CN104178884B - Super-comfortable imitated cashmere thermal fabric and production method thereof - Google Patents
Super-comfortable imitated cashmere thermal fabric and production method thereof Download PDFInfo
- Publication number
- CN104178884B CN104178884B CN201410450642.1A CN201410450642A CN104178884B CN 104178884 B CN104178884 B CN 104178884B CN 201410450642 A CN201410450642 A CN 201410450642A CN 104178884 B CN104178884 B CN 104178884B
- Authority
- CN
- China
- Prior art keywords
- yarn
- yarns
- proviscose
- spinning
- comfortable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a super-comfortable imitated cashmere thermal fabric and a production method thereof. The super-comfortable imitated cashmere thermal fabric comprises warp yarns and weft yarns, the warp yarns are compound untwisted yarns comprising main yarns and framework yarns, the main yarns comprise Proviscose, Dralon and POREL, the framework yarns are made of Proviscose fibers, and the weft yarns comprise Proviscose, Dralon and POREL. Various functional properties such as moisture absorption, breathability, quick-dry property, softness, comfortableness and warmth retention of the super-comfortable imitated cashmere thermal fabric (Tianshu brand) are combined by the aid of polyester fiber technology and novel textile dyeing and finishing technology. The imitated cashmere fabric is more vivid and really comfortable, casual and noble in terms of improving wearing comfortableness, antistatic property, pilling and skin touch. The bottleneck problem of restricting market development of imitated cashmere products at present is solved.
Description
Technical field
The present invention relates to a kind of super comfortable Hair style thermal fabric and production method thereof.
Background technology
Current domestic cashmere-like fabric is main mainly with Hair style acrylic fibers, and the function of its uniqueness is bulkiness and flexibility.Wool top bulkiness after steam heat sizing is significantly better than before steam heat sizing, and its flexibility of the fabric of composition is that any natural, animal fiber is beyond one's reach, but its hygroscopicity is worse than natural fabric, in reality dress, still cannot break away from the problem that acrylic plays electrostatic.Hair style product specification domestic is at present general lower, and function singleness, can not meet that domestic and international medium-to-high grade market is comfortable to product, the demand of function, fashion.
Summary of the invention
The object of the present invention is to provide a kind of moisture absorption, the super comfortable Hair style thermal fabric that ventilative, rapid-curing cutback, soft comfortable, thermal property are good and production method thereof.
Technical solution of the present invention is:
A kind of super comfortable Hair style thermal fabric, comprise warp thread, weft yarn, it is characterized in that: the compound untwisted yarn that warp thread is made up of main body yarn and Skeletal yarn, wherein main body yarn is made up of weight components:
Proviscose 30-40%
Dralon 15-20%
POREL 45-50%；
Skeletal yarn adopts Proviscose fiber;
The moisture absorption heating high pulling torque yarn that weft yarn is made up of weight components:
Proviscose 30-40%
Dralon 15-20%
POREL 45-50%。
A kind of production method of super comfortable Hair style thermal fabric, comprise spinning processing, warping, sizing, wear palm fibre, weave, Final finishing, it is characterized in that: spinning processing comprises warp thread processing, weft yarn processing, and warp thread adds man-hour: by weight components mixing composition main body yarn raw material:
Proviscose 30-40%
Dralon 15-20%
POREL 45-50%
Then through scutching cotton → comb and parallel cotton fibers prior to spinning → drafting → rove → spun yarn → doff processing;
Skeletal yarn Proviscose fiber is processed through scutching cotton → comb and parallel cotton fibers prior to spinning → drafting → rove → spun yarn → doff simultaneously;
Again by through the main body yarn of above-mentioned processing and the doubling of Skeletal yarn compound, form functional compound untwisted yarn;
Weft yarn adds man-hour: by weight components mixing composition weft yarn raw material:
Proviscose 30-40%
Dralon 15-20%
POREL 45-50%
Then through scutching cotton → comb and parallel cotton fibers prior to spinning → drafting → rove → high pulling torque spinning → doff;
Sizing adds man-hour, adopts AW-8502 to carry out after waxing; During sizing, slurry is grouped into by the one-tenth of following weight portion:
K5000 50 parts
A-620A converted starch 50 parts
15 parts, NP-350 liquid propene wintercherry material
SLMO-02 finish 3 parts
963 2 parts, antistatic additive;
Fabric adopts satin weave alternative construction;
Final finishing adopts the light sanding afterfinish method of carbon element.
During sizing, adopt " two high one low " slashing technique.
