CN103450615A - 一种高弹性的塑胶材料及其制备方法 - Google Patents

一种高弹性的塑胶材料及其制备方法 Download PDF

Info

Publication number
CN103450615A
CN103450615A CN2013103694575A CN201310369457A CN103450615A CN 103450615 A CN103450615 A CN 103450615A CN 2013103694575 A CN2013103694575 A CN 2013103694575A CN 201310369457 A CN201310369457 A CN 201310369457A CN 103450615 A CN103450615 A CN 103450615A
Authority
CN
China
Prior art keywords
parts
plastic material
maleic anhydride
banburying
elasticity
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013103694575A
Other languages
English (en)
Other versions
CN103450615B (zh
Inventor
倪迪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenzhen Jinji Digital Technology Co ltd
Original Assignee
WUJIANG YINGLIDA PLASTIC PACKAGING CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUJIANG YINGLIDA PLASTIC PACKAGING CO Ltd filed Critical WUJIANG YINGLIDA PLASTIC PACKAGING CO Ltd
Priority to CN201310369457.5A priority Critical patent/CN103450615B/zh
Publication of CN103450615A publication Critical patent/CN103450615A/zh
Application granted granted Critical
Publication of CN103450615B publication Critical patent/CN103450615B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高弹性的塑胶材料及其制备方法，该高弹性的塑胶材料包括以下重量份计的原料：顺丁烯二酸酐-苯乙烯共聚物20-30份、环烷酸钴10-20份、2-羟基-4-辛氧基二苯甲酮20-30份、月桂酸酰胺10-20份、偏苯三酸三辛酯10-25份、高氯酸钠7-13份、聚二甲基硅氧烷23-25份、硅烷偶联剂10-16份、环氧大豆油8-15份、马来酸酐10-20份，将上述组分经过两次密炼，造粒、放入模具成型。本发明的塑胶材料回弹性接近50%，压缩变形在28%左右，热收缩率为0.8-0.9%，本发明的弹性好，抗缓冲优异，具有持久舒适和持久的抗缓冲性能。

