CN202895824U - 中性色的双银复合结构低辐射镀膜玻璃 - Google Patents

中性色的双银复合结构低辐射镀膜玻璃 Download PDF

Info

Publication number
CN202895824U
CN202895824U CN 201220569459 CN201220569459U CN202895824U CN 202895824 U CN202895824 U CN 202895824U CN 201220569459 CN201220569459 CN 201220569459 CN 201220569459 U CN201220569459 U CN 201220569459U CN 202895824 U CN202895824 U CN 202895824U
Authority
CN
China
Prior art keywords
layer
silver
composite
glass
dielectric layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn - After Issue
Application number
CN 201220569459
Other languages
English (en)
Inventor
陈波
吴斌
孙大海
葛剑君
董华明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
YAOPI ENGINEERING GLASS Co Ltd SHANGHAI
SHANGHAI YAOPI GLASS GROUP CO Ltd
Original Assignee
YAOPI ENGINEERING GLASS Co Ltd SHANGHAI
SHANGHAI YAOPI GLASS GROUP CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YAOPI ENGINEERING GLASS Co Ltd SHANGHAI, SHANGHAI YAOPI GLASS GROUP CO Ltd filed Critical YAOPI ENGINEERING GLASS Co Ltd SHANGHAI
Priority to CN 201220569459 priority Critical patent/CN202895824U/zh
Application granted granted Critical
Publication of CN202895824U publication Critical patent/CN202895824U/zh
Anticipated expiration legal-status Critical
Withdrawn - After Issue legal-status Critical Current

Abstract

本实用新型提供一种中性色的双银复合结构低辐射镀膜玻璃，该玻自玻璃基板向外的结构层依次为：玻璃/电介质层Ⅰ/复合吸收层Ⅰ/铜合金层Ⅰ/银层Ⅰ/保护层Ⅰ/复合电介质层Ⅰ/银层Ⅱ/保护层Ⅱ/电介质层Ⅱ；采用真空磁控溅射镀膜工艺，优点是，在原有复合结构中新增加一层铜合金层，能够使其透过颜色呈中性色。并且，铜合金和银的特性使得该玻璃对远红外线的放射率大大提高，即达到了低辐射的性能。

