CN103333003A - Special fertilizer for nano carbon tea and preparation method of special fertilizer - Google Patents

Abstract

The invention discloses a special fertilizer for nano carbon tea and a preparation method of the special fertilizer. The special fertilizer is characterized by being prepared from the following raw materials in parts by weight: 12-14 parts of urea, 18-20 parts of ardealite, 5-7 parts of peat, 8-10 parts of ground vermiculite, 5-7 parts of potassium chloride, 10-12 parts of ammonium chloride, 1-2 parts of zinc sulfate, 2-3 parts of sodium sulphide, 2-3 parts of ferric trichloride, 3-5 parts of brown sugar, 3-4 parts of foots, 1-2 parts of nano carbon, 1-2 parts of cinnamon oil, 15-20 parts of a soil conditioner and a defined amount of water. The special fertilizer is capable of completely meeting the demand of growth and the development of tea on nutrients; the nano carbon plays a role of synergism; the fertilizer effect is prolonged. Meanwhile, the special fertilizer is reasonable in preparation of nutrient elements, and has a controlled release effect.

Description

Special-purpose fertilizer of a kind of nano-sized carbon tealeaves and preparation method thereof

Technical field

The present invention relates to technical field of fertilizers, is special-purpose fertilizer of a kind of nano-sized carbon tealeaves and preparation method thereof.

Background technology

The used fertilizer type of current tea tree planting is a lot, the special-purpose loose nitrogen-phosphorus-potassium compound fertilizers that can buy on the market that adopt of tealeaves wherein more, and it mainly is made up of N, P, K three big inorganic elementss, can satisfy the growth needs of tea tree at short notice.But life-time service can make soil aggregate be destroyed, and easily causes soil compaction, soil property hardening, thereby influences growth of tea plant, and tea leaf quality descends.

Though simple fertilizer is rich in organic matter simultaneously, nutrient discharges slowly, and tea tree absorbs slowly, fertilizer efficiency is low, do not reach active balance between the various available nutrients, because the tealeaves fertilizer formula is science not, causes tea yield not high, chemical ingredients and micronutrient levels are not high in the tealeaves.

Summary of the invention

The purpose of this invention is to provide special-purpose fertilizer of a kind of nano-sized carbon tealeaves and preparation method thereof,

Technical scheme of the present invention is as follows:

A kind of nano-sized carbon tealeaves is special-purpose fertile, it is characterized in that being made by the raw material of following weight part:

Urea 12-14, phosphogypsum 18-20, peat composed of rotten mosses 5-7, vermiculite power 8-10, Repone K 5-7, ammonium chloride 10-12, zinc sulfate 1-2, sodium sulphite 2-3, iron trichloride 2-3, brown sugar 3-5, oil foot 3-4, nano-sized carbon 1-2, Oleum Cinnamomi 1-2, soil conditioner 15-20, water are an amount of.

Described soil conditioner is made by the raw material of following weight part: urea 10-12, attapulgite 6-8, citric acid 3-4, analysis for soybean powder 10-12, acid-sludge 5-6, sodium lauryl sulphate 2-3, zinc sulfate 3-4, Sodium Selenite 1-2, manganous sulfate 2-3, ferrous sulfate 3-4, silkworm excrement 4-6, brown sugar 2-3, vermiculite power 1-2, kaolin 2-3, white lime 1-2, oil foot 3-4, Oil of Eucalyptus 2-3, borax 1-2, tripoly phosphate sodium STPP 1-2, silane coupling agent KH550 2-3, water are an amount of.

The preparation method is:

(1) attapulgite mixes with zinc sulfate, Sodium Selenite, manganous sulfate, ferrous sulfate, borax, adds silane silane coupling agent KH550 and stirs to such an extent that mixing is fertile;

(2) again with the urea fusing, add Oil of Eucalyptus, stir, add gained and mix fertilizer, stir;

(3) again other remaining component is added suitable quantity of water furnishing slurry, add step (2) gained material, mix, granulation, oven dry is namely.

The special-purpose fertile preparation method of described nano-sized carbon tealeaves is characterized in that may further comprise the steps:

(1) with the urea heat fused, add after nano-sized carbon stirs, add zinc sulfate, sodium sulphite, iron trichloride, Oleum Cinnamomi, soil conditioner again and stir;

(2) with the suitable quantity of water heating, add brown sugar and oil foot, after confusing, add step (1) material and other remaining component again, after mixing, granulation, oven dry, namely.

The present invention can satisfy tea growth more all sidedly and grow nutrient demand, and nano-sized carbon plays synergism, has prolonged fertilizer efficiency, and simultaneously, nutritive element of the present invention is equipped with rationally, and has slow release effect.

