CN103254788A - 一种抗紫外线防锈油及其制备方法 - Google Patents

一种抗紫外线防锈油及其制备方法 Download PDF

Info

Publication number
CN103254788A
CN103254788A CN2013101316933A CN201310131693A CN103254788A CN 103254788 A CN103254788 A CN 103254788A CN 2013101316933 A CN2013101316933 A CN 2013101316933A CN 201310131693 A CN201310131693 A CN 201310131693A CN 103254788 A CN103254788 A CN 103254788A
Authority
CN
China
Prior art keywords
uvioresistant
oil
forming agent
preparation
constitutive material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013101316933A
Other languages
English (en)
Inventor
芮明功
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MAANSHAN TUORUI METAL SURFACE TECHNOLOGY Co Ltd
Original Assignee
MAANSHAN TUORUI METAL SURFACE TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MAANSHAN TUORUI METAL SURFACE TECHNOLOGY Co Ltd filed Critical MAANSHAN TUORUI METAL SURFACE TECHNOLOGY Co Ltd
Priority to CN2013101316933A priority Critical patent/CN103254788A/zh
Publication of CN103254788A publication Critical patent/CN103254788A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种抗紫外线防锈油及其制备方法，其组成原料为：46#机械油、苯并三唑、成膜剂、氨丙基三乙氧基硅烷、2,6-二叔丁基-4-甲基苯酚、硬酯酸单甘油酯、纳米陶瓷粉体、乙酸乙酯、聚二甲基硅氧烷、紫外线吸收剂UV-327和邻苯二甲酸二丁酯；本发明制备的防锈油在金属表面附着力好、干燥快、抗紫外线性能好，环保无污染，采用46#机械油为主料，并添加了成膜剂，成膜速度快，防锈油表面不易氧化，不易影响工件的外观，综合性能好，而且本发明制备方法简单，成本低，适合大规模生产。

Description

一种抗紫外线防锈油及其制备方法
技术领域
本发明涉及一种防锈材料，具体涉及一种抗紫外线防锈油及其制备方法。
背景技术
    金属腐蚀是使紧固件破坏的主要形式之一，对汽车、摩托车以及各种车辆、机械会造成很大的损失，据统计，每年由于金属腐蚀所造成的直接经济损失约占国民经济总产值的2-4%，为避免锈蚀、减少损失，人们采用了各种各样的方法，用防锈油脂来保护金属紧固件，便是目前最常见的防护方法之一。
发明内容
本发明的目的在于提供一种抗紫外线防锈油及其制备方法。
本发明采用如下技术方案：
抗紫外线防锈油，其组成原料的重量份为：46#机械油65-70、苯并三唑3.5-5.5、成膜剂3.0-5.0、氨丙基三乙氧基硅烷2.0-4.0、2,6-二叔丁基-4-甲基苯酚1.3-1.5、硬酯酸单甘油酯0.2-0.4、纳米陶瓷粉体2.5-3.5、乙酸乙酯5.5-6.5、聚二甲基硅氧烷2.0-3.5、紫外线吸收剂UV-32713-15和邻苯二甲酸二丁酯8.0-10.0。
抗紫外线防锈油，其组成原料的重量份为：46#机械油68、苯并三唑4.5、成膜剂4.0、氨丙基三乙氧基硅烷3.0、2,6-二叔丁基-4-甲基苯酚1.4、硬酯酸单甘油酯0.3、纳米陶瓷粉体3.0、乙酸乙酯6.0、聚二甲基硅氧烷2.8、紫外线吸收剂UV-32714和邻苯二甲酸二丁酯9.0。
抗紫外线防锈油的制备方法，包括以下步骤：
（1）按组成原料的重量份量取46#机械油，加入反应釜中加热搅拌，至140-160℃时加入紫外线吸收剂UV-327，反应10-20min；
（2）在步骤（1）中加入成膜剂、2,6-二叔丁基-4-甲基苯酚和乙酸乙酯，继续搅拌，冷却至35-45℃；
（3）在步骤（2）中按组成原料的重量份加入其它组成原料，继续搅拌2-4h过滤后，即得成品。
所述的成膜剂的制备方法如下：
（1）首先将18-22份邻苯二甲酸二丁酯、3.5-4.5 份二甲苯、2.0-3.0份乙二醇二缩水甘油醚、8-12份E-12环氧树脂混合加入反应釜中，在70-110℃温度下反应2-3小时；
（2）在步骤（1）的反应釜中加入15-18份顺丁烯二酸酐、1.3-1.5份苯乙烯、1-2份乙烯基三甲氧基硅烷、1.5-1.8份交联剂 TAIC，搅拌混合，在50-80℃温度条件下反应3-5小时，即得。
本发明的有益效果：
本发明制备的防锈油在金属表面附着力好、干燥快、抗紫外线性能好，环保无污染，采用46#机械油为主料，并添加了成膜剂，成膜速度快，防锈油表面不易氧化，不易影响工件的外观，综合性能好，而且本发明制备方法简单，成本低，适合大规模生产。
具体实施方式
实施例1：抗紫外线防锈油，其组成原料的重量份（kg）为：46#机械油68、苯并三唑4.5、成膜剂4.0、氨丙基三乙氧基硅烷3.0、2,6-二叔丁基-4-甲基苯酚1.4、硬酯酸单甘油酯0.3、纳米陶瓷粉体3.0、乙酸乙酯6.0、聚二甲基硅氧烷2.8、紫外线吸收剂UV-32714和邻苯二甲酸二丁酯9.0。
抗紫外线防锈油的制备方法，包括以下步骤：
（1）按组成原料的重量份量取46#机械油，加入反应釜中加热搅拌，至150℃时加入紫外线吸收剂UV-327，反应15min；
（2）在步骤（1）中加入成膜剂、2,6-二叔丁基-4-甲基苯酚和乙酸乙酯，继续搅拌，冷却至40℃；
（3）在步骤（2）中按组成原料的重量份加入其它组成原料，继续搅拌3h过滤后，即得成品。
所述的成膜剂的制备方法如下：
（1）首先将20份邻苯二甲酸二丁酯、4.0份二甲苯、2.5份乙二醇二缩水甘油醚、10份E-12环氧树脂混合加入反应釜中，在90℃温度下反应2.5小时；
（2）在步骤（1）的反应釜中加入17份顺丁烯二酸酐、1.4份苯乙烯、1.5份乙烯基三甲氧基硅烷、1.6份交联剂 TAIC，搅拌混合，在65℃温度条件下反应4小时，即得。
上述实施例1制备的防锈油的综合性能如下：
1、附着力/级≤1级；2、中性盐雾腐蚀试验（h）≥95；3、湿热试验（h）＞980；4、油膜干燥时间（min）19-21；5、涂膜厚度（μm）＜3；6、紫外线老化试验（h）＞450。

