CN103386558A - 镀锌钢结构用埋弧焊剂 - Google Patents

镀锌钢结构用埋弧焊剂 Download PDF

Info

Publication number
CN103386558A
CN103386558A CN2013103147817A CN201310314781A CN103386558A CN 103386558 A CN103386558 A CN 103386558A CN 2013103147817 A CN2013103147817 A CN 2013103147817A CN 201310314781 A CN201310314781 A CN 201310314781A CN 103386558 A CN103386558 A CN 103386558A
Authority
CN
China
Prior art keywords
parts
submerged
welding flux
arc welding
arc
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013103147817A
Other languages
English (en)
Other versions
CN103386558B (zh
Inventor
杨杰
张艳荣
丁一峰
徐文敏
楼祖良
傅水忠
李济和
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
YUNNAN ATLANTIC WELDING CONSUMABLES Co Ltd
Guandaer Steel Structure (jiangsu) Co Ltd
Original Assignee
YUNNAN ATLANTIC WELDING CONSUMABLES Co Ltd
Guandaer Steel Structure (jiangsu) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YUNNAN ATLANTIC WELDING CONSUMABLES Co Ltd, Guandaer Steel Structure (jiangsu) Co Ltd filed Critical YUNNAN ATLANTIC WELDING CONSUMABLES Co Ltd
Priority to CN201310314781.7A priority Critical patent/CN103386558B/zh
Publication of CN103386558A publication Critical patent/CN103386558A/zh
Application granted granted Critical
Publication of CN103386558B publication Critical patent/CN103386558B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了镀锌钢结构用埋弧焊剂，其特征在于：该焊剂的成分按质量份为：SiO2 19-21份；TiO2 0.5-1.0份；MnO 3-5份；Al2O3 21-23份；CaO 3-5份；MgO 27-32份；CaF2 19-22份；不可避免的杂质2份。本发明的优点是：调整原材料配比，控制埋弧焊熔池弧长适中，渣熔点、粘度、表面张力适合、选择夹杂物少的原材料控制焊缝结晶过程带来的不理因素，调整高温烧结温度，控制焊剂中部分氧化物的再还原和焊接时熔池气氛，从而使埋弧焊缝表面光洁，热镀锌光亮无黑点。

Description

镀锌钢结构用埋弧焊剂
技术领域
本发明涉及一种镀锌钢结构用埋弧焊剂。
背景技术
烧结焊剂用原材料主要有CaF2、Al2O3、MgO、K2O、MnO等矿物，其中有部分矿物是已煅烧过，煅烧过的有些高价氧化物已被还原成低价氧化物，如高价的Fe2O3高温段稍后失氧成为FeO。Fe2O3+C=2FeO+CO，Feo+C=Fe+CO，FeO在埋弧焊高温熔池中极易还原，在埋弧焊熔池飞溅，焊接熔池中熔渣熔点、表面张力、粘度、熔池弧长不适宜时，在焊缝表面时有毛刺，毛刺周围带有细小粘渣，热度镀锌时形成黑点。
因此，为解决上述问题，特提供一种新的技术方案。
发明内容
本发明的目的是提供一种镀锌钢结构用埋弧焊剂。
本发明采用的技术方案是：
镀锌钢结构用埋弧焊剂，该焊剂的成分按质量份为：
SiO2        19-21份；
TiO2     0.5-1.0份；
MnO     3-5份；
Al2O3    21-23份；
CaO      3-5份；
MgO     27-32份；
CaF2     19-22份；
不可避免的杂质  2份。
本发明的优点是：通过调整原材料配比，来调整熔池中熔渣的熔点、表面张力、粘度、熔池弧长，控制熔池反应过程，其中CaF2在焊剂中主要是稀渣、提高碱度，在埋弧焊熔池中减低熔点、粘度、减小表面张力，增加弧长，Al2O3在焊剂中主要是造渣、降低碱度，在埋弧焊熔池中提高熔点、粘度，增加表面张力；MgO在焊剂中主要是提高碱度，在埋弧焊熔池中提高熔点、粘度，增加表面张力，K2O在埋弧焊熔池中稳弧，增加弧长，MnO在焊剂中提高力学性能，在埋弧焊熔池中减低粘度；
调整原材料配比，控制埋弧焊熔池弧长适中，渣熔点、粘度、表面张力适合、选择夹杂物少的原材料控制焊缝结晶过程带来的不理因素，调整高温烧结温度，控制焊剂中部分氧化物的再还原和焊接时熔池气氛，从而使埋弧焊缝表面光洁，热镀锌光亮无黑点。
具体实施方式
为了加深对本发明的理解，下面将结合实施例对本发明的作进一步详述，该实施例仅用于解释本发明的，并不构成对本发明的保护范围的限定。
实施例1
镀锌钢结构用埋弧焊剂，该焊剂的成分按质量份为：
SiO2        19份；
TiO2     0.5份；
MnO     3份；
Al2O3    21份；
CaO      3份；
MgO     27份；
CaF2     19份；
不可避免的杂质  2份。
实施例2
镀锌钢结构用埋弧焊剂，该焊剂的成分按质量份为：
SiO2        20份；
TiO2     0.8份；
MnO     4份；
Al2O3    22份；
CaO      4份；
MgO     30份；
CaF2     20份；
不可避免的杂质  2份。
实施例3
镀锌钢结构用埋弧焊剂，该焊剂的成分按质量份为：
SiO2        21份；
TiO2     1.0份；
MnO     5份；
Al2O3    23份；
CaO      5份；
MgO     32份；
CaF2     22份；
不可避免的杂质  2份。
本发明的优点是：通过调整原材料配比，来调整熔池中熔渣的熔点、表面张力、粘度、熔池弧长，控制熔池反应过程，其中CaF2在焊剂中主要是稀渣、提高碱度，在埋弧焊熔池中减低熔点、粘度、减小表面张力，增加弧长，Al2O3在焊剂中主要是造渣、降低碱度，在埋弧焊熔池中提高熔点、粘度，增加表面张力；MgO在焊剂中主要是提高碱度，在埋弧焊熔池中提高熔点、粘度，增加表面张力，K2O在埋弧焊熔池中稳弧，增加弧长，MnO在焊剂中提高力学性能，在埋弧焊熔池中减低粘度；
调整原材料配比，控制埋弧焊熔池弧长适中，渣熔点、粘度、表面张力适合、选择夹杂物少的原材料控制焊缝结晶过程带来的不理因素，调整高温烧结温度，控制焊剂中部分氧化物的再还原和焊接时熔池气氛，从而使埋弧焊缝表面光洁，热镀锌光亮无黑点。
表1  熔敷金属的力学性能
Figure DEST_PATH_IMAGE002A
从表1中可以看出镀锌钢结构用烧结焊剂的力学性能达到了要求并且具有较好的低温冲击韧性。

Claims (1)

1.镀锌钢结构用埋弧焊剂，其特征在于：该焊剂的成分按质量份为：
SiO2        19-21份；
TiO2     0.5-1.0份；
MnO     3-5份；
Al2O3    21-23份；
CaO      3-5份；
MgO     27-32份；
CaF2     19-22份；
不可避免的杂质  2份。
CN201310314781.7A 2013-07-25 2013-07-25 镀锌钢结构用埋弧焊剂 Expired - Fee Related CN103386558B (zh)