CN103351514A - 一种高强度高填充可降解木塑复合材料及其生产工艺 - Google Patents

一种高强度高填充可降解木塑复合材料及其生产工艺 Download PDF

Info

Publication number
CN103351514A
CN103351514A CN2013102859778A CN201310285977A CN103351514A CN 103351514 A CN103351514 A CN 103351514A CN 2013102859778 A CN2013102859778 A CN 2013102859778A CN 201310285977 A CN201310285977 A CN 201310285977A CN 103351514 A CN103351514 A CN 103351514A
Authority
CN
China
Prior art keywords
parts
plastic composite
wood plastic
filling degradable
degradable wood
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013102859778A
Other languages
English (en)
Inventor
冯红华
殷久鹏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HANGZHOU ZHENRAN WOOD PLASTIC COMPOSITE Co Ltd
Original Assignee
HANGZHOU ZHENRAN WOOD PLASTIC COMPOSITE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HANGZHOU ZHENRAN WOOD PLASTIC COMPOSITE Co Ltd filed Critical HANGZHOU ZHENRAN WOOD PLASTIC COMPOSITE Co Ltd
Priority to CN2013102859778A priority Critical patent/CN103351514A/zh
Publication of CN103351514A publication Critical patent/CN103351514A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高强度高填充可降解木塑复合材料及其生产工艺，该木塑复合材料以回收PE废料、植物纤维、轻质碳酸钙、润滑剂、相容剂、稳定剂为原料，经混合机组混合均匀后挤出造粒，再经挤出至模具后冷却定型、切割制成。本发明的木塑复合材料具有强度高、成本低、生物降解性好等优点。其生产工艺简单，节能环保。

Description

一种高强度高填充可降解木塑复合材料及其生产工艺
技术领域
  本发明涉及复合建筑材料技术领域，具体属于一种高强度高填充可降解木塑复合材料及其生产工艺。
背景技术  
 目前市政、园林、装修广泛采用木塑复合材料，但市场上的木塑复合材料存在强度低、成本高等缺点，难以满足现有市场的需求，而且，产品中塑料及橡胶成分较高，弃用后不易降解，最终形成二次污染，对生态环境造成破坏。
发明内容
  本发明的目的在于针对上述技术上的不足之处，以回收PE废料、植物纤维、轻质碳酸钙、润滑剂、相容剂、稳定剂为原料，经混合机组混合均匀后挤出造粒，再经挤出至模具后冷却定型、切割成木塑复合材料，该木塑复合材料中植物纤维和轻质碳酸钙填料的比重大，填充度高，制得的产品具有强度高、生物降解性好、成本低的优点，同时其生产工艺简单，能耗低。
  本发明所采用的技术方案是：
一种高强度高填充可降解木塑复合材料，该木塑复合材料由以下重量份数的各原料制成：回收PE废料20～30份，植物纤维70～80份，轻质碳酸钙10～15份，润滑剂2～4份，相容剂5～10份，稳定剂2～3份。
作为优选，所述润滑剂为EBS、白油、PE蜡、硬脂酸中的一种或多种。
作为优选，所述的相容剂为MAPE、MAPP、丙烯酸改性的聚四氟乙烯中的一种或多种。
作为优选，所述的稳定剂为抗氧剂1010、DLTP、液体钙锌复合稳定剂中的一种或多种。
作为优选，所述的植物纤维为木料、竹料、秸秆中的一种或多种。
一种针对上述高强度可降解木塑复合材料的生产工艺如下：
步骤1：将植物纤维研磨成40～60目的粉状颗粒；
步骤2：按重量份计，将20～30份回收PE废料、70～80份植物纤维、10～15份轻质碳酸钙、2～4份润滑剂、5～10份相容剂、2～3份稳定剂放入高速混合机中混合均匀，在120℃～130℃混合10～20分钟，然后将温度降至45℃～55℃低温混合30～40分钟，再经挤出机挤出成木塑粒子；
步骤3：将木塑粒子送入锥形挤出机中经模具后冷却定型，定长切割成木塑复合材料。
与现有技术相比，本发明具有以下优点：
1.添加了轻质碳酸钙，显著改善了产品的弯曲模量和弯曲强度，经久耐用。 
2.该木塑复合材料中生物降解性能好的植物纤维含量高，经粉碎后可自行降解或再次回收利用，对环境污染少。 
3.价格低廉的植物纤维含量高，产品成本低。
4.生产工艺简单，环保节能。
具体实施方式
以下结合具体实施例对本发明作进一步详细描述。
实施例1：
步骤1：将秸秆研磨成40～60目的粉状颗粒；
步骤2：按重量份计，将20份回收PE废料、70份秸秆粉、10份轻质碳酸钙、2份白油、6份MAPE、2份1010放入高速混合机中混合均匀，在120℃混合20分钟，然后将温度降至55℃低温混合30分钟，再经挤出机挤出成木塑粒子；
步骤3：将木塑粒子送入锥形挤出机中经模具后冷却定型，定长切割成木塑复合材料。
实施例2：
步骤1：将木屑研磨成40～60目的粉状颗粒；
步骤2：按重量份计，将30份回收PE废料、75份木粉、15份轻质碳酸钙、4份EBS、10份MAPP、2.5份DLTP放入高速混合机中混合均匀，在130℃混合30分钟，然后将温度降至45℃低温混合40分钟，再经挤出机挤出成木塑粒子；
步骤3：将木塑粒子送入锥形挤出机中经模具后冷却定型，定长切割成木塑复合材料。
实施例3：
步骤1：将竹料研磨成40～60目的粉状颗粒；
步骤2：按重量份计，将25份回收PE废料、80份竹粉、14份轻质碳酸钙、3份PE蜡、9份丙烯酸改性聚四氟乙烯、3份液体钙锌复合稳定剂放入高速混合机中混合均匀，在125℃混合27分钟，然后将温度降至50℃低温混合35分钟，再经挤出机挤出成木塑粒子；
步骤3：将木塑粒子送入锥形挤出机中经模具后冷却定型，定长切割成木塑复合材料。 

