CN103381316A - 一种具有杀菌抑菌作用的空气过滤网及制备方法 - Google Patents

一种具有杀菌抑菌作用的空气过滤网及制备方法 Download PDF

Info

Publication number
CN103381316A
CN103381316A CN2012101401448A CN201210140144A CN103381316A CN 103381316 A CN103381316 A CN 103381316A CN 2012101401448 A CN2012101401448 A CN 2012101401448A CN 201210140144 A CN201210140144 A CN 201210140144A CN 103381316 A CN103381316 A CN 103381316A
Authority
CN
China
Prior art keywords
matrix
preparation
substrate
metal
filter screen
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012101401448A
Other languages
English (en)
Other versions
CN103381316B (zh
Inventor
陈华棠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DONGGUAN DAOGU ELECTRONIC MATERIAL TECHNOLOGY Co Ltd
Original Assignee
DONGGUAN DAOGU ELECTRONIC MATERIAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DONGGUAN DAOGU ELECTRONIC MATERIAL TECHNOLOGY Co Ltd filed Critical DONGGUAN DAOGU ELECTRONIC MATERIAL TECHNOLOGY Co Ltd
Priority to CN201210140144.8A priority Critical patent/CN103381316B/zh
Publication of CN103381316A publication Critical patent/CN103381316A/zh
Application granted granted Critical
Publication of CN103381316B publication Critical patent/CN103381316B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及清洁用具技术领域，特指一种具有杀菌抑菌作用的空气过滤网及制备方法，其包括过滤网上设有杀菌、抑菌镀膜金属，具体步骤如下：(1)、选择基体，基体选择海绵，无纺布、网纱、柔性可卷绕透气材料中的任意一种；(2)、对上述基体进行表面清洗，除污，表面粗化处理；(3)、氩气保护下真空磁控溅射镀膜；(4)、然后再在钝化溶液中浸泡，使其表面形成钝化膜，将基材清洗，烘干，再进行提高金属层的结合力真空淬火工序；(5)、将上述基材两层中间添加活性炭，制成过滤网，本方法很好地抑制细菌、病毒、藻类和真菌，又有强有力的对抗疾病的效果。

