CN103272994A - 一种耐热时间长的型砂及其制作方法 - Google Patents

一种耐热时间长的型砂及其制作方法 Download PDF

Info

Publication number
CN103272994A
CN103272994A CN2013101312383A CN201310131238A CN103272994A CN 103272994 A CN103272994 A CN 103272994A CN 2013101312383 A CN2013101312383 A CN 2013101312383A CN 201310131238 A CN201310131238 A CN 201310131238A CN 103272994 A CN103272994 A CN 103272994A
Authority
CN
China
Prior art keywords
sand
molding sand
parts
long
heat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013101312383A
Other languages
English (en)
Inventor
周道虎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FANCHANG COUNTY HENGXIN AUTO PARTS Co Ltd
Original Assignee
FANCHANG COUNTY HENGXIN AUTO PARTS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FANCHANG COUNTY HENGXIN AUTO PARTS Co Ltd filed Critical FANCHANG COUNTY HENGXIN AUTO PARTS Co Ltd
Priority to CN2013101312383A priority Critical patent/CN103272994A/zh
Publication of CN103272994A publication Critical patent/CN103272994A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐热时间长的型砂及其制作方法，其组成原料的重量份为：石英砂75-80、纳米莹石粉15-17、尿素1.2-1.4、氯化石蜡0.1-0.3、偏苯三酸三辛酯0.8-1.2、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷1.4-1.6、乙烯基三苯胺23-25、生石膏粉0.1-0.2、磷酸二氢钾粘土砖渣粉末1.8-2.2和成膜剂3.5-5.5；本发明配方合理，采用石英砂为主料，并加入纳米莹石粉，石英砂的粒度为280-320目，石英砂的粒度有助于提高型砂的强度与耐热性，固化剂乙烯基三苯胺有助于降低型砂构建的砂型的粗糙度，而且本发明不仅耐热性较好，而且粗糙度较小，透气性较好，可避免于铸件上粘砂。

Description

一种耐热时间长的型砂及其制作方法
技术领域
本发明涉及一种铸造用砂的配制方法，具体涉及一种耐热时间长的型砂及其制作方法。
背景技术
型砂在铸造生产中的作用极为重要，因型砂的质量不好而造成的铸件废品约占铸件总废品的30～50%，通常对型砂的要求有强度和热稳定性、流动性、可塑性、透气性和溃散性，即在铸件凝固后型砂是否容易破坏，是否容易从铸件上清除的性能。
目前，在型砂的制备过程中，一般由新砂、旧砂、粘结剂和辅料按一定比例混合制成。
发明内容
本发明的目的在于提供一种耐热时间长的型砂及其制作方法。
本发明采用如下技术方案：
耐热时间长的型砂，其组成原料的重量份为：石英砂75-80、纳米莹石粉15-17、尿素1.2-1.4、氯化石蜡0.1-0.3、偏苯三酸三辛酯0.8-1.2、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷1.4-1.6、乙烯基三苯胺23-25、生石膏粉0.1-0.2、磷酸二氢钾粘土砖渣粉末1.8-2.2和成膜剂3.5-5.5。
耐热时间长的型砂，其组成原料的重量份为：石英砂78、纳米莹石粉16、尿素1.3、氯化石蜡0.2、偏苯三酸三辛酯1、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷1.5、乙烯基三苯胺24、生石膏粉0.15、磷酸二氢钾粘土砖渣粉末2.0和成膜剂4.5。
耐热时间长的型砂的制作方法，包括以下步骤：
（1）首先将石英砂和纳米莹石粉粉碎至280-320目，然后在原砂加热机中将石英砂和纳米莹石粉加热至200-240℃；
（2）将步骤（1）的石英砂和纳米莹石粉倒入混砂机中搅拌均匀，自然冷却至80-100℃，然后依次加入其他组成原料并不断搅拌，控制加入原料间隔时间为3-5s，待全部原料加完后，继续自然冷却，破碎，过筛，即得型砂成品。
所述的成膜剂的制备方法如下：
配方：水20-25、3-氨丙基三甲氧基硅烷1-2、顺丁烯二酸酐  15-18、二乙二醇丁醚 5-8、硼酸1-2、丙二醇8-12、聚乙烯吡咯烷酮2-3、明矾1-2、尿素1-2、过硫酸钠0.5-1；
制备方法如下：
（1）、将水加热至80-95℃，加入3-氨丙基三甲氧基硅烷、明矾、过硫酸钠溶解，搅拌反应50-60分钟；
（2）、将步骤（1）的反应体系升温至140-145℃，加入二乙二醇丁醚、硼酸、聚乙烯吡咯烷酮，搅拌反应40-50分钟；
（3）、将步骤（2）的反应体系升温至110-125℃，加入顺丁烯二酸酐、尿素、丙二醇，搅拌反应40-50分钟；得到。
本发明的有益效果：
本发明配方合理，采用石英砂为主料，并加入纳米莹石粉，石英砂的粒度为280-320目，石英砂的粒度有助于提高型砂的强度与耐热性，固化剂乙烯基三苯胺有助于降低型砂构建的砂型的粗糙度，而且本发明不仅耐热性较好，而且粗糙度较小，透气性较好，可避免于铸件上粘砂。
具体实施方式
实施例1：耐热时间长的型砂，其组成原料的重量份（kg）为：石英砂78、纳米莹石粉16、尿素1.3、氯化石蜡0.2、偏苯三酸三辛酯1、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷1.5、乙烯基三苯胺24、生石膏粉0.15、磷酸二氢钾粘土砖渣粉末2.0和成膜剂4.5。
耐热时间长的型砂的制作方法，包括以下步骤：
（1）首先将石英砂和纳米莹石粉粉碎至280-320目，然后在原砂加热机中将石英砂和纳米莹石粉加热至230-240℃；
（2）将步骤（1）的石英砂和纳米莹石粉倒入混砂机中搅拌均匀，自然冷却至80-100℃，然后依次加入其他组成原料并不断搅拌，控制加入原料间隔时间为3-5s，待全部原料加完后，继续自然冷却，破碎，过筛，即得型砂成品。
所述的成膜剂的制备方法如下：
配方：水22、3-氨丙基三甲氧基硅烷1.5、顺丁烯二酸酐  17、二乙二醇丁醚 6.5、硼酸1.5、丙二醇10、聚乙烯吡咯烷酮2.5、明矾1、尿素1.5、过硫酸钠0.8；
制备方法如下：
（1）、将水加热至80-95℃，加入3-氨丙基三甲氧基硅烷、明矾、过硫酸钠溶解，搅拌反应50-60分钟；
（2）、将步骤（1）的反应体系升温至140-145℃，加入二乙二醇丁醚、硼酸、聚乙烯吡咯烷酮，搅拌反应40-50分钟；
（3）、将步骤（2）的反应体系降温至110-125℃，加入顺丁烯二酸酐、尿素、丙二醇，搅拌反应40-50分钟；得到。
通过上述实施例制得的型砂的性能数据：
高温抗压强度在0.87Mpa以上，发气量低于15.6ml/g以下，耐热时间200-210秒，室温抗拉强度大于3.95Mpa，热拉强度大于119Mpa，本发明不仅耐热性较好、粗糙度较小，而且透气性较好，可生产各种材质的复杂精密铸件。

