CN103333593B - 一种耐油性双酚a型聚碳酸酯的粉末涂料及其制备方法 - Google Patents

一种耐油性双酚a型聚碳酸酯的粉末涂料及其制备方法 Download PDF

Info

Publication number
CN103333593B
CN103333593B CN201310207630.1A CN201310207630A CN103333593B CN 103333593 B CN103333593 B CN 103333593B CN 201310207630 A CN201310207630 A CN 201310207630A CN 103333593 B CN103333593 B CN 103333593B
Authority
CN
China
Prior art keywords
bisphenol
polycarbonate
powder coating
proofness
pottery
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310207630.1A
Other languages
English (en)
Other versions
CN103333593A (zh
Inventor
张洪滨
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Huizhou Yongmingfeng Industrial Co., Ltd.
Original Assignee
BENGBU HONGAN PRECISION MACHINERY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BENGBU HONGAN PRECISION MACHINERY Co Ltd filed Critical BENGBU HONGAN PRECISION MACHINERY Co Ltd
Priority to CN201310207630.1A priority Critical patent/CN103333593B/zh
Publication of CN103333593A publication Critical patent/CN103333593A/zh
Application granted granted Critical
Publication of CN103333593B publication Critical patent/CN103333593B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种耐油性双酚A型聚碳酸酯的粉末涂料及其制备方法，其组成原料为：双酚A型聚碳酸酯48-55、松香树脂1.5-2.0、4,4-二氨基二苯基甲烷12-15、磷酸三丁酯0.8-1.2、氨丙基三乙氧基硅烷3.3-3.8、超细硫酸钡15-25、聚丙烯酰胺6.0-8.0、二乙烯三胺1.1-1.3和陶瓷渣粉末25-30。本发明通过增加陶瓷渣粉末作为填料，大大提高了粉末涂料的疏水性，同时，本发明通过松香树脂、4,4-二氨基二苯基甲烷、磷酸三丁酯、氨丙基三乙氧基硅烷、超细硫酸钡、陶瓷渣粉末混合，提高了原料的分散性与相容性，使得粉末涂料涂布性提高，成膜平滑。