Description

一种具有杀菌抑菌作用的空气过滤网及制备方法
技术领域：
本发明涉及清洁用具技术领域，特指一种具有杀菌抑菌作用的空气过滤网及制备方法。
背景技术：
空气的清洁度决定人们健康质量的品质，人们长期呼入不清洁的空气会产生疾病。
目前，空调、空气清洁器采用的过滤网，在长期的使用过程中，空气中的细菌吸附在过滤网中，由于普通过滤网难以杀灭所捕集的细菌，同时，细菌在过滤网繁殖并随着空气流动引起二次污染，给人们的生活带来不健康的因素。
发明内容：
本发明的目的是针对现有技术的不足而提供一种具有杀菌抑菌作用的空气过滤网及制备方法，本方法所解决的技术问题是通过在海绵、网纱等材料上利用真空溅射镀膜技术，在其表面溅射一种或多种具有杀菌抑菌作用的金属或多种金属的合金，再进行钝化处理，很好地抑制细菌、病毒、藻类和真菌，又有强有力的对抗疾病的效果。
为实现上述目的，本发明采用如下技术方案：其包括过滤网上设有杀菌、抑菌镀膜金属。
一种具有杀菌抑菌作用的空气过滤网的制备方法，具体步骤如下：
(1)、选择基体，基体选择海绵，无纺布、网纱、柔性可卷绕透气材料中的任意一种，基体宽度为500MM至1200MM之间，厚度为0.005MM至3MM之间。
(2)、对上述基体进行表面清洗，除污，表面粗化处理，然后修边备用。
(3)、氩气保护下真空磁控溅射镀膜；真空度6×10-1至9×10-4Pa，基体移动速度为0.5m/min-50m/min；金属离子溅射厚度50-5000埃，溅射靶材为：纯黄铜金属靶或几种金属的合金靶，合金比例为黄铜70％-90％，银5％-1％，纯铜25％-9％。
(4)、基体的单面或双面附着一层上述金属镀层后，然后进行化学沉铜处理工艺，沉铜配比如下：酒石酸钾钠90-120克、硫酸铜20-30克、氢氧化纳30-40克、蒸馏水1升制成A液，然后A液与8-15毫升的甲酫(浓度为36-40％)按比例100∶8-15混合。
(5)、化学沉铜处理完毕后，进行抗氧化保护处理，将基材放置在抗氧化溶液中浸泡0.5-3分钟，使其表面形成防止金属层长期暴露在空气氧化的一层钝化膜，将基材清洗.烘干，最后包装成品。
(6)、再进行提高金属层的结合力真空淬火工序，将上述基材两层中间添加活性炭，制成过滤网。
抗氧化溶液(钝化液)的制方法如下：将5.0g苯并三唑，5.0g甲基苯并三氮唑，20mL水与10mL甲醛(体积分数为37％水溶液)混合，加热，电磁搅拌，有白色粉末状物质产生后，加热到100℃，沉淀完全溶解，保温50-70分钟，冷却，过滤得到白色针状1-羟甲基苯并三氮唑，1-羟甲基苯并三氮唑与乙二胺混合，呈淡黄色溶液。
本发明有益效果为：氩气保护下真空磁控溅射镀膜；真空度6×10-1至9×10-4Pa，基体移动速度为0.5m/min-50m/min；金属离子溅射厚度50-5000埃，溅射靶材为：纯黄铜金属靶或几种金属的合金靶，合金比例为黄铜70％-90％，银5％-1％，纯铜25％-9％，基体的单面或双面附着一层上述金属镀层后，然后再在抗氧化溶液(钝化溶)液中浸泡0.5-3分钟，使其表面形成防止金属层长期暴露在空气氧化的一层钝化膜，将基材清洗，烘干，再进行提高金属层的结合力真空淬火工序，将上述基材两层中间添加活性炭，制成过滤网，在其表面溅射一种或多种具有杀菌抑菌作用的金属或多种金属的合金，再进行钝化处理，很好地抑制细菌、病毒、藻类和真菌，又有强有力的对抗疾病的效果。
附图说明：
图1是本发明的截面结构示意图。
具体实施方式：
见图1所示：本发明包括过滤网上设有杀菌、抑菌镀膜金属。
一种具有杀菌抑菌作用的空气过滤网的制备方法，具体步骤如下：
(1)、选择基体，基体选择海绵，无纺布、网纱、柔性可卷绕透气材料中的任意一种，基体宽度为500MM至1200MM之间，厚度为0.005MM至3MM之间。
(2)、对上述基体进行表面清洗，除污，表面粗化处理，然后修边备用。
(3)、氩气保护下真空磁控溅射镀膜；真空度6×10-1至9×10-4Pa，基体移动速度为0.5m/min-50m/min；金属离子溅射厚度50-5000埃，溅射靶材为：纯黄铜金属靶或几种金属的合金靶，合金比例为黄铜70％-90％，银5％-1％，纯铜25％-9％。
(4)、基体的单面或双面附着一层上述金属镀层后，然后进行化学沉铜处理工艺，沉铜配比如下：酒石酸钾钠90-120克、硫酸铜20-30克、氢氧化纳30-40克、蒸馏水1升制成A液，然后A液与8-15毫升的甲酸(浓度为36-40％)按比例100∶8-15混合。
(5)、化学沉铜处理完毕后，进行抗氧化保护处理，将基材放置在抗氧化溶液中浸泡0.5-3分钟，使其表面形成防止金属层长期暴露在空气氧化的一层钝化膜，使其表面形成防止金属层长期暴露在空气氧化的一层钝化膜，将基材清洗，烘干，淬火工序。将基材放入真空炉中，抽真空达到1.0×10-2Pa。充入保护气体氩气，加温到200-500度，取出基体迅速放入0°的纯水中，纯水的导电率要小于1.0μs/cm2。当基材温度降到50度时，取出基材，烘干。
(6)、再进行提高金属层的结合力真空淬火工序，将上述基材两层中间添加活性炭，制成过滤网。
抗氧化溶液(钝化液)的制方法如下：将5.0g苯并三唑，5.0g甲基苯并三氮唑，20mL水与10mL甲醛(体积分数为37％水溶液)混合，加热，电磁搅拌，有白色粉末状物质产生后，加热到100℃，沉淀完全溶解，保温50-70分钟，冷却，过滤得到白色针状1-羟甲基苯并三氮唑，1-羟甲基苯并三氮唑与乙二胺混合，呈淡黄色溶液。
本发明安装在空调、空气清洁器上作过滤网用，铜对艾希氏大肠杆菌，产气肠杆菌，沙门氏菌，大肠杆菌、螺旋菌、军团菌、葡萄球菌、脊髓灰质病毒等有抑止繁衍和杀死的作用，银离子和含银化合物可以杀死或者抑制细菌、病毒、藻类和真菌，它又有对抗疾病的效果，所以又被称为亲生物金属，本发明能给人们的生活带来健康的保障，净化空气，清洁空气。
主要步骤如下：1；真空溅射一层金属膜层→化学沉铜处理→抗氧化保护。传统的工艺流程；1；真空溅射一层金属膜层→电镀铜→抗氧化保护。2；沉铜前的处理→活化处理→化学镀铜→抗氧化保护。传统工艺流程(1)主要缺点是电镀铜的电镀设备造价高和生产受制于供电的影响。传统工艺流程(2)主要缺点是沉铜前的处理和活化处理的工艺复杂，有大量的废水要处理并且生产成本比较高。我们整个先进的工艺流程都在传统工艺流程(1)和(2)的缺点中改进，无论在设备造价、生产成本、废水处理都比传统工艺流程(1)和(2)要好，所以具有创新性。第二特征，抗氧化保护处理液的使用为37％水溶液)混合，加热，电磁搅拌，有白色粉末状物质产生后，加热到100℃，沉淀完全溶解，保温50-70分钟，冷却，过滤得到白色针状1-羟甲基苯并三氮唑。将1-羟甲基苯并三氮唑与乙二胺1；4摩尔比混合，呈淡黄色溶液。
以上所述仅是本发明的较佳实施例，故凡依本发明专利申请范围所述的构造、特征及原理所做的等效变化或修饰，均包括于本发明专利申请范围内。

