CN103360708A - 一种变压器用耐油丙烯酸酯橡胶密封垫及其制备方法 - Google Patents

一种变压器用耐油丙烯酸酯橡胶密封垫及其制备方法 Download PDF

Info

Publication number
CN103360708A
CN103360708A CN201310246996XA CN201310246996A CN103360708A CN 103360708 A CN103360708 A CN 103360708A CN 201310246996X A CN201310246996X A CN 201310246996XA CN 201310246996 A CN201310246996 A CN 201310246996A CN 103360708 A CN103360708 A CN 103360708A
Authority
CN
China
Prior art keywords
parts
oil
acrylic rubber
transformer
rubber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310246996XA
Other languages
English (en)
Inventor
沈必亮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Chunhui Instrument Cable Group Co Ltd
Original Assignee
Anhui Chunhui Instrument Cable Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Chunhui Instrument Cable Group Co Ltd filed Critical Anhui Chunhui Instrument Cable Group Co Ltd
Priority to CN201310246996XA priority Critical patent/CN103360708A/zh
Publication of CN103360708A publication Critical patent/CN103360708A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种变压器用耐油丙烯酸酯橡胶密封垫及其制备方法，其由下列重量份的原料制成：丙烯酸酯橡胶45-55、氯醚橡胶15-20、氟橡胶8-12、改性海泡石粉5-10、硼酸锌3-6、三氧化二锑2-4、2-羟基咪唑啉2-3、氯化石蜡3-4、氧化镁0.5-1.5、有机膨润土8-12、煅烧黄土3-5、乙撑双油酸酰胺1-2、钙锌稳定剂1-2、硫磺2-4、马来酸二辛酯3-4、偏苯三酸三辛酯2-3、防老剂ODA 1-2、防老剂TPPD 1-2、促进剂CZ 1-2、促进剂ZDC 2-3。本发明选用耐热氧老化性能优异、耐油性能优异的丙烯酸酯橡胶作为主料，辅以氯醚橡胶、氟橡胶进行共混，改善丙烯酸酯胶料的耐寒性、耐高温性、耐水性、拉伸强度等性能。

Description

一种变压器用耐油丙烯酸酯橡胶密封垫及其制备方法
技术领域
本发明涉及一种密封垫，具体涉及一种变压器用耐油丙烯酸酯橡胶密封垫及其制备方法。
背景技术
变压器渗漏多发生在密封胶垫处，主要是由密封垫老化龟裂引起的。密封胶垫质量的好坏主要取决于它的耐油性能，耐油性能较差的，老化速度就较快，特别是在高温下，其老化速度就更快，极易引起密封垫老化龟裂，造成变压器渗漏油。因此开发一种高耐油变压器耐油橡胶密封垫已成为当务之急。
发明内容
本发明的目的在于针对现有技术的不足，提供一种变压器用耐油丙烯酸酯橡胶密封垫及其制备方法，提高橡胶密封垫的耐油性能。
本发明采用的技术方案如下：
一种变压器用耐油丙烯酸酯橡胶密封垫，由下列重量份的原料制成：丙烯酸酯橡胶（AR-200） 45-55、氯醚橡胶（C-55） 15-20、氟橡胶（246）8-12、改性海泡石粉5-10、硼酸锌3-6、三氧化二锑2-4、2-羟基咪唑啉2-3、氯化石蜡3-4、氧化镁0.5-1.5、有机膨润土8-12、煅烧黄土3-5、乙撑双油酸酰胺1-2、钙锌稳定剂 1-2、硫磺2-4、马来酸二辛酯 3-4、偏苯三酸三辛酯2-3、防老剂ODA 1-2、防老剂TPPD 1-2、促进剂 CZ 1-2、促进剂ZDC 2-3。
所述的改性海泡石粉由以下方法制得：将海泡石放入0.5-1mol/L硫酸溶液中浸泡1-2小时，洗净，120-140℃干燥10-12h，然后在340-360℃下煅烧3-4h，取出，冷却，打碎研细；再加入相当于海泡石重量5-10%的白云石粉、3-6%的硅酸镁、2-3%的沉淀白炭黑、3-4%的聚异丁烯、4-6%的木质素磺酸钙，混合研磨20-30min，然后再喷入相当于海泡石重量3-5%的硼酸酯偶联剂LK-640和1-2%的二甲基硅油，在14000-16000 r/min下搅拌30-50min，烘干即可。
一种变压器用耐油丙烯酸酯橡胶密封垫的制备方法，包括以下步骤：
（1）将丙烯酸酯橡胶、改性海泡石粉、硼酸锌、2-羟基咪唑啉、马来酸二辛酯、有机膨润土、乙撑双油酸酰胺在60-65℃下预混合10-12min，得混合料A；
（2）将氯醚橡胶、氟橡胶、偏苯三酸三辛酯、三氧化二锑、氧化镁、煅烧黄土、氯化石蜡在65-75℃下预混合12-16min，得混合料B；
（3）将混合料A和混合料B混合均匀后送入炼胶机中，加入其余原料在85-95℃下炼胶15-20min；
1）炼胶完成后，取出胶料铺平，送入平板硫化机内，在180-220℃温度下硫化10-15min，将硫化的制品取出，经检验合格者，修整毛边后即可成为成品。
本发明的有益效果：
本发明选用耐热氧老化性能优异、耐油性能优异的丙烯酸酯橡胶作为主料，辅以氯醚橡胶、氟橡胶进行共混，改善丙烯酸酯胶料的耐寒性、耐高温性、耐水性、弹性和拉伸强度等性能；本发明还对海泡石进行了改性，可以显著提高其与胶料的相容性，从而提高胶料的机械强度以及耐高温性能。本发明生产出来的密封垫本发明密封垫密封效果好，高耐油，抗腐蚀性好，在酸，碱，油等介质中能长期工作，其体积和硬度变化小，不易龟裂；还具有良好的压缩回弹性、耐高温性、耐寒性、耐天候老化和臭氧老化性能等优点。
具体实施方式
一种变压器用耐油丙烯酸酯橡胶密封垫，由下列重量（kg）的原料制成：丙烯酸酯橡胶（AR-200） 50、氯醚橡胶（C-55） 18、氟橡胶（246）10、改性海泡石粉8、硼酸锌4、三氧化二锑3、2-羟基咪唑啉2、氯化石蜡3、氧化镁1、有机膨润土10、煅烧黄土4、乙撑双油酸酰胺1.5、钙锌稳定剂 1.5、硫磺3、马来酸二辛酯 4、偏苯三酸三辛酯2、防老剂ODA 1、防老剂TPPD 2、促进剂 CZ 2、促进剂ZDC2。
所述的改性海泡石粉由以下方法制得：将海泡石放入0.5mol/L硫酸溶液中浸泡2小时，洗净，130℃干燥12h，然后在350℃下煅烧4h，取出，冷却，打碎研细；再加入相当于海泡石重量8%的白云石粉、4%的硅酸镁、2%的沉淀白炭黑、3%的聚异丁烯、5%的木质素磺酸钙，混合研磨25min，然后再喷入相当于海泡石重量4%的硼酸酯偶联剂LK-640和1.5%的二甲基硅油，在15000 r/min下搅拌40min，烘干即可。
一种变压器用耐油丙烯酸酯橡胶密封垫的制备方法，包括以下步骤：
（1）将丙烯酸酯橡胶、改性海泡石粉、硼酸锌、2-羟基咪唑啉、马来酸二辛酯、有机膨润土、乙撑双油酸酰胺在65℃下预混合10min，得混合料A；
（2）将氯醚橡胶、氟橡胶、偏苯三酸三辛酯、三氧化二锑、氧化镁、煅烧黄土、氯化石蜡在70℃下预混合15min，得混合料B；
（3）将混合料A和混合料B混合均匀后送入炼胶机中，加入其余原料在90℃下炼胶18min；
（4）炼胶完成后，取出胶料铺平，送入平板硫化机内，在210℃温度下硫化12min，将硫化的制品取出，经检验合格者，修整毛边后即可成为成品。
本发明密封垫物理性能如下：
Figure BDA0000338114521

