CN103289167A - 硅烷交联聚乙烯专用料 - Google Patents

硅烷交联聚乙烯专用料 Download PDF

Info

Publication number
CN103289167A
CN103289167A CN2013102301511A CN201310230151A CN103289167A CN 103289167 A CN103289167 A CN 103289167A CN 2013102301511 A CN2013102301511 A CN 2013102301511A CN 201310230151 A CN201310230151 A CN 201310230151A CN 103289167 A CN103289167 A CN 103289167A
Authority
CN
China
Prior art keywords
agent
resin
oxidation inhibitor
emulsus
flow rate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013102301511A
Other languages
English (en)
Inventor
镇国广
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2013102301511A priority Critical patent/CN103289167A/zh
Publication of CN103289167A publication Critical patent/CN103289167A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种硅烷交联聚乙烯专用料。由普通线性聚乙烯树脂、高流动速率线性树脂、硅烷偶联剂、催化剂、引发剂、抗铜剂、乳状流变剂、抗氧剂和润滑剂组成，所述普通线性聚乙烯树脂、高流动速率线性树脂、硅烷偶联剂、催化剂、引发剂、抗铜剂、乳状流变剂、抗氧剂和润滑剂的质量比为：80：10.0～12.5：1.5～2.0∶1.0～1.25∶0.5～1.25∶0.5～0.75∶0.5～1.0∶0.75～1.5:0.75～1.6:1.25～1.5。本发明产品稳定性好，主要用于给水管材、电线电缆、汽车配件等行业，“体积电阻率”检测结果达到相关国家标准的8倍，经过一定温度（25℃及以上）条件下存放后能够自然交联，效果优于二步法交联绝缘料，且工艺简单操作方便。

Description

硅烷交联聚乙烯专用料
技术领域
本发明涉及一种电缆的生产原料，尤其涉及一种硅烷交联聚乙烯专用料。
背景技术
传统交联聚乙烯材料应用于大型管材、电缆和塑料配件时，须进行二步蒸煮，既受限于体积长度蒸煮不均匀还需消耗大量能源，同时因交联结构原因，材料老化周期亦较短，因此厂家建设水浴池或蒸汽房，大大增加了企业的负担，增加生产成本。
发明内容
本发明目的在于提供一种只需一步完成、在一定温度条件下、自然形成交联过程的硅烷交联聚乙烯专用料。
本发明的技术方案是：由普通线性聚乙烯树脂、高流动速率线性树脂、硅烷偶联剂、催化剂、引发剂、抗铜剂、乳状流变剂、抗氧剂和润滑剂组成，所述普通线性聚乙烯树脂、高流动速率线性树脂、硅烷偶联剂、催化剂、引发剂、抗铜剂、乳状流变剂、抗氧剂和润滑剂的质量比为：80： 10.0～12.5：1.5～2.0∶1.0～1.25∶0.5～1.25∶0.5～0.75∶0.5～1.0∶0.75～1.5: 0.75～1.6: 1.25～1.5。
所述抗氧剂由抗氧剂168和抗氧剂1024组成，抗氧剂168和抗氧剂1024的质量比为1∶1。
本发明将聚乙烯树脂、硅烷、过氧化物和交联催化剂等只经过均匀混合，直接加入到挤出机中生产管材或电线电缆等产品。本发明中所用乳状流变剂，目的在于在混合过程中，能够将配方中的粉状材料均匀分散并包裹于粒状聚乙烯材料外表，充分分散配方中的粉状材料。
本发明产品稳定性好，主要用于给水管材、电线电缆、汽车配件等行业。本发明产品经“机械工业电工材料及特种线缆产品质量监督检测中心”检测，符合相关要求，“体积电阻率”检测结果达到相关国家标准的8倍，经多家客户试用本材料生产的给水管材、电线电缆、汽车配件，经过一定温度（25℃及以上）条件下存放后能够自然交联，效果优于二步法交联绝缘料，且工艺简单操作方便。
具体实施方式
实施例1
硅烷交联聚乙烯专用料，由普通线性聚乙烯树脂、高流动速率线性树脂、硅烷偶联剂、催化剂、引发剂、抗铜剂、乳状流变剂、抗氧剂和润滑剂组成，所述普通线性聚乙烯树脂80kg、高流动速率线性树脂12.5kg、硅烷偶联剂1.5kg、催化剂二丁基锡1.0kg、引发剂(DCP )1.25kg、抗铜剂(1076)0.5kg、乳状流变剂(PPA)0.5kg、抗氧剂(168)0.75kg、抗氧剂（1024）0.75kg和润滑剂PE蜡1.25kg，将配制好的名种材料，置于高速混合机内，混五分钟后放出，抽真空后包装即可。
实施例2
硅烷交联聚乙烯专用料，由普通线性聚乙烯树脂、高流动速率线性树脂、硅烷偶联剂、催化剂、引发剂、抗铜剂、乳状流变剂、抗氧剂和润滑剂组成，所述普通线性聚乙烯树脂80kg、高流动速率线性树脂10.0kg、硅烷偶联剂2.0kg、催化剂二丁基锡1.25kg、引发剂(DCP )0.5kg、抗铜剂(1076)0.75kg、乳状流变剂(PPA)1.0kg、抗氧剂(168)1.5kg、抗氧剂（1024）1.5kg和润滑剂PE蜡1.5kg，将配制好的名种材料，置于高速混合机内，混五分钟后放出，抽真空后包装即可。
实施例3
硅烷交联聚乙烯专用料，由普通线性聚乙烯树脂、高流动速率线性树脂、硅烷偶联剂、催化剂、引发剂、抗铜剂、乳状流变剂、抗氧剂和润滑剂组成，所述普通线性聚乙烯树脂80kg、高流动速率线性树脂11kg、硅烷偶联剂1.8kg、催化剂二丁基锡1.1kg、引发剂(DCP )0.8kg、抗铜剂(1076)0.6kg、乳状流变剂(PPA)0.7kg、抗氧剂(168)1.0kg、抗氧剂（1024）1.0kg和润滑剂PE蜡1.35kg，将配制好的名种材料，置于高速混合机内，混五分钟后放出，抽真空后包装即可。

Claims (2)

1.硅烷交联聚乙烯专用料，其特征在于：由普通线性聚乙烯树脂、高流动速率线性树脂、硅烷偶联剂、催化剂、引发剂、抗铜剂、乳状流变剂、抗氧剂和润滑剂组成，所述普通线性聚乙烯树脂、高流动速率线性树脂、硅烷偶联剂、催化剂、引发剂、抗铜剂、乳状流变剂、抗氧剂和润滑剂的质量比为：80： 10.0～12.5：1.5～2.0∶1.0～1.25∶0.5～1.25∶0.5～0.75∶0.5～1.0∶0.75～1.5: 0.75～1.6: 1.25～1.5。
2.根据权利要求1所述的硅烷交联聚乙烯专用料，其特征在于：所述抗氧剂由抗氧剂168和抗氧剂1024组成，抗氧剂168和抗氧剂1024的质量比为1∶1。
CN2013102301511A 2013-06-09 2013-06-09 硅烷交联聚乙烯专用料 Pending CN103289167A (zh)