CN103342959A - 有机硅耐热面漆及其制备方法 - Google Patents

有机硅耐热面漆及其制备方法 Download PDF

Info

Publication number
CN103342959A
CN103342959A CN2013102608318A CN201310260831A CN103342959A CN 103342959 A CN103342959 A CN 103342959A CN 2013102608318 A CN2013102608318 A CN 2013102608318A CN 201310260831 A CN201310260831 A CN 201310260831A CN 103342959 A CN103342959 A CN 103342959A
Authority
CN
China
Prior art keywords
resistant finish
heat resistant
organosilicon heat
powder
organic silicon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013102608318A
Other languages
English (en)
Inventor
祝盆鑫
孙巨福
戴宇钧
汪鹏程
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianchang Julong Car and Ship Coating Co Ltd
Original Assignee
Tianchang Julong Car and Ship Coating Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianchang Julong Car and Ship Coating Co Ltd filed Critical Tianchang Julong Car and Ship Coating Co Ltd
Priority to CN2013102608318A priority Critical patent/CN103342959A/zh
Publication of CN103342959A publication Critical patent/CN103342959A/zh
Pending legal-status Critical Current

Abstract

本发明提供有机硅耐热面漆及其制备方法,有机硅耐热面漆由有机硅树脂、铝粉、云母粉、滑石粉、防沉剂、溶剂等组成。本发明的有机硅耐热面漆的耐高温性能好,且干燥性好,表干在1小时内,而实干在4小时内;其附着力和耐腐蚀性能等均有显著提高。

