CN102409500B - Method for drying and forming artificial-cotton spandex cloth - Google Patents
Method for drying and forming artificial-cotton spandex cloth Download PDFInfo
- Publication number
- CN102409500B CN102409500B CN 201110277073 CN201110277073A CN102409500B CN 102409500 B CN102409500 B CN 102409500B CN 201110277073 CN201110277073 CN 201110277073 CN 201110277073 A CN201110277073 A CN 201110277073A CN 102409500 B CN102409500 B CN 102409500B
- Authority
- CN
- China
- Prior art keywords
- cloth
- forming
- spandex
- grey cloth
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a method for drying and forming an artificial-cotton spandex cloth. The method comprises the following steps of: putting a spandex grey cloth in a forming machine before dyeing; then, uniformly warming the temperature of the forming machine to 195-200 degrees centigrade; and then forming the grey cloth, finally obtaining a formed fabric. In the method for drying and forming the artificial-cotton spandex cloth of the invention, the dry spandex grey cloth is directly performed forming by warming the forming machine to replace the traditional craft that the spandex grey cloth is firstly performed water padding process, then put in the forming machine to perform warming and drying, and then performed warming forming; therefore, on the basis of achieving original effect, the obtained formed fabric is featured with high width and weight stability performance and high production efficiency, simultaneously, the forming cost is reduced.
Description
Technical field
The present invention relates to the fabric process field, particularly relate to the cotton spandex cloth of a kind of people and do the method for deciding.
Background technology
Spandex fibre not only has better elastic, and intensity height, elastic modelling quantity are big, restorative good, in recent years, and the fashionable whole world.By fabrics feel soft, the high resilience of its braiding, can significantly improve snugness of fit and added value of product.If naked spandex yarn mixes use with the high-grade knitted fabric of artificial cotton fiber's blending, two kinds of fibre properties are given full play to, bring out the best in each other, make something perfect even more perfect.That the clothes of being made by this fabric have is high-elastic, soft, comfortable, moisture absorption, ventilative, smooth, easily many characteristics such as arrange, genus is at the high-tech product of the suitable human body of people's build and skin characteristic exploitation, its performance is that common fabric is incomparable, value-added content of product is quite high, and fashionable market for many years.
Yet, the artificial cotton short texture, degree of crystallinity, the degree of orientation are lower, amorphous region and all bigger to the absorbability of dyestuff; And wet is by force to do strong half, has easy dyeing flower in dyeing course, easily broken first-class phenomenon; The knit fabric that has spandex to participate in braiding exists DIMENSIONAL STABILITY, grammes per square metre and the unmanageable difficult problem of dyeing and finishing fabric width processing coefficient again.
Therefore, before dyeing, to carry out the molecular structure that high temperature is scheduled to the cotton spandex cloth of stabilizes, eliminate above-mentioned phenomenon.Traditional handicraft adopts to wet decides method, spandex cloth grey cloth was carried out water logging earlier roll wet process, enters setting machine again, is warming up to 80-100 ℃, after the grey cloth oven dry, is warming up to 195-200 ℃ again and carries out HEAT SETTING.Because the elastic recovery rate of elastic fabric hygrometric state is relatively poor, so the typing fabric door width of cloth, the grammes per square metre less stable of using this method to obtain, production efficiency is low, and the typing cost is higher.
Summary of the invention
The technical problem that the present invention mainly solves provides the cotton spandex cloth of a kind of people and does the method for decide, can be under the situation that reaches the typing effect, the typing fabric door width of cloth that obtains, grammes per square metre stability better, production efficiency is higher, the while has also been reduced the typing cost.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: provide the cotton spandex cloth of a kind of people to do and decide method, comprising:
Spandex cloth grey cloth before the dyeing is gone into setting machine; Then setting machine at the uniform velocity is warming up to 195-200 ℃, then grey cloth is finalized the design, and obtains the fabric of finalizing the design.
In a preferred embodiment of the present invention, the grey cloth moisture is less than and equals 10%.
In a preferred embodiment of the present invention, the temperature of described setting machine is 200 ℃.
The invention has the beneficial effects as follows: the cotton spandex cloth of a kind of people of the present invention is done the method for deciding, the direct dried cloth of spandex cloth grey cloth is advanced setting machine intensification typing, replace in the traditional handicraft spandex cloth grey cloth to carry out water logging earlier and roll wet process, enter setting machine again and heat up after the oven dry, typing again heats up.Because the elastic recovery rate of elastic fabric when dry state be better, thus the method reaching on the former basis that produces effect, the typing fabric door width of cloth that obtains, grammes per square metre stability better, production efficiency is higher, has also reduced the typing cost simultaneously.
The specific embodiment
Below in conjunction with the specific embodiment preferred embodiment of the present invention is described in detail, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that protection scope of the present invention is made more explicit defining.
The embodiment of the invention comprises:
The cotton spandex cloth of a kind of people is done and is decided method, specifically comprises:
Spandex cloth grey cloth before the dyeing is gone into setting machine; Then setting machine at the uniform velocity is warming up to 195-200 ℃, is preferably 200 ℃, then grey cloth is finalized the design, and obtains the fabric of finalizing the design.
Described grey cloth moisture is less than and equals 10%.
The cotton spandex cloth of a kind of people of the present invention is done the method for decide, and the spandex cloth grey cloth before the dyeing is directly advanced the setting machine typing that heats up, and replaces in the traditional handicraft spandex cloth grey cloth to carry out water logging earlier and rolls wet process, enters setting machine again and heats up after the oven dry, heats up and finalizes the design.The typing fabric door width of cloth that obtains, grammes per square metre stability better, production efficiency is higher, has also reduced the typing cost simultaneously.Further calculate relatively: accelerated typing speed more than 40%, reduced the typing cost more than 40%.
The above only is embodiments of the invention; be not so limit claim of the present invention; every equivalent structure or equivalent flow process conversion that utilizes description of the present invention to do; or directly or indirectly be used in other relevant technical fields, all in like manner be included in the scope of patent protection of the present invention.
Claims (2)
1. the cotton spandex cloth of people is done and is decided method, it is characterized in that, comprising:
The cotton spandex cloth of people before dyeing grey cloth is gone into setting machine; Then setting machine at the uniform velocity is warming up to 195-200 ℃, then grey cloth is finalized the design, and obtains the fabric of finalizing the design, and described grey cloth moisture is less than and equals 10%.
2. the cotton spandex cloth of a kind of people according to claim 1 is done and is decided method, it is characterized in that the temperature of described setting machine is 200 ℃.