CN103361007A - 一种聚乙烯类热熔胶组合物 - Google Patents
一种聚乙烯类热熔胶组合物 Download PDFInfo
- Publication number
- CN103361007A CN103361007A CN 201210096726 CN201210096726A CN103361007A CN 103361007 A CN103361007 A CN 103361007A CN 201210096726 CN201210096726 CN 201210096726 CN 201210096726 A CN201210096726 A CN 201210096726A CN 103361007 A CN103361007 A CN 103361007A
- Authority
- CN
- China
- Prior art keywords
- content
- parts
- melt adhesive
- hot melt
- lldpe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种聚乙烯类热熔胶组合物,由基体材料、引发剂、改性剂、接枝单体、增白剂、黏度调节剂、抗氧剂组成,其中,所述的基体材料为高分子量聚乙烯(HDPE)和线型低密度聚乙烯(LLDPE)混合组成,所述引发剂为过氧化二异丙苯(DCP),所述改性剂为乙烯类弹性体、石油树脂或苯乙烯类弹性体种的一种,所述接枝单体为顺丁烯二酸酐(MAH)与丙烯酸(AA)的混合物,所述增白剂为无机Ti0,所述黏度调节剂为聚乙烯蜡。发明所述的热熔胶与基体材料具有良好的相容性、粘接力和热稳定性。
Description
技术领域
本发明涉及一种高分子组合物,具体为一种铝塑复合管用接枝型聚乙烯类热熔胶组合物。
背景技术
热熔胶是指室温呈固态,加热熔融呈液态,经涂布、润湿、压合和冷却后,可在短时间内完成粘接的胶粘剂。热熔胶按其用途不同主要有聚乙烯(PE)类热熔胶、乙烯/醋酸乙烯(EVA)类热熔胶、聚酰胺类热熔胶和丁基热熔胶等。
铝塑复合管由五层结构组成:PE/热熔胶/铝/热熔胶/PE。由于金属材料铝箔表面多含有-OAI、-OH和-COOH等极性基团,而PE是非极性物质,故两者在一般情况下较难复合。采用马来酸酐对PE进行接枝功能化改性,使其带有极性基团,然后将改性后的PE作为基体用于热熔胶中,可对铝箔形成持久的粘接。
目前,国产的这类热熔胶对铝箔的粘接强度都比较低,耐老化性能也不太好,这是由于单靠接枝改性方法还无法实现胶粘剂的高粘接性能。接枝型PE热熔胶的粘接性能与其接枝率有关,接枝率越高粘接性能越强;当接枝率超过一定值时,热熔胶的粘接性能随接枝率的升高而趋于稳定。另外,在熔融接枝反应过程中很难实现高接枝率,这是由于接枝反应中存在着交联副反应,通常接枝率的增加会不可避免地导致凝胶含量的增加,从而严重影响了热熔胶的流动性。通常,铝塑复合管用热熔胶要求其具有良好的粘接性能和熔融流动性。
发明内容
为解决上述技术问题,本发明提供一种聚乙烯类热熔胶组合物。
本发明采用的技术方案是:
一种聚乙烯类热熔胶组合物,由基体材料、引发剂、改性剂,接枝单体、增白剂、黏度调节剂、抗氧剂组成,其中,所述的基体材料为高分子量聚乙烯(HDPE)和线型低密度聚乙烯(LLDPE)混合组成,含量为24-60份,所述引发剂为过氧化二异丙苯(DCP),含量为0.1-0.3份,所述改性剂为乙烯类弹性体、石油树脂或苯乙烯类弹性体种的一种,含量为10-30份,所述接枝单体为顺丁烯二酸酐(MAH)与丙烯酸(AA)的混合物,含量为0.5-6份,所述增白剂为无机TiO,含量为1-5份,所述黏度调节剂为聚乙烯蜡,含量为3-5份,所述抗氧剂含量为0.2-1份(份数为质量份数)。
