CN103374704B - 制造异地可钢化双银低辐射镀膜玻璃的方法 - Google Patents

制造异地可钢化双银低辐射镀膜玻璃的方法 Download PDF

Info

Publication number
CN103374704B
CN103374704B CN201210124827.4A CN201210124827A CN103374704B CN 103374704 B CN103374704 B CN 103374704B CN 201210124827 A CN201210124827 A CN 201210124827A CN 103374704 B CN103374704 B CN 103374704B
Authority
CN
China
Prior art keywords
layer
silver
plating
power
toughened
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210124827.4A
Other languages
English (en)
Other versions
CN103374704A (zh
Inventor
杨宏斌
李忠祥
康延坡
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing Wuhua Tianbao Coating S & T Co Ltd
Original Assignee
Beijing Wuhua Tianbao Coating S & T Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing Wuhua Tianbao Coating S & T Co Ltd filed Critical Beijing Wuhua Tianbao Coating S & T Co Ltd
Priority to CN201210124827.4A priority Critical patent/CN103374704B/zh
Publication of CN103374704A publication Critical patent/CN103374704A/zh
Application granted granted Critical
Publication of CN103374704B publication Critical patent/CN103374704B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明所述的一种制造异地可钢化双银低辐射镀膜玻璃的方法，包含以下步骤：镀基层复合介质层，镀第一阻挡层，镀第一银层，镀中层介质层，镀第二阻挡层，镀第二银层，镀顶层。异地可钢化LOWE无须马上合成中空，生产出来的双银低辐射玻璃，镀完膜后可以保存6个月之久，并且可以远程运输到异地加工。在镀膜后可以进行异地高温钢化处理工艺热处理，而不影响产品的质量。这就意味该膜层的表面机械性能，化学性能，光学性能都远远超过过去所谓先钢后镀的双银产品。

