CN103289142A - 一种胎面橡胶组合物 - Google Patents
一种胎面橡胶组合物 Download PDFInfo
- Publication number
- CN103289142A CN103289142A CN2013102583113A CN201310258311A CN103289142A CN 103289142 A CN103289142 A CN 103289142A CN 2013102583113 A CN2013102583113 A CN 2013102583113A CN 201310258311 A CN201310258311 A CN 201310258311A CN 103289142 A CN103289142 A CN 103289142A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber composition
- rubber
- tread rubber
- cutting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种胎面橡胶组合物,其特征在于:以100质量份的天然橡胶为基准,以质量份计还包括:炭黑20-30份;白炭黑3-5份;二氧化硅5-10份;发泡剂1-2份;耐切割尼龙短纤维5-8份;竹炭3-5份;橡胶粘合剂0.5-3份;防护蜡0.5-1份;硫化促进剂2-3份。本发明的优点是:各个成分之间通过相互配比制成的橡胶,在使用过程中耐磨效果好,增加了安全性和节能性,耐切割尼龙短纤维和二氧化硅的添加,增加了橡胶的拉伸和安全性能,竹炭,使制成的橡胶组合物性能更加稳定,提高了轮胎的综合性能,延长了使用寿命。
Description
技术领域
本发明涉及一种胎面橡胶组合物。
背景技术
随着工程车辆技术的不断进步,现代采矿、建筑等领域使用的工程机械车辆不断向大吨位、高载荷、高强度工作使用的方向发展,随着车辆负荷与工作强度的不断提高,无论是斜交线结构的工程轮胎还是子午线钢丝结构的工程轮胎,轮胎胎面胶磨耗性能、轮胎滚动阻力性能及轮胎湿滑性能都不是很理想,同时使用寿命短,对轮胎的安全性和节能性有着一定的影响。
因此,为解决上述问题,特提供一种新的技术方案来满足需求。
发明内容
本发明的目的是提供一种胎面橡胶组合物。
本发明采用的技术方案是:
一种胎面橡胶组合物,以100质量份的天然橡胶为基准,以质量份计还包括:
炭黑 20-30份;
白炭黑 3-5份;
二氧化硅 5-10份;
发泡剂 1-2份;
耐切割尼龙短纤维 5-8份;
竹炭 3-5份;
橡胶粘合剂 0.5-3份;
防护蜡 0.5-1份;
硫化促进剂 2-3份。
所述发泡剂为碳酸氢钠、碳酸氢铵、偶氮类化合物或亚硝基化合物。
所述硫化促进剂为N-叔丁基-2-笨并噻唑磺酰胺。
本发明的优点是:各个成分之间通过相互配比制成的橡胶,在使用过程中耐磨效果好,增加了安全性和节能性,耐切割尼龙短纤维和二氧化硅的添加,增加了橡胶的拉伸和安全性能,竹炭,使制成的橡胶组合物性能更加稳定,提高了轮胎的综合性能,延长了使用寿命。
具体实施方式
为了加深对本发明的理解,下面将结合实施例对本发明作进一步详述,该实施例仅用于解释本发明,并不构成对本发明保护范围的限定。
实施例1
一种胎面橡胶组合物,以100质量份的天然橡胶为基准,以质量份计还包括:
炭黑 20份;
白炭黑 3份;
二氧化硅 5份;
碳酸氢钠 1份;
耐切割尼龙短纤维 5份;
竹炭 3份;
橡胶粘合剂 0.5份;
防护蜡 0.5份;
N-叔丁基-2-笨并噻唑磺酰胺 2份。
实施例2
一种胎面橡胶组合物,以100质量份的天然橡胶为基准,以质量份计还包括:
炭黑 25份;
白炭黑 4份;
二氧化硅 8份;
碳酸氢铵 1.5份;
耐切割尼龙短纤维 7份;
竹炭 4份;
橡胶粘合剂 2份;
防护蜡 0.5-1份;
N-叔丁基-2-笨并噻唑磺酰胺 2.5份。
实施例3
一种胎面橡胶组合物,以100质量份的天然橡胶为基准,以质量份计还包括:
炭黑 30份;
白炭黑 5份;
二氧化硅 10份;
偶氮类化合物 2份;
耐切割尼龙短纤维 8份;
竹炭 5份;
橡胶粘合剂 3份;
防护蜡 1份;
N-叔丁基-2-笨并噻唑磺酰胺 3份。
实施例4
一种胎面橡胶组合物,以100质量份的天然橡胶为基准,以质量份计还包括:
炭黑 21份;
白炭黑 5份;
二氧化硅 6份;
亚硝基化合物 1.8份;
耐切割尼龙短纤维 5份;
竹炭 4份;
橡胶粘合剂 1.5份;
防护蜡 1份;
N-叔丁基-2-笨并噻唑磺酰胺 3份。
本发明的优点是:各个成分之间通过相互配比制成的橡胶,在使用过程中耐磨效果好,增加了安全性和节能性,耐切割尼龙短纤维和二氧化硅的添加,增加了橡胶的拉伸和安全性能,竹炭,使制成的橡胶组合物性能更加稳定,提高了轮胎的综合性能,延长了使用寿命。
Claims (3)
1.一种胎面橡胶组合物,其特征在于:以100质量份的天然橡胶为基准,以质量份计还包括:
炭黑 20-30份;
白炭黑 3-5份;
二氧化硅 5-10份;
发泡剂 1-2份;
耐切割尼龙短纤维 5-8份;
竹炭 3-5份;
橡胶粘合剂 0.5-3份;
防护蜡 0.5-1份;
硫化促进剂 2-3份。
2.根据权利要求1所述的一种胎面橡胶组合物,其特征在于:所述发泡剂为碳酸氢钠、碳酸氢铵、偶氮类化合物或亚硝基化合物。
3.根据权利要求1所述的一种胎面橡胶组合物,其特征在于:所述硫化促进剂为N-叔丁基-2-笨并噻唑磺酰胺。