CN103275291A - 一种抗菌除臭聚氨酯鞋底材料 - Google Patents
一种抗菌除臭聚氨酯鞋底材料 Download PDFInfo
- Publication number
- CN103275291A CN103275291A CN2013102131258A CN201310213125A CN103275291A CN 103275291 A CN103275291 A CN 103275291A CN 2013102131258 A CN2013102131258 A CN 2013102131258A CN 201310213125 A CN201310213125 A CN 201310213125A CN 103275291 A CN103275291 A CN 103275291A
- Authority
- CN
- China
- Prior art keywords
- antibacterial
- polyurethane sole
- deodouring
- sole materials
- bamboo charcoal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗菌除臭聚氨酯鞋底材料,以重量百分比计,包括如下组分:多元醇35%-50%;扩链剂4%-9%;催化剂0.03%-2%;发泡剂0.09%-0.3%;匀泡剂0.05%-2%;增塑剂2%-8%;预聚体35%-50%;竹炭粉末1%-5%;抗菌性沸石粉0.5%-5%;硫磺 0.5%-3%。本发明使用的竹炭粉末,抗菌性沸石粉以及硫磺均是天然的抗菌剂。其中,竹炭粉末不但有抗菌的功效,亦有较好的吸湿性,通过添加在鞋底材料中,能够较好地提高材料的吸湿透气性;另外,抗菌性沸石粉和硫磺有很好地杀灭细菌的功效,能抑制细菌的滋生和繁殖。通过此法制得的聚氨酯鞋底材料具有抗菌除臭的功效,且工艺简单,所用抗菌剂环保无毒。
Description
技术领域:
本发明涉及鞋材技术领域,具体地说涉及一种聚氨酯鞋底材料。
背景技术:
脚臭(脚气)是目前困扰大家的一个问题,一方面,脚臭不但会影响周围人的环境,另一方面,脚气所导致的奇痒无比也让自身不舒服。脚臭(脚气)是由于脚心汗腺多,容易出汗,汗液里除含水分、盐分外,还含有乳酸及尿素。在多汗条件下,脚上的细菌大量繁殖并分解角质蛋白,再加上汗液中的尿素、乳酸,这样就会发出一种臭味。细菌的滋生和大量繁殖导致脚气。聚氨酯鞋底由于其轻便耐磨,弹性好,防滑耐油,穿着舒适等特点,越来越受到广大消费者的欢迎。但聚氨酯鞋材透气吸湿性差,容易导致脚臭和脚气。
目前有通过添加纳米银于聚氨酯材料中用做抗菌剂,但此法比较昂贵,经济效益差。申请号为2006100053015.X的中国专利申请公开了一种在鞋底的大底和垫底之间设置一层竹炭材质的中间层,且在鞋面和内衬之间加入纳米级二氧化钛的竹炭颗粒。但随使用次数的增加,内衬与鞋面之间的竹炭颗粒会逐渐减少而导致制得的鞋子抗菌性下降。另外,还有一些通过添加有机抗菌剂来达到抗菌效果如添加有机含氮离子化合物,虽然杀菌力强,来源丰富,但是存在耐热性差、易水解等缺点,并具有一定挥发性和毒性。因此,需要开发出一种无毒,高效且持久的鞋底材料。
发明内容:
本发明的目的在于针对现有聚氨酯鞋底材料因吸湿透气性差而容易引起脚臭脚气的缺陷,提供一种能有效抗菌除臭的聚氨酯鞋底材料。
本发明是通过以下技术方案实现的。
一种抗菌除臭聚氨酯鞋底材料,以重量百分比计,包括如下组分:
