CN103289606B - 一种鞋用热熔胶及其制备方法 - Google Patents

一种鞋用热熔胶及其制备方法 Download PDF

Info

Publication number
CN103289606B
CN103289606B CN201310164211.4A CN201310164211A CN103289606B CN 103289606 B CN103289606 B CN 103289606B CN 201310164211 A CN201310164211 A CN 201310164211A CN 103289606 B CN103289606 B CN 103289606B
Authority
CN
China
Prior art keywords
terpolymer
rubber
tackifying resin
hot
antioxidant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310164211.4A
Other languages
English (en)
Other versions
CN103289606A (zh
Inventor
方菊萍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Goldmen Industry & Trading Co Ltd
Original Assignee
Anhui Goldmen Industry & Trading Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Goldmen Industry & Trading Co Ltd filed Critical Anhui Goldmen Industry & Trading Co Ltd
Priority to CN201310164211.4A priority Critical patent/CN103289606B/zh
Publication of CN103289606A publication Critical patent/CN103289606A/zh
Application granted granted Critical
Publication of CN103289606B publication Critical patent/CN103289606B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种鞋用热熔胶，由下列重量份的组分制备而成：EVA树脂50-60、三元乙丙橡胶增粘树脂15-20、氧化聚乙烯蜡10-14、石灰石粉4-5、氧化锆1-2、抗氧剂1010？0.2-0.3、抗氧剂736？0.1-0.2、抗氧剂2246-S？0.1-0.2、乙酰柠檬酸三乙酯5-6、环氧四氢邻苯二甲酸二辛酯4-6。首先制备三元乙丙橡胶增粘树脂，然后和其它原料混合，在通过挤出机挤出，冷却，切粒即可。本发明的热熔胶在配方中添加了自制的橡胶增粘树脂，使制得的热熔胶的粘结性能增强，耐侯性好，且韧性好、耐水性好。

Description

一种鞋用热熔胶及其制备方法
技术领域
本发明涉及热熔胶领域，具体涉及一种鞋用热熔胶及其制备方法。
背景技术
热熔胶是以热塑性树脂或弹性体为基料，添加增黏剂、增塑剂、抗氧化剂、阻燃剂及填料，经熔融混合而成的固体状粘合剂。与热固型、溶剂型和水基型胶粘剂相比具有很多优越性，所以从20世纪50年代至今，热熔胶已经在许多领域得到了快速发展，尤其在印刷、包装等行业已用热熔胶取代钉装和线装，并开始用于建筑、飞机、舰船和汽车内装饰等领域。
现有市场上热熔胶相关产品较多，但随着温度的变化，传统热熔胶的性能也在变化，当温度升到一定高温或降到一定低温热熔胶的性能都会降低，对材料的结合强度削弱，最终影响材料的强度。
发明内容
本发明提供一种鞋用热熔胶，本发明的热熔胶耐热性好，粘结性强，耐水性好。
本发明采用的技术方案如下：
EVA树脂50-60、三元乙丙橡胶增粘树脂15-20、氧化聚乙烯蜡10-14、石灰石粉4-5、氧化锆1-2、抗氧剂10100.2-0.3、抗氧剂7360.1-0.2、抗氧剂2246-S0.1-0.2、乙酰柠檬酸三乙酯5-6、环氧四氢邻苯二甲酸二辛酯4-6，
其中，所述三元乙丙橡胶增粘树脂由下列方法制备而得：
（1）将15-20重量份三元乙丙橡胶、24-28重量份二甲苯、0.1-0.2重量份的防老剂DNP、6-9重量份顺丁烯二酸酐、0.2-0.3重量份的交联剂TAIC混合，在80-110℃下，反应2-3小时；
（2）然后加入聚合松香、凹凸棒土，在130-150℃下，反应2-3小时，要求，聚合松香、三元乙丙橡胶、凹凸棒土三者的重量比为:100:15-18：0.5-0.6；
（3）再加入氨丙基三乙氧基硅烷、二茂铁在140-175℃下反应1-2小时，要求，聚合松香、氨丙基三乙氧基硅烷烷、二茂铁的重量比为100:0.5-0.8:0.5-1.0；
（4）最后蒸馏除去溶剂二甲苯，得到三元乙丙橡胶增粘树脂。
所述的鞋用热熔胶的制备方法，其特征在于，包括以下步骤：
（1）首先制备三元乙丙橡胶增粘树脂；
（2）按配方比例称取各配方原料，将原料倒入高速搅拌机混合均匀；
（3）搅拌均匀的混合料由双螺杆挤出机中挤出造粒，设定机筒加热温度为138-168℃，口模温度为168-185℃，螺杆转速为12-45rpm，加料转速为8-35rpm，待物料从口模挤出后经水槽冷却后切料，得到成品热熔胶。
与现有技术相比，本发明具有如下有益效果：
本发明的热熔胶粘结性强，在配方中添加了自制的橡胶增粘树脂，使制得的热熔胶的粘结性能增强，同时耐侯性好，韧性好、耐水性好。
具体实施方式
称取下列重量（kg）的组分原料：EVA树脂55、三元乙丙橡胶增粘树脂18、氧化聚乙烯蜡12、石灰石粉5、氧化锆2、抗氧剂10100.2、抗氧剂7360.1、抗氧剂2246-S0.1、乙酰柠檬酸三乙酯5、环氧四氢邻苯二甲酸二辛酯6，
制备方法：
（1）将18kg三元乙丙橡胶、28kg二甲苯、0.1kg的防老剂DNP、9kg顺丁烯二酸酐、0.2kg的交联剂TAIC混合，在80-110℃下，反应2-3小时；
（2）然后加入100kg聚合松香、0.1kg凹凸棒土，在130-150℃下，反应2-3小时；
（3）再加入0.6kg氨丙基三乙氧基硅烷、0.5kg二茂铁在140-175℃下反应1-2小时；
（4）最后蒸馏除去溶剂二甲苯，得到三元乙丙橡胶增粘树脂；
（5）按配方比例称取三元乙丙橡胶增粘树脂和配方中的其它原料，将所有原料投入高速搅拌机混合均匀；
（6）搅拌均匀的混合料由双螺杆挤出机中挤出造粒，设定机筒加热温度为138-168℃，口模温度为168-185℃，螺杆转速为12-45rpm，加料转速为8-35rpm，待物料从口模挤出后经水槽冷却后切料，得到成品热熔胶。
本发明方法制得的热熔胶的的主要技术指标如下：
拉伸强度（Mpa）　3.7
粘接强度（N/2.5cm）92
固化时间（s）4
环球软化点（℃）　100
熔融粘度（Pa.s）2.5-3.0。

