CN103694606A - 一种改性氟橡胶密封垫材料及其制备方法 - Google Patents

一种改性氟橡胶密封垫材料及其制备方法 Download PDF

Info

Publication number
CN103694606A
CN103694606A CN201310631847.5A CN201310631847A CN103694606A CN 103694606 A CN103694606 A CN 103694606A CN 201310631847 A CN201310631847 A CN 201310631847A CN 103694606 A CN103694606 A CN 103694606A
Authority
CN
China
Prior art keywords
parts
mixing
gasket material
clay
zinc oxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310631847.5A
Other languages
English (en)
Inventor
陈贤锋
阚蕾
申大伟
沈根
骆敏
申丽霞
陈玉娟
沈春花
沈红梅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MAANSHAN ZHONGLAN RUBBER AND PLASTIC PRODUCTS CO Ltd
Original Assignee
MAANSHAN ZHONGLAN RUBBER AND PLASTIC PRODUCTS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MAANSHAN ZHONGLAN RUBBER AND PLASTIC PRODUCTS CO Ltd filed Critical MAANSHAN ZHONGLAN RUBBER AND PLASTIC PRODUCTS CO Ltd
Priority to CN201310631847.5A priority Critical patent/CN103694606A/zh
Publication of CN103694606A publication Critical patent/CN103694606A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种改性氟橡胶密封垫材料，其特征在于，由下列重量份的原料制成：氟橡胶65-70、石墨3-4、酚醛树脂10-12、硅烷偶联剂KH-5502-3、邻苯二甲酸二丁酯4-6、聚异丁烯2-3、一缩二乙二醇苯甲酸酯2-5、氧化镁2-3、氧化锌2-3、防老剂ODA1-2、促进剂CZ1-2、单丁基氧化锡1-2、硫磺1-2、N550炭黑30-35、碳酸钙粉10-12、纳米陶土15-18、改性凹凸棒土10-12；本发明添加改性凹凸棒土，改善了胶料的工艺性能，使用环保型配合剂，减少其毒副作用和对环境的污染；本发明具有良好的密封性、耐压缩性、耐老化性、耐油性、耐摩耗性能。

