CN103382108A - 一种低功耗软磁锰锌铁氧体材料及其制备方法 - Google Patents

一种低功耗软磁锰锌铁氧体材料及其制备方法 Download PDF

Info

Publication number
CN103382108A
CN103382108A CN201310258936XA CN201310258936A CN103382108A CN 103382108 A CN103382108 A CN 103382108A CN 201310258936X A CN201310258936X A CN 201310258936XA CN 201310258936 A CN201310258936 A CN 201310258936A CN 103382108 A CN103382108 A CN 103382108A
Authority
CN
China
Prior art keywords
hour
power consumption
ferrite material
sintering
consumption soft
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310258936XA
Other languages
English (en)
Other versions
CN103382108B (zh
Inventor
肖宪书
文庆华
张俊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BENGBU CITY GAOHUA ELECTRONIC Co Ltd
Original Assignee
BENGBU CITY GAOHUA ELECTRONIC Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BENGBU CITY GAOHUA ELECTRONIC Co Ltd filed Critical BENGBU CITY GAOHUA ELECTRONIC Co Ltd
Priority to CN201310258936.XA priority Critical patent/CN103382108B/zh
Publication of CN103382108A publication Critical patent/CN103382108A/zh
Application granted granted Critical
Publication of CN103382108B publication Critical patent/CN103382108B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种低功耗软磁锰锌铁氧体材料及其制备方法，其特征在于,主成分按摩尔份计包括：0.2-0.3mol In2O3、31-31.5mol Fe3O4、8-8.5mol ZnO、18-18.5mol Fe2O3、9.2-9.5mol Mn3O4，主成分中添加的改性杂质按照占所述低功耗软磁锰锌铁氧体材料的重量计包括：360-380ppm HfO2、110-130ppm La2O3、210-240ppm ZrO2、430-450ppm V2O5、460-480ppm CaO、220-230ppm Cr2O3、320-330ppm Be；本发明具有高初始磁导率ui、高居里温度且具宽频特性等优点。

Description

一种低功耗软磁锰锌铁氧体材料及其制备方法
技术领域
本发明涉及磁性材料技术领域，具体地，本发明涉及一种低功耗软磁锰锌铁氧体材料及其制备方法。
背景技术
磁通密度高铁氧体磁粉、磁芯是实现程控通讯、数字技术、网络通讯彩电等电子设备中用作电感器、滤波器、脉冲变压器等产品使其小型化、轻量化必不可少的电子材料，不断提高磁性材料中的磁通密度，一直是从事该专业的工程技术人员和生产厂商的追求，且材料的性能指标，如损耗、频率特性、居里温度等都不尽人意。
发明内容
本发明的目的是提供一种低功耗软磁锰锌铁氧体材料及其制备方法。
本发明所采用的技术方案是：
    一种低功耗软磁锰锌铁氧体材料，其特征在于,主成分按摩尔份计包括：0.2-0.3mol In2O3、31-31.5mol Fe3O4、8-8.5molZnO、18-18.5mol Fe2O3、9.2-9.5mol Mn3O4，主成分中添加的改性杂质按照占所述低功耗软磁锰锌铁氧体材料的重量计包括：360-380ppm HfO2、110-130ppm La2O3、210-240ppm ZrO2、430-450ppm V2O5、460-480ppm CaO、220-230ppm Cr2O3、320-330ppm Be；
所述的低功耗软磁锰锌铁氧体材料的制备方法，其特征在于包括以下步骤：
（1）配料：对主成分进行配料，并添加改性杂质；
（2）一次烧结：配料混合在360℃-380℃的条件下预烧1-2小时，再升温至670℃-690℃的条件下预烧1-2小时，再升温至870℃-930℃的条件下预烧2-3小时，得预烧料；
 （3）球磨、压坯：将预烧料放入砂磨机中，同时加入相当于配料0.6-1.0wt%聚乙烯醇、1.0-1.2wt%分散料、适量去离子水进行砂磨90-120分钟，得浆料，并烘干；将烘干的粉料加入1.2-1.8wt%的聚乙烯醇、0.2-0. 4wt%的硬酯酸，造粒，装入模具，在75-85Mpa压力下压制成坯件，自然晾干；
 （4）二次烧结：将磁芯毛坯放入氮气气氛保护推板窑内烧结，先以150-190℃/小时的升温速率升至620-650℃，烧结2-3小时；再以180-220℃/小时的升温速率升至820-840℃，烧结1-2小时；调整氮气氛中氧含量为0.5%-0.6%，以80-110℃/小时的升温速率升温至1050-1090℃，保温120-150分钟；再以180-210℃/小时的升温速率升至1370-1410℃，保温烧结3-4小时；然后降温，调整氮气氛中氧含量为1.1%-1.3%以130-160℃/小时的降温速率降温至750-780℃，保温1-2小时，再以150-180℃/小时的降温速率降温至室温。
步骤（3）中所述的分散料由以下重量份的原料制得：微晶石蜡3-4、硬脂酸锌2-3、氨丙基三乙氧基硅烷0.5-0.8、SnO2 0.3-0.5、纳米级二氧化钛0.3-0.5、铁粉1.2-0.5、丙三醇三甘油酸酯2.3-2.5；
制备方法是：将各物料混合，研磨分散均匀即可。
 本发明具有高初始磁导率ui、高居里温度且具宽频特性等优点。
具体实施方式
    一种低功耗软磁锰锌铁氧体材料，其特征在于,主成分按摩尔份计包括：0.3mol In2O3、31.5mol Fe3O4、8.5molZnO、18.5mol Fe2O3、9.5mol Mn3O4,主成分中添加的改性杂质按照占所述低功耗软磁锰锌铁氧体材料的重量计包括：380ppm HfO2、130ppm La2O3、240ppm ZrO2、450ppm V2O5、480ppm CaO、220ppm Cr2O3、330ppm Be；
    低功耗软磁锰锌铁氧体材料的制备方法，包括以下步骤：
   （1）配料：对主成分进行配料，并添加改性杂质；
（2）一次烧结：配料混合在360℃-380℃的条件下预烧1-2小时，再升温至670℃-690℃的条件下预烧1-2小时，再升温至870℃-930℃的条件下预烧2-3小时，得预烧料；
 （3）球磨、压坯：将预烧料放入砂磨机中，同时加入相当于配料0.6-1.0wt%聚乙烯醇、1.0-1.2wt%分散料、适量去离子水进行砂磨90-120分钟，得浆料，并烘干；将烘干的粉料加入1.2-1.8wt%的聚乙烯醇、0.2-0. 4wt%的硬酯酸，造粒，装入模具，在75-85Mpa压力下压制成坯件，自然晾干；
（4）二次烧结：将磁芯毛坯放入氮气气氛保护推板窑内烧结，先以150-190℃/小时的升温速率升至620-650℃，烧结2-3小时；再以180-220℃/小时的升温速率升至820-840℃，烧结1-2小时；调整氮气氛中氧含量为0.5%-0.6%，以80-110℃/小时的升温速率升温至1050-1090℃，保温120-150分钟；再以180-210℃/小时的升温速率升至1370-1410℃，保温烧结3-4小时；然后降温，调整氮气氛中氧含量为1.1%-1.3%以130-160℃/小时的降温速率降温至750-780℃，保温1-2小时，再以150-180℃/小时的降温速率降温至室温；
步骤（3）中所述的分散料由以下重量份（公斤）的原料制得：微晶石蜡4、硬脂酸锌3、氨丙基三乙氧基硅烷0.8、SnO20.5、纳米级二氧化钛0.5、铁粉1.2、丙三醇三甘油酸酯2.5；
制备方法是：将各物料混合，研磨分散均匀即可。
通过上述实施例制得的软磁铁氧体磁芯的性能数据：
序号 技术指标名称 技术指标 备注
1 初始磁导率（25±3℃） 8700±25%  
2 功率损耗（100Kc、200mT）单位：KW/m3 573(25±2℃), 295(100±2℃)  
3 饱和磁通密度mT（100℃） 498  
4 居里温度℃ >270  

