CN103892492A - Production method of crease-resistant suit fabric - Google Patents
Production method of crease-resistant suit fabric Download PDFInfo
- Publication number
- CN103892492A CN103892492A CN201410128010.3A CN201410128010A CN103892492A CN 103892492 A CN103892492 A CN 103892492A CN 201410128010 A CN201410128010 A CN 201410128010A CN 103892492 A CN103892492 A CN 103892492A
- Authority
- CN
- China
- Prior art keywords
- parts
- fabric
- wrinkle resistant
- fiber
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a production method of a crease-resistant suit fabric. The production method includes the steps of 1, treating wool fiber with low-pressure plasma; 2, blending the treated wool fiber, cotton fiber and pearl fiber to produce surface fabric; 3, coating the surface of lining fabric with crease-resistant hot melt glue; 4, melting to glue the surface fabric and the lining fabric by a hot press; 5, performing fabric post-treatment. The crease-resistant hot melt glue is made with, by weight, 30-40 parts of polytetramethylene ether glycol, 20-25 parts of butyl acrylate, 18-22 parts of polymaleic hexenoic acid, 50-60 parts of polyurethane, and 5-8 parts of dioctyl phthalate. The production method of the crease-resistant suit fabric has the advantages that the crease-resistant suit fabric can be higher in drapability and crease resistance and size shrinkage rate is decreased.
Description
Technical field
The present invention relates to a kind of preparation method of wrinkle resistant suiting, belong to garment technology field.
Background technology
A western-style clothes great variety of models, fabric texture is soft, and young man likes western-style clothes class clothes, also more and more higher to the requirement that western-style clothes is wrinkle resistant.Pearl fiber belongs to viscose rayon, pearl powder content is in 5% left and right, contain the trace elements such as calcium, potassium, magnesium, can improve the health care of fabric, in suiting, add pearl fiber can improve drapability, transmissibility, gas permeability, the wrinkle resistance of fabric, strengthen feel, the comfort level that meets people and wear western-style clothes.
Summary of the invention
The object of this invention is to provide a kind of preparation method of wrinkle resistant suiting, improved drapability and the wrinkle resistance of fabric, reduced dimensional contraction rate.
For realizing above object, the preparation method of a kind of wrinkle resistant suiting of the present invention, comprises following method: 1) by wool fiber through low pressure plasma processing; 2) by wool fiber after treatment, cotton fiber and pearl fiber blending preparation table shell fabric; 3), at the wrinkle resistant PUR of top layer fabric surface-coated, the component of described wrinkle resistant PUR and weight portion are polytetramethylene ether diol 30-40 part, butyl acrylate 20-25 part, poly hexenoic acid 18-22 part, two mercaptan butanedioic acid 15-20 parts, polyurethane 50-60 part, dioctyl phthalate 5-8 part; 4) use pressing machine by melt bonded to top layer fabric and nexine fabric; 5) fabric post processing.
Further, the mass ratio of described wool fiber, cotton fiber, pearl fiber is 100:20-30:5-10; Preferably, the mass ratio of wool fiber, cotton fiber, pearl fiber is 100:25:8.
Further, the process conditions of described low pressure plasma processing are that argon plasma gas pressure intensity is 50-70Pa, and glow discharge power is 30-40W, and the processing time is 2-3min; Preferably, argon plasma gas pressure intensity is 60Pa, and glow discharge power is 35W, and the processing time is 3min.
Further, the component of described wrinkle resistant PUR and weight portion are 35 parts of polytetramethylene ether diols, 22 parts of butyl acrylates, 20 parts of poly hexenoic acids, 18 parts of two mercaptan butanedioic acids, 55 parts of polyurethane, 6 parts of dioctyl phthalates.
Further, described melt bonded temperature is 120-140 ℃, and pressure is 120-130Pa, and the time is 8-12s; Preferably, melt bonded temperature is 130 ℃, and pressure is 120Pa, and the time is 10s.
The beneficial effect that the present invention produces is the present invention by wool fiber after low pressure plasma is processed, increase the specific area of wool fiber, make it more easily to receive the pearl powder in pearl fiber, pearl fiber is evenly distributed in the fabric of whole top layer, is conducive to improve drapability and the wrinkle resistance of fabric.
In addition, using pressing machine by top layer fabric and the melt bonded process of nexine fabric, need suitable temperature, pressure and time to realize best bonding effect, excess Temperature, overlong time, pressure be excessive easily causes bonding infiltration, feel hardening, otherwise easily cause bonding strength to weaken, easily peel off.Wool fiber of the present invention, cotton fiber and pearl fiber blending top layer fabric in conjunction with novel wrinkle resistant PUR, improve the dispersiveness of wrinkle resistant PUR in fabric, improve the cohesive force of PUR, effectively reduce the melt bonded time, the size changing rate that has reduced fabric, has improved crease resistance.