Description

一种高弹性的塑胶材料及其制备方法
技术领域
     本发明涉及塑胶领域，尤其涉及一种高弹性的塑胶材料及其制备方法。
背景技术
    目前，鞋底的构造相当复杂，就广义而言，可包括外底、中底与鞋跟等所有构成底部的材料。依狭义来说，则仅指外底而言，一般鞋底材料共通的特性应具备耐磨、耐水，耐油、耐热、耐压、耐冲击、弹性好、容易适合脚型、定型后不易变型、保温、易吸收湿气等，同时更要配合中底，在走路换脚时有刹车作用不致于滑倒及易于停步等各项条件。鞋底用料的种类很多，可分为天然类底料和合成类底料两种。天然类底料包括天然底革、竹、木材等，合成类底料包括橡胶、塑料、橡塑合用材料、再生革、弹性硬纸板等。鞋底如果过硬不仅穿着不舒适，而且对人体健康有一定的影响。
发明内容
针对现有技术的不足，本发明提供了一种弹性好、抗缓冲性能优异的高弹性的塑胶材料及其制备方法。
本发明采用以下技术方案：
一种高弹性的塑胶材料，包括以下重量份计的原料：顺丁烯二酸酐-苯乙烯共聚物20-30份、环烷酸钴10-20份、2-羟基-4-辛氧基二苯甲酮20-30份、月桂酸酰胺10-20份、偏苯三酸三辛酯10-25份、高氯酸钠7-13份、聚二甲基硅氧烷23-25份、硅烷偶联剂10-16份、环氧大豆油8-15份、马来酸酐10-20份。
    一种高弹性的塑胶材料制备方法，包括以下步骤：将顺丁烯二酸酐-苯乙烯共聚物、环烷酸钴、2-羟基-4-辛氧基二苯甲酮、月桂酸酰胺、偏苯三酸三辛酯、高氯酸钠混合，放入密炼机中密炼，100-110℃密炼7-8min；加入聚二甲基硅氧烷、硅烷偶联剂、环氧大豆油、马来酸酐，再次密炼，110-120℃密炼1-2min；造粒、放入模具成型。
本发明的高弹性的塑胶材料回弹性接近50%，压缩变形在28%左右，热收缩率为0.8-0.9%，本发明的弹性好，抗缓冲优异，具有持久舒适和持久的抗缓冲性能。
具体实施方式
下面通过具体实施例对本发明作进一步详细介绍。
实施例1
一种高弹性的塑胶材料，包括以下重量份计的原料：顺丁烯二酸酐-苯乙烯共聚物20份、环烷酸钴10份、2-羟基-4-辛氧基二苯甲酮20份、月桂酸酰胺10份、偏苯三酸三辛酯10份、高氯酸钠7份、聚二甲基硅氧烷23份、硅烷偶联剂10份、环氧大豆油8份、马来酸酐10份。
    高弹性的塑胶材料制备方法，包括以下步骤：将顺丁烯二酸酐-苯乙烯共聚物、环烷酸钴、2-羟基-4-辛氧基二苯甲酮、月桂酸酰胺、偏苯三酸三辛酯、高氯酸钠混合，放入密炼机中密炼，100℃密炼7min；加入聚二甲基硅氧烷、硅烷偶联剂、环氧大豆油、马来酸酐，再次密炼，110℃密炼1min；造粒、放入模具成型。
实施例2
一种高弹性的塑胶材料，包括以下重量份计的原料：顺丁烯二酸酐-苯乙烯共聚物30份、环烷酸钴20份、2-羟基-4-辛氧基二苯甲酮30份、月桂酸酰胺20份、偏苯三酸三辛酯25份、高氯酸钠13份、聚二甲基硅氧烷25份、硅烷偶联剂16份、环氧大豆油15份、马来酸酐20份。
    高弹性的塑胶材料制备方法，包括以下步骤：将顺丁烯二酸酐-苯乙烯共聚物、环烷酸钴、2-羟基-4-辛氧基二苯甲酮、月桂酸酰胺、偏苯三酸三辛酯、高氯酸钠混合，放入密炼机中密炼，110℃密炼8min；加入聚二甲基硅氧烷、硅烷偶联剂、环氧大豆油、马来酸酐，再次密炼，120℃密炼2min；造粒、放入模具成型。
实施例3
一种高弹性的塑胶材料，包括以下重量份计的原料：顺丁烯二酸酐-苯乙烯共聚物25份、环烷酸钴15份、2-羟基-4-辛氧基二苯甲酮25份、月桂酸酰胺15份、偏苯三酸三辛酯20份、高氯酸钠11份、聚二甲基硅氧烷24份、硅烷偶联剂13份、环氧大豆油10份、马来酸酐15份。
    高弹性的塑胶材料制备方法，包括以下步骤：将顺丁烯二酸酐-苯乙烯共聚物、环烷酸钴、2-羟基-4-辛氧基二苯甲酮、月桂酸酰胺、偏苯三酸三辛酯、高氯酸钠混合，放入密炼机中密炼，105℃密炼7.5min；加入聚二甲基硅氧烷、硅烷偶联剂、环氧大豆油、马来酸酐，再次密炼，115℃密炼1.5min；造粒、放入模具成型。
下面通过试验测试本发明的性能：
检测项目 实施例1 实施例2 实施例3
回弹性% 48 49 50
热收缩% 0.9 0.8 0.8
压缩变形% 28 27 28
断裂伸长率% 289 296 290
本发明的高弹性的塑胶材料回弹性接近50%，压缩变形在28%左右，热收缩率为0.8-0.9%，本发明的弹性好，抗缓冲优异，具有持久舒适和持久的抗缓冲性能。
另外，本发明不限于上述实施方式，只要在不超出本发明的范围内，可以采取各种方式实施本发明。

Claims (2)

1.一种高弹性的塑胶材料，其特征在于包括以下重量份计的原料：顺丁烯二酸酐-苯乙烯共聚物20-30份、环烷酸钴10-20份、2-羟基-4-辛氧基二苯甲酮20-30份、月桂酸酰胺10-20份、偏苯三酸三辛酯10-25份、高氯酸钠7-13份、聚二甲基硅氧烷23-25份、硅烷偶联剂10-16份、环氧大豆油8-15份、马来酸酐10-20份。
2.权利要求1所述的高弹性的塑胶材料的制备方法，其特征在于包括以下步骤：将顺丁烯二酸酐-苯乙烯共聚物、环烷酸钴、2-羟基-4-辛氧基二苯甲酮、月桂酸酰胺、偏苯三酸三辛酯、高氯酸钠混合，放入密炼机中密炼，100-110℃密炼7-8min；加入聚二甲基硅氧烷、硅烷偶联剂、环氧大豆油、马来酸酐，再次密炼，110-120℃密炼1-2min；造粒、放入模具成型。
CN201310369457.5A 2013-08-22 2013-08-22 一种高弹性的塑胶材料及其制备方法 Active CN103450615B (zh)