进一步地,所述的基体材料中,高分子量聚乙烯(HDPE)和线型低密度聚乙烯(LLDPE)的重量比为I∶5。
进一步地,所述的基体材料85份,引发剂0.2份,接枝单体2份,改性剂15份,黏度调节剂3.5份,增白剂2份,抗氧剂0.4份。
本发明所述的热熔胶的增黏树脂,与基体材料具有良好的相容性、粘接力和热稳定性。即使与高温水接触时,其粘合力也不减小,非常适合在铝塑复合管种使用。
具体实施方式
下面通过实施例对本发明进行具体描述。
鉴于LLDPE的内聚能密度较低,接枝物的粘接强度很难得到保证,故将适量的HDPE与LLDPE混合后进行接枝反应。热熔胶的粘接性能随HDPE含量的增加呈先升后降的趋势;当m(HDPE)∶m(LLDPE)=1∶5时,热熔胶的剥离强度达到最大值。
在PE与MAH的接枝反应过程中,DCP引发分解产生的初级自由基可使PE脱氢产生自由基;该自由基除与MAH单体发生接枝反应外,也会与PE发生交联副反应;体系中两种反应(交联和接枝)相互竞争,并且两种反应的活化能各不相同。当DCP含量较低时,随着DCP用量的增加,分解产生自由基的速率及浓度增大,接枝率提高,即接枝反应占主导地位,故热熔胶的粘接性能提高;随着DCP用量的继续增加,体系中大分子自由基浓度增大,偶合终止反应几率增加,交联反应占主导地位,故反应产物的流动性下降,凝胶含量增加,热熔胶的剥离强度也呈下降趋势。
下面列举几个组合物的较佳组分方案:
实施例1:
基体材料80份、引发剂0.1份、接枝单体0.5份、改性剂10份,黏度调节剂3份、增白剂1份、抗氧剂0.2份。
实施例2:
基体材料85份、引发剂0.2份、接枝单体2份、改性剂15份,黏度调节剂3.5份、增白剂2份、抗氧剂0.4份。
实施例3:
基体材料95份、引发剂0.25份、接枝单体4份、改性剂25份,黏度调节剂4份、增白剂4份、抗氧剂0.6份。
实施例4:
基体材料100份、引发剂0.3份、接枝单体6份、改性剂30份,黏度调节剂5份、增白剂5份、抗氧剂1份。
本领域技术人员应该认识到,上述的具体实施方式只是示例性的,是为了使本领域技术人员能够更好的理解本专利内容,不应理解为是对本专利保护范围的限制,只要是根据本专利所揭示精神所作的任何等同变更或修饰,均落入本专利保护范围。
Claims (3)
1.一种聚乙烯类热熔胶组合物,由基体材料、引发剂、改性剂、接枝单体、增白剂、黏度调节剂、抗氧剂组成,其中,所述的基体材料为高分子量聚乙烯(HDPE)和线型低密度聚乙烯(LLDPE)混合组成,含量为24-60份;所述引发剂为过氧化二异丙苯(DCP),含量为0.1-0.3份;所述改性剂为乙烯类弹性体、石油树脂或苯乙烯类弹性体种的一种,含量为10-30份;所述接枝单体为顺丁烯二酸酐(MAH)与丙烯酸(AA)的混合物,含量为0.5-6份;所述增白剂为无机TiO,含量为1-5份;所述黏度调节剂为聚乙烯蜡,含量为3-5份;所述抗氧剂含量为0.2-1份(以上份数均指质量份数)。
2.根据权利要求1所述的组合物,其特征在于,所述的基体材料中,高分子量聚乙烯(HDPE)和线型低密度聚乙烯(LLDPE)的重量比为1∶5。
3.根据权利要求1所述的组合物,其特征在于,所述的基体材料85份,引发剂0.2份,接枝单体2份,改性剂15份,黏度调节剂3.5份,增白剂2份,抗氧剂0.4份。