CN103194908A - Cool wool knitted fabric and processing method thereof - Google Patents
Cool wool knitted fabric and processing method thereof Download PDFInfo
- Publication number
- CN103194908A CN103194908A CN2013100886978A CN201310088697A CN103194908A CN 103194908 A CN103194908 A CN 103194908A CN 2013100886978 A CN2013100886978 A CN 2013100886978A CN 201310088697 A CN201310088697 A CN 201310088697A CN 103194908 A CN103194908 A CN 103194908A
- Authority
- CN
- China
- Prior art keywords
- wool
- cool
- nice
- hydrophobic
- processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a cool wool knitted fabric and a processing method of the cool wool knitted fabric. The fabric is processed by respectively carrying out hydrophilic and hydrophobic processing on wool fibers scaled and lightened through enzyme treatment and then blending the hydrophilic and hydrophobic wool fibers according to an appropriate proportion, wherein the hydrophilic processing method is low-pressure plasma treatment. The processing method is characterized by respectively carrying out hydrophilic and hydrophobic processing on the wool fibers scaled and lightened through enzyme treatment; and blending the hydrophilic and hydrophobic wool fibers according to an appropriate proportion, wherein the hydrophilic processing method is low-pressure plasma treatment; and the hydrophobic processing method is characterized by using a three-proofing finishing agent for hydrophobic processing. The processing method of the cool wool fabric is simple in production process. The produced cool wool fabric product has good fastness to washing and an excellent cool effect and is especially suitable for spring and summer sportswear.
Description
Technical field
The invention belongs to the knitting technology field, relate to a kind of nice and cool wool knit fabric and processing method thereof.
Background technology
The wool fabric unique style, wrinkle resistance and hygroscopicity are outstanding especially, often are used to produce the autumn and winter garment material, and wool product has characteristics such as good hand feeling, warmth retention property be good, comfortable and easy to wear.The extensive use of wool in knit product mainly is outstanding its warmth retention property, and the research of exploitation wool thermal fabric is ripe relatively, and constantly has new product to come out.And wool clothing of spring and summer product is less relatively.The scale of wool has good hydrophobicity, but scale changes wool fabric size felting, also can allow the wearer that prodding and itching feeling is arranged.Present studies show that, handles by biology enzyme, can carry out felt proofing processing to wool, alleviates prodding and itching feeling, simultaneously, through enzyme handle wool shelled the processing of scale decrement after, make that wool attenuates, surface smoothing etc., can make clothing of spring and summer with nice and cool wool fabric.But, directly unsatisfactory with the nice and cool effect of the knitting fabric that processes of wool fibre after the enzyme processing stripping scale decrement at present.
Summary of the invention
The objective of the invention is to overcome the deficiencies in the prior art, a kind of nice and cool wool knit fabric and processing method thereof of nice and cool effect excellence are provided, should can be used for producing sportswear in spring and autumn, T-shirt etc. by nice and cool wool knit fabric, and can satisfy the consumer to Woolens' in spring and autumn demand.
Technical scheme of the present invention is as follows:
A kind of nice and cool wool knit fabric, it is that the wool fibre that will handle through enzyme after the stripping scale decrement carries out hydrophilic and hydrophobic processing respectively, then hydrophilic wool fibre and hydrophobic wool fibre is undertaken by proper proportion that blending processes; Wherein said hydrophilic processing method is that low pressure plasma is handled.
A kind of processing method of nice and cool wool knit fabric:
Wool fibre after enzyme is handled stripping scale decrement is carried out hydrophilic and hydrophobic processing respectively, then hydrophilic wool fibre and hydrophobic wool fibre are carried out blending processing by proper proportion; Described hydrophilic processing method is that low pressure plasma is handled; Described hydrophobic processing method is for to carry out hydrophobic processing with three-proof finishing agent.
Described low pressure plasma treatment process condition is: the argon plasma gas pressure intensity is 50-70Pa, and glow discharge power is 45-55W, and the processing time is 5-15min; Preferably: the argon plasma gas pressure intensity is 60Pa, and glow discharge power is 50W, and the processing time is 10min.
Described three-proof finishing agent is preferably gone up the three-proof finishing agent TRW that sea blue Song industry and trade Co., Ltd produces, and the hydrophobic finishing process conditions are:
1-3min is dried in wool fibre dehydration back after the processing under 150-160 ℃ of temperature.
Preferred 1:4～the 4:1 of the blending rate of described hydrophilic cotton fibers and hydrophobic cotton fiber, preferably 2:3.
