CN103261453B - 钢带的连续退火方法以及熔融镀锌方法 - Google Patents

钢带的连续退火方法以及熔融镀锌方法 Download PDF

Info

Publication number
CN103261453B
CN103261453B CN201180060152.5A CN201180060152A CN103261453B CN 103261453 B CN103261453 B CN 103261453B CN 201180060152 A CN201180060152 A CN 201180060152A CN 103261453 B CN103261453 B CN 103261453B
Authority
CN
China
Prior art keywords
zone
gas
furnace
soaking zone
soaking
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201180060152.5A
Other languages
English (en)
Chinese (zh)
Other versions
CN103261453A (zh
Inventor
高桥秀行
佐藤伸行
中里和树
伊理正人
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JFE Steel Corp
Original Assignee
JFE Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JFE Steel Corp filed Critical JFE Steel Corp
Publication of CN103261453A publication Critical patent/CN103261453A/zh
Application granted granted Critical
Publication of CN103261453B publication Critical patent/CN103261453B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0273—Final recrystallisation annealing
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/74—Methods of treatment in inert gas, controlled atmosphere, vacuum or pulverulent material
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/74—Methods of treatment in inert gas, controlled atmosphere, vacuum or pulverulent material
    • C21D1/76—Adjusting the composition of the atmosphere
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/0006—Details, accessories not peculiar to any of the following furnaces
    • C21D9/0012—Rolls; Roll arrangements
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/52—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for wires; for strips ; for rods of unlimited length
    • C21D9/54—Furnaces for treating strips or wire
    • C21D9/56—Continuous furnaces for strip or wire
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/52—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for wires; for strips ; for rods of unlimited length
    • C21D9/54—Furnaces for treating strips or wire
    • C21D9/56—Continuous furnaces for strip or wire
    • C21D9/561—Continuous furnaces for strip or wire with a controlled atmosphere or vacuum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/003—Apparatus
    • C23C2/0035—Means for continuously moving substrate through, into or out of the bath
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/003—Apparatus
    • C23C2/0038—Apparatus characterised by the pre-treatment chambers located immediately upstream of the bath or occurring locally before the dipping process
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0222—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating in a reactive atmosphere, e.g. oxidising or reducing atmosphere
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F27—FURNACES; KILNS; OVENS; RETORTS
    • F27B—FURNACES, KILNS, OVENS OR RETORTS IN GENERAL; OPEN SINTERING OR LIKE APPARATUS
    • F27B9/00—Furnaces through which the charge is moved mechanically, e.g. of tunnel type; Similar furnaces in which the charge moves by gravity
    • F27B9/28—Furnaces through which the charge is moved mechanically, e.g. of tunnel type; Similar furnaces in which the charge moves by gravity for treating continuous lengths of work
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F27—FURNACES; KILNS; OVENS; RETORTS
    • F27D—DETAILS OR ACCESSORIES OF FURNACES, KILNS, OVENS OR RETORTS, IN SO FAR AS THEY ARE OF KINDS OCCURRING IN MORE THAN ONE KIND OF FURNACE
    • F27D7/00—Forming, maintaining or circulating atmospheres in heating chambers
    • F27D7/06—Forming or maintaining special atmospheres or vacuum within heating chambers

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • General Engineering & Computer Science (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Strip Materials And Filament Materials (AREA)
  • Furnace Details (AREA)
  • Coating With Molten Metal (AREA)
CN201180060152.5A 2010-12-17 2011-12-13 钢带的连续退火方法以及熔融镀锌方法 Active CN103261453B (zh)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2010281406A JP5071551B2 (ja) 2010-12-17 2010-12-17 鋼帯の連続焼鈍方法、溶融亜鉛めっき方法
JP2010-281406 2010-12-17
PCT/JP2011/079277 WO2012081719A1 (ja) 2010-12-17 2011-12-13 鋼帯の連続焼鈍方法、及び、溶融亜鉛めっき方法

Publications (2)

Publication Number Publication Date
CN103261453A CN103261453A (zh) 2013-08-21
CN103261453B true CN103261453B (zh) 2014-10-22

Family

ID=46244809

Family Applications (1)

Application Number Title Priority Date Filing Date
CN201180060152.5A Active CN103261453B (zh) 2010-12-17 2011-12-13 钢带的连续退火方法以及熔融镀锌方法

Country Status (8)

Country Link
US (1) US9163305B2 (enExample)
EP (1) EP2653572B1 (enExample)
JP (1) JP5071551B2 (enExample)
KR (1) KR101340331B1 (enExample)
CN (1) CN103261453B (enExample)
BR (1) BR112013015229A2 (enExample)
MX (1) MX2013006906A (enExample)
WO (1) WO2012081719A1 (enExample)

