CN103289611A - 一种丙烯酸树脂热转印胶及其制备方法 - Google Patents

一种丙烯酸树脂热转印胶及其制备方法 Download PDF

Info

Publication number
CN103289611A
CN103289611A CN2013101944928A CN201310194492A CN103289611A CN 103289611 A CN103289611 A CN 103289611A CN 2013101944928 A CN2013101944928 A CN 2013101944928A CN 201310194492 A CN201310194492 A CN 201310194492A CN 103289611 A CN103289611 A CN 103289611A
Authority
CN
China
Prior art keywords
parts
acrylic resin
thermal transfer
minute
polyisobutene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013101944928A
Other languages
English (en)
Other versions
CN103289611B (zh
Inventor
姜成浩
朱学贵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI YICAI GLASSWARE Co Ltd
Original Assignee
ANHUI YICAI GLASSWARE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI YICAI GLASSWARE Co Ltd filed Critical ANHUI YICAI GLASSWARE Co Ltd
Priority to CN201310194492.8A priority Critical patent/CN103289611B/zh
Publication of CN103289611A publication Critical patent/CN103289611A/zh
Application granted granted Critical
Publication of CN103289611B publication Critical patent/CN103289611B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种丙烯酸树脂热转印胶及其制备方法，由下列重量份的原料制成：丙烯酸树脂（AR-1520）25-28、聚异丁烯12-15、氨丙基三乙氧基硅烷4-6、甲基三乙氧基硅烷3-5、过氧化二异丙苯2-3、顺丁烯二酸二丁酯12-15、十二烷基硫醇4-6、松香5-8、交联剂TAC1-2、二辛酯3-5、1-羟乙基-2-油基咪唑啉1-2、对苯二胺2-3、丙酮55-60、二甲苯40-45。本发明和现有技术相比，具有粘结牢固，不易破损、脱落、变黄的优点，提高产品质量。本发明配方中增加了松香、聚异丁烯，通过聚合交联，大大提高了本发明的粘结能力，提高了耐候性。1-羟乙基-2-油基咪唑啉使得耐腐蚀性大大提高。

Description

一种丙烯酸树脂热转印胶及其制备方法
技术领域
本发明涉及一种热转印胶粘剂，属于印刷材料领域。
背景技术
热转印是将有图案的转印膜与承印物直接接触，转印膜上的图文层熔解并转移到承印物上。热转印膜上包括有载体层、离型层、保护层、油墨层、粘结层，各涂层间紧密联系，相互影响。其中，粘结层就是用来粘结油墨信息层和各种材料的基材胶黏剂，须具备高的粘附力、耐高温性能、耐刮伤性、耐水性、耐蒸煮和耐化学品性能。现有技术中热转印胶黏剂质量问题，导致转印图案耐刮伤性、附着性、耐水性和耐高温等性能都不理想。
发明内容
本发明的目的是提供一种丙烯酸树脂热转印胶及其制备方法，提高转印图案的耐候性能。
本发明的技术方案如下：
一种丙烯酸树脂热转印胶，其特征在于由下列重量份的原料制成：丙烯酸树脂（AR-1520）25-28、聚异丁烯12-15、氨丙基三乙氧基硅烷4-6、甲基三乙氧基硅烷3-5、过氧化二异丙苯2-3、顺丁烯二酸二丁酯12-15、十二烷基硫醇4-6、松香5-8、交联剂 TAC 1-2、二辛酯3-5、1-羟乙基-2-油基咪唑啉1-2、对苯二胺2-3、丙酮55-60、二甲苯40-45。
所述的丙烯酸树脂热转印胶的制备方法，其特征在于包括以下步骤：
（1）、将聚异丁烯、氨丙基三乙氧基硅烷放入丙酮中，加热至60-65℃，然后，过入过氧化二异丙苯、顺丁烯二酸二丁酯，搅拌10-20分钟，再加入十二烷基硫醇、松香，反应40-50分钟，升温至130-140℃，加入交联剂 TAC 、二辛酯、1-羟乙基-2-油基咪唑啉，搅拌反应2-3小时；
（2）、将丙烯酸类树脂（AR-1520）、对苯二胺等其它物料加入二甲苯中，搅拌10-20分钟；将步骤（1）物料加入其中，搅拌40-50分钟，即得。
本发明和现有技术相比，具有粘结牢固，不易破损、脱落、变黄的优点，提高产品质量。本发明配方中增加了松香、聚异丁烯，通过聚合交联，大大提高了本发明的粘结能力，提高了耐候性。1-羟乙基-2-油基咪唑啉使得耐腐蚀性大大提高。
具体实施方式
一种丙烯酸树脂热转印胶，由下列重量份（公斤）的原料制成：丙烯酸树脂（AR-1520）28、聚异丁烯15、氨丙基三乙氧基硅烷6、甲基三乙氧基硅烷3、过氧化二异丙苯2、顺丁烯二酸二丁酯15、十二烷基硫醇4、松香5、交联剂 TAC 1、二辛酯5、1-羟乙基-2-油基咪唑啉2、对苯二胺2、丙酮55、二甲苯45。
制备方法，包括以下步骤：
（1）、将聚异丁烯、氨丙基三乙氧基硅烷放入丙酮中，加热至60-65℃，然后，过入过氧化二异丙苯、顺丁烯二酸二丁酯，搅拌10-20分钟，再加入十二烷基硫醇、松香，反应40-50分钟，升温至130-140℃，加入交联剂 TAC 、二辛酯、1-羟乙基-2-油基咪唑啉，搅拌反应2-3小时；
（2）、将丙烯酸类树脂（AR-1520）、对苯二胺等其它物料加入二甲苯中，搅拌10-20分钟；将步骤（1）物料加入其中，搅拌40-50分钟，即得。
将本发明热转印胶用于酒瓶的图案转印，油墨层上为本发明胶粘剂层，进行下列检测：
    用指甲去刮擦其油墨层，图案完好如初；酒瓶表面干燥，无粘手感；将酒瓶放入水中浸泡36小时，图案无变化，无脱落；将酒瓶放入60℃热水中，12小时，图案无变化，无脱落，指甲去刮擦其油墨层，图案完好如初；图案无裂纹。

Claims (2)

1.一种丙烯酸树脂热转印胶，其特征在于由下列重量份的原料制成：丙烯酸树脂（AR-1520）25-28、聚异丁烯12-15、氨丙基三乙氧基硅烷4-6、甲基三乙氧基硅烷3-5、过氧化二异丙苯2-3、顺丁烯二酸二丁酯12-15、十二烷基硫醇4-6、松香5-8、交联剂 TAC 1-2、二辛酯3-5、1-羟乙基-2-油基咪唑啉1-2、对苯二胺2-3、丙酮55-60、二甲苯40-45。
2.根据权利要求1所述的丙烯酸树脂热转印胶的制备方法，其特征在于包括以下步骤：
（1）、将聚异丁烯、氨丙基三乙氧基硅烷放入丙酮中，加热至60-65℃，然后，过入过氧化二异丙苯、顺丁烯二酸二丁酯，搅拌10-20分钟，再加入十二烷基硫醇、松香，反应40-50分钟，升温至130-140℃，加入交联剂 TAC 、二辛酯、1-羟乙基-2-油基咪唑啉，搅拌反应2-3小时；
（2）、将丙烯酸类树脂（AR-1520）、对苯二胺等其它物料加入二甲苯中，搅拌10-20分钟；将步骤（1）物料加入其中，搅拌40-50分钟，即得。
CN201310194492.8A 2013-05-23 2013-05-23 一种丙烯酸树脂热转印胶及其制备方法 Active CN103289611B (zh)