CN103194830A - Moisture-absorbing and quick drying pure cotton fabric and production method thereof - Google Patents
Moisture-absorbing and quick drying pure cotton fabric and production method thereof Download PDFInfo
- Publication number
- CN103194830A CN103194830A CN2013100805307A CN201310080530A CN103194830A CN 103194830 A CN103194830 A CN 103194830A CN 2013100805307 A CN2013100805307 A CN 2013100805307A CN 201310080530 A CN201310080530 A CN 201310080530A CN 103194830 A CN103194830 A CN 103194830A
- Authority
- CN
- China
- Prior art keywords
- cotton
- hydrophilic
- drying
- production method
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a moisture-absorbing and quick drying pure cotton fabric and a production method of the moisture-absorbing and quick drying pure cotton fabric. The moisture-absorbing and quick drying pure cotton fabric is produced by implementing hydrophilic and hydrophobic treatments on cotton fibers respectively, and then blending and weaving the cotton fibers of two functions in a proper proportion. The production method is as follows: hydrophilic and hydrophobic operations are implemented on the cotton fibers respectively, and then the cotton fibers of the two functions are blended in a proper proportion to blend and weave the moisture-absorbing and quick drying pure cotton fabric. The hydrophilic treatment technology for the cotton fibers is as follows: the cotton fibers are firstly refined to remove the fiber surface, then the hydrophilic treatment is implemented with an impregnation method, and then the cotton fibers are dehydrated and dried, or the hydrophilic treatment is implemented with a padding method and then the cotton fibers are predried and then baked. The hydrophobic treatment technology for the cotton fibers is as follows: the cotton fibers are subjected to hydrophobic treatment with an impregnation method and then are dehydrated and dried. The production process of the moisture-absorbing and quick drying pure cotton fabric is simple in production technology, the requirement on the weave structure of the fabric is relatively low, and the material of pure cotton fibers guarantees the soft and comfortable hand feeling of a product and the comfort when worn.
Description
Technical field
The invention belongs to the weaving face fabric technical field, relate to a kind of absorbing fast-drying pure-cotton fabric and production method thereof.
Background technology
The absorbing fast-drying dress-goods is of a great variety in the market, but the absorbing fast-drying dress-goods of pure-cotton fabric is very rare.Common absorbing fast-drying class garment material is the polyester fiber of modification or odd-shaped cross section mostly, common weaving structure more complicated, and weaving process had relatively high expectations, increased the burden of weaving link; And polyester fibers having deformed section cost height, the cost control that is unfavorable for producing wet absorption quick drying fabric.
Summary of the invention
The objective of the invention is to overcome the deficiencies in the prior art, the production method of the simple absorbing fast-drying pure-cotton fabric of a kind of production technology is provided, and the absorbing fast-drying pure-cotton fabric that obtains with this method.
Technical scheme of the present invention is as follows:
A kind of absorbing fast-drying pure-cotton fabric, it is earlier cotton fiber to be carried out hydrophilic and hydrophobic finishing respectively, in the proper ratio the cotton fiber of two kinds of functions is carried out blending processing again and weaves and form.
A kind of production method of absorbing fast-drying pure-cotton fabric: earlier cotton fiber is carried out hydrophilic and hydrophobic finishing respectively, in the proper ratio the cotton fiber of two kinds of functions is carried out blending processing again, be woven into the absorbing fast-drying pure-cotton fabric; Wherein
Cotton fiber hydrophilic finish technology is:
After the concise removal fiber surface wax of cotton fiber elder generation, adopt infusion process to carry out hydrophilic finish, dewatered drying then again; Perhaps, after the concise removal fiber surface wax of cotton fiber elder generation, adopt padding method to carry out hydrophilic finish again, first preliminary drying bakes again then;
Infusion process hydrophilic finish process conditions are as follows:
Padding method hydrophilic finish process conditions are as follows:
Hydrophilic finishing agent 15~35g/L
Pick-up 70~80%
Bake under 150-160 ℃ temperature, baked 1-2 minute.
