CN103642071A - 一种由多种橡胶混炼而成的密封垫材料及其制备方法 - Google Patents

一种由多种橡胶混炼而成的密封垫材料及其制备方法 Download PDF

Info

Publication number
CN103642071A
CN103642071A CN201310571283.0A CN201310571283A CN103642071A CN 103642071 A CN103642071 A CN 103642071A CN 201310571283 A CN201310571283 A CN 201310571283A CN 103642071 A CN103642071 A CN 103642071A
Authority
CN
China
Prior art keywords
mixing
rubber
antioxidant
gasket material
sealing gasket
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310571283.0A
Other languages
English (en)
Other versions
CN103642071B (zh
Inventor
夏云
夏建生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bengbu Zhengyuan Electronic Technology Co., Ltd
Original Assignee
BENGBU ZHENGYUAN ELECTRONIC TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BENGBU ZHENGYUAN ELECTRONIC TECHNOLOGY Co Ltd filed Critical BENGBU ZHENGYUAN ELECTRONIC TECHNOLOGY Co Ltd
Priority to CN201310571283.0A priority Critical patent/CN103642071B/zh
Publication of CN103642071A publication Critical patent/CN103642071A/zh
Application granted granted Critical
Publication of CN103642071B publication Critical patent/CN103642071B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种由多种橡胶混炼而成的密封垫材料，其特征在于，由下列重量份的原料制成：天然橡胶40-45、丁腈橡胶35-40、硬脂酸3-5、抗氧剂10101-2、双马来酰亚胺3-4、沉淀法白炭黑30-35、抗氧剂1010 1-2、3-氨丙基三甲氧基硅烷2-3、N330炭黑24-28、促进剂CBS0.5-1.5、硫磺2-3、氧化锌3-4、癸二酸丙二醇聚酯6-8、改性凹凸棒土10-12；本发明添加改性凹凸棒土，改善了胶料的工艺性能，使用环保型配合剂，减少其毒副作用和对环境的污染；本发明具有很好的密封性能，耐油、耐腐蚀，而且工艺简单，成本低，适合工业化生产。