Description

中性色的双银复合结构低辐射镀膜玻璃
技术领域
本实用新型涉及一种中性色的双银复合结构低辐射镀膜玻璃 
特别是涉及镀有金属铜镀层的双银复合结构低辐射镀膜玻璃。 
背景技术
市场上目前的双银复合结构的低辐射镀膜玻璃，在保证反射颜色呈中性色时，其透过颜色无法同时呈现中性色效果，从室内观测室外情况，经常呈现出淡淡的绿色或者黄色。主要是因为这种双银产品其多层复合结构的光线干涉所造成的。 
发明内容
本实用新型目的，为了能够保持反射颜色不变的情况下，透射颜色呈中性色的双层银的镀膜玻璃，提供一种含有铜铝合金层的双银复合结构的低辐射镀膜玻璃。该玻璃膜层结构自玻璃基板向外依次为： 
电介质层Ⅰ、复合吸收层Ⅰ、铜合金层Ⅰ、银层Ⅰ、保护层Ⅰ、复合电介质层Ⅰ、银层Ⅱ、保护层Ⅱ、电介质层Ⅱ；
其中：电介质层Ⅰ为SiNx，膜层厚度为   25nm～50nm;
      复合吸收层Ⅰ为在NiCr镀层上再镀陶瓷ZnOx层，总膜层厚度为12nm~14nm;
铜铝合金层Ⅰ为CuAlNx层，膜层厚度为2~10nm；
银层Ⅰ、Ⅱ为Ag，膜层厚度为    5nm~15nm;
保护层Ⅰ、Ⅱ为NiCr，膜层厚度为  0nm~14nm;
      复合电介质层Ⅰ为在ZnO镀层上再依次镀SnO2层、ZnO层结构，总膜层厚度为 50nm~110nm;
        电介质层Ⅱ为Si3N4，膜层厚度为 35nm~50nm。
所述铜铝合金层，在该多层复合膜层结构中，其位置位于电介质层Ⅰ和Ⅱ之间的任何位置。 
所述铜铝合金层，为镀制的氮化铜合金。 
本实用新型采用真空磁控溅射镀膜工艺, 镀制各膜层。 
本实用新型优点是，在保证原先双银低辐射镀膜玻璃性能的基础上，其透射颜色呈中性色。并且，铜合金和银的特性使得该玻璃对远红外线的放射率大大提高，即达到了低辐射的性能。  
附图说明
附图1为本实用新型的层结构截面图。 
图中标号说明： 
1-玻璃基板；2-电介质层Ⅰ；3-复合吸收层Ⅰ；4-铜铝合金层Ⅰ；5-银层Ⅰ；6-保护层Ⅰ；7-复合电介质层Ⅰ；8-银层Ⅱ；9-保护层Ⅱ；10-电介质层Ⅱ。
具体实施方式
本实用新型用平板玻璃双端连续式镀膜机进行生产，其中一种优选的工艺方案，使用6个交流双靶，6个直流单靶，共12个靶位进行生产，制出本实用新型的中性色的双银复合结构低辐射镀膜玻璃。 
用上述工艺参数制出的玻璃光学性能如下： 
玻璃可见光透过率T=66%
可见光玻璃面反射率=10%
可见光玻璃面反射色坐标a*值= -1
               色坐标b*值= -6.5
可见光透射色坐标a*值= -0.8
          色坐标b*值= 1.2
玻璃的辐射率ε=0.040。
本实用新型制成中空玻璃间隔为12mm充空气窗结构，按照ISO10292标准测定的数据如下： 
可见光透过率T=61%
可见光玻璃面反射率（Out）=12%
可见光玻璃面反射率（In）=12%
太阳能透过率T=31%
太阳能反射率（Out）=30%
G-value=0.37
遮阳系数SC=0.42
传热系数U=1.63W/m2·K。

Claims (3)

1.一种中性色的双银复合结构低辐射镀膜玻璃，其特征在于：在玻璃基板镀制包含有复合吸收层在内的多层膜层的结构，各膜层结构，自玻璃基板向外依次为：
电介质层Ⅰ、复合吸收层Ⅰ、铜合金层Ⅰ、银层Ⅰ、保护层Ⅰ、复合电介质层Ⅰ、银层Ⅱ、保护层Ⅱ、电介质层Ⅱ；
其中：电介质层Ⅰ为SiNx，膜层厚度为   25nm～50nm;
      复合吸收层Ⅰ为在NiCr镀层上再镀陶瓷ZnOx层，总膜层厚度为12nm~14nm;
铜铝合金层Ⅰ为CuAlNx层，膜层厚度为2~10nm；
银层Ⅰ、Ⅱ为Ag，膜层厚度为    5nm~15nm;
保护层Ⅰ、Ⅱ为NiCr，膜层厚度为  0nm~14nm;
      复合电介质层Ⅰ为在ZnO镀层上再依次镀SnO2层、ZnO层结构，总膜层厚度为 50nm~110nm;
        电介质层Ⅱ为Si3N4，膜层厚度为 35nm~50nm。
2.根据权利要求1所述的中性色的双银复合结构低辐射镀膜玻璃，其特征在于：所述铜铝合金层，在该多层复合膜层结构中，其位置位于电介质层Ⅰ和Ⅱ之间的任何位置。
3.根据权利要求2所述的中性色的双银复合结构低辐射镀膜玻璃，其特征在于：所述铜铝合金层，为镀制的氮化铜合金。
CN 201220569459 2012-11-01 2012-11-01 中性色的双银复合结构低辐射镀膜玻璃 Withdrawn - After Issue CN202895824U (zh)