Embodiment

A kind of nano-sized carbon tealeaves is special-purpose fertile, is made by the raw material (kilogram) of following weight part:

Urea 12, phosphogypsum 20, the peat composed of rotten mosses 7, vermiculite power 8, Repone K 7, ammonium chloride 12, zinc sulfate 2, sodium sulphite 3, iron trichloride 3, brown sugar 5, oil foot 3, nano-sized carbon 2, Oleum Cinnamomi 2, soil conditioner 20, water are an amount of.

Described soil conditioner is made by the raw material of following weight part (kilogram): urea 10, attapulgite 8, citric acid 3, analysis for soybean powder 12, acid-sludge 6, sodium lauryl sulphate 2, zinc sulfate 4, Sodium Selenite 2, manganous sulfate 2, ferrous sulfate 3, silkworm excrement 6, brown sugar 3, vermiculite power 2, kaolin 3, white lime 1, oil foot 4, Oil of Eucalyptus 2, borax 2, tripoly phosphate sodium STPP 2, silane coupling agent KH550 2, water are an amount of.

The preparation method is:

(1) attapulgite mixes with zinc sulfate, Sodium Selenite, manganous sulfate, ferrous sulfate, borax, adds silane silane coupling agent KH550 and stirs to such an extent that mixing is fertile;

(2) again with the urea fusing, add Oil of Eucalyptus, stir, add gained and mix fertilizer, stir;

(3) again other remaining component is added suitable quantity of water furnishing slurry, add step (2) gained material, mix, granulation, oven dry is namely.

The special-purpose fertile preparation method of nano-sized carbon tealeaves may further comprise the steps:

(1) with the urea heat fused, add after nano-sized carbon stirs, add zinc sulfate, sodium sulphite, iron trichloride, Oleum Cinnamomi, soil conditioner again and stir;

(2) with the suitable quantity of water heating, add brown sugar and oil foot, after confusing, add step (1) material and other remaining component again, after mixing, granulation, oven dry, namely.

Fertilizer of the present invention is grown growth of tea plant and is improved output and has promoter action preferably, is conducive to tea growth density, hundred buds weight, the long increase of standard bud-leaf.By every mu of 70 kilograms of fertilisings, tealeaves cured leaf output reaches 120.3kg ∕ mu, adopts the tea place tealeaves cured leaf output 86.8kg ∕ mu of traditional NPK fertilizers in the test tea place in the present invention, and output obviously improves.

Claims (2)

1. a nano-sized carbon tealeaves is special-purpose fertile, it is characterized in that being made by the raw material of following weight part:

Urea 12-14, phosphogypsum 18-20, peat composed of rotten mosses 5-7, vermiculite power 8-10, Repone K 5-7, ammonium chloride 10-12, zinc sulfate 1-2, sodium sulphite 2-3, iron trichloride 2-3, brown sugar 3-5, oil foot 3-4, nano-sized carbon 1-2, Oleum Cinnamomi 1-2, soil conditioner 15-20, water are an amount of;

Described soil conditioner is made by the raw material of following weight part: urea 10-12, attapulgite 6-8, citric acid 3-4, analysis for soybean powder 10-12, acid-sludge 5-6, sodium lauryl sulphate 2-3, zinc sulfate 3-4, Sodium Selenite 1-2, manganous sulfate 2-3, ferrous sulfate 3-4, silkworm excrement 4-6, brown sugar 2-3, vermiculite power 1-2, kaolin 2-3, white lime 1-2, oil foot 3-4, Oil of Eucalyptus 2-3, borax 1-2, tripoly phosphate sodium STPP 1-2, silane coupling agent KH550 2-3, water are an amount of;

The preparation method is:

(1) attapulgite mixes with zinc sulfate, Sodium Selenite, manganous sulfate, ferrous sulfate, borax, adds silane silane coupling agent KH550 and stirs to such an extent that mixing is fertile;

(2) again with the urea fusing, add Oil of Eucalyptus, stir, add gained and mix fertilizer, stir;

(3) again other remaining component is added suitable quantity of water furnishing slurry, add step (2) gained material, mix, granulation, oven dry is namely.

2. the special-purpose fertile preparation method of nano-sized carbon tealeaves according to claim 1 is characterized in that may further comprise the steps:

(1) with the urea heat fused, add after nano-sized carbon stirs, add zinc sulfate, sodium sulphite, iron trichloride, Oleum Cinnamomi, soil conditioner again and stir;

(2) with the suitable quantity of water heating, add brown sugar and oil foot, after confusing, add step (1) material and other remaining component again, after mixing, granulation, oven dry, namely.