Claims (6)

1.一种高强度高填充可降解木塑复合材料，其特征在于，该木塑复合材料由以下重量份数的各原料制成：回收PE废料20～30份，植物纤维70～80份，轻质碳酸钙10～15份，润滑剂2～4份，相容剂5～10份，稳定剂2～3份。
2.根据权利要求1所述的高强度高填充可降解木塑复合材料，其特征在于，所述润滑剂为EBS、白油、PE蜡、硬脂酸中的一种或多种。
3.根据权利要求1所述的高强度高填充可降解木塑复合材料，其特征在于，所述的相容剂为MAPE、MAPP、丙烯酸改性的聚四氟乙烯中的一种或多种。
4.根据权利要求1所述的高强度高填充可降解木塑复合材料，其特征在于，所述的稳定剂为抗氧剂1010、DLTP、液体钙锌复合稳定剂中的一种或多种。
5.根据权利要求1所述的高强度高填充可降解木塑复合材料，其特征在于，所述的植物纤维为木纤维、竹纤维、秸秆纤维中的一种或多种。
6.一种权利要求1所述的高强度高填充可降解木塑复合材料的生产工艺，其特征在于，采用以下工艺步骤：
步骤1：将植物纤维研磨成40～60目的粉状颗粒；
步骤2：按重量份计，将20～30份回收PE废料、70～80份植物纤维粉、10～15份轻质碳酸钙、2～4份润滑剂、5～10份相容剂、2～3份稳定剂放入高速混合机中混合均匀，在120℃～130℃混合20～30分钟，然后将温度降至45～55℃低温混合30～40分钟，再经挤出机挤出成木塑粒子；
步骤3：将木塑粒子送入锥形挤出机中经模具后冷却定型，定长切割成木塑复合材料。
CN2013102859778A 2013-07-09 2013-07-09 一种高强度高填充可降解木塑复合材料及其生产工艺 Pending CN103351514A (zh)