Beneficial effect of the present invention:
The processing method of a kind of nice and cool wool knit fabric of the present invention by studying the cooling function effect of hydrophilic wool fibre and hydrophobic fleece fibre blended spinning yarn, is produced the nice and cool wool fabric and the clothes that are fit to spring and summer dress in season.Wool fibre has had good hydrophily after handling stripping scale decrement through enzyme, in order to obtain more excellent hydrophily, the present invention carries out low pressure plasma with the mercerized wool fiber after enzyme is handled stripping scale decrement and handles, present hole, nano level hole through the wool surface after the low pressure plasma processing, increased the hydrophilic group quantity of wool surface, made it have super hydrophilic.Have the hydrophilic wool fibre of super hydrophilic and a wool fabric that hydrophobic fleece fibre blended spinning processes with this, easy especially absorbing sweat, and the sweat of absorption spreads easily, improved the evaporation rate of sweat and the efficient of heat conduction thus, made wool fabric have well nice and cool effect.
Nice and cool wool fabric processing method production technology of the present invention is simple, and the nice and cool wool fabric product fastness to washing of producing is good, and nice and cool effect excellence is particularly suitable for the spring and summer sportswear.
The specific embodiment
The present invention is further detailed explanation below in conjunction with embodiment:
Embodiment 1
One, wool fibre
Select the mercerising decrement wool fibre that the enzyme facture produces (by the enzyme processing section or all degraded the scale layer on wool surface) for use
Two, the functional processing of wool fibre
1, wool fibre hydrophily processing
Carry out low pressure plasma and handle that (the argon plasma gas pressure intensity is 50Pa handle mercerized wool fiber after the stripping scale decrement through enzyme, glow discharge power is 45W, processing time is 10min), present hole, nano level hole through the wool surface after the low pressure plasma processing, increased the hydrophilic group quantity of wool surface, made it have super hydrophilic.
2, wool fibre hydrophobicity processing
Handle through the mercerized wool fiber after the enzyme processing stripping scale decrement with three-proof finishing agent TRW, make it have hydrophobicity:
The upward sea blue Song industry and trade of three-proof finishing agent TRW(Co., Ltd) 2.0%(o.w.f)
2min is dried in wool fibre dehydration back after the processing under 155 ℃ of temperature.
Three, blended yarn and fabric structure
Hydrophilic wool fibre and hydrophobic fleece fibre blended spinning ratio 1:4, blended yarn number 32S.
Fabric structure: two-sided mesh
Four, nice and cool performance test
Nice and cool performance test methods: we select the nice and cool performance that 20 experimenters estimate the present case product.Allow 20 experimenters in constant-temperature constant-humidity environment, under a small amount of situation of perspiring, estimate the cooling feeling of present case product motion T-shirt and conventional polyester motion T-shirt respectively, evaluation is benchmark with conventional polyester motion T-shirt, and the cooling feeling of experiment product is divided into three ranks: 1 does not have (not than conventional polyester fabric feel cool) fully; 2 have (can feel a little has cooling feeling than ordinary polyester fabric, but not obvious) a little; 3 obviously have (obviously nice and cool than ordinary polyester fabric sensation)
The nice and cool performance test result of the fabric that present case is produced:
| ? | 1 grade (not having fully) | 2 grades (having a little) | 3 grades (obviously having) |
| Number | 1 | 3 | 16 |
This product measure of merit result that feels nice and cool: that obviously feels nice and cool property reaches 80%.
Embodiment 2
One, wool fibre
The mercerising decrement wool fibre that the enzyme facture is produced
Two, the functional processing of wool fibre
1, wool fibre hydrophily processing
The mercerized wool fiber is carried out the low pressure plasma processing, and (the argon plasma gas pressure intensity is 60Pa, glow discharge power is 50W, processing time is 10min), present hole, nano level hole through the wool surface after the low pressure plasma processing, increased the hydrophilic group quantity of wool surface, made it have super hydrophilic.
2, wool fibre hydrophobicity processing
Handle through the mercerized wool fiber after the enzyme processing stripping scale decrement with three-proof finishing agent TRW, make it have hydrophobicity:
The upward sea blue Song industry and trade of three-proof finishing agent TRW(Co., Ltd) 3.5%(o.w.f)
Wool fibre after the processing dewaters back 150 ℃ and dries 3min.
Three, blended yarn and fabric structure
Hydrophilic wool fibre and hydrophobic fleece fibre blended spinning ratio blending rate 2:3, blended yarn number 50S.
