CN103224354A - 一种新型瓷砖粘结剂及其制备方法 - Google Patents
一种新型瓷砖粘结剂及其制备方法 Download PDFInfo
- Publication number
- CN103224354A CN103224354A CN 201310185799 CN201310185799A CN103224354A CN 103224354 A CN103224354 A CN 103224354A CN 201310185799 CN201310185799 CN 201310185799 CN 201310185799 A CN201310185799 A CN 201310185799A CN 103224354 A CN103224354 A CN 103224354A
- Authority
- CN
- China
- Prior art keywords
- parts
- preparation
- aggregate
- auxiliary material
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种新型瓷砖粘结剂及其制备方法,涉及一种建筑材料高强耐水无收缩的界面砂浆技术领域。是将水泥、粉煤灰、石英砂三种骨料与羟丙基甲基纤维素、木质纤维这两种辅料进行混合搅拌后分袋包装制成成品。本发明的生产成本较低,具有良好的保水性能,粘结性能好,而且使用方法简单,不容易脱落。
Description
技术领域
本发明涉及一种建筑材料技术领域,尤其涉及一种一种新型瓷砖粘结剂及其制备方法。
背景技术
随着我国经济总量的持续稳步增长,能源供需矛盾日益凸现,现已成为制约我国经济持续健康发展的瓶颈。改革开放以后,建筑业的迅速发展已成为我国经济发展的支柱产业。随着居住建筑竣工面积的增加,势必会带来建筑能耗的加大。
瓷砖粘结剂是介于瓷砖与墙面、地面等之间起到一种粘结作用的物质,也被称作瓷砖胶。截止当前传统的用水泥砂浆的粘贴方式依然占据着主角的地位,由于此类粘结剂质量无法得到保证、保水性能差,经常发生瓷砖产生空鼓,脱落等问题。
发明内容
本发明所要解决的技术问题是提供一种一种成本较低,具有良好的保水性能,粘结性能好的新型瓷砖粘结剂及其制备方法。
本发明所要解决的技术问题采用以下技术方案来实现:
一种新型瓷砖粘结剂,其特征在于,包括骨料和辅料,所述骨料包括水泥、粉煤灰和石英砂,所述的辅料包括羟丙基甲基纤维素和木质纤维,所述水泥、粉煤灰和石英砂及羟丙基甲基纤维素和木质纤维配比的重量份数为,水泥40份、粉煤灰5份、石英砂55份、羟丙基甲基纤维素0.35份、木质纤维0.3份。
所述的石英砂为40-70目石英砂10份、75-95目石英砂45份。
制备一种新型瓷砖粘结剂的方法,制备步骤如下:
首先按重量配比称取各个骨料和辅料,将称取的骨料和辅料放入混合搅拌机内,混合搅拌5分钟后停止搅拌,然后打开混合搅拌机,对物料进行分袋包装。
本发明有益效果是:本发明的生产成本较低,具有良好的保水性能,粘结性能好,而且使用方法简单,不容易脱落。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施方式的实例对本发明做进一步详细说明。
实施例1
首先按重量配比称取各个骨料和辅料,水泥40kg、粉煤灰5kg、40-70目石英砂10kg、75-95目石英砂45kg、羟丙基甲基纤维素0.35kg、木质纤维0.3kg,将称取的骨料和辅料放入混合搅拌机内,混合搅拌5分钟后停止搅拌,然后打开混合搅拌机,对物料进行分袋包装。
实施例2
首先按重量配比称取各个骨料和辅料,水泥60kg、粉煤灰15kg、40-70目石英砂30kg、75-95目石英砂85kg、羟丙基甲基纤维素1kg、木质纤维0.6kg,将称取的骨料和辅料放入混合搅拌机内,混合搅拌5分钟后停止搅拌,然后打开混合搅拌机,对物料进行分袋包装。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (3)
1.一种新型瓷砖粘结剂,其特征在于,包括骨料和辅料,所述骨料包括水泥、粉煤灰和石英砂,所述的辅料包括羟丙基甲基纤维素和木质纤维,所述水泥、粉煤灰和石英砂及羟丙基甲基纤维素和木质纤维配比的重量份数为,水泥40份、粉煤灰5份、石英砂55份、羟丙基甲基纤维素0.35份、木质纤维0.3份。
2.根据权利要求1所述的一种新型瓷砖粘结剂,其特征在于:所述的石英砂为40-70目石英砂10份、75-95目石英砂45份。
3.制备如权利要求1所述的一种新型瓷砖粘结剂的方法,其特征在于,制备步骤如下:
首先按重量配比称取各个骨料和辅料,将称取的骨料和辅料放入混合搅拌机内,混合搅拌5分钟后停止搅拌,然后打开混合搅拌机,对物料进行分袋包装。