Claims (4)

1.一种抗紫外线防锈油，其特征在于其组成原料的重量份为：46#机械油65-70、苯并三唑3.5-5.5、成膜剂3.0-5.0、氨丙基三乙氧基硅烷2.0-4.0、2,6-二叔丁基-4-甲基苯酚1.3-1.5、硬酯酸单甘油酯0.2-0.4、纳米陶瓷粉体2.5-3.5、乙酸乙酯5.5-6.5、聚二甲基硅氧烷2.0-3.5、紫外线吸收剂UV-327 13-15和邻苯二甲酸二丁酯8.0-10.0。
2.根据权利要求1所述的抗紫外线防锈油，其特征在于其组成原料的重量份为：46#机械油68、苯并三唑4.5、成膜剂4.0、氨丙基三乙氧基硅烷3.0、2,6-二叔丁基-4-甲基苯酚1.4、硬酯酸单甘油酯0.3、纳米陶瓷粉体3.0、乙酸乙酯6.0、聚二甲基硅氧烷2.8、紫外线吸收剂UV-32714和邻苯二甲酸二丁酯9.0。
3.一种如权利要求1所述的抗紫外线防锈油的制备方法，其特征在于包括以下步骤：
（1）按组成原料的重量份量取46#机械油，加入反应釜中加热搅拌，至140-160℃时加入紫外线吸收剂UV-327，反应10-20min；
（2）在步骤（1）中加入成膜剂、2,6-二叔丁基-4-甲基苯酚和乙酸乙酯，继续搅拌，冷却至35-45℃；
（3）在步骤（2）中按组成原料的重量份加入其它组成原料，继续搅拌2-4h过滤后，即得成品。
4.根据权利要求1所述的抗紫外线防锈油，其特征在于：所述的成膜剂的制备方法如下：
（1）首先将18-22份邻苯二甲酸二丁酯、3.5-4.5 份二甲苯、2.0-3.0份乙二醇二缩水甘油醚、8-12份E-12环氧树脂混合加入反应釜中，在70-110℃温度下反应2-3小时；
（2）在步骤（1）的反应釜中加入15-18份顺丁烯二酸酐、1.3-1.5份苯乙烯、1-2份乙烯基三甲氧基硅烷、1.5-1.8份交联剂 TAIC，搅拌混合，在50-80℃温度条件下反应3-5小时，即得。
CN2013101316933A 2013-04-17 2013-04-17 一种抗紫外线防锈油及其制备方法 Pending CN103254788A (zh)