Claims (4)

1.一种耐热时间长的型砂，其特征在于其组成原料的重量份为：石英砂75-80、纳米莹石粉15-17、尿素1.2-1.4、氯化石蜡0.1-0.3、偏苯三酸三辛酯0.8-1.2、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷1.4-1.6、乙烯基三苯胺23-25、生石膏粉0.1-0.2、磷酸二氢钾粘土砖渣粉末1.8-2.2和成膜剂3.5-5.5。
2.根据权利要求1所述的耐热时间长的型砂，其特征在于其组成原料的重量份为：石英砂78、纳米莹石粉16、尿素1.3、氯化石蜡0.2、偏苯三酸三辛酯1、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷1.5、乙烯基三苯胺24、生石膏粉0.15、磷酸二氢钾粘土砖渣粉末2.0和成膜剂4.5。
3.一种如权利要求1所述的耐热时间长的型砂的制作方法，其特征在于包括以下步骤：
（1）首先将石英砂和纳米莹石粉粉碎至280-320目，然后在原砂加热机中将石英砂和纳米莹石粉加热至200-240℃；
（2）将步骤（1）的石英砂和纳米莹石粉倒入混砂机中搅拌均匀，自然冷却至80-100℃，然后依次加入其他组成原料并不断搅拌，控制加入原料间隔时间为3-5s，待全部原料加完后，继续自然冷却，破碎，过筛，即得型砂成品。
4.根据权利要求1所述的耐热时间长的型砂，其特征在于：所述的成膜剂的制备方法如下：
配方：水20-25、3-氨丙基三甲氧基硅烷1-2、顺丁烯二酸酐  15-18、二乙二醇丁醚 5-8、硼酸1-2、丙二醇8-12、聚乙烯吡咯烷酮2-3、明矾1-2、尿素1-2、过硫酸钠0.5-1；
制备方法如下：
（1）、将水加热至80-95℃，加入3-氨丙基三甲氧基硅烷、明矾、过硫酸钠溶解，搅拌反应50-60分钟；
（2）、将步骤（1）的反应体系升温至140-145℃，加入二乙二醇丁醚、硼酸、聚乙烯吡咯烷酮，搅拌反应40-50分钟；
（3）、将步骤（2）的反应体系升温至110-125℃，加入顺丁烯二酸酐、尿素、丙二醇，搅拌反应40-50分钟；得到。
CN2013101312383A 2013-04-16 2013-04-16 一种耐热时间长的型砂及其制作方法 Pending CN103272994A (zh)