The hydrophilic silicone oil LES that Co., Ltd produces in the business is kept in the preferred river of the used hydrophilic finishing agent of described infusion process; The hydrophilic finishing agent AQUA-RESINSR-203C that the preferred Shanghai of the used hydrophilic finishing agent of described padding method is profound and trade Co., Ltd produces.
Cotton fiber hydrophobicity finishing technique is: cotton fiber adopts infusion process to carry out hydrophobicity arrangement, dewatered drying then with three-proof finishing agent;
Cotton fiber hydrophobicity finishing technique condition is as follows:
Described three-proof finishing agent is preferably gone up the three-proof finishing agent TRW that sea blue Song industry and trade Co., Ltd produces, or the three-proof finishing agent SFA that produces of Shanghai Fluoropolymer Medical Products Co., Ltd..
Preferred 1:4~the 4:1 of the blending rate of described hydrophilic cotton fibers and hydrophobic cotton fiber, preferably 2:3.
The present invention is by hydrophile function processing and the waterproofing function processing of research cotton fiber, obtain a kind of production method of absorbing fast-drying pure-cotton fabric, earlier cotton fiber is carried out hydrophilic and hydrophobic finishing respectively, in the proper ratio two kinds of function cotton fibers are carried out blending processing again, in conjunction with weaving and dyeing and finishing technology of optimizing, realized the hydroscopic fast-drying function of pure-cotton fabric.
Beneficial effect of the present invention:
The production method production technology of a kind of absorbing fast-drying pure-cotton fabric of the present invention is simple, and is lower to the requirement of fabric weaving structure, and textile fibrous material has guaranteed soft comfort feel and the wearing comfortableness of product.
The specific embodiment
The present invention is further detailed explanation below in conjunction with embodiment:
Embodiment 1
One, cotton fiber function processing
1, hydrophilic cotton fibers processing
Cotton fiber refining is removed fiber surface wax → hydrophilic finish → oven dry
Hydrophilic finish technology:
2, hydrophobic cotton fiber processing
The hydrophobicity finishing technique:
Under 155 ℃ temperature, dried 2 minutes.
Two, blended yarn and fabric structure
Hydrophilic cotton fibers and hydrophobic cotton fiber blending rate 1:4
The 16s blended yarn, single jersey
Three, performance test
Hygroscopicity test: test sample (10 minutes measure wicking heights of 30cm * 2.5cm), the average capillary rise height of having tested 5 samples is:
Numbering | 1 | 2 | 3 | 4 | 5 | Mean value |
Measure wicking height | 8.5 | 8.3 | 8.2 | 8.8 | 8.6 | 8.48cm |
cm | ? | ? | ? | ? | ? | ? |
The quick-drying method of testing: (10cm * 10cm) places the beaker oral area with sample, circle is tight, specimen surface requires smooth, placed it under the environment of 20 ± 1 ℃ of temperature, relative humidity 65 ± 2% balance 24 hours, be placed on then on the electronic balance of degree of accuracy 0.001g, highly drip 0.05mL distilled water in specimen surface with the titration mouth of pipe from test coupon surface 1cm, test its water evaporates rate after 12 minutes.
The weight of water evaporates rate (%)=sample weight numbering/0.05mL water
The wet absorption quick drying fabric measure wicking height mean value that present case is produced is 8.48cm, and 12 minutes water evaporates rates of quick-drying test are 89%.
Embodiment 2
One, cotton fiber function processing
1, hydrophilic cotton fibers processing
Cotton fiber refining is removed fiber surface wax → hydrophilic finish → oven dry
Hydrophilic finish technology:
2, hydrophobic cotton fiber processing
The hydrophobicity finishing technique:
Under 150 ℃ temperature, dried 3 minutes.
Two, blended yarn and fabric structure
Hydrophilic cotton fibers and hydrophobic cotton fiber blending rate 3:2
The 50s blended yarn, the single face eyelet fabric
Three, performance test
Hygroscopicity test: test sample (10 minutes measure wicking heights of 30cm * 2.5cm), the average capillary rise height of having tested 5 samples is:
The quick-drying method of testing is with embodiment 1.