Families Citing this family (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5505430B2 (ja) * 2012-01-17 2014-05-28 Ｊｆｅスチール株式会社 鋼帯の連続焼鈍炉及び連続焼鈍方法
CN104204240B (zh) 2012-04-06 2017-03-08 杰富意钢铁株式会社 连续式熔融镀锌设备
JP5874818B2 (ja) 2012-04-09 2016-03-02 Ｊｆｅスチール株式会社 焼鈍炉内雰囲気ガスの露点低減方法、その装置及び冷延焼鈍鋼板の製造方法
KR101564870B1 (ko) * 2012-04-09 2015-10-30 제이에프이 스틸 가부시키가이샤 어닐링로 내 분위기 가스의 노점 저감 방법, 그 장치 및 냉연 어닐링 강판의 제조 방법
JP5510495B2 (ja) 2012-05-24 2014-06-04 Ｊｆｅスチール株式会社 鋼帯の連続焼鈍炉、連続焼鈍方法、連続溶融亜鉛めっき設備及び溶融亜鉛めっき鋼帯の製造方法
JP5655955B2 (ja) 2012-06-13 2015-01-21 Ｊｆｅスチール株式会社 鋼帯の連続焼鈍方法、鋼帯の連続焼鈍装置、溶融亜鉛めっき鋼帯の製造方法及び溶融亜鉛めっき鋼帯の製造装置
JP5971155B2 (ja) * 2012-10-11 2016-08-17 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法および高強度溶融亜鉛めっき鋼板
CN104838034A (zh) * 2012-12-04 2015-08-12 杰富意钢铁株式会社 连续热浸镀锌钢板的制造设备及制造方法
EP2942407B1 (en) * 2013-01-28 2017-04-05 JFE Steel Corporation Method for adjusting in-furnace atmosphere of continuous heat-treating furnace
CN109913624B (zh) * 2013-02-06 2022-02-01 安赛乐米塔尔公司 钢板的热处理方法及用于实施该方法的设备
JP5942884B2 (ja) 2013-02-18 2016-06-29 Ｊｆｅスチール株式会社 方向性電磁鋼板の窒化処理設備および窒化処理方法
JP5565485B1 (ja) * 2013-02-25 2014-08-06 Ｊｆｅスチール株式会社 鋼帯の連続焼鈍装置および連続溶融亜鉛めっき装置
JP5884748B2 (ja) * 2013-02-25 2016-03-15 Ｊｆｅスチール株式会社 鋼帯の連続焼鈍装置および連続溶融亜鉛めっき装置
US10415115B2 (en) 2013-11-07 2019-09-17 Jfe Steel Corporation Continuous annealing system and continuous annealing method
FR3014447B1 (fr) * 2013-12-05 2016-02-05 Fives Stein Procede et installation de traitement thermique en continu d'une bande d'acier
KR101797417B1 (ko) * 2013-12-13 2017-11-13 제이에프이 스틸 가부시키가이샤 고강도 합금화 용융 아연 도금 강판의 제조 방법
JP6052270B2 (ja) * 2013-12-13 2016-12-27 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板およびその製造方法
JP6131919B2 (ja) * 2014-07-07 2017-05-24 Ｊｆｅスチール株式会社 合金化溶融亜鉛めっき鋼板の製造方法
CN104232877B (zh) * 2014-08-21 2016-08-03 马钢(集团)控股有限公司 一种带钢退火炉炉辊辊面防结瘤装置
JP6020605B2 (ja) * 2015-01-08 2016-11-02 Ｊｆｅスチール株式会社 合金化溶融亜鉛めっき鋼板の製造方法
WO2016156125A1 (en) * 2015-04-02 2016-10-06 Cockerill Maintenance & Ingénierie S.A. Method and device for reaction control
CN106884131B (zh) * 2017-01-13 2018-12-18 浙江华达新型材料股份有限公司 一种钢板二次镀锌的工艺及连续热镀锌钢带退火炉
JP6832200B2 (ja) * 2017-03-10 2021-02-24 日本製鉄株式会社 水蒸気処理用の密閉容器
MX2020006497A (es) * 2017-12-22 2020-09-17 Jfe Steel Corp Metodo para la produccion de lamina de acero galvanizada por inmersion en caliente y aparato de galvanizacion por inmersion en caliente continua.
CN109988893A (zh) * 2019-04-26 2019-07-09 宝钢湛江钢铁有限公司 一种减少纳米氧化物生成的连退工艺