Description

一种耐油性双酚A型聚碳酸酯的粉末涂料及其制备方法
技术领域
本发明涉及粉末涂料领域，尤其涉及一种耐油性双酚A型聚碳酸酯的粉末涂料及其制备方法。
背景技术
随着我国经济的持续稳定增长以及人民生活水平的不断提高，金属构件的粉末涂装业务也不断增加，尤其是家用电器、仪器仪表、交通设施、铝型材、各种车辆以及日用五金等行业，粉末涂层能给金属提供优良的防腐保护及装饰性能，但由于用于上述领域的现有涂料的抗污染性能不理想，涂层上经常附着各类灰尘、污垢甚至是油污；抗粘贴能力也不理想，且现有粉末涂料形成的涂层在户外长期暴晒、雨淋等自然条件影响下易出现起泡、开裂、剥离等现象，因此，涂层的机械性能也不理想。
发明内容
本发明所要解决的技术问题是克服现有技术的不足，提供一种耐油性双酚A型聚碳酸酯的粉末涂料及其制备方法。
为了实现上述目的本发明采用如下技术方案：
一种耐油性双酚A型聚碳酸酯的粉末涂料，其特征在于其组成原料的重量份为：双酚A型聚碳酸酯48-55、松香树脂1.5-2.0、4,4-二氨基二苯基甲烷12-15、磷酸三丁酯0.8-1.2、氨丙基三乙氧基硅烷3.3-3.8、超细硫酸钡15-25、聚丙烯酰胺6.0-8.0、二乙烯三胺1.1-1.3和陶瓷渣粉末25-30。
所述的耐油性双酚A型聚碳酸酯的粉末涂料，其特征在于其组成原料的重量份为：双酚A型聚碳酸酯52、松香树脂1.8、4,4-二氨基二苯基甲烷14、磷酸三丁酯1.0、氨丙基三乙氧基硅烷3.5、超细硫酸钡15、聚丙烯酰胺7.0、二乙烯三胺1.2和陶瓷渣粉末28。
所述的耐油性双酚A型聚碳酸酯的粉末涂料的制备方法，其特征在于包括以下步骤：
（1）将松香树脂、4,4-二氨基二苯基甲烷、磷酸三丁酯、氨丙基三乙氧基硅烷、超细硫酸钡、陶瓷渣粉末混合，在120-130℃下搅拌1-2小时；
（2）按组成原料的重量份称取其它原料与步骤（1）物料混合，然后送入挤出机造粒，挤出机温度130-140℃，冷却，研磨至40-50μm时；停止研磨，包装。
本发明的有益效果：
本发明通过增加陶瓷渣粉末作为填料，大大提高了粉末涂料的疏水性，同时，本发明通过松香树脂、4,4-二氨基二苯基甲烷、磷酸三丁酯、氨丙基三乙氧基硅烷、超细硫酸钡、陶瓷渣粉末混合，提高了原料的分散性与相容性，使得粉末涂料涂布性提高，成膜平滑。
具体实施方式
实施例1：耐油性双酚A型聚碳酸酯的粉末涂料，其组成原料的重量份为：双酚A型聚碳酸酯52、松香树脂1.8、4,4-二氨基二苯基甲烷14、磷酸三丁酯1.0、氨丙基三乙氧基硅烷3.5、超细硫酸钡15、聚丙烯酰胺7.0、二乙烯三胺1.2和陶瓷渣粉末28。
所述的耐油性双酚A型聚碳酸酯的粉末涂料的制备方法，包括以下步骤：
（1）将松香树脂、4,4-二氨基二苯基甲烷、磷酸三丁酯、氨丙基三乙氧基硅烷、超细硫酸钡、陶瓷渣粉末混合，在120-130℃下搅拌1-2小时；
（2）按组成原料的重量份称取其它原料与步骤（1）物料混合，然后送入挤出机造粒，挤出机温度130-140℃，冷却，研磨至40-50μm时；停止研磨，包装。
将该粉末涂料采用静电喷涂施工方法作用于经喷涂处理的标志牌上，经180℃的充分固化，自然冷却至室温，放置22h后，测定涂层性能，其涂层冲击强度≥94cm，耐盐雾时间≥2975h，人工加速老化时间≥3070h，耐热性能≥458℃，天然曝晒11个月不起泡、不生锈、不开裂、不剥离，对油污的分解率≥99.3。

Claims (3)

1.一种耐油性双酚A型聚碳酸酯的粉末涂料，其特征在于其组成原料的重量份为：双酚A型聚碳酸酯48-55、松香树脂1.5-2.0、4,4-二氨基二苯基甲烷12-15、磷酸三丁酯0.8-1.2、氨丙基三乙氧基硅烷3.3-3.8、超细硫酸钡15-25、聚丙烯酰胺6.0-8.0、二乙烯三胺1.1-1.3和陶瓷渣粉末25-30。
2.根据权利要求1所述的耐油性双酚A型聚碳酸酯的粉末涂料，其特征在于其组成原料的重量份为：双酚A型聚碳酸酯52、松香树脂1.8、4,4-二氨基二苯基甲烷14、磷酸三丁酯1.0、氨丙基三乙氧基硅烷3.5、超细硫酸钡15、聚丙烯酰胺7.0、二乙烯三胺1.2和陶瓷渣粉末28。
3.一种如权利要求1所述的耐油性双酚A型聚碳酸酯的粉末涂料的制备方法，其特征在于包括以下步骤：
（1）将松香树脂、4,4-二氨基二苯基甲烷、磷酸三丁酯、氨丙基三乙氧基硅烷、超细硫酸钡、陶瓷渣粉末混合，在120-130℃下搅拌1-2小时；
（2）按组成原料的重量份称取其它原料与步骤（1）物料混合，然后送入挤出机造粒，挤出机温度130-140℃，冷却，研磨至40-50μm时；停止研磨，包装。
CN201310207630.1A 2013-05-30 2013-05-30 一种耐油性双酚a型聚碳酸酯的粉末涂料及其制备方法 Expired - Fee Related CN103333593B (zh)