The super comfortable Hair style thermal fabric (Tianshu board) of the present invention's exploitation, adopts multi-component fibre technology compound, fabric dyeing and finishing process technology, realizes the compound of the moisture absorption of fabric, ventilative, rapid-curing cutback, soft comfortable, the several functions characteristic such as warming.Cashmere-like fabric is more true to nature, improve snugness of fit, antistatic behaviour, pilling tendency, skin touch sensitivity in, really accomplish comfortable, that leisure is noble boundary.Solve the bottleneck problem of restriction Hair style produce market development at present.
Fabric feature:
1, there is the style of cashmere fabric.Flexibility is better than cashmere fabric, specific performance index: compress ional resilience index (KES) >=50%; Static drape coefficient≤45%, dynamic suspended coefficient≤61%.
2, there is the moisture-absorbing and fast-drying function being better than cashmere fabric, and the assurance function forever property held.Water absorption rate>=140%, drip diffusion time≤4S, measure wicking height>=105mm, evaporation rate>=0.2 g/h, vapor transfer rate>=1095g/ (m
2d).
3, there is moisture absorption heating and heat-preserving function.Most promotion temperature value >=6.5 DEG C, in 30 minutes average intensification value >=3.1 DEG C, insulation rate >=35%.
4, fabric good stability of the dimension.Warp-wise washing shrinkage is≤-3.1%, and broadwise washing shrinkage≤-3.4%.
Below in conjunction with embodiment, the invention will be further described.
Detailed description of the invention
A production method for super comfortable Hair style thermal fabric, comprises spinning processing, warping, sizing, wears palm fibre, weaves, Final finishing, and spinning processing comprises warp thread processing, weft yarn processing, and warp thread adds man-hour: by weight components mixing composition main body yarn raw material:
Proviscose 30-40%
Dralon 15-20%
POREL 45-50%
Then through scutching cotton → comb and parallel cotton fibers prior to spinning → drafting → rove → spun yarn → doff processing;
Skeletal yarn Proviscose fiber is processed through scutching cotton → comb and parallel cotton fibers prior to spinning → drafting → rove → spun yarn → doff simultaneously;
Again by through the main body yarn of above-mentioned processing and the doubling of Skeletal yarn compound, form functional compound untwisted yarn;
Weft yarn adds man-hour: by weight components mixing composition weft yarn raw material:
Proviscose 30-40%
Dralon 15-20%
POREL 45-50%
Then through scutching cotton → comb and parallel cotton fibers prior to spinning → drafting → rove → high pulling torque spinning → doff; Obtained moisture absorption heating high pulling torque yarn; Described high pulling torque spinning can adopt the method for ZL201310568506.8.
Sizing adds man-hour, adopts AW-8502 to carry out after waxing; During sizing, slurry is grouped into by the one-tenth of following weight portion:
K5000 50 parts
A-620A converted starch 50 parts
15 parts, NP-350 liquid propene wintercherry material
SLMO-02 finish 3 parts
963 2 parts, antistatic additive;
Fabric adopts satin weave alternative construction;
Final finishing adopts the light sanding afterfinish method of carbon element.
During sizing, adopt " two high one low " slashing technique.
Claims (2)
1. the production method of a super comfortable Hair style thermal fabric, comprise spinning processing, warping, sizing, gait, weave, Final finishing, it is characterized in that: spinning processing comprises warp thread processing, weft yarn processing, and warp thread adds man-hour: by weight components mixing composition main body yarn raw material:
Proviscose 30‐40％
Dralon 15‐20％
POREL 45‐50％
Then through scutching cotton → comb and parallel cotton fibers prior to spinning → drafting → rove → spun yarn → doff processing;
Skeletal yarn Proviscose fiber is processed through scutching cotton → comb and parallel cotton fibers prior to spinning → drafting → rove → spun yarn → doff simultaneously;
Again by through the main body yarn of above-mentioned processing and the doubling of Skeletal yarn compound, form functional compound untwisted yarn;
Weft yarn adds man-hour: by weight components mixing composition weft yarn raw material:
Proviscose 30‐40％
Dralon 15‐20％
POREL 45‐50％
Then through scutching cotton → comb and parallel cotton fibers prior to spinning → drafting → rove → high pulling torque spinning → doff;
Sizing adds man-hour, adopts AW ?8502 finish to carry out after waxing; During sizing, slurry is grouped into by the one-tenth of following weight portion:
Fabric adopts satin weave alternative construction;
Final finishing adopts the light sanding afterfinish method of carbon element.
2. the production method of super comfortable Hair style thermal fabric according to claim 1, is characterized in that: during sizing, adopts " two high one low " slashing technique.