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2567130B2 (ja) * 1990-05-07 1996-12-25 日本冶金工業株式会社 光輝焼鈍炉
JP2567140B2 (ja) * 1990-09-04 1996-12-25 日本冶金工業株式会社 光輝焼鈍炉
JP2005171294A (ja) * 2003-12-09 2005-06-30 Nippon Steel Corp 連続焼鈍炉雰囲気ガスの露点調節方法及び連続焼鈍炉

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2820359B2 (ja) * 1993-11-16 1998-11-05 川崎製鉄株式会社 連続焼鈍炉の炉内雰囲気調整方法
JPH08109417A (ja) * 1994-10-12 1996-04-30 Nippon Steel Corp 連続焼鈍炉の雰囲気ガス置換法
JPH09324210A (ja) * 1996-06-07 1997-12-16 Kawasaki Steel Corp 溶融亜鉛めっき鋼板の製造方法および製造設備
JP3509405B2 (ja) * 1996-07-30 2004-03-22 Ｊｆｅスチール株式会社 鋼帯の連続熱処理炉における炉内雰囲気改善方法
JPH10176225A (ja) * 1996-12-13 1998-06-30 Daido Steel Co Ltd 金属ストリップの連続焼鈍炉
FR2782326B1 (fr) * 1998-08-13 2000-09-15 Air Liquide Procede de galvanisation d'une bande metallique
JP2002206117A (ja) 2000-10-26 2002-07-26 Nkk Corp 連続焼鈍処理装置および連続焼鈍処理方法
US20070259203A1 (en) * 2003-11-26 2007-11-08 Bluescope Steel Limited Coated Steel Strip
KR101011897B1 (ko) 2005-10-14 2011-02-01 신닛뽄세이테쯔 카부시키카이샤 Ｓｉ를 함유하는 강판의 연속 어닐링 용융 도금 방법 및연속 어닐링 용융 도금 장치

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2567130B2 (ja) * 1990-05-07 1996-12-25 日本冶金工業株式会社 光輝焼鈍炉
JP2567140B2 (ja) * 1990-09-04 1996-12-25 日本冶金工業株式会社 光輝焼鈍炉
JP2005171294A (ja) * 2003-12-09 2005-06-30 Nippon Steel Corp 連続焼鈍炉雰囲気ガスの露点調節方法及び連続焼鈍炉

Non-Patent Citations (6)

* Cited by examiner, † Cited by third party
Title
JP特开2005-171294A 2005.06.30
JP特开平10-46237A 1998.02.17
JP特开平7-138652A 1995.05.30
JP特开平8-109417A 1996.04.30
JP特许2567130B2 1996.12.25
JP特许2567140B2 1996.12.25

Also Published As

Publication number Publication date
WO2012081719A1 (ja) 2012-06-21
JP2012126983A (ja) 2012-07-05
EP2653572A1 (en) 2013-10-23
KR20130109192A (ko) 2013-10-07
MX2013006906A (es) 2013-07-15
BR112013015229A2 (pt) 2016-09-13
KR101340331B1 (ko) 2013-12-11
EP2653572B1 (en) 2016-08-10
CN103261453A (zh) 2013-08-21
EP2653572A4 (en) 2014-10-22
US20130273251A1 (en) 2013-10-17
US9163305B2 (en) 2015-10-20
JP5071551B2 (ja) 2012-11-14

Similar Documents

Publication Publication Date Title
CN103261453B (zh) 钢带的连续退火方法以及熔融镀锌方法
CN104053796B (zh) 钢带的连续退火炉及连续退火方法
JP6455544B2 (ja) 溶融亜鉛めっき鋼板の製造方法
CN104321447B (zh) 钢带的连续退火炉、连续退火方法、连续热浸镀锌设备以及热浸镀锌钢带的制造方法
CN104379776B (zh) 钢带的连续退火方法、钢带的连续退火装置、熔融镀锌钢带的制造方法以及熔融镀锌钢带的制造装置
CN105074021B (zh) 连续熔融镀锌装置
JP6607339B1 (ja) 溶融亜鉛めっき鋼板の製造方法及び連続溶融亜鉛めっき装置
CN104334753A (zh) 钢带的连续退火炉、钢带的连续退火方法、连续熔融镀锌设备以及熔融镀锌钢带的制造方法
WO2016006159A1 (ja) 合金化溶融亜鉛めっき鋼板の製造方法
CN104379777B (zh) 钢带的连续退火方法及热镀锌钢带的制造方法

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant