CN103289457A - Uv淋涂柔性亮光面漆涂料 - Google Patents

Uv淋涂柔性亮光面漆涂料 Download PDF

Info

Publication number
CN103289457A
CN103289457A CN2012100528460A CN201210052846A CN103289457A CN 103289457 A CN103289457 A CN 103289457A CN 2012100528460 A CN2012100528460 A CN 2012100528460A CN 201210052846 A CN201210052846 A CN 201210052846A CN 103289457 A CN103289457 A CN 103289457A
Authority
CN
China
Prior art keywords
top coat
showering
glycol diacrylate
functional monomer
kilograms
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012100528460A
Other languages
English (en)
Inventor
周利民
程绍楠
周庚
王飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Fuchen Chemical Co Ltd
Beijing Zhanchen Chemical Co Ltd
Zhanchen Paint Group Co Ltd
Original Assignee
Shanghai Fuchen Chemical Co Ltd
Beijing Zhanchen Chemical Co Ltd
Zhanchen Paint Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Fuchen Chemical Co Ltd, Beijing Zhanchen Chemical Co Ltd, Zhanchen Paint Group Co Ltd filed Critical Shanghai Fuchen Chemical Co Ltd
Priority to CN2012100528460A priority Critical patent/CN103289457A/zh
Publication of CN103289457A publication Critical patent/CN103289457A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种UV淋涂柔性亮光面漆涂料，其特征在于，由下列组成物及重量百分比组分：功能性单体28%-38%；聚丙烯酸酯18%-26%；聚氨酯丙烯酸树脂37%-45%；流平剂0.3%-0.4%；光引发剂7%-9%。所述功能性单体为甲基丙烯酸羟基乙酯(HEMA)、二丙二醇二丙烯酸酯(DPGDA)、三丙二醇二丙烯酸酯(TPGDA)的混合物。本发明的UV淋涂柔性亮光面漆涂料柔韧性极佳，耐黄性好，低气味，成本低廉，操作简单灵活，无浪费，生产效率高。