The wet absorption quick drying fabric measure wicking height mean value that present case is produced is 12.62cm, and 12 minutes water evaporates rates of quick-drying test are 92%.
Embodiment 3
One, cotton fiber function processing
1, hydrophilic cotton fibers processing
Cotton fiber refining is removed fiber surface wax → hydrophilic finish → oven dry
Hydrophilic finish technology:
2, hydrophobic cotton fiber processing
The hydrophobicity finishing technique:
Under 160 ℃ temperature, dried 1 minute.
Two, blended yarn and fabric structure
Hydrophilic cotton fibers and hydrophobic cotton fiber blending rate 4:1
The 32s blended yarn, single jersey
Three, performance test
Hygroscopicity test: test sample (10 minutes measure wicking heights of 30cm * 2.5cm), the average capillary rise height of having tested 5 samples is:
The quick-drying method of testing is with embodiment 1.
The wet absorption quick drying fabric measure wicking height mean value that present case is produced is 13.22cm, and 12 minutes water evaporates rates of quick-drying test are 85%.
Embodiment 4
One, cotton fiber function processing
1, hydrophilic cotton fibers processing
Cotton fiber refining is removed fiber surface wax → hydrophilic finish → oven dry
Hydrophilic finish technology:
2, hydrophobic cotton fiber processing
The hydrophobicity finishing technique:
Under 150 ℃ temperature, dried 3 minutes.
Two, blended yarn and fabric structure
Hydrophilic cotton fibers and hydrophobic cotton fiber blending rate 2:3
The 50s blended yarn, two-sided eyelet fabric
Three, performance test
Hygroscopicity test: test sample (10 minutes measure wicking heights of 30cm * 2.5cm), the average capillary rise height of having tested 5 samples is:
The quick-drying method of testing is with embodiment 1.
The wet absorption quick drying fabric measure wicking height mean value that present case is produced is 12.06cm, and 12 minutes water evaporates rates of quick-drying test are 94%.
Embodiment 5
One, cotton fiber function processing
1, hydrophilic cotton fibers processing
Cotton fiber refining is removed fiber surface wax → pad working solution (the profound and trade Co., Ltd's production in hydrophilic finishing agent AQUA-RESINSR-203C(Shanghai) 35g/L, pick-up 80%) → preliminary drying → bake (160 ℃ * 1min)
2, hydrophobic cotton fiber processing
The hydrophobicity finishing technique:
Under 150 ℃ temperature, dried 3 minutes.
Two, blended yarn and fabric structure
Hydrophilic cotton fibers and hydrophobic cotton fiber blending rate 2:3
The 50s blended yarn, two-sided eyelet fabric
Three, performance test
Hygroscopicity test: test sample (10 minutes measure wicking heights of 30cm * 2.5cm), the average capillary rise height of having tested 5 samples is:
The quick-drying method of testing is with embodiment 1.
The wet absorption quick drying fabric measure wicking height mean value that present case is produced is 13.46cm, and 12 minutes water evaporates rates of quick-drying test are 94%.
Embodiment 6
One, cotton fiber function processing
1, hydrophilic cotton fibers processing
Cotton fiber refining is removed fiber surface wax → pad working solution (hydrophilic finishing agent AQUA-RESINSR-203C(Shanghai Zhan and trade Co., Ltd) 15g/L, pick-up 70%) → preliminary drying → bake (150 ℃ * 2min)
2, hydrophobic cotton fiber processing
The hydrophobicity finishing technique:
Under 160 ℃ temperature, dried 1 minute.
Two, blended yarn and fabric structure
Hydrophilic cotton fibers and hydrophobic cotton fiber blending rate 1:4
The 16s blended yarn, Woven Fabrics
Three, performance test
Hygroscopicity test: test sample (10 minutes measure wicking heights of 30cm * 2.5cm), the average capillary rise height of having tested 5 samples is:
The quick-drying method of testing is with embodiment 1.