Claims (3)

1.一种变压器用耐油丙烯酸酯橡胶密封垫，其特征在于，由下列重量份的原料制成：丙烯酸酯橡胶（AR-200） 45-55、氯醚橡胶（C-55） 15-20、氟橡胶（246）8-12、改性海泡石粉5-10、硼酸锌3-6、三氧化二锑2-4、2-羟基咪唑啉2-3、氯化石蜡3-4、氧化镁0.5-1.5、有机膨润土8-12、煅烧黄土3-5、乙撑双油酸酰胺1-2、钙锌稳定剂 1-2、硫磺2-4、马来酸二辛酯 3-4、偏苯三酸三辛酯2-3、防老剂ODA 1-2、防老剂TPPD 1-2、促进剂 CZ 1-2、促进剂ZDC 2-3。
2.根据权利要求1所述的一种变压器用耐油丙烯酸酯橡胶密封垫，其特征在于，所述的改性海泡石粉由以下方法制得：将海泡石放入0.5-1mol/L硫酸溶液中浸泡1-2小时，洗净，120-140℃干燥10-12h，然后在340-360℃下煅烧3-4h，取出，冷却，打碎研细；再加入相当于海泡石重量5-10%的白云石粉、3-6%的硅酸镁、2-3%的沉淀白炭黑、3-4%的聚异丁烯、4-6%的木质素磺酸钙，混合研磨20-30min，然后再喷入相当于海泡石重量3-5%的硼酸酯偶联剂LK-640和1-2%的二甲基硅油，在14000-16000 r/min下搅拌30-50min，烘干即可。
3.一种如权利要求1所述的变压器用耐油丙烯酸酯橡胶密封垫的制备方法，其特征在于包括以下步骤：
（1）将丙烯酸酯橡胶、改性海泡石粉、硼酸锌、2-羟基咪唑啉、马来酸二辛酯、有机膨润土、乙撑双油酸酰胺在60-65℃下预混合10-12min，得混合料A；
（2）将氯醚橡胶、氟橡胶、偏苯三酸三辛酯、三氧化二锑、氧化镁、煅烧黄土、氯化石蜡在65-75℃下预混合12-16min，得混合料B；
   （3）将混合料A和混合料B混合均匀后送入炼胶机中，加入其余原料在85-95℃下炼胶15-20min；
（4）炼胶完成后，取出胶料铺平，送入平板硫化机内，在180-220℃温度下硫化10-15min，将硫化的制品取出，经检验合格者，修整毛边后即可成为成品。
CN201310246996XA 2013-06-20 2013-06-20 一种变压器用耐油丙烯酸酯橡胶密封垫及其制备方法 Pending CN103360708A (zh)