Description

UV淋涂柔性亮光面漆涂料
技术领域
本发明涉及一种UV淋涂柔性亮光面漆涂料。
背景技术
舒适、和谐的居家环境是我们归航停泊的港湾，合适的装饰画不仅能点缀亮丽家居，画龙点睛，而且能为家人带来好运祥和。如果在装饰画上涂上一层油漆，不仅可以起到保护作用，而且还能让画面的装饰效果更好。根据这一需求，我们开发了一种涂装在画布上的UV淋涂柔性亮光面漆涂料。
发明内容
本发明的目的在于克服UV淋涂亮光面漆柔韧性的不足，提供一种UV淋涂柔性亮光面漆涂料，该面漆柔韧性极佳，耐黄性好，低气味，成本低廉，操作简单灵活，无浪费，生产效率高，与同类产品相比，处于国内领先水平。
本发明一种UV淋涂柔性亮光面漆涂料，其特征在于，由下列组成物及重量百分比组分：
功能性单体                        28%-38%，
聚丙烯酸酯树脂                            18%-26%，
聚氨酯丙烯酸树脂                  37%-45%，
流平剂                            0.3%-0.4%，
光引发剂                          7%-9%。
其特征在于，所述功能性单体为甲基丙烯酸羟基乙酯(HEMA)、二丙二醇二丙烯酸酯(DPGDA)、三丙二醇二丙烯酸酯(TPGDA)的其混合物。其特征在于，所述的功能性单体混合物含有：
甲基丙烯酸羟基乙酯                 4~6重量份，
二丙二醇二丙烯酸酯                 11~20重量份，
三丙二醇二丙烯酸酯                 15~30重量份，
所述聚氨酯丙烯酸酯（PUA）可采用江门恒光牌号5310的产品。
所述聚丙烯酸树脂，可采用长兴牌号为7119的产品。
所述流平剂为丙烯酸反应型流平剂，可采用毕克公司牌号为BYK371的产品。
所述光引发剂为2-羟基-2-甲基-1-苯基-1-丙酮，如汽巴公司1173；或1-羟基-环已基-苯基甲酮，如汽巴公司的184；或二者混合物。
本发明的UV淋涂柔性亮光面漆涂料具有极佳柔韧性，耐黄性好，低气味，成本低廉，操作简单灵活，无浪费，生产效率高等特点。
具体实施方式
下面结合实施例对本发明做详细说明。
实施例1
取功能性单体甲基丙烯酸羟基乙酯（HEMA）4千克，二丙二醇二丙烯酸酯（DPGDA）13千克，三丙二醇二丙烯酸酯（TPGDA）18千克，聚氨酯丙烯酸酯38千克，聚丙烯酸树脂19千克，流平剂（BYK371）0.3千克，混合搅拌，充分分散后，加入光引发剂( 1173)7.7千克，搅拌充分分散均匀无硬块即可。
实施例2
取功能性单体甲基丙烯酸羟基乙酯（HEMA）4千克，二丙二醇二丙烯酸酯（DPGDA）13千克，三丙二醇二丙烯酸酯（TPGDA）18千克，聚氨酯丙烯酸酯37千克，聚丙烯酸树脂20千克，流平剂（BYK371）0.4千克，混合搅拌，充分分散后，加入光引发剂( 184)7.6千克，搅拌充分分散均匀无硬块即可。
实施例3
取功能性单体甲基丙烯酸羟基乙酯（HEMA）4千克，二丙二醇二丙烯酸酯（DPGDA）11千克，三丙二醇二丙烯酸酯（TPGDA）18千克，聚氨酯丙烯酸酯40千克，聚丙烯酸树脂19千克，流平剂（BYK371）0.3千克，混合搅拌，充分分散后，加入光引发剂( 1173)4.7千克，光引发剂( 184)3千克，搅拌充分分散均匀无硬块即可。
实施例4
取功能性单体的甲基丙烯酸羟基乙酯（HEMA）5千克，二丙二醇二丙烯酸酯（DPGDA）12千克，三丙二醇二丙烯酸酯（TPGDA）18千克，聚氨酯丙烯酸酯40千克，聚丙烯酸树脂17千克，流平剂（BYK371）0.3千克，混合搅拌，充分分散后，加入光引发剂( 1173)7.7千克，搅拌充分分散均匀无硬块即可。
本发明的UV淋涂柔性亮光面漆涂料，为透明粘稠液，粘度为85~100kμ（25℃），油漆固含量90.5 wt%~92wt%，低气味。在储存时应避免紫外光或者太阳光直接照射，经测试其贮存稳定性（50℃/7d），结果无异常。
涂装时，分散好本产品，用淋涂方式涂布，涂布量为80~120g/㎡，然后进行紫外光固化即可。半固化紫外光能量：160~180mj/m2，全固化紫外光能量：200~250mj/m2。经测试，柔韧性可经180度对折，光泽96以上，硬度1H，室外暴晒3天无明显黄变。当室温低于20℃时，采用水浴将UV漆加热至50～60℃后再施工。
本发明的UV淋涂柔性亮光面漆涂料柔韧性极佳，耐黄性好，低气味，成本低廉，操作简单灵活，无浪费，生产效率高。
应理解，以上实施例仅用于说明本发明而非用于限制本发明的范围。对于本领域技术人员来说，在不脱离本申请构思的前提下，可以对本发明作各种改动或修改，这些等价形式同样落于本申请所附权利要求书所限定的范围内。

Claims (5)

1.一种UV淋涂柔性亮光面漆涂料，其特征在于，由下列组成物及重量百分比组分：
功能性单体                        28%-38%，
聚丙烯酸酯树脂                    18%-26%，
聚氨酯丙烯酸树脂                  37%-45%，
流平剂                            0.3%-0.4%，
光引发剂                          7%-9%。
2.按权利要求1所述的一种UV淋涂柔性亮光面漆涂料，其特征在于，所述功能性单体为甲基丙烯酸羟基乙酯(HEMA)、二丙二醇二丙烯酸酯(DPGDA)、三丙二醇二丙烯酸酯(TPGDA)的混合物。
3.按权利要求2所述的一种UV淋涂柔性亮光面漆涂料，其特征在于，所述的功能性单体混合物含有：
甲基丙烯酸羟基乙酯                 4~6重量份，
二丙二醇二丙烯酸酯                 11~20重量份，
三丙二醇二丙烯酸酯                 15~30重量份。
4.按权利要求1所述的一种UV淋涂柔性亮光面漆涂料，其特征在于，所述流平剂为丙烯酸反应型流平剂。
5.按权利要求1所述的一种UV淋涂柔性亮光面漆涂料，其特征在于，所述光引发剂为2-羟基-2-甲基-1-苯基-1-丙酮，或1-羟基-环已基-苯基甲酮。
CN2012100528460A 2012-03-02 2012-03-02 Uv淋涂柔性亮光面漆涂料 Pending CN103289457A (zh)