Claims (2)

1.一种低功耗软磁锰锌铁氧体材料，其特征在于,主成分按摩尔份计包括：0.2-0.3mol In2O3、31-31.5mol Fe3O4、8-8.5molZnO、18-18.5mol Fe2O3、9.2-9.5mol Mn3O4，主成分中添加的改性杂质按照占所述低功耗软磁锰锌铁氧体材料的重量计包括：360-380ppm HfO2、110-130ppm La2O3、210-240ppm ZrO2、430-450ppm V2O5、460-480ppm CaO、220-230ppm Cr2O3、320-330ppm Be。
2.根据权利要求1所述的低功耗软磁锰锌铁氧体材料的制备方法，其特征在于包括以下步骤：
（1）配料：对主成分进行配料，并添加改性杂质；
（2）一次烧结：配料混合在360℃-380℃的条件下预烧1-2小时，再升温至670℃-690℃的条件下预烧1-2小时，再升温至870℃-930℃的条件下预烧2-3小时，得预烧料；
（3）球磨、压坯：将预烧料放入砂磨机中，同时加入相当于配料0.6-1.0wt%聚乙烯醇、1.0-1.2wt%分散料、适量去离子水进行砂磨90-120分钟，得浆料，并烘干；将烘干的粉料加入1.2-1.8wt%的聚乙烯醇、0.2-0.4wt%的硬酯酸，造粒，装入模具，在75-85Mpa压力下压制成坯件，自然晾干；
（4）二次烧结：将磁芯毛坯放入氮气气氛保护推板窑内烧结，先以150-190℃/小时的升温速率升至620-650℃，烧结2-3小时；再以180-220℃/小时的升温速率升至820-840℃，烧结1-2小时；调整氮气氛中氧含量为0.5%-0.6%，以80-110℃/小时的升温速率升温至1050-1090℃，保温120-150分钟；再以180-210℃/小时的升温速率升至1370-1410℃，保温烧结3-4小时；然后降温，调整氮气氛中氧含量为1.1%-1.3%以130-160℃/小时的降温速率降温至750-780℃，保温1-2小时，再以150-180℃/小时的降温速率降温至室温；
步骤（3）中所述的分散料由以下重量份的原料制得：微晶石蜡3-4、硬脂酸锌2-3、氨丙基三乙氧基硅烷0.5-0.8、SnO2 0.3-0.5、纳米级二氧化钛0.3-0.5、铁粉1.2-1.5、丙三醇三甘油酸酯2.3-2.5；
制备方法是：将各物料混合，研磨分散均匀即可。
CN201310258936.XA 2013-06-26 2013-06-26 一种低功耗软磁锰锌铁氧体材料及其制备方法 Expired - Fee Related CN103382108B (zh)