作为上述技术方案的优选,所述的多元醇为聚醚多元醇、聚酯多元醇中的一种或两种。
作为上述技术方案的优选,所述的扩链剂为乙二醇、1,4-丁二醇、甘油中的一种或几种。
作为上述技术方案的优选,所述的催化剂为吗啡啉、三乙胺、三乙烯二胺中的一种或几种。
作为上述技术方案的优选,所述的发泡剂为水。
作为上述技术方案的优选,所述匀泡剂为聚二甲基硅氧烷、聚醚改性聚硅氧烷中的一种或两种。
作为上述技术方案的优选,所述的增塑剂为苯二甲酸二甲氧基乙二醇酯、苯二甲酸二丙二醇酯中的一种或两种。
本发明的有益效果在于:其使用的竹炭粉末,抗菌性沸石粉以及硫磺均是天然的抗菌剂。其中,竹炭粉末不但有抗菌的功效,亦有较好的吸湿性,通过添加在鞋底材料中,能够较好地提高材料的吸湿透气性;另外,抗菌性沸石粉和硫磺有很好地杀灭细菌的功效,能抑制细菌的滋生和繁殖。通过此法制得的聚氨酯鞋底材料具有抗菌除臭的功效,且工艺简单,所用抗菌剂环保无毒。
具体实施方式:
以下所述仅为体现本发明原理的较佳实施例,并不因此而限定本发明的保护范围。
实施例1:
将聚氧化丙烯醚多元醇经过脱水处理,具体操作方法:将聚氧化丙烯醚多元醇置于真空烘箱中于95~105℃下,烘干2~4h。
取经脱水处理的聚氧化丙烯醚多元醇:40g,丙三醇:5.4g,三乙烯二胺:0.2g,水:0.2g,聚醚改性聚硅氧烷:0.2g,苯二甲酸二甲氧基乙二醇酯:5g,搅拌均匀制得A料。
在氮气保护下,将纯MDI加热熔化,加入经脱水处理的聚氧化丙烯醚多元醇,于70~80℃下反应2~3h,真空脱除气泡,自然降温制得端基为-NCO的预聚体。预聚体中端基-NCO的重量分数为16%~25%。
取预聚体:41g,为B料。
取竹炭粉末:4g,抗菌性沸石粉:2g,硫磺:2g,混合均匀制得C料。
在45℃下,将B料加入A料中,快速搅拌均匀,再将C料加入其中混合,经浇注,熟化,脱模制得抗菌除臭聚氨酯鞋材。
实施例2:
将己二酸聚酯多元醇经过脱水处理,具体操作方法:将己二酸聚酯多元醇置于真空烘箱中于95~105℃下,烘干2~4h。
取经脱水处理的己二酸聚酯多元醇:42g,1,4-丁二醇:4.4g,三乙烯二胺:0.2g,水:0.2g,聚醚改性聚硅氧烷:0.2g,苯二甲酸二丙二醇酯:4g,搅拌均匀制得A料。
在氮气保护下,将纯MDI加热熔化,加入经脱水处理的己二酸聚酯多元醇,于70~80℃下反应2~3h,真空脱除气泡,自然降温制得端基为-NCO的预聚体。预聚体中端基-NCO的重量分数为16%~25%。
取预聚体:42g,为B料。
取竹炭粉末:3g,抗菌性沸石粉:2g,硫磺:2g,混合均匀制得C料。
在45℃下,将B料加入A料中,快速搅拌均匀,再将C料加入其中混合,经浇注,熟化,脱模制得抗菌除臭聚氨酯鞋材。
Claims (7)
2.根据权利要求1 所述的一种抗菌除臭聚氨酯鞋底材料,其特征在于:所述的多元醇为聚醚多元醇、聚酯多元醇中的一种或两种。
3.根据权利要求1 所述的一种抗菌除臭聚氨酯鞋底材料,其特征在于:所述的扩链剂为乙二醇、1,4-丁二醇、甘油中的一种或几种。
4.根据权利要求1 所述的一种抗菌除臭聚氨酯鞋底材料,其特征在于:所述的催化剂为吗啡啉、三乙胺、三乙烯二胺中的一种或几种。
5.根据权利要求1 所述的一种抗菌除臭聚氨酯鞋底材料,其特征在于:所述的发泡剂为水。
6.根据权利要求1 所述的一种抗菌除臭聚氨酯鞋底材料,其特征在于:所述匀泡剂为聚二甲基硅氧烷、聚醚改性聚硅氧烷中的一种或两种。
7.根据权利要求1 所述的一种抗菌除臭聚氨酯鞋底材料,其特征在于:所述的增塑剂为苯二甲酸二甲氧基乙二醇酯、苯二甲酸二丙二醇酯中的一种或两种。