Fabric structure: single face mesh
Four, nice and cool performance test
Nice and cool performance test methods is with embodiment 1.
The nice and cool performance test result of the fabric that present case is produced:
| ? | 1 grade (not having fully) | 2 grades (having a little) | 3 grades (obviously having) |
| Number | 0 | 3 | 17 |
This product measure of merit result that feels nice and cool: that obviously feels nice and cool property reaches 85%.
Embodiment 3
One, wool fibre
The mercerising decrement wool fibre that the enzyme facture is produced
Two, the functional processing of wool fibre
1, wool fibre hydrophily processing
The mercerized wool fiber is carried out the low pressure plasma processing, and (the argon plasma gas pressure intensity is 70Pa, glow discharge power is 55W, processing time is 5min), present hole, nano level hole through the wool surface after the low pressure plasma processing, increased the hydrophilic group quantity of wool surface, made it have super hydrophilic.
2, wool fibre hydrophobicity processing
Handle through the mercerized wool fiber after the enzyme processing stripping scale decrement with three-proof finishing agent TRW, make it have hydrophobicity:
The upward sea blue Song industry and trade of three-proof finishing agent TRW(Co., Ltd) 5.0%(o.w.f)
Wool fibre after the processing dewaters back 160 ℃ and dries 1min.
Three, blended yarn and fabric structure
Hydrophilic wool fibre and hydrophobic fleece fibre blended spinning ratio 3:2, blended yarn number 42S.
Fabric structure: single jersey
Four, nice and cool performance test
Nice and cool performance test methods is with embodiment 1.
The nice and cool performance test result of the fabric that present case is produced:
| ? | 1 grade (not having fully) | 2 grades (having a little) | 3 grades (obviously having) |
| Number | 0 | 4 | 16 |
This product measure of merit result that feels nice and cool: that obviously feels nice and cool property reaches 80%.
Embodiment 4
One, wool fibre
The mercerising decrement wool fibre that the enzyme facture is produced
Two, the functional processing of wool fibre
1, wool fibre hydrophily processing
The mercerized wool fiber is carried out the low pressure plasma processing, and (the argon plasma gas pressure intensity is 60Pa, glow discharge power is 50W, processing time is 10min), present hole, nano level hole through the wool surface after the low pressure plasma processing, increased the hydrophilic group quantity of wool surface, made it have super hydrophilic.
2, wool fibre hydrophobicity processing
Handle through the mercerized wool fiber after the enzyme processing stripping scale decrement with three-proof finishing agent, make it have hydrophobicity:
Three-proof finishing agent LF-95(Shanghai Li Feng Chemical Industry Science Co., Ltd) 2.0%(o.w.f)
Wool fibre after the processing dewaters back 150 ℃ and dries 2.5min.
Three, blended yarn and fabric structure
Hydrophilic wool fibre and hydrophobic fleece fibre blended spinning ratio 2:3, blended yarn number 42S.
Fabric structure: single face mesh
Four, nice and cool performance test
Nice and cool performance test methods is with embodiment 1.
The nice and cool performance test result of the fabric that present case is produced:
| ? | 1 grade (not having fully) | 2 grades (having a little) | 3 grades (obviously having) |
| Number | 0 | 3 | 17 |
This product measure of merit result that feels nice and cool: that obviously feels nice and cool property reaches 85%.
Embodiment 5
One, wool fibre
The mercerising decrement wool fibre that the enzyme facture is produced
Two, the functional processing of wool fibre
1, wool fibre hydrophily processing
The mercerized wool fiber is carried out the low pressure plasma processing, and (the argon plasma gas pressure intensity is 70Pa, glow discharge power is 55W, processing time is 5min), present hole, nano level hole through the wool surface after the low pressure plasma processing, increased the hydrophilic group quantity of wool surface, made it have super hydrophilic.
2, wool fibre hydrophobicity processing
Handle through the mercerized wool fiber after the enzyme processing stripping scale decrement with three-proof finishing agent, make it have hydrophobicity:
Three-proof finishing agent LF-95(Shanghai Li Feng Chemical Industry Science Co., Ltd) 1.0%(o.w.f)
Wool fibre after the processing dewaters back 150 ℃ and dries 2.5min.
Three, blended yarn and fabric structure
Hydrophilic wool fibre and hydrophobic fleece fibre blended spinning ratio 4:1, blended yarn number 42S.
Fabric structure: two-sided mesh
Four, nice and cool performance test
Nice and cool performance test methods is with embodiment 1.