Description

有机硅耐热面漆及其制备方法
技术领域
本发明涉及涂料技术领域,具体涉及有机硅耐热面漆及其制备方法。
背景技术
某些设备如汽车的排气管、石化工厂中的高温反应釜、火电厂锅炉等经常处于高温和腐蚀介质中,它们协同作用会加速设备的腐蚀穿孔,增加设备的维修费用,并给安全生产带来很大的隐患。对于金属设备的高温氧化腐蚀问题,采用耐高温抗氧化涂层保护是一种行之有效的方法。
现在市场上大多数用于涂覆耐高温金属构件设备的耐热涂料,其漆膜在200℃以上保持不变色、不脱落,而仍保持适当物理机械性能。常用的有机硅耐高温涂料虽具有优异的耐高温性能,但这种要求远远达不到一些特殊产品耐热性的需求;另外这些耐热涂料不但在没有经高温烘烤的条件下不能用明火烧烤,否则会产生大量的烟雾,而且也不能在200℃以上的高温条件上施工,不能耐800℃以上的高温,其使用范围和应用比较小。现有的有机硅耐高温涂料在常温下干燥性差,一般还得进行烘干,且存在机械强度、附着力和耐腐蚀性能差等问题。
发明内容
为克服现有技术的不足,本发明公开了一种耐超高温的有机硅耐热面漆及其制备方法,达到提高有机硅耐热面漆的机械性能,扩大其应用范围。
本发明的技术方案为:有机硅耐热面漆,由下列原料按重量份组成:
进一步,所述有机硅树脂为固体质量分数为50%的甲基苯基有机硅树脂。
进一步,所述防沉剂为有机膨润土、气相二氧化硅或蓖麻油。
进一步,所述铝粉、云母粉与滑石粉的粒径均为不大于325目。
进一步,所述助溶剂为丁酯;所述溶剂为甲苯、二甲苯、甲基异戊基甲酮、环己酮、丙二醇、甲醚醋酸酯中至少一种。
本发明的另一个目的是提供上述的有机硅耐热面漆的制备方法,其包括如下步骤:
(1)按配比将有机硅树脂、铝粉、云母粉、滑石粉、磷酸锌、防沉剂与部分溶剂共同混合搅拌成糊状;
(2)将(1)中混合均匀的物料投入砂磨机进行研磨20-30分钟,使物料的粒径为不大于30μm;
(3)向(2)中物料加入助溶剂与剩余的溶剂进行分散,过滤得有机硅耐热面漆。
本发明采用金属铝粉为着色颜料,由于铝粉的热稳定性好,当在高温下有机硅耐热面漆的漆膜中的有机硅树脂受热氧化时,其残余的SiO2可与铝粉熔合生成Si-O-Al硅酸盐无机化合物的涂层,增强对底材的附着力与耐高温性能。
本发明采用云母粉、滑石粉作为耐高温填料,对有机硅耐热面漆的涂层起到补强的作用,由于两者都是硅酸盐填料,它们表面带有少量羟基,在研磨过程中及高温下能与聚有机硅氧烷的官能基产生一定的化学反应,从而增强有机硅耐热面漆的耐磨性等机械性能。其中滑石粉可有利于防止漆膜开列和减缓涂料贮存时的沉降,并可防止涂膜流挂,而提高涂膜的耐水性、耐磨性。云母粉有利于提高有机硅耐热面漆的耐高温性能,防止介质向底材渗透,在耐热涂料中能提高涂膜强度,并且不影响涂层的外观颜料。
本发明采用磷酸锌为保护填料,云母粉、滑石粉作为耐高温填料,金属铝粉为着色颜料,通过有机-无机相结合的方法来提高其耐热、防腐蚀、抗氧化等性能。
防沉剂可提高有机硅耐热面漆的耐盐水性及贮存稳定性,并使有机硅耐热面漆具有更好的防腐蚀性。
具体实施方式
为更好理解本发明,下面结合实施例对本发明作进一步描述,以下实施例仅是对本发明进行说明而非对其加以限定。
实施例中有机硅树脂选用固体质量分数为50%的甲基苯基有机硅树脂。
实施例一:
有机硅耐热面漆,由下列原料按重量份组成:
Figure BDA0000341575912
具体制备方法如下:
(1)按配比将有机硅树脂、铝粉、云母粉、滑石粉、磷酸锌、防沉剂与部分溶剂共同混合搅拌成糊状;
(2)将(1)中混合均匀的物料投入砂磨机进行研磨20分钟,使物料的粒径为不大于30μm;
(3)向(2)中物料加入助溶剂与剩余的溶剂进行分散,过滤得有机硅耐热面漆。
实施例二:
有机硅耐热面漆,由下列原料按重量份组成:
Figure BDA0000341575913
具体制备方法如下:
(1)按配比将有机硅树脂、铝粉、云母粉、滑石粉、磷酸锌、防沉剂与部分溶剂共同混合搅拌成糊状;
(2)将(1)中混合均匀的物料投入砂磨机进行研磨25分钟,使物料的粒径为不大于30μm;
(3)向(2)中物料加入助溶剂与剩余的溶剂进行分散,过滤得有机硅耐热面漆。
实施例三:
有机硅耐热面漆,由下列原料按重量份组成:
Figure BDA0000341575914
具体制备方法如下:
(1)按配比将有机硅树脂、铝粉、云母粉、滑石粉、磷酸锌、防沉剂与部分溶剂共同混合搅拌成糊状;
(2)将(1)中混合均匀的物料投入砂磨机进行研磨30分钟,使物料的粒径为不大于30μm;
(3)向(2)中物料加入助溶剂与剩余的溶剂进行分散,过滤得有机硅耐热面漆。
将上述实施例1-3制得的有机硅耐热面漆按涂料检测标准进行相关性能的检测,其数据如下表所示:
上表说明本发明的有机硅耐热面漆的干燥性好,表干在1小时内,而实干在4小时内;其附着力和耐腐蚀性能等均有显著提高。
将本发明的有机硅耐热面漆涂刷在锅炉烟道内部,其温度可达300-400℃,三个月后观察漆膜,其漆膜光亮、附着力与硬度均很好,也没有出现漆膜起泡、龟裂或脱落的现象。说明本发明的有机硅耐热面漆具有很高的耐高温性。
上述的对实施例的描述是为便于该技术领域的普通技术人员能理解和应用本发明。熟悉本领域技术的人员显然可以容易地对这些实施例做出各种修改,并把在此说明的一般原理应用到其他实施例中而不必经过创造性的劳动。因此,本发明不限于这里的实施例,本领域技术人员根据本发明的揭示,不脱离本发明范畴所做出的改进和修改都应该在本发明的保护范围之内。

Claims (6)

1.有机硅耐热面漆,其特征在于:由下列原料按重量份组成:
Figure FDA0000341575901
2.根据权利要求1所述的有机硅耐热面漆,其特征在于:所述有机硅树脂为固体质量分数为50%的甲基苯基有机硅树脂。
3.根据权利要求1所述的有机硅耐热面漆,其特征在于:所述防沉剂为有机膨润土、气相二氧化硅或蓖麻油。
4.根据权利要求1所述的有机硅耐热面漆,其特征在于:所述铝粉、云母粉与滑石粉的粒径均为不大于325目。
5.根据权利要求1所述的有机硅耐热面漆,其特征在于:所述助溶剂为丁酯;所述溶剂为甲苯、二甲苯、甲基异戊基甲酮、环己酮、丙二醇、甲醚醋酸酯中至少一种。
6.一种制备如权利要求1所述的有机硅耐热面漆的方法,其特征在于:包括如下步骤:
(1)按配比将有机硅树脂、铝粉、云母粉、滑石粉、磷酸锌、防沉剂与部分溶剂共同混合搅拌成糊状;
(2)将(1)中混合均匀的物料投入砂磨机进行研磨20-30分钟,使物料的粒径为不大于30μm;
(3)向(2)中物料加入助溶剂与剩余的溶剂进行分散,过滤得有机硅耐热面漆。
CN2013102608318A 2013-06-27 2013-06-27 有机硅耐热面漆及其制备方法 Pending CN103342959A (zh)