Claims (2)

1.一种鞋用热熔胶，其特征在于，由下列重量份的组分制备而成：EVA树脂50-60、三元乙丙橡胶增粘树脂15-20、氧化聚乙烯蜡10-14、石灰石粉4-5、氧化锆1-2、抗氧剂10100.2-0.3、抗氧剂7360.1-0.2、抗氧剂2246-S0.1-0.2、乙酰柠檬酸三乙酯5-6、环氧四氢邻苯二甲酸二辛酯4-6，其中，所述三元乙丙橡胶增粘树脂由下列方法制备而得：
（1）将15-20重量份三元乙丙橡胶、24-28重量份二甲苯、0.1-0.2重量份的防老剂DNP、6-9重量份顺丁烯二酸酐、0.2-0.3重量份的交联剂TAIC混合，在80-110℃下，反应2-3小时；
（2）然后加入聚合松香、凹凸棒土，在130-150℃下，反应2-3小时，要求，聚合松香、三元乙丙橡胶、凹凸棒土三者的重量比为:100:15-18：0.5-0.6；
（3）再加入氨丙基三乙氧基硅烷、二茂铁在140-175℃下反应1-2小时，要求，聚合松香、氨丙基三乙氧基硅烷、二茂铁的重量比为100:0.5-0.8:0.5-1.0；
（4）最后蒸馏除去溶剂二甲苯，得到三元乙丙橡胶增粘树脂。
2.　根据权利要求1所述的鞋用热熔胶的制备方法，其特征在于，包括以下步骤：
（1）首先制备三元乙丙橡胶增粘树脂；
（2）按配方比例称取各配方原料，将原料倒入高速搅拌机混合均匀；
（3）搅拌均匀的混合料由双螺杆挤出机中挤出造粒，设定机筒加热温度为138-168℃，口模温度为168-185℃，螺杆转速为12-45rpm，加料转速为8-35rpm，待物料从口模挤出后经水槽冷却后切料，得到成品热熔胶。
CN201310164211.4A 2013-05-07 2013-05-07 一种鞋用热熔胶及其制备方法 Active CN103289606B (zh)