CN103382540A - 一种耐疲劳的不锈钢丝制备方法 - Google Patents

一种耐疲劳的不锈钢丝制备方法 Download PDF

Info

Publication number
CN103382540A
CN103382540A CN 201210132611 CN201210132611A CN103382540A CN 103382540 A CN103382540 A CN 103382540A CN 201210132611 CN201210132611 CN 201210132611 CN 201210132611 A CN201210132611 A CN 201210132611A CN 103382540 A CN103382540 A CN 103382540A
Authority
CN
China
Prior art keywords
stainless steel
steel wire
austenite
ferrite
phase stainless
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201210132611
Other languages
English (en)
Inventor
由国峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 201210132611 priority Critical patent/CN103382540A/zh
Publication of CN103382540A publication Critical patent/CN103382540A/zh
Pending legal-status Critical Current

Abstract

本发明是涉及一种耐疲劳的不锈钢丝制备方法。本发明提供了一种具有高抗疲劳性的不锈钢丝的制备方法。本发明包括奥氏体-铁素体双相不锈钢丝，在奥氏体-铁素体双相不锈钢丝外设置有奥氏体-铁素体双相不锈钢丝十分之一厚的抗疲劳层；将奥氏体-铁素体双相不锈钢丝放置于1150℃～1175℃的氮气内，1atm下反应23～25分钟；加压至7～8atm下升温至1200℃持续反应60～65分钟；降压至1atm气压下再升温至1240摄氏度，持续3小时，迅速降温至600～750℃，将氮气去除，保持45～50分钟；使奥氏体-铁素体双相不锈钢丝的组织共析转变。以65～70％的减面率冷拔成型。

Description

一种耐疲劳的不锈钢丝制备方法
技术领域
本发明是涉及一种耐疲劳的不锈钢丝制备方法。
背景技术
现有的不锈钢，具有很好的耐腐蚀性，在各种行业上，均有应用；不锈钢有四种，1、铁素体不锈钢，其耐蚀性、韧性和可焊性随含铬量的增加而提高，耐氯化物应力腐蚀性能优于其他种类不锈钢。2、奥氏体不锈钢，可耐多种介质腐蚀。3、马氏体不锈钢，强度高，但塑性和可焊性较差。4、奥氏体-铁素体双相不锈钢，兼有奥氏体和铁素体不锈钢的优点，并具有超塑性。
利用奥氏体-铁素体双相不锈钢可以制作一些不锈钢丝，应用于特殊领域。
但是，这种不锈钢丝的抗疲劳性差。某些既需要抗腐蚀，又需要具有良好的抗疲劳性的场合下，无法使用。
发明内容
本发明就是针对上述问题，提供了一种具有高抗疲劳性的不锈钢丝的制备方法。
本发明包括奥氏体-铁素体双相不锈钢丝，在奥氏体-铁素体双相不锈钢丝外设置有奥氏体-铁素体双相不锈钢丝十分之一厚的抗疲劳层；所述的奥氏体-铁素体双相不锈钢丝的成分为：
C： 0.005～0.05％、
Si：0.1～3.0％、
Mn：0.2～5.0％、
Ni：0.2～4.0％、
Cr：18～30％、
Mo：3.0％以下、
Cu：2.0％以下、
N： 0.35～1.0％
余量为Fe和无法去除的杂质；
其特征在于：1、将上述成分的奥氏体-铁素体双相不锈钢丝放置于1150℃～1175℃的氮气内，1atm下反应23～25分钟；加压至7～8atm下升温至1200℃持续反应60～65分钟；降压至1atm气压下再升温至1240摄氏度，持续3小时，
2、迅速降温至600～750℃，将氮气去除，保持45～50分钟；使奥氏体-铁素体双相不锈钢丝的组织共析转变。
3、以65～70％的减面率冷拔成型。
本发明的有益效果：
本发明的方法可使不锈钢丝的抗疲劳强度达到2000MPa～3500MPa。
具体实施方式
本发明包括奥氏体-铁素体双相不锈钢丝，在奥氏体-铁素体双相不锈钢丝外设置有奥氏体-铁素体双相不锈钢丝十分之一厚的抗疲劳层；所述的奥氏体-铁素体双相不锈钢丝的成分为：
C： 0.005～0.05％、
Si：0.1～3.0％、
Mn：0.2～5.0％、
Ni：0.2～4.0％、
Cr：18～30％、
Mo：3.0％以下、
Cu：2.0％以下、
N： 0.35～1.0％，
余量为Fe和无法去除的杂质；
抗疲劳层的其制备方法是：1、将上述成分的奥氏体-铁素体双相不锈钢丝放置于1150℃～1175℃的氮气内，1atm下反应23～25分钟；加压至7～8atm下升温至1200℃持续反应60～65分钟；降压至1atm气压下再升温至1240摄氏度，持续3小时；
2、迅速降温至600～750℃，将氮气去除，保持45～50分钟；使奥氏体-铁素体双相不锈钢丝的组织共析转变；
3、以65～70％的减面率冷拔成型。
实施例1：
奥氏体-铁素体双相不锈钢丝的成分为：
C： 0.005～0.05％、
Si：0.1～3.0％、
Mn：0.2～5.0％、
Ni：0.2～4.0％、
Cr：18～30％、
Mo：3.0％以下、
Cu：2.0％以下、
N： 0.35～1.0％，
余量为Fe和无法去除的杂质；
抗疲劳层的其制备方法是：1、将上述成分的奥氏体-铁素体双相不锈钢丝放置于1150℃～1175℃的氮气内，1atm下反应23～25分钟；加压至7～8atm下升温至1200℃持续反应60～65分钟；降压至1atm气压下再升温至1240摄氏度，持续3小时；
2、迅速降温至695～697℃，将氮气去除，保持48分钟；使奥氏体-铁素体双相不锈钢丝的组织共析转变；
3、以65.5％的减面率冷拔成型。
经试验证明：该方法所获得的不锈钢丝的抗疲劳强度可达5000MPa。