The nice and cool performance test result of the fabric that present case is produced:
| ? | 1 grade (not having fully) | 2 grades (having a little) | 3 grades (obviously having) |
| Number | 1 | 4 | 15 |
This product measure of merit result that feels nice and cool: that obviously feels nice and cool property reaches 75%.
Embodiment 6
One, wool fibre
The mercerising decrement wool fibre that the enzyme facture is produced
Two, the functional processing of wool fibre
1, wool fibre hydrophily processing
The mercerized wool fiber is carried out the low pressure plasma processing, and (the argon plasma gas pressure intensity is 50Pa, glow discharge power is 45W, processing time is 15min), present hole, nano level hole through the wool surface after the low pressure plasma processing, increased the hydrophilic group quantity of wool surface, made it have super hydrophilic.
2, wool fibre hydrophobicity processing
Handle through the mercerized wool fiber after the enzyme processing stripping scale decrement with three-proof finishing agent, make it have hydrophobicity:
Three-proof finishing agent LF-95(Shanghai Li Feng Chemical Industry Science Co., Ltd) 3.0%(o.w.f)
Wool fibre after the processing dewaters back 150 ℃ and dries 2.5min.
Three, blended yarn and fabric structure
Hydrophilic wool fibre and hydrophobic fleece fibre blended spinning ratio 4:1, blended yarn number 42S.
Fabric structure: single jersey
Four, nice and cool performance test
Nice and cool performance test methods is with embodiment 1.
The nice and cool performance test result of the fabric that present case is produced:
| ? | 1 grade (not having fully) | 2 grades (having a little) | 3 grades (obviously having) |
| Number | 1 | 3 | 16 |
This product measure of merit result that feels nice and cool: that obviously feels nice and cool property reaches 80%.
Claims (10)
1. a nice and cool wool knit fabric is characterized in that, it is that the wool fibre that will handle through enzyme after the stripping scale decrement carries out hydrophilic and hydrophobic processing respectively, then hydrophilic wool fibre and hydrophobic wool fibre is undertaken by proper proportion that blending processes; Wherein said hydrophilic processing method is that low pressure plasma is handled.
2. nice and cool wool knit fabric as claimed in claim 1 is characterized in that, the blending rate of described hydrophilic cotton fibers and hydrophobic cotton fiber is 1:4～4:1.
3. nice and cool wool knit fabric as claimed in claim 2 is characterized in that, the blending rate of described hydrophilic cotton fibers and hydrophobic cotton fiber is 2:3.
4. the processing method of a nice and cool wool knit fabric as claimed in claim 1, it is characterized in that, wool fibre after enzyme is handled stripping scale decrement is carried out hydrophilic and hydrophobic processing respectively, then hydrophilic wool fibre and hydrophobic wool fibre are carried out blending processing by proper proportion; Described hydrophilic processing method is that low pressure plasma is handled; Described hydrophobic processing method is for to carry out hydrophobic processing with three-proof finishing agent.
5. the processing method of nice and cool wool knit fabric as claimed in claim 4 is characterized in that, the blending rate of described hydrophilic cotton fibers and hydrophobic cotton fiber is 1:4～4:1.
6. the processing method of nice and cool wool knit fabric as claimed in claim 5 is characterized in that, the blending rate of described hydrophilic cotton fibers and hydrophobic cotton fiber is 2:3.
7. as the processing method of claim 4,5 or 6 described nice and cool wool knit fabrics, it is characterized in that described three-proof finishing agent is the three-proof finishing agent TRW that last sea blue Song industry and trade Co., Ltd produces, hydrophobic fabrication process condition is:
1-3min is dried in wool fibre dehydration back after the processing under 150-160 ℃ of temperature.
8. as the processing method of claim 4,5 or 6 described nice and cool wool knit fabrics, it is characterized in that, described low pressure plasma treatment process condition is: the argon plasma gas pressure intensity is 50-70Pa, and glow discharge power is 45-55W, and the processing time is 5-15min.
9. the processing method of nice and cool wool knit fabric as claimed in claim 7 is characterized in that, described low pressure plasma treatment process condition is: the argon plasma gas pressure intensity is 50-70Pa, and glow discharge power is 45-55W, and the processing time is 5-15min.
10. the processing method of nice and cool wool knit fabric as claimed in claim 8 is characterized in that, described low pressure plasma treatment process condition is: the argon plasma gas pressure intensity is 60Pa, and glow discharge power is 50W, and the processing time is 10min.