Description

一种由多种橡胶混炼而成的密封垫材料及其制备方法
技术领域
本发明涉及橡胶复合材料加工领域，特别是一种由多种橡胶混炼而成的密封垫材料及其制备方法。 
背景技术
密封垫，是一种用于机械、设备、管道等内部，起密封作用的材料。目前使用的密封垫多为橡胶密封垫，其特点是：耐高温、耐臭氧、耐天然老化、耐真空、耐燃料油、耐润滑油、耐强氧化剂、耐药品性和电绝缘性能好，广泛用于国防工业和民用工业。但是现有的橡胶密封垫密封效果不理想、耐磨性较差、强度低等缺陷，已远不能满足现实要求。因此研发一种高性能橡胶密封垫已成为当务之急。 
发明内容
本发明的目的是提供一种由多种橡胶混炼而成的密封垫材料及其制备方法。 
为了实现本发明的目的，本发明通过以下方案实施： 
一种由多种橡胶混炼而成的密封垫材料，由下列重量份的原料制成：天然橡胶40-45、丁腈橡胶35-40、硬脂酸3-5、抗氧剂10101-2、双马来酰亚胺3-4、沉淀法白炭黑30-35、抗氧剂10101-2、3-氨丙基三甲氧基硅烷2-3、N330炭黑24-28、促进剂CBS0.5-1.5、硫磺2-3、氧化锌3-4、癸二酸丙二醇聚酯6-8、改性凹凸棒土10-12； 
所述改性凹凸棒土由下列重量份的原料制成：凹凸棒土20-24、粘土12-15、1,6-己二异氰酸酯3-4、二缩三丙二醇二丙烯酸酯2-3、纳米二氧化钛3-4、纳米二氧化硅1-2、氧化锌1-2、促进剂TMTD1-2、阳起石粉8-10、花椒籽油1-2；制备方法是将凹凸棒土、粘土混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。 
本发明所述由多种橡胶混炼而成的密封垫材料，由以下具体步骤制成：将天然橡胶、丁腈橡胶、硬脂、抗氧剂1010、双马来酰亚胺加入密炼机中，加热至80-90℃，混炼3-5min；然后升温至110-120℃，再加入沉淀法白炭黑、抗氧剂1010、3-氨丙基三甲氧基硅烷，混炼6-8min，再加入3-氨丙基三甲氧基硅烷、 N330炭黑、促进剂CBS、硫磺继续混炼4-6min；加入其余剩余成分混炼5-6min，即得。 
本发明的优异效果是：本发明添加改性凹凸棒土，改善了胶料的工艺性能，使用环保型配合剂，减少其毒副作用和对环境的污染；本发明具有很好的密封性能，耐油、耐腐蚀，而且工艺简单，成本低，适合工业化生产。 
具体实施方式
下面通过具体实例对本发明进行详细说明。 
一种由多种橡胶混炼而成的密封垫材料，由下列重量份（公斤）的原料制成：天然橡胶40、丁腈橡胶35、硬脂酸3、抗氧剂10101、双马来酰亚胺3、沉淀法白炭黑30、抗氧剂10101、3-氨丙基三甲氧基硅烷2、N330炭黑24、促进剂CBS0.5、硫磺2、氧化锌3、癸二酸丙二醇聚酯6、改性凹凸棒土10； 
所述改性凹凸棒土由下列重量份（公斤）的原料制成：凹凸棒土20、粘土12、1,6-己二异氰酸酯3、二缩三丙二醇二丙烯酸酯2、纳米二氧化钛3、纳米二氧化硅1、氧化锌1、促进剂TMTD1、阳起石粉8、花椒籽油1；制备方法是将凹凸棒土、粘土混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。 
本发明所述由多种橡胶混炼而成的密封垫材料，由以下具体步骤制成：将天然橡胶、丁腈橡胶、硬脂、抗氧剂1010、双马来酰亚胺加入密炼机中，加热至80-90℃，混炼3-5min；然后升温至110-120℃，再加入沉淀法白炭黑、抗氧剂1010、3-氨丙基三甲氧基硅烷，混炼6-8min，再加入3-氨丙基三甲氧基硅烷、N330炭黑、促进剂CBS、硫磺继续混炼4-6min；加入其余剩余成分混炼5-6min，即得。 
用本发明的密封垫材料与普通橡胶料物理性能对比如下表。 
Figure BDA0000414811430000021
从表中可以看出用本发明的橡胶密封垫材料，综合性能比较好。 

Claims (2)

1.一种由多种橡胶混炼而成的密封垫材料，其特征在于，由下列重量份的原料制成：天然橡胶40-45、丁腈橡胶35-40、硬脂酸3-5、抗氧剂1010 1-2、双马来酰亚胺3-4、沉淀法白炭黑30-35、抗氧剂1010  1-2、3-氨丙基三甲氧基硅烷2-3、N330炭黑24-28、促进剂CBS 0.5-1.5、硫磺2-3、氧化锌3-4、癸二酸丙二醇聚酯6-8、改性凹凸棒土10-12；
所述改性凹凸棒土由下列重量份的原料制成：凹凸棒土20-24、粘土12-15、1,6-己二异氰酸酯3-4、二缩三丙二醇二丙烯酸酯2-3、纳米二氧化钛3-4、纳米二氧化硅1-2、氧化锌1-2、促进剂TMTD 1-2、阳起石粉8-10、花椒籽油1-2；制备方法是将凹凸棒土、粘土混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
2.根据权利要求1所述由多种橡胶混炼而成的密封垫材料，其特征在于，由以下具体步骤制成：将天然橡胶、丁腈橡胶、硬脂、抗氧剂1010、双马来酰亚胺加入密炼机中，加热至80-90℃，混炼3-5min；然后升温至110-120℃，再加入沉淀法白炭黑、抗氧剂1010、3-氨丙基三甲氧基硅烷，混炼6-8min，再加入3-氨丙基三甲氧基硅烷、N330炭黑、促进剂CBS、硫磺继续混炼4-6min；加入其余剩余成分混炼5-6min，即得。
CN201310571283.0A 2013-11-15 2013-11-15 一种由多种橡胶混炼而成的密封垫材料及其制备方法 Active CN103642071B (zh)