CN102977731A - 汽车铸铁发动机工件用速干型喷淋防锈油及制备方法 - Google Patents
汽车铸铁发动机工件用速干型喷淋防锈油及制备方法 Download PDFInfo
- Publication number
- CN102977731A CN102977731A CN201210518011XA CN201210518011A CN102977731A CN 102977731 A CN102977731 A CN 102977731A CN 201210518011X A CN201210518011X A CN 201210518011XA CN 201210518011 A CN201210518011 A CN 201210518011A CN 102977731 A CN102977731 A CN 102977731A
- Authority
- CN
- China
- Prior art keywords
- cast iron
- preparation
- dimethylbenzene
- stirred
- iron engine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种汽车铸铁发动机工件用速干型喷淋防锈油,由如下质量百分比的组分构成:二壬基萘磺酸钡1~5%、叔丁酚甲醛树脂1~8%、环烷酸锌1~4%、工业蓖麻油1~2%、邻苯二甲酸二丁酯0.1~1.0%、二甲苯1~10%、航空煤油1~10%、120#溶剂汽油余量。制备方法是先将二甲苯和航空煤油装入不锈钢容器内,然后再加入二壬基萘磺酸钡和叔丁酚甲醛树脂,搅拌至全部溶解,备用;将120#溶剂汽油加入到反应釜中,再将所得备用料徐徐加入到反应釜中充分搅拌至均匀溶解;然后把环烷酸锌、工业蓖麻油、邻苯二甲酸二丁酯依次徐徐加入到反应釜中,搅拌至溶液呈棕色透明均匀液体。
Description
技术领域
本发明涉及一种防锈油及制备方法,尤其是一种成膜速度快,可延长汽车铸铁发动机工件封存防锈期的汽车铸铁发动机工件用速干型喷淋防锈油及制备方法。
背景技术
汽车发动机工件的材质为铸铁,在空气中极易氧化生锈。因此,发动机工件加工后,其表面必需喷涂防锈油。但是,目前发动机并没有专用封存防锈油,在工件表面成膜速度慢,导致防锈期短,影响发动机的使用寿命。
发明内容
本发明是为了解决现有技术所存在的上述技术问题,提供一种成膜速度快,可延长汽车铸铁发动机工件封存防锈期的汽车铸铁发动机工件用速干型喷淋防锈油及制备方法。
本发明的技术解决方案是:一种汽车铸铁发动机工件用速干型喷淋防锈油,其特征在于由如下质量百分比的组分构成:二壬基萘磺酸钡1~5%、叔丁酚甲醛树脂1~8%、环烷酸锌1~4%、工业蓖麻油1~2%、邻苯二甲酸二丁酯0.1~1.0%、二甲苯1~10%、航空煤油1~10%、120#溶剂汽油余量。
一种上述的汽车铸铁发动机工件用速干型喷淋防锈油的制备方法,其特征在于依次按如下步骤进行:
a. 先将计算称量的二甲苯和航空煤油装入不锈钢容器内,然后再加入计算称量的二壬基萘磺酸钡和叔丁酚甲醛树脂,搅拌至全部溶解,备用;
b. 将计算称量的120#溶剂汽油加入到反应釜中,启动搅拌器,控制转速30转/分,再将a步骤所得备用料徐徐加入到反应釜中充分搅拌至均匀溶解;然后把计算称量的环烷酸锌、工业蓖麻油、邻苯二甲酸二丁酯依次徐徐加入到反应釜中,每加入一种原料均需搅拌至充分溶解,最后搅拌至溶液呈棕色透明均匀液体。
本发明是针对铸铁发动机工件而设计,成膜速度快,喷淋后三分钟内即可在工件表面干透成膜,防锈期达到两年以上,继而延长了发动机的使用寿命。
具体实施方式
实施例1:
原料组分及重量百分比如下:二壬基萘磺酸钡1%、叔丁酚甲醛树脂8%、环烷酸锌1%、工业蓖麻油2%、邻苯二甲酸二丁酯0.1%、二甲苯10%、航空煤油1%、120#溶剂汽油余量。
制备方法依次按如下步骤进行:
a. 先将计算称量的二甲苯和航空煤油装入不锈钢容器内,然后再加入计算称量的二壬基萘磺酸钡和叔丁酚甲醛树脂,搅拌至全部溶解,备用;
b. 将计算称量的120#溶剂汽油加入到反应釜中,启动搅拌器,控制转速30转/分,再将a步骤所得备用料徐徐加入到反应釜中充分搅拌至均匀溶解;然后把计算称量的环烷酸锌、工业蓖麻油、邻苯二甲酸二丁酯依次徐徐加入到反应釜中,每加入一种原料均需搅拌至充分溶解,最后搅拌至溶液呈棕色透明均匀液体。
实施例2:
原料及生产方法均同实施例1,其原料质量百分比如下:二壬基萘磺酸钡5%、叔丁酚甲醛树脂1%、环烷酸锌4%、工业蓖麻油1%、邻苯二甲酸二丁酯1.0%、二甲苯1%、航空煤油10%、120#溶剂汽油余量。
实施例3:
原料及生产方法均同实施例1,其原料质量百分比如下:二壬基萘磺酸钡3%、叔丁酚甲醛树脂5%、环烷酸锌2%、工业蓖麻油1.5%、邻苯二甲酸二丁酯0.5%、二甲苯5%、航空煤油5%、120#溶剂汽油余量。
使用时,用本发明实施例1、2或3原液常温喷淋,喷淋压力0.08~0.12MPa,喷淋时间90s,再经90s冷风(压缩空气)吹干即可。
Claims (2)
1. 一种汽车铸铁发动机工件用速干型喷淋防锈油,其特征在于由如下质量百分比的组分构成:二壬基萘磺酸钡1~5%、叔丁酚甲醛树脂1~8%、环烷酸锌1~4%、工业蓖麻油1~2%、邻苯二甲酸二丁酯0.1~1.0%、二甲苯1~10%、航空煤油1~10%、120#溶剂汽油余量。
2.一种如权利要求1所述的汽车铸铁发动机工件用速干型喷淋防锈油的制备方法,其特征在于依次按如下步骤进行:
a. 先将计算称量的二甲苯和航空煤油装入不锈钢容器内,然后再加入计算称量的二壬基萘磺酸钡和叔丁酚甲醛树脂,搅拌至全部溶解,备用;
b. 将计算称量的120#溶剂汽油加入到反应釜中,启动搅拌器,控制转速30转/分,再将a步骤所得备用料徐徐加入到反应釜中充分搅拌至均匀溶解;然后把计算称量的环烷酸锌、工业蓖麻油、邻苯二甲酸二丁酯依次徐徐加入到反应釜中,每加入一种原料均需搅拌至充分溶解,最后搅拌至溶液呈棕色透明均匀液体。