Claims (3)

1.一种具有杀菌抑菌作用的空气过滤网，其包括，其特征在于：过滤网上设有杀菌、抑菌镀膜金属。
2.根据权利要求1所述的一种具有杀菌抑菌作用的空气过滤网的制备方法，具体步骤如下：
(1)、选择基体，基体选择海绵，无纺布、网纱、柔性可卷绕透气材料中的任意一种，基体宽度为500MM至1200MM之间，厚度为0.005MM至3MM之间。
(2)、对上述基体进行表面清洗，除污，表面粗化处理，然后修边备用。
(3)、氩气保护下真空磁控溅射镀膜；真空度6×10-1至9×10-4Pa，基体移动速度为0.5m/min-50m/min；金属离子溅射厚度50-5000埃，溅射靶材为：纯黄铜金属靶或几种金属的合金靶，合金比例为黄铜70％-90％，银5％-1％，纯铜25％-9％。
(4)、基体的单面或双面附着一层上述金属镀层后，然后进行化学沉铜处理工艺，沉铜配比如下：酒石酸钾钠90-120克、硫酸铜20-30克、氢氧化纳30-40克、蒸馏水1升制成A液，然后A液与8-15毫升的甲酸(浓度为36-40％)按比例100∶8-15混合。
(5)、化学沉铜处理完毕后，进行抗氧化保护处理，将基材放置在抗氧化溶液中浸泡0.5-3分钟，使其表面形成防止金属层长期暴露在空气氧化的一层钝化膜，将基材清洗.烘干，最后包装成品。
(6)、再进行提高金属层的结合力真空淬火工序，将上述基材两层中间添加活性炭，制成过滤网。
3.根据权利要求2所述的一种具有杀菌抑菌作用的空气过滤网的制备方法，其特征在于：抗氧化溶液(钝化液)的制方法如下：将5.0g苯并三唑，5.0g甲基苯并三氮唑，20mL水与10mL甲醛(体积分数为37％水溶液)混合，加热，电磁搅拌，有白色粉末状物质产生后，加热到100℃，沉淀完全溶解，保温50-70分钟，冷却，过滤得到白色针状1-羟甲基苯并三氮唑，1-羟甲基苯并三氮唑与乙二胺混合，呈淡黄色溶液。
CN201210140144.8A 2012-05-04 2012-05-04 一种具有杀菌抑菌作用的空气过滤网及制备方法 Expired - Fee Related CN103381316B (zh)