The wet absorption quick drying fabric measure wicking height mean value that present case is produced is 9.12cm, and 12 minutes water evaporates rates of quick-drying test are 90%.
Embodiment 7
One, cotton fiber function processing
1, hydrophilic cotton fibers processing
Cotton fiber refining is removed fiber surface wax → pad working solution (hydrophilic finishing agent AQUA-RESINSR-203C(Shanghai Zhan and trade Co., Ltd) 25g/L, pick-up 75%) → preliminary drying → bake (155 ℃ * 1.5min)
2, hydrophobic cotton fiber processing
The hydrophobicity finishing technique:
Under 155 ℃ temperature, dried 2 minutes.
Two, blended yarn and fabric structure
Hydrophilic cotton fibers and hydrophobic cotton fiber blending rate 4:1
The 32s blended yarn, single jersey
Three, performance test
Hygroscopicity test: test sample (10 minutes measure wicking heights of 30cm * 2.5cm), the average capillary rise height of having tested 5 samples is:
The quick-drying method of testing is with embodiment 1.
The wet absorption quick drying fabric measure wicking height mean value that present case is produced is 12.94cm, and 12 minutes water evaporates rates of quick-drying test are 87%.
Claims (10)
1. an absorbing fast-drying pure-cotton fabric is characterized in that, it is earlier cotton fiber to be carried out hydrophilic and hydrophobic finishing respectively, in the proper ratio the cotton fiber of two kinds of functions is carried out blending processing again and weaves and form.
2. the production method of an absorbing fast-drying pure-cotton fabric as claimed in claim 1, it is characterized in that: earlier cotton fiber is carried out hydrophilic and hydrophobic finishing respectively, in the proper ratio the cotton fiber of two kinds of functions is carried out blending processing again, be woven into the absorbing fast-drying pure-cotton fabric.
3. the production method of absorbing fast-drying pure-cotton fabric as claimed in claim 2 is characterized in that, the blending rate of described hydrophilic cotton fibers and hydrophobic cotton fiber is 1:4~4:1.
4. the production method of absorbing fast-drying pure-cotton fabric as claimed in claim 3 is characterized in that, the blending rate of described hydrophilic cotton fibers and hydrophobic cotton fiber is 2:3.
5. as the production method of claim 2,3 or 4 described absorbing fast-drying pure-cotton fabrics, it is characterized in that, wherein cotton fiber hydrophilic finish technology is: after the concise removal fiber surface wax of cotton fiber elder generation, adopt infusion process to carry out hydrophilic finish, dewatered drying then again; Perhaps, after the concise removal fiber surface wax of cotton fiber elder generation, adopt padding method to carry out hydrophilic finish again, first preliminary drying bakes again then.
6. as the production method of claim 2,3 or 4 described absorbing fast-drying pure-cotton fabrics, it is characterized in that wherein cotton fiber hydrophobicity finishing technique is: cotton fiber adopts infusion process to carry out hydrophobicity arrangement, dewatered drying then with three-proof finishing agent.
7. the production method of absorbing fast-drying pure-cotton fabric as claimed in claim 5 is characterized in that, wherein infusion process hydrophilic finish process conditions are:
Padding method hydrophilic finish process conditions are:
Hydrophilic finishing agent 15~35g/L
Pick-up 70~80%
Bake under 150-160 ℃ temperature, baked 1-2 minute.
9. the production method of absorbing fast-drying pure-cotton fabric as claimed in claim 7 is characterized in that, the used hydrophilic finishing agent of described infusion process is that the hydrophilic silicone oil LES that Co., Ltd produces in the business is kept in the river; The used hydrophilic finishing agent of described padding method is the hydrophilic finishing agent AQUA-RESINSR-203C that Shanghai is profound and trade Co., Ltd produces.
10. the production method of absorbing fast-drying pure-cotton fabric as claimed in claim 8, it is characterized in that, described three-proof finishing agent is the three-proof finishing agent TRW that last sea blue Song industry and trade Co., Ltd produces, or the three-proof finishing agent SFA that produces of Shanghai Fluoropolymer Medical Products Co., Ltd..