.J.Bailey等研究发现环氧树脂固化时收缩率低的理由:通常含双键单体为聚合时的间距较长,一旦聚合,生成共价键,间距缩短,体积收缩,所以不饱和聚酯地说缩率高,但是开环聚合则不同,因为聚合的原子间原先已有共价键连接,所以聚合后体积变化不大。2)、抗化学品性能优良,因树脂中仅有烃基及醚健,没有酯键,所以耐碱性尤其突出。一般的油脂系或醇酸防锈底漆,在腐蚀时阴极部位呈碱性会被皂化破坏。环氧树脂漆耐碱而且附着力好,故大量用作防腐蚀底漆,例如汽车的阴极电沉积底漆等等。又因环氧树脂漆固化后成三维网状结构,有能耐油类等浸渍,大量应用于油槽、油轮、飞机的整体油箱内壁衬里等。3)与热固性酚醛树脂涂料相比较,环氧树脂漆含芳环而坚硬,但有醚健便于分子链的旋转,具有一定的韧性,不象酚醛树脂很脆。环氧树脂交联间距长,便于内旋转。环氧树脂漆具有很多优点,但也有不足之处。1)、光老化性差环氧树脂中含有芳香蜜饯,漆膜经日光(紫外线)照射后易降解断链,所以户外耐候性较差。2)、通常的双酚A系环氧树脂不耐户外日晒,漆膜已失去光泽,然后粉化,不易用作户外的面漆。例如我国秦皇岛煤码头、按德国公司要求采用环氧树脂面漆、结果发生了粉化。3)、低温固化性差环氧树脂一般需在10℃以上固化,在10℃以下则反应缓慢而困难,对于大型物体如船舶、桥梁、港湾、油槽等旱季施工实为不便。虽可加些促进剂,或用多异氰酸酯作为固化剂,但毕竟是弱点。
发明内容
本发明的目的是克服现有技术的不足,提供一种高性能水性环保涂料的制备方法。
本发明采用的技术方案为:
一种高性能水性环保涂料的制备方法,该涂料由环氧树脂、三聚磷酸铝APW-1、云母粉、5A分子筛、固化剂制备得到,优选地,所述的环氧树脂为环氧树脂E-20(平均分子量900)、环氧树脂E-12(平均分子量1400)、环氧树脂E-06(平均分子量2900)或环氧树脂E-03(平均分子量3750)中的一种或两种以上的混合物。
优选地,所述的固化剂为聚酰胺胺类固化剂。
更优选地,所述的固化剂为聚酰胺树脂。
更优选地,各组分的重量份数为:环氧树脂:50-70份、三聚磷酸铝APW-1为10-12份,云母粉为4-6份,5A分子筛4-8份,固化剂10-20份,将上述组分充分混合,熟化0.5-1h即可使用。
本发明所具有的有益效果:
1)、漆膜对金属和非金属都有很强的粘接强度。可以制得高弹性的漆膜;
2)、耐气候性较好,户外用时漆膜较不易失光、粉化;
3)、施工性能好,漆膜不易产生桔皮、泛白的病态;漆的施工时限较长,对人体毒性较小;
4)、可以在除锈不充分的或较潮湿的钢铁表面施工,可制成水下施工的涂料;
5)、漆膜的耐化学品性,比多元胺固化环氧树脂漆有所下降。
6)、水性高性能环氧防腐涂料,由于其优良的附着力、抗化学性品腐蚀性、耐户外老化性,使得它的应用领域比普通的双酚A环氧防腐涂料大大扩展,不仅用于户内的机械设备、石油储罐内壁,也适用于防腐年限要求不是特别长的某些户外的机械设备、储罐外壁等。特别是它特有的环保性能,使它更具有普通环氧涂料所不具备的、能否满足某些具有环保要求的领域。
7)、本发明由于使用的是低分子量的环氧树脂,可以用水代替有机溶剂,符合环保要求。
具体实施方式
下面结合具体实施例对本发明作进一步说明,但不限定本发明的保护范围。
实施例1
一种高性能水性环保涂料的制备方法,该涂料由环氧树脂E-20、三聚磷酸铝APW-1、云母粉、5A分子筛、聚酰胺树脂制备得到,其中各组分的重量份数为:环氧树脂E-20:55份、三聚磷酸铝APW-1为12份,云母粉为6份,5A分子筛4份,聚酰胺树脂12份,将上述组分充分混合,熟化1h即可使用。
本发明产品已经通过具体的实施例进行了描述。本领域技术人员可以借鉴本发明的内容适当改变原料、工艺条件等环节来实现相应的其它目的,其相关改变都没有脱离本发明的内容,所有类似的替换和改动对于本领域技术人员来说是显而易见的,都被视为包括在本发明的范围之内。
Claims (5)
1.一种高性能水性环保涂料的制备方法,其特征在于:该涂料由环氧树脂、三聚磷酸铝APW-1、云母粉、5A分子筛、固化剂制备得到。
2.根据权利要求1所述的一种高性能水性环保涂料的制备方法,其特征在于:所述的环氧树脂为环氧树脂E-20、环氧树脂E-12、环氧树脂E-06或环氧树脂E-03中的一种或两种以上的混合物。
3.根据权利要求1所述的一种高性能水性环保涂料的制备方法,其特征在于:所述的固化剂为聚酰胺胺类固化剂。
4.根据权利要求3所述的一种高性能水性环保涂料的制备方法,其特征在于:所述的固化剂为聚酰胺树脂。
5.根据权利要求1所述的一种高性能水性环保涂料的制备方法,各组分的重量份数为:环氧树脂:50-70份、三聚磷酸铝APW-1为10-12份,云母粉为4-6份,5A分子筛4-8份,固化剂10-20份,将上述组分充分混合,熟化0.5-1h即可使用。