Description

制造异地可钢化双银低辐射镀膜玻璃的方法
技术领域
本发明涉及一种制造玻璃的工艺，特别是一种制造异地可钢化双银低辐射镀膜玻璃的方法。
背景技术
LOWE玻璃，即低辐射玻璃。通俗讲LOWE玻璃对短波辐射基本透明，使可见光基本通过，而对长波红外辐射则不能通过。即冬天保持房间热能，使其难以向外散发，而夏天将室外高温散发的大量热辐射阻挡在外，使其难以进入房间，做到“冬暖夏凉”，从而具有优异的隔热，保温效果。
异地可钢化双银低辐射镀膜玻璃生产技术主要采用磁控真空溅射法和离线真空溅射法，离线真空溅射法又分为两种：先钢后镀和远程可钢。先钢后镀是先将浮法原片钢化后镀双银LOWE，镀膜后必须马上合成中空玻璃，否则膜层与空气长时间接触会被氧化从而容易丧失LOWE节能性。
发明内容
本发明所要解决的技术问题是提供一种制造异地可钢化双银低辐射镀膜玻璃的方法。
为解决上述技术问题，本发明是按如下方式实现的：一种制造异地可钢化双银低辐射镀膜玻璃的方法，包含以下步骤：
镀基层复合介质层，Si3N4工作气压控制在在3-5mbar，功率为30-50KW；ZnO在氧氩气之比为1∶30的氛围中沉积，功率为5kw-30kw；
镀第一阻挡层，在纯氩氛围中溅射镍铬合金，功率为3kw-15kw；
镀第一银层，在纯氩气氛围中沉积，功率为2kw-15kw；
镀中层介质层，功率为30kw-80kw；
镀第二阻挡层，在纯氩氛围中溅射镍铬合金，功率为3kw-15kw；
镀第二银层，在纯氩气氛围中沉积，功率为2kw-15kw。
镀顶层，功率为15kw-60kw。
本发明的积极效果是：异地可钢化LOWE无须马上合成中空，生产出来的双银低辐射玻璃，镀完膜后可以保存6个月之久，并且可以远程运输到异地加工。在镀膜后可以进行异地高温钢化处理工艺热处理，而不影响产品的质量。这就意味该膜层的表面机械性能，化学性能，光学性能都远远超过过去所谓先钢后镀的双银产品。该产品光学性能如下：
可见光透过率T＝64％
可见光玻璃面反射率＝10％
可见光玻璃面色坐标a*值＝-2.2
色坐标b*值＝-11
玻璃的辐射率“＝0.028
附图说明
图1是本发明第一实施例所提供的制造异地可钢化双银低辐射镀膜玻璃的方法示意图。
具体实施方式
下面结合附图和具体实施方式对本发明作进一步详细的说明。
异地可钢化双银低辐射的膜层结构自浮法原片向外层依次为：浮法原片/基层复合介质层/第一阻挡层/第一银层/中层复合介质层/第二阻挡层/第二银层/复合顶层。
1、基层复合介质层包含：Si3N4和ZnO，膜层厚度为30nm～55nm。
2、第一银层包含：Ag，膜层厚度为10nm～25nm。
3、阻挡层通常为Cr、NiCr、Ti等金属元素，膜层厚度为3nm～10nm。
4、中层复合介质层包含：Si3N4和ZnO，膜层厚度为60nm～90nm。
5、第二银层包含：Ag，膜层厚度为10nm～25nm。
6、复合顶层包含Si3N4或SnO2、TiO2，膜层厚度为40nm～70nm。
如图1所示，本发明第一实施例所提供的制造异地可钢化双银低辐射镀膜玻璃的方法，包括以下步骤：
1)、浮法原片的清洗和干燥。
2)、镀基层复合介质层：包含氮化硅(Si3N4)和氧化锌(ZnO)，Si3N4工作气压在3-5mbar，功率为30-50KW。吸收层为ZnO，ZnO在氧氩气之比1∶30氛围中沉积，功率为5kw-30kw。
3)、镀第一阻挡层：包含NiCr：在纯氩氛围中溅射镍铬合金，功率为3kw-15kw。
4)、镀第一银层：包含银(Ag)在纯氩气氛围中沉积，功率为2kw-15kw。
5)、镀中层介质层：包含氮化硅(S13N4)，功率为30kw-80kw。
6)、镀第二阻挡层：包含NiCr：在纯氩氛围中溅射镍铬合金，功率为3kw-15kw。
7)、镀第二银层：包含银(Ag)在纯氩气氛围中沉积，功率为2kw-15kw。
8)、镀顶层：顶层氮化硅Si3N；镀层：Si3N；功率为15kw-60kw。
9)、检验产品。
本发明的积极效果是：异地可钢化LOWE无须马上合成中空，生产出来的双银低辐射玻璃，镀完膜后可以保存6个月之久，并且可以远程运输到异地加工。在镀膜后可以进行异地高温钢化处理工艺热处 理，而不影响产品的质量。这就意味该膜层的表面机械性能，化学性能，光学性能都远远超过过去所谓先钢后镀的双银产品。。

Claims (2)

1.一种制造异地可钢化双银低辐射镀膜玻璃的方法，其特征在于，包括以下步骤，
镀基层复合介质层，Si3N4工作气压控制在3-5mbar,功率为30-50kW；Zn0在氧氩气之比为1:30的氛围中沉积，功率为5kW-30kW；
镀第一阻挡层，在纯氩氛围中溅射镍铬合金，功率为3kW-15kW；
镀第一银层，在纯氩气氛围中沉积，功率为2kW-15kW；
镀中层介质层，功率为30kW-80kW；
镀第二阻挡层，在纯氩氛围中溅射镍铬合金，功率为3kW-15kW；
镀第二银层，在纯氩气氛围中沉积，功率为2kW-15kW；
镀顶层，功率为15kW-60kW。
2.如权利要求1所述的制造异地可钢化双银低辐射镀膜玻璃的方法，其特征在于：所述基层复合介质层包含Si3N4和ZnO；所述第一银层包含Ag；所述第一阻挡层和第二阻挡层包含Cr、NiCr或Ti；中层复合介质层包含Si3N4和ZnO；所述第二银层包含Ag；复合顶层包含Si3N4或SnO2、TiO2。
CN201210124827.4A 2012-04-26 2012-04-26 制造异地可钢化双银低辐射镀膜玻璃的方法 Active CN103374704B (zh)