CN103352180A - 一种碳合金的制造方法 - Google Patents

一种碳合金的制造方法 Download PDF

Info

Publication number
CN103352180A
CN103352180A CN2013102573018A CN201310257301A CN103352180A CN 103352180 A CN103352180 A CN 103352180A CN 2013102573018 A CN2013102573018 A CN 2013102573018A CN 201310257301 A CN201310257301 A CN 201310257301A CN 103352180 A CN103352180 A CN 103352180A
Authority
CN
China
Prior art keywords
carbon alloy
carbon
ingot
manufacturing
antimony
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013102573018A
Other languages
English (en)
Other versions
CN103352180B (zh
Inventor
应春光
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
PURENOVO STAINLESS STEEL Co Ltd
Original Assignee
PURENOVO STAINLESS STEEL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by PURENOVO STAINLESS STEEL Co Ltd filed Critical PURENOVO STAINLESS STEEL Co Ltd
Priority to CN201310257301.8A priority Critical patent/CN103352180B/zh
Publication of CN103352180A publication Critical patent/CN103352180A/zh
Application granted granted Critical
Publication of CN103352180B publication Critical patent/CN103352180B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种碳合金的制造方法，该方法包括下列过程：将钢料在高频真空熔炉中熔融，随后进行浇铸，在该浇铸中冷却速度为1.2℃/min以形成锭料；将锭料在950℃下保持10小时，然后在500℃下保持90分钟；此后使用500吨锤式锻造机进行热锻，这样制得碳合金；所述钢料的组成为（以重量%计）：0.25%至0.29%的碳；0.10%至1.20%的锰；0.09%至0.13%的磷；0.10%至0.19%的硫；0.60%至1.00%的硅；≤0.09%的铝；≤0.01%的氮；0.45%至0.83%的碲；0.04%至0.07%的铌；≤0.50%的铜；0.05%至0.60%的镍；0.2%至2.00%的钼；0.2%至0.4%的钒；0.0030%至0.0065%的锑；0.010%至0.050%的钛：其余为铁和不可避免的杂质。本发明所述的方法可以制造碳合金。

Description

一种碳合金的制造方法
技术领域
本发明涉及金属领域，具体地说，涉及一种碳合金的制造方法。
背景技术
碳合金是应用最多的合金，广泛用于碳钢和铸铁。但是由于目前对于合金的要求越来越高，目前的一些合金已经满足不了要求。
发明内容
本发明的目的是提供一种碳合金的制造方法。
为了实现本发明的目的，本发明提供一种碳合金的制造方法，该方法包括下列过程：将钢料在高频真空熔炉中熔融，随后进行浇铸，在该浇铸中冷却速度为1.2℃/min以形成锭料；将锭料在950℃下保持10小时，然后在500℃下保持90分钟；此后使用500吨锤式锻造机进行热锻，这样制得碳合金；所述钢料的组成为（以重量%计）：
0.25%至0.29%的碳；
0.10%至1.20%的锰；
0.09%至0.13%的磷；
0.10%至0.19%的硫；
0.60%至1.00%的硅；
≤0.09%的铝；
≤0.01%的氮；
0.45%至0.83%的碲；
0.04%至0.07%的铌；
≤0.50%的铜；
0.05%至0.60%的镍；
0.2%至2.00%的钼；
0.2%至0.4%的钒；
0.0030%至0.0065%的锑；
0.010%至0.050%的钛：
其余为铁和不可避免的杂质。
优选地，所述钢料的组成为（以重量%计）：
0.28%的碳；
1.0%的锰；
0.13%的磷；
0.17%的硫；
1.00%的硅；
0.06%的铝；
0.01%的氮；
0.61%的碲；
0.05%的铌；
0.40%的铜；
0.40%的镍；
1.00%的钼；
0.2%的钒；
0.0055%的锑；
0.040%的钛：
其余为铁和不可避免的杂质。
本发明所述的方法可以制造碳合金。
具体实施方式
以下通过具体实施方式的描述对本发明作进一步说明，但这并非是对本发明的限制，本领域技术人员根据本发明的基本思想，可以做出各种修改或改进，但是只要不脱离本发明的基本思想，均在本发明的范围之内。
实施例1合金的制备
碳合金的组成为（以重量%计）：
0.28%的碳；
1.0%的锰；
0.13%的磷；
0.17%的硫；
1.00%的硅；
0.06%的铝；
0.01%的氮；
0.61%的碲；
0.05%的铌；
0.40%的铜；
0.40%的镍；
1.00%的钼；
0.2%的钒；
0.0055%的锑；
0.040%的钛：
其余为铁和不可避免的杂质。
将具有上述成分组成的30kg钢料在高频真空熔炉中熔融，随后进行浇铸，在该浇铸中冷却速度为1.2℃/min以形成锭料。将锭料在950℃下保持10小时，然后在500℃下保持90分钟。此后使用500吨锤式锻造机进行热锻，这样制得碳合金1。
实施例2碳合金的制备
按照和实施例1相同的方式制备碳合金2，不同之处在于不使用钼。
实施例3碳合金的制备
按照和实施例1相同的方式制备碳合金3，不同之处在于不使用锑。
实施例4碳合金的制备
按照和实施例1相同的方式制备碳合金4，不同之处在于不使用镍。
实验例1
根据GB/T230.1-2009来测定碳合金1-4的洛氏硬度。结果如下：碳合金1的洛氏硬度为91HRC，碳合金2的洛氏硬度为58HRC，碳合金3的洛氏硬度为61HRC，碳合金4的洛氏硬度为62HRC。
实验例2
根据GB/T228-2002测定抗拉强度。结果如下：碳合金1的抗拉强度Rm为879兆帕，碳合金2的抗拉强度Rm为611兆帕，碳合金3的抗拉强度Rm为581兆帕，碳合金4的抗拉强度Rm为602兆帕。

Claims (2)

1.一种碳合金的制造方法，该方法包括下列过程：将钢料在高频真空熔炉中熔融，随后进行浇铸，在该浇铸中冷却速度为1.2℃/min以形成锭料；将锭料在950℃下保持10小时，然后在500℃下保持90分钟；此后使用500吨锤式锻造机进行热锻，这样制得碳合金；其特征在于，所述钢料的组成为（以重量%计）：
0.25%至0.29%的碳；
0.10%至1.20%的锰；
0.09%至0.13%的磷；
0.10%至0.19%的硫；
0.60%至1.00%的硅；
≤0.09%的铝；
≤0.01%的氮；
0.45%至0.83%的碲；
0.04%至0.07%的铌；
≤0.50%的铜；
0.05%至0.60%的镍；
0.2%至2.00%的钼；
0.2%至0.4%的钒；
0.0030%至0.0065%的锑；
0.010%至0.050%的钛：
其余为铁和不可避免的杂质。
2.根据权利要求1所述的碳合金的制造方法，其特征在于，所述钢料的组成为（以重量%计）：
0.28%的碳；
1.0%的锰；
0.13%的磷；
0.17%的硫；
1.00%的硅；
0.06%的铝；
0.01%的氮；
0.61%的碲；
0.05%的铌；
0.40%的铜；
0.40%的镍；
1.00%的钼；
0.2%的钒；
0.0055%的锑；
0.040%的钛：
其余为铁和不可避免的杂质。
CN201310257301.8A 2013-06-23 2013-06-23 一种碳合金的制造方法 Expired - Fee Related CN103352180B (zh)