CN103214712A - 一种耐寒聚乙烯电缆料及其制备方法 - Google Patents

一种耐寒聚乙烯电缆料及其制备方法 Download PDF

Info

Publication number
CN103214712A
CN103214712A CN2013100989974A CN201310098997A CN103214712A CN 103214712 A CN103214712 A CN 103214712A CN 2013100989974 A CN2013100989974 A CN 2013100989974A CN 201310098997 A CN201310098997 A CN 201310098997A CN 103214712 A CN103214712 A CN 103214712A
Authority
CN
China
Prior art keywords
cold
parts
antioxidant
ethylene
trees ashes
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013100989974A
Other languages
English (en)
Other versions
CN103214712B (zh
Inventor
唐伟
唐世荣
王社兵
肖吕荣
王岳嵩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI SHUANGRONG ELECTRICAL APPLIANCE CABLE Co Ltd
Original Assignee
ANHUI SHUANGRONG ELECTRICAL APPLIANCE CABLE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI SHUANGRONG ELECTRICAL APPLIANCE CABLE Co Ltd filed Critical ANHUI SHUANGRONG ELECTRICAL APPLIANCE CABLE Co Ltd
Priority to CN201310098997.4A priority Critical patent/CN103214712B/zh
Publication of CN103214712A publication Critical patent/CN103214712A/zh
Application granted granted Critical
Publication of CN103214712B publication Critical patent/CN103214712B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种耐寒聚乙烯电缆料及其制备方法，其组成原料的重量份为：线型聚乙烯1802：95-105、聚乙烯蜡：0.04-0.06、乙二醇：0.04-0.06、抗氧剂1010：0.09-0.11、乙撑双硬脂酸酰胺：0.02-0.04、流变剂PPA：0.07-0.09、防老剂MB：0.01-0.03、改性树木灰烬：0.3-0.5、硼酸锌：0.008-0.012和抗氧剂1024：0.04-0.06；本发明采用线型聚乙烯1802作为本发明的基础材料，同时增加了辅料聚乙烯蜡、乙二醇、改性树木灰烬、防老剂、硼酸锌和多种抗氧剂，解决了电缆材料不能满足在耐寒的环境下工作使用现状，以及具有良好的耐磨、耐油、绝缘电气、物理机械以及柔软的特性。