Claims (2)

1.一种耐疲劳的不锈钢丝制备方法，其特征在于：包括奥氏体-铁素体双相不锈钢丝，在奥氏体-铁素体双相不锈钢丝外设置有奥氏体-铁素体双相不锈钢丝十分之一厚的抗疲劳层；所述的奥氏体-铁素体双相不锈钢丝的成分为：
C： 0.005～0.05％、
Si：0.1～3.0％、
Mn：0.2～5.0％、
Ni：0.2～4.0％、
Cr：18～30％、
Mo：3.0％以下、
Cu：2.0％以下、
N： 0.35～1.0％，
余量为Fe和无法去除的杂质；
抗疲劳层的其制备方法是：(1)将上述成分的奥氏体-铁素体双相不锈钢丝放置于1150℃～1175℃的氮气内，1atm下反应23～25分钟；加压至7～8atm下升温至1200℃持续反应60～65分钟；降压至1atm气压下再升温至1240摄氏度，持续3小时；
(2)迅速降温至600～750℃，将氮气去除，保持45～50分钟；使奥氏体-铁素体双相不锈钢丝的组织共析转变；
(3)以65～70％的减面率冷拔成型。
2.根据权利要求1所述的一种耐疲劳的不锈钢丝制备方法，其特征在于：抗疲劳层的其制备方法是：
步骤1：
将上述成分的奥氏体-铁素体双相不锈钢丝放置于1150℃～1175℃的氮气内，1atm下反应23～25分钟；加压至7～8atm下升温至1200℃持续反应60～65分钟；降压至1atm气压下再升温至1240摄氏度，持续3小时；
步骤2：
迅速降温至695～697℃，将氮气去除，保持48分钟；使奥氏体-铁素体双相不锈钢丝的组织共析转变；
步骤3：
以65.5％的减面率冷拔成型。
CN 201210132611 2012-05-02 2012-05-02 一种耐疲劳的不锈钢丝制备方法 Pending CN103382540A (zh)