CN103242584B - 一种耐磨eva鞋底料 - Google Patents
一种耐磨eva鞋底料 Download PDFInfo
- Publication number
- CN103242584B CN103242584B CN201310155881.XA CN201310155881A CN103242584B CN 103242584 B CN103242584 B CN 103242584B CN 201310155881 A CN201310155881 A CN 201310155881A CN 103242584 B CN103242584 B CN 103242584B
- Authority
- CN
- China
- Prior art keywords
- bed material
- shoes bed
- vinyl acetate
- material according
- antiwear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种耐磨EVA鞋底料，该耐磨料的配方包括以下几种原料及重量分数：乙烯—醋酸乙烯酯共聚物65%~85%，耐磨剂5%~10%，光稳定剂0.5%~5%，粒径≤200nm的无机填料5%~20%，发泡剂1%~3%，交联剂0.5%~2%，分散润滑剂1%~3%。与现有技术相比，本发明通过选取一种分子量适当的超高分子量有机硅耐磨剂从而制备出具有优异耐磨性能EVA鞋底料。<!--1-->
Description
技术领域
本发明涉及聚合物复合材料技术领域，尤其涉及一种耐磨EVA鞋底料组合物。
背景技术
乙烯-醋酸乙烯共聚物(EVA)具有很好的可塑性、弹性和可加工性，并且发泡后的材料具有密度小、力学性能好、易着色等优点，被广泛应用于鞋底材料，但EVA材料具有耐磨性能不如橡胶鞋材的缺点，因而也限制了其部分的应用。
发明内容
本发明的目的是提供一种耐磨性能优异的EVA鞋底料。
本发明的目的可以通过以下技术方案来实现：一种耐磨EVA鞋底料，由以下质量分数组分组成：
乙烯—醋酸乙烯酯共聚物65%~85%，耐磨剂5%~10%，光稳定剂0.5%~5%，粒径≤200nm的无机填料5%~20%，发泡剂1%~3%，交联剂0.5%~2%，分散润滑剂1%~3%。
所述的耐磨EVA鞋底料，其特征在于所述的乙烯—醋酸乙烯酯共聚物，其中醋酸乙烯酯的质量百分比含量为15%~28%。
所述的耐磨EVA鞋底料，其特征在于所述的耐磨剂是由乙烯—醋酸乙烯酯共聚物和超高分子量有机硅聚合物组成；各组分质量百分比为：乙烯—醋酸乙烯酯共聚物50~60%，超高分子量有机硅聚合物40~50%，所述的乙烯—醋酸乙烯酯共聚物中醋酸乙烯酯的质量百分比含量为15%~28%。
所述的耐磨EVA鞋底料，其特征在于其特征在于所述的超高分子量有机硅聚合物分子量在80万至100万之间。
所述的耐磨EVA鞋底料，其特征在于所述的光稳定剂为氧化锌。
所述的耐磨EVA鞋底料，其特征在于所述的粒径≤200nm的无机填料为滑石粉、碳酸钙、白炭黑中的一种或两种以上混合而成。
所述的耐磨EVA鞋底料，其特征在于所述的发泡剂为偶氮二甲酰胺AC发泡剂。
所述的耐磨EVA鞋底料，其特征在于所述的交联剂为过氧化二异丙苯DCP。
所述的耐磨EVA鞋底料，其特征在于所述的分散润滑剂为硬脂酸、硬脂酸锌、硬脂酸钙、硬脂酸镁、低分子蜡中的一种或两种以上混合而成。
与现有技术相比，本发明由于采用以上技术方案，EVA鞋底料耐磨性能更优，材料体系的均匀度及表面光洁性更好。
具体实施方式
下面结合实施例对本发明做进一步说明。
表1 耐磨EVA鞋底料配方
| 原料 | 实施例1 | 实施例2 | 实施例3 |
| EVA | 76 | 80 | 80 |
| 耐磨剂 | 8 | 8 | 6 |
| 氧化锌 | 2 | 2 | 2 |
| 粒径≤200nm的无机填料 | 8 | 6 | 7 |
| AC发泡剂 | 2.5 | 2 | 2 |
| DCP | 1.5 | 1 | 1 |
| 分散润滑剂 | 2 | 1 | 2 |
其中，
实施例1：EVA采用台塑7470，耐磨剂采用含100万分子量有机硅聚合物50%的耐磨剂，无机填料采用粒径小于200nm的白炭黑，分散润滑剂采用硬脂酸。
实施例2：EVA采用台塑7350，耐磨剂采用含80万分子量有机硅聚合物50%的耐磨剂，无机填料采用粒径小于200nm的滑石粉，分散润滑剂采用硬脂酸锌。
实施例3：EVA采用50%质量份数台塑7470和50%质量份数台塑7350，耐磨剂采用含80万分子量有机硅聚合物50%的耐磨剂，无机填料采用粒径小于200nm的滑石粉，分散润滑剂采用硬脂酸锌。
各实施例制备得到的耐磨料的性能列于表2中。
表2 三种实施例耐磨料的性能
| 性能 | 单位 | 实施例1 | 实施例2 | 实施例3 |
| 密度 | g/cm3 | 0.215 | 0.202 | 0.208 |
| 拉伸强度 | MPa | 3.8 | 3.6 | 3.5 |
| 断裂伸长率 | % | 269 | 323 | 308 |
| 硬度 | Shore D | 61 | 59 | 58 |
| DIN耐磨 | mm3 | 122 | 123 | 125 |
| 磨痕 | mm | 8.1 | 7.2 | 7.7 |
Claims (8)
1.一种耐磨EVA鞋底料，其特征在于，以质量百分比计，由以下组分组成：
其中，耐磨剂是由乙烯—醋酸乙烯酯共聚物和超高分子量有机硅聚合物组成，各组分质量百分比为：乙烯—醋酸乙烯酯共聚物50～60％，超高分子量有机硅聚合物40～50％，所述的乙烯—醋酸乙烯酯共聚物中醋酸乙烯酯的质量百分比含量为15％～28％。
2.根据权利要求1所述的耐磨EVA鞋底料，其特征在于所述的乙烯—醋酸乙烯酯共聚物，其中醋酸乙烯酯的质量百分比含量为15％～28％。
3.根据权利要求1所述的耐磨EVA鞋底料，其特征在于其特征在于所述的超高分子量有机硅聚合物分子量在80万至100万之间。
4.根据权利要求1所述的耐磨EVA鞋底料，其特征在于所述的光稳定剂为氧化锌。
5.根据权利要求1所述的耐磨EVA鞋底料，其特征在于所述的粒径≤200nm的无机填料为滑石粉、碳酸钙、白炭黑中的一种或两种以上混合而成。
6.根据权利要求1所述的耐磨EVA鞋底料，其特征在于所述的发泡剂为偶氮二甲酰胺AC发泡剂。
7.根据权利要求1所述的耐磨EVA鞋底料，其特征在于所述的交联剂为过氧化二异丙苯DCP。
8.根据权利要求1所述的耐磨EVA鞋底料，其特征在于所述的分散润滑剂为硬脂酸、硬脂酸锌、硬脂酸钙、硬脂酸镁、低分子蜡中的一种或两种以上混合而成。