CN103342508A - 以废弃聚苯乙烯泡沫为填充物的水泥预制块的制备方法 - Google Patents

以废弃聚苯乙烯泡沫为填充物的水泥预制块的制备方法 Download PDF

Info

Publication number
CN103342508A
CN103342508A CN2013102763807A CN201310276380A CN103342508A CN 103342508 A CN103342508 A CN 103342508A CN 2013102763807 A CN2013102763807 A CN 2013102763807A CN 201310276380 A CN201310276380 A CN 201310276380A CN 103342508 A CN103342508 A CN 103342508A
Authority
CN
China
Prior art keywords
polystyrene foam
waste polystyrene
concrete
cement
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013102763807A
Other languages
English (en)
Other versions
CN103342508B (zh
Inventor
温国华
温泉
郭玉婷
杨洋
杨永启
张雨亭
巴音其木格
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Inner Mongolia University
Original Assignee
Inner Mongolia University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Inner Mongolia University filed Critical Inner Mongolia University
Priority to CN201310276380.7A priority Critical patent/CN103342508B/zh
Publication of CN103342508A publication Critical patent/CN103342508A/zh
Application granted granted Critical
Publication of CN103342508B publication Critical patent/CN103342508B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种以废弃聚苯乙烯泡沫为填充物的水泥预制块制备方法，主要工艺过程是：将水泥、水、砂及石按照JGJ55-2000普通混凝土配比，制得混凝土。将制得的混凝土与废弃聚苯乙烯泡沫按照一定的体积比混合，将混凝土与废弃聚苯乙烯泡沫拌和均匀，成型、养护，即得以废弃聚苯乙烯泡沫为填充物水泥预制块。本方法制备的以废弃聚苯乙烯泡沫为填充物水泥预制块质量轻、保温及隔音。在建筑领域有望发挥很大的作用。

Description

以废弃聚苯乙烯泡沫为填充物的水泥预制块的制备方法
技术领域
本发明涉及可用于建筑的一种预制块的制备方法，特别指以水泥、沙子及废弃聚苯乙烯泡沫为主要原料来制备水泥预制块的方法。
背景技术
本发明主要针对目前聚苯乙烯泡沫造成的严重环境污染而没有合理利用，同时在建筑领域对于轻质及保温建材的需求增长迅速。利用废弃聚苯乙烯泡沫作为水泥预制块的填充物，一方面可以减轻废弃聚苯乙烯泡沫造成的环境污染，另一方面可以提供一种轻质、保温及隔音性能优于传统预制块的新型水泥预制块。
由于本发明是利用水泥、水、砂、石及废弃聚苯乙烯泡沫为原料，制备的水泥预制块的成本低廉，目前还未见该方面的相关报道，而其独特的设计和性能使其在废弃物利用及建筑领域有广阔的应用前景。
发明内容
本发明要解决的技术问题是提供一种以废弃聚苯乙烯泡沫为填充物的水泥预制块的制备方法，这种制备方法以水泥、水、砂、石及废弃聚苯乙烯泡沫为原料，经合理配比，通过一定的工艺过程而制得。
本发明要解决的技术问题是由如下方案解决的：以废弃聚苯乙烯泡沫为填充物的水泥预制块的制备方法，其特征是：将水泥、水、砂及石按照JGJ55-2000普通混凝土配比，即：水泥329kg/m3、水122.5kg/m3、砂705.24 kg/m3、石1339.26 kg/m3，按照以上比例制得混凝土，将制得的混凝土与废弃聚苯乙烯泡沫按照一定的体积比混合，将混凝土与废弃聚苯乙烯泡沫拌和均匀，成型、养护，即得以废弃聚苯乙烯泡沫为填充物水泥预制块，其中JGJ55-2000普通混凝土与废弃聚苯乙烯泡沫的体积比为1：0.1-1.0。
本发明的优点是：1、用本方法制备的以废弃聚苯乙烯泡沫为填充物的水泥预制块成本低。2、可以利用大量的废弃聚苯乙烯泡沫，变废为宝、减轻其对环境造成影响。3、将其应用到建筑领域可以节约大量的水泥和砂石。4、与传统的预制块相比，其重量轻、保温及隔音，因此对于建筑的节能减排具有重要的作用。
附图说明
图1是以废弃聚苯乙烯泡沫为填充物的水泥预制块的制备工艺流程图。
具体实施方式
混凝土的制备：将水泥、水、砂及石按照JGJ55-2000普通混凝土配比，即：水泥329kg/m3、水122.5kg/m3、砂705.24 kg/m3、石1339.26 kg/m3。按照以上比例制得混凝土。
以废弃聚苯乙烯泡沫为填充物水泥预制块的制备：
实施例1：将制得的混凝土与废弃聚苯乙烯泡沫按照1:1的体积比混合，将混凝土与废弃聚苯乙烯泡沫拌和均匀，成型、养护，即得以废弃聚苯乙烯泡沫为填充物水泥预制块。
实施例2：将制得的混凝土与废弃聚苯乙烯泡沫按照1:0.8的体积比混合，将混凝土与废弃聚苯乙烯泡沫拌和均匀，成型、养护，即得以废弃聚苯乙烯泡沫为填充物水泥预制块。
实施例3：将制得的混凝土与废弃聚苯乙烯泡沫按照1:0.6的体积比混合，将混凝土与废弃聚苯乙烯泡沫拌和均匀，成型、养护，即得以废弃聚苯乙烯泡沫为填充物水泥预制块。
实施例4：将制得的混凝土与废弃聚苯乙烯泡沫按照1:0.33的体积比混合，将混凝土与废弃聚苯乙烯泡沫拌和均匀，成型、养护，即得以废弃聚苯乙烯泡沫为填充物水泥预制块。
实施例5：将制得的混凝土与废弃聚苯乙烯泡沫按照1:0.2的体积比混合，将混凝土与废弃聚苯乙烯泡沫拌和均匀，成型、养护，即得以废弃聚苯乙烯泡沫为填充物水泥预制块。
实施例6：将制得的混凝土与废弃聚苯乙烯泡沫按照1:0.1的体积比混合，将混凝土与废弃聚苯乙烯泡沫拌和均匀，成型、养护，即得以废弃聚苯乙烯泡沫为填充物水泥预制块。
 本发明专利所得水泥预制块的比重小，以实施例4为例：JGJ55-2000普通混凝土的比重是1919.04kg/m3；实施例4制备的水泥预制块的比重为1682.97 kg/m3，二者相比，后者的比重减少了12.30%；由上述实验数据可知，以废弃聚苯乙烯泡沫为填充物制备的水泥预制块比重小，有良好的实际应用及市场推广前景。

Claims (1)

1.以废弃聚苯乙烯泡沫为填充物的水泥预制块的制备方法，其特征是：将水泥、水、砂及石按照JGJ55-2000普通混凝土配比，即：水泥329kg/m3、水122.5kg/m3、砂705.24 kg/m3、石1339.26 kg/m3，按照以上比例制得混凝土，将制得的混凝土与废弃聚苯乙烯泡沫按照一定的体积比混合，将混凝土与废弃聚苯乙烯泡沫拌和均匀，成型、养护，即得以废弃聚苯乙烯泡沫为填充物水泥预制块，其中JGJ55-2000普通混凝土与废弃聚苯乙烯泡沫的体积比为1：0.1-1.0。
CN201310276380.7A 2013-07-03 2013-07-03 以废弃聚苯乙烯泡沫为填充物的水泥预制块的制备方法 Expired - Fee Related CN103342508B (zh)