The specific embodiment
Embodiment 1:
A preparation method for wrinkle resistant suiting, comprises following method:
1) by wool fiber through low pressure plasma processing, process conditions are that argon plasma gas pressure intensity is 50Pa, glow discharge power is 30W, the processing time is 3min;
2) by wool fiber after treatment, cotton fiber and pearl fiber blending preparation table shell fabric, the mass ratio of described wool fiber, cotton fiber, pearl fiber is 100:20:5;
3), at the wrinkle resistant PUR of top layer fabric surface-coated, the component of described wrinkle resistant PUR and weight portion are 30 parts of polytetramethylene ether diols, 20 parts of butyl acrylates, 18 parts of poly hexenoic acids, 15 parts of two mercaptan butanedioic acids, 60 parts of polyurethane, 8 parts of dioctyl phthalates;
4) use pressing machine by melt bonded to top layer fabric and nexine fabric, described melt bonded temperature is 120 ℃, and pressure is 120Pa, and the time is 12s;
5) fabric post processing, the suiting making.
Embodiment 2:
A preparation method for wrinkle resistant suiting, comprises following method:
1) by wool fiber through low pressure plasma processing, process conditions are that argon plasma gas pressure intensity is 60Pa, glow discharge power is 35W, the processing time is 3min;
2) by wool fiber after treatment, cotton fiber and pearl fiber blending preparation table shell fabric, the mass ratio of described wool fiber, cotton fiber, pearl fiber is 100:25:8;
3), at top layer fabric surface-coated PUR, the component of described wrinkle resistant PUR and weight portion are 35 parts of polytetramethylene ether diols, 22 parts of butyl acrylates, 20 parts of poly hexenoic acids, 18 parts of two mercaptan butanedioic acids, 55 parts of polyurethane, 6 parts of dioctyl phthalates;
4) use pressing machine by melt bonded to top layer fabric and nexine fabric, described melt bonded temperature is 130 ℃, and pressure is 120Pa, and the time is 10s;
5) fabric post processing, the suiting making.
Embodiment 3:
A preparation method for wrinkle resistant suiting, comprises following method:
1) by wool fiber through low pressure plasma processing, process conditions are that argon plasma gas pressure intensity is 70Pa, glow discharge power is 40W, the processing time is 2min;
2) by wool fiber after treatment, cotton fiber and pearl fiber blending preparation table shell fabric, the mass ratio of described wool fiber, cotton fiber, pearl fiber is 100:30:10;
3), at the wrinkle resistant PUR of top layer fabric surface-coated, the component of described wrinkle resistant PUR and weight portion are 40 parts of polytetramethylene ether diols, 25 parts of butyl acrylates, 22 parts of poly hexenoic acids, 20 parts of two mercaptan butanedioic acids, 50 parts of polyurethane, 5 parts of dioctyl phthalates;
4) use pressing machine by melt bonded to top layer fabric and nexine fabric, described melt bonded temperature is 140 ℃, and pressure is 120Pa, and the time is 8s;
5) fabric post processing, the suiting making.
The experimental data of creasy recovery angle, breaking strength retention, washing size changing rate and the dry-cleaning size changing rate of suiting prepared by three groups of embodiment is as shown in the table:
。
Claims (7)
1. a preparation method for wrinkle resistant suiting, is characterized in that: comprise following method: 1) by wool fiber through low pressure plasma processing; 2) by wool fiber after treatment, cotton fiber and pearl fiber blending preparation table shell fabric; 3), at the wrinkle resistant PUR of top layer fabric surface-coated, the component of described wrinkle resistant PUR and weight portion are polytetramethylene ether diol 30-40 part, butyl acrylate 20-25 part, poly hexenoic acid 18-22 part, two mercaptan butanedioic acid 15-20 parts, polyurethane 50-60 part, dioctyl phthalate 5-8 part; 4) use pressing machine by melt bonded to top layer fabric and nexine fabric; 5) fabric post processing.
2. the preparation method of a kind of wrinkle resistant suiting according to claim 1, is characterized in that: the mass ratio of described wool fiber, cotton fiber, pearl fiber is 100:20-30:5-10.
3. the preparation method of a kind of wrinkle resistant suiting according to claim 2, is characterized in that: the mass ratio of described wool fiber, cotton fiber, pearl fiber is 100:25:8.
4. the preparation method of a kind of wrinkle resistant suiting according to claim 1, is characterized in that: the process conditions of described low pressure plasma processing are that argon plasma gas pressure intensity is 50-70Pa, and glow discharge power is 30-40W, and the processing time is 2-3min.
5. the preparation method of a kind of wrinkle resistant suiting according to claim 4, is characterized in that: the process conditions of described low pressure plasma processing are that argon plasma gas pressure intensity is 60Pa, and glow discharge power is 35W, and the processing time is 3min.
6. the preparation method of a kind of wrinkle resistant suiting according to claim 1, is characterized in that: the component of described wrinkle resistant PUR and weight portion are 35 parts of polytetramethylene ether diols, 22 parts of butyl acrylates, 20 parts of poly hexenoic acids, 18 parts of two mercaptan butanedioic acids, 55 parts of polyurethane, 6 parts of dioctyl phthalates.
7. the preparation method of a kind of wrinkle resistant suiting according to claim 1, is characterized in that: described melt bonded temperature is 120-140 ℃, and pressure is 120-130Pa, and the time is 8-12s.
The preparation method of a kind of wrinkle resistant suiting according to claim 7, is characterized in that: described melt bonded temperature is 130 ℃, and pressure is 120Pa, and the time is 10s.