Description

一种改性氟橡胶密封垫材料及其制备方法
技术领域
本发明涉及橡胶复合材料加工领域，特别是一种改性氟橡胶密封垫材料及其制备方法。 
背景技术
密封垫，是一种用于机械、设备、管道等内部，起密封作用的材料。目前使用的密封垫多为橡胶密封垫，其特点是：耐高温、耐臭氧、耐天然老化、耐真空、耐燃料油、耐润滑油、耐强氧化剂、耐药品性和电绝缘性能好，广泛用于国防工业和民用工业。但是现有的橡胶密封垫密封效果不理想、耐磨性较差、强度低等缺陷，已远不能满足现实要求。因此研发一种高性能橡胶密封垫已成为当务之急。 
发明内容
本发明的目的是提供一种改性氟橡胶密封垫材料及其制备方法。 
为了实现本发明的目的，本发明通过以下方案实施： 
一种改性氟橡胶密封垫材料，由下列重量份的原料制成：氟橡胶65-70、石墨3-4、酚醛树脂10-12、硅烷偶联剂KH-5502-3、邻苯二甲酸二丁酯4-6、聚异丁烯2-3、一缩二乙二醇苯甲酸酯2-5、氧化镁2-3、氧化锌2-3、防老剂ODA1-2、促进剂CZ1-2、单丁基氧化锡1-2、硫磺1-2、N550炭黑30-35、碳酸钙粉10-12、纳米陶土15-18、改性凹凸棒土10-12； 
所述改性凹凸棒土由下列重量份的原料制成：凹凸棒土20-24、粘土20-24、1,6-己二异氰酸酯3-4、二缩三丙二醇二丙烯酸酯4-5、明矾5-6、铁矿渣1-2、聚四氟乙烯4-5、硅烷偶联剂KH-5502-3、碳化硅4-5、氧化锌8-10、2，6-二叔丁基对甲酚1-2、花椒籽油1-2；制备方法是将凹凸棒土、粘土、铁矿渣混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。 
本发明所述改性氟橡胶密封垫材料，由以下具体步骤制成：将氟橡胶、石墨、酚醛树脂、硅烷偶联剂KH-550加入密炼机中，加热至30-40℃，混炼3-5min；然后升温至50-60℃，再加入邻苯二甲酸二丁酯、聚异丁烯、一缩二乙二醇苯 甲酸酯、氧化镁、氧化锌、防老剂ODA，混炼6-8min，再加入促进剂CZ、单丁基氧化锡、硫磺、N550炭黑继续混炼4-6min；加入其余剩余成分混炼5-6min，即得。 
本发明的优异效果是：本发明添加改性凹凸棒土，改善了胶料的工艺性能，使用环保型配合剂，减少其毒副作用和对环境的污染；本发明具有良好的密封性、耐压缩性、耐老化性、耐油性、耐摩耗性能。 
具体实施方式
下面通过具体实例对本发明进行详细说明。 
一种改性氟橡胶密封垫材料，由下列重量份（公斤）的原料制成：氟橡胶65、石墨3、酚醛树脂10、硅烷偶联剂KH-5502、邻苯二甲酸二丁酯4、聚异丁烯2、一缩二乙二醇苯甲酸酯2、氧化镁2、氧化锌2、防老剂ODA1、促进剂CZ1、单丁基氧化锡1、硫磺1、N550炭黑30、碳酸钙粉10、纳米陶土15、改性凹凸棒土10； 
所述改性凹凸棒土由下列重量份（公斤）的原料制成：凹凸棒土20、粘土20、1,6-己二异氰酸酯3、二缩三丙二醇二丙烯酸酯4、明矾5、铁矿渣1、聚四氟乙烯4、硅烷偶联剂KH-5502、碳化硅4、氧化锌8、2，6-二叔丁基对甲酚1、花椒籽油1；制备方法是将凹凸棒土、粘土、铁矿渣混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。 
本发明所述改性氟橡胶密封垫材料，由以下具体步骤制成：将氟橡胶、石墨、酚醛树脂、硅烷偶联剂KH-550加入密炼机中，加热至30-40℃，混炼3-5min；然后升温至50-60℃，再加入邻苯二甲酸二丁酯、聚异丁烯、一缩二乙二醇苯甲酸酯、氧化镁、氧化锌、防老剂ODA，混炼6-8min，再加入促进剂CZ、单丁基氧化锡、硫磺、N550炭黑继续混炼4-6min；加入其余剩余成分混炼5-6min，即得。 
用本发明的密封垫材料与普通橡胶料物理性能对比如下表。 
Figure BDA0000426162000000021
Figure 20131063184751000021
从表中可以看出用本发明的橡胶密封垫材料，综合性能比较好。 

Claims (2)

1.一种改性氟橡胶密封垫材料，其特征在于，由下列重量份的原料制成：氟橡胶65-70、石墨3-4、酚醛树脂10-12、硅烷偶联剂KH-550 2-3、邻苯二甲酸二丁酯4-6、聚异丁烯2-3、一缩二乙二醇苯甲酸酯2-5、氧化镁2-3、氧化锌2-3、防老剂ODA 1-2、促进剂CZ 1-2、单丁基氧化锡1-2、硫磺1-2、N550炭黑30-35、碳酸钙粉10-12、纳米陶土15-18、改性凹凸棒土10-12；
所述改性凹凸棒土由下列重量份的原料制成：凹凸棒土20-24、粘土20-24、1,6-己二异氰酸酯3-4、二缩三丙二醇二丙烯酸酯4-5、明矾5-6、铁矿渣1-2、聚四氟乙烯4-5、硅烷偶联剂KH-550 2-3、碳化硅4-5、氧化锌8-10、2，6- 二叔丁基对甲酚1-2、花椒籽油1-2；制备方法是将凹凸棒土、粘土、铁矿渣混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
2.根据权利要求1所述改性氟橡胶密封垫材料，其特征在于，由以下具体步骤制成：将氟橡胶、石墨、酚醛树脂、硅烷偶联剂KH-550加入密炼机中，加热至30-40℃，混炼3-5min；然后升温至50-60℃，再加入邻苯二甲酸二丁酯、聚异丁烯、一缩二乙二醇苯甲酸酯、氧化镁、氧化锌、防老剂ODA，混炼6-8min，再加入促进剂CZ、单丁基氧化锡、硫磺、N550炭黑继续混炼4-6min；加入其余剩余成分混炼5-6min，即得。
CN201310631847.5A 2013-11-29 2013-11-29 一种改性氟橡胶密封垫材料及其制备方法 Pending CN103694606A (zh)