Description

一种耐寒聚乙烯电缆料及其制备方法
技术领域
本发明涉及一种电缆料，具体涉及一种耐寒聚乙烯电缆料及其制备方法。
背景技术
随着经济的迅速发展，电线电缆在各个行业、领域中都得到广泛的应用，特别在气候不好的地区，对电缆的要求极高，耐寒、耐高温等等都是必备条件，本发明提供一种耐寒聚乙烯电缆料及其制备方法。
发明内容
本发明的目的在于提供一种耐寒聚乙烯电缆料及其制备方法。
本发明采用如下技术方案：
耐寒聚乙烯电缆料，其组成原料的重量份为：线型聚乙烯1802   95-105、聚乙烯蜡0.04-0.06、乙二醇0.04-0.06、抗氧剂 1010  0.09-0.11、乙撑双硬脂酸酰胺 0.02-0.04、流变剂PPA  0.07-0.09、防老剂MB   0.01-0.03、改性树木灰烬0.3-0.5、硼酸锌  0.008-0.012和抗氧剂1024  0.04-0.06。
耐寒聚乙烯电缆料，其组成原料的重量份为：线型聚乙烯1802   100、聚乙烯蜡0.05、乙二醇0.05、抗氧剂 1010  0.1、乙撑双硬脂酸酰胺 0.03、流变剂PPA  0.08、防老剂MB  0.02、改性树木灰烬0.4、硼酸锌  0.01和抗氧剂1024  0.05。
耐寒聚乙烯电缆料的制备方法，包括以下步骤：
（1）按组成原料的重量份称取各原料，配好料后加入高搅机中，搅拌10-15分钟，温度在100-115℃，脱潮后放料；
（2）将步骤（1）放料后的混料放入料斗，依次通过造粒、挤出处理，并通过水冷、风干、烘干、牵引和分筛得到成品。
所述的改性树木灰烬的制备方法为：
a、树木灰烬用10-15%双氧水浸泡3-4小时，去离子水洗涤，再用10-12%氢氧化钠溶液浸泡3-4小时，再用去离子水洗涤至中性，烘干；
b、在上述处理后的树木灰烬中加入相当于其重量2-3%的三苯乙基酚聚氧乙烯醚、1-2%的硅烷偶联剂KH550、2-3%的氮化铝粉、3-5%的二茂铁，高速1200-1500转/分搅拌，烘干粉碎成超细粉末。
本发明的有益效果：
本发明采用线型聚乙烯1802作为本发明的基础材料，同时增加了辅料聚乙烯蜡、乙二醇、改性树木灰烬、防老剂、硼酸锌和多种抗氧剂，解决了电缆材料不能满足在耐寒的环境下工作使用现状，以及具有良好的耐磨、耐油、绝缘电气、物理机械以及柔软的特性。
具体实施方式
实施例1：耐寒聚乙烯电缆料，其组成原料的重量份（kg）为：线型聚乙烯1802   100、聚乙烯蜡0.05、乙二醇0.05、抗氧剂 1010  0.1、乙撑双硬脂酸酰胺 0.03、流变剂PPA  0.08、防老剂MB  0.02、改性树木灰烬0.4、硼酸锌  0.01和抗氧剂1024  0.05。
耐寒聚乙烯电缆料的制备方法，包括以下步骤：
（1）按组成原料的重量份称取各原料，配好料后加入高搅机中，搅拌10-15分钟，温度在100-115℃，脱潮后放料；
（2）将步骤（1）放料后的混料放入料斗，依次通过造粒、挤出处理，并通过水冷、风干、烘干、牵引和分筛得到成品。
所述的改性树木灰烬的制备方法为：
a、树木灰烬用10%双氧水浸泡3小时，去离子水洗涤，再用10%氢氧化钠溶液浸泡3小时，再用去离子水洗涤至中性，烘干；
b、在上述处理后的树木灰烬中加入相当于其重量2.5%的三苯乙基酚聚氧乙烯醚、1.5%的硅烷偶联剂KH550、2.5%的氮化铝粉、4%的二茂铁，高速1400转/分搅拌，烘干粉碎成超细粉末。
通过上述实施例1制得的电缆料性能数据：绝缘0.45-0.62mm，火花实验通过，耐火实验3.8/5min通过，电缆弯曲半径：17倍电缆直径，低温-60℃下不开裂，-60℃温度下拉伸实验：240%，热延伸实验：载荷下伸张率≤170，冷却后永久伸张率≤13。

Claims (4)

1.一种耐寒聚乙烯电缆料，其特征在于其组成原料的重量份为：线型聚乙烯1802   95-105、聚乙烯蜡0.04-0.06、乙二醇0.04-0.06、抗氧剂 1010  0.09-0.11、乙撑双硬脂酸酰胺 0.02-0.04、流变剂PPA  0.07-0.09、防老剂MB   0.01-0.03、改性树木灰烬0.3-0.5、硼酸锌  0.008-0.012和抗氧剂1024  0.04-0.06。
2.根据权利要求1所述的耐寒聚乙烯电缆料，其特征在于其组成原料的重量份为：线型聚乙烯1802   100、聚乙烯蜡0.05、乙二醇0.05、抗氧剂 1010  0.1、乙撑双硬脂酸酰胺 0.03、流变剂PPA  0.08、防老剂MB  0.02、改性树木灰烬0.4、硼酸锌  0.01和抗氧剂1024  0.05。
3.一种如权利要求1所述的耐寒聚乙烯电缆料的制备方法，其特征在于包括以下步骤：
（1）按组成原料的重量份称取各原料，配好料后加入高搅机中，搅拌10-15分钟，温度在100-115℃，脱潮后放料；
（2）将步骤（1）放料后的混料放入料斗，依次通过造粒、挤出处理，并通过水冷、风干、烘干、牵引和分筛得到成品。
4.根据权利要求1所述的耐寒聚乙烯电缆料，其特征在于，所述的改性树木灰烬的制备方法为：
a、树木灰烬用10-15%双氧水浸泡3-4小时，去离子水洗涤，再用10-12%氢氧化钠溶液浸泡3-4小时，再用去离子水洗涤至中性，烘干；
b、在上述处理后的树木灰烬中加入相当于其重量2-3%的三苯乙基酚聚氧乙烯醚、1-2%的硅烷偶联剂KH550、2-3%的氮化铝粉、3-5%的二茂铁，高速1200-1500转/分搅拌，烘干粉碎成超细粉末。
CN201310098997.4A 2013-03-26 2013-03-26 一种耐寒聚乙烯电缆料及其制备方法 Expired - Fee Related CN103214712B (zh)