CN103892492B - A kind of preparation method of wrinkle resistant suiting - Google Patents
A kind of preparation method of wrinkle resistant suiting Download PDFInfo
- Publication number
- CN103892492B CN103892492B CN201410128010.3A CN201410128010A CN103892492B CN 103892492 B CN103892492 B CN 103892492B CN 201410128010 A CN201410128010 A CN 201410128010A CN 103892492 B CN103892492 B CN 103892492B
- Authority
- CN
- China
- Prior art keywords
- fabric
- wrinkle resistant
- fiber
- preparation
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of preparation method of wrinkle resistant suiting, comprise the steps: 1) by wool fiber through low pressure plasma process; 2) by wool fiber, cotton fiber and the pearl fiber blending preparation table shell fabric after process; 3) at nexine web surface applying hot melt adhesives, the component of described wrinkle resistant PUR and weight portion are polytetramethylene ether diol 30-40 part, butyl acrylate 20-25 part, poly hexenoic acid 18-22 part, polyurethane 50-60 part, dioctyl phthalate 5-8 part; 4) use pressing machine by surface layer fabric and nexine fabric melt bonded; 5) fabric post processing.The preparation method of a kind of wrinkle resistant suiting of the present invention improves drapability and the wrinkle resistance of fabric, reduces dimensional contraction rate.
Description
Technical field
The present invention relates to a kind of preparation method of wrinkle resistant suiting, belong to garment technology field.
Background technology
A western-style clothes great variety of models, fabric texture is soft, and young man likes western-style clothes class clothes, and the requirement wrinkle resistant to western-style clothes is also more and more higher.Pearl fiber belongs to viscose rayon, pearl powder content is about 5%, containing trace elements such as calcium, potassium, magnesium, the health care of fabric can be improved, drapability, transmissibility, gas permeability, wrinkle resistance that pearl fiber can improve fabric is added in suiting, strengthen feel, meet the comfort level that people wear western-style clothes.
Summary of the invention
The object of this invention is to provide a kind of preparation method of wrinkle resistant suiting, improve drapability and the wrinkle resistance of fabric, reduce dimensional contraction rate.
For realizing above object, the preparation method of a kind of wrinkle resistant suiting of the present invention, comprises following method: 1) by wool fiber through low pressure plasma process; 2) by wool fiber, cotton fiber and the pearl fiber blending preparation table shell fabric after process; 3) at the wrinkle resistant PUR of surface layer fabric surface coating, the component of described wrinkle resistant PUR and weight portion are polytetramethylene ether diol 30-40 part, butyl acrylate 20-25 part, poly hexenoic acid 18-22 part, two mercaptan butanedioic acid 15-20 parts, polyurethane 50-60 part, dioctyl phthalate 5-8 part; 4) use pressing machine by surface layer fabric and nexine fabric melt bonded; 5) fabric post processing.
Further, the mass ratio of described wool fiber, cotton fiber, pearl fiber is 100:20-30:5-10; Preferably, the mass ratio of wool fiber, cotton fiber, pearl fiber is 100:25:8.
Further, the process conditions of described low pressure plasma process are argon plasma gas pressure is 50-70Pa, and glow discharge power is 30-40W, and the processing time is 2-3min; Preferably, argon plasma gas pressure is 60Pa, and glow discharge power is 35W, and the processing time is 3min.
Further, the component of described wrinkle resistant PUR and weight portion are polytetramethylene ether diol 35 parts, butyl acrylate 22 parts, poly hexenoic acid 20 parts, two mercaptan butanedioic acid 18 parts, polyurethane 55 parts, dioctyl phthalate 6 parts.
Further, described melt bonded temperature is 120-140 DEG C, and pressure is 120-130Pa, and the time is 8-12s; Preferably, melt bonded temperature is 130 DEG C, and pressure is 120Pa, and the time is 10s.
The present invention produce beneficial effect be the present invention by wool fiber after low pressure plasma process, add the specific area of wool fiber, make it the pearl powder more easily received in pearl fiber, pearl fiber is evenly distributed in whole surface layer fabric, is conducive to the drapability and the wrinkle resistance that improve fabric.
In addition, using pressing machine by surface layer fabric and the melt bonded process of nexine fabric, need suitable temperature, pressure and time to realize best bonding effect, temperature is too high, overlong time, pressure excessively easily cause bonding infiltration, feel is hardening, otherwise then easily cause bonding strength to weaken, easily peel off.Wool fiber of the present invention, cotton fiber and pearl fiber blending surface layer fabric in conjunction with novel wrinkle resistant PUR, improve the dispersiveness of wrinkle resistant PUR in fabric, improve the cohesive force of PUR, effectively reduce the melt bonded time, reduce the size changing rate of fabric, improve crease resistance.
Detailed description of the invention
Embodiment 1:
A preparation method for wrinkle resistant suiting, comprises following method:
1) by wool fiber through low pressure plasma process, process conditions are argon plasma gas pressure is 50Pa, and glow discharge power is 30W, and the processing time is 3min;
2) by wool fiber, cotton fiber and the pearl fiber blending preparation table shell fabric after process, the mass ratio of described wool fiber, cotton fiber, pearl fiber is 100:20:5;
3) at the wrinkle resistant PUR of surface layer fabric surface coating, the component of described wrinkle resistant PUR and weight portion are polytetramethylene ether diol 30 parts, butyl acrylate 20 parts, poly hexenoic acid 18 parts, two mercaptan butanedioic acid 15 parts, polyurethane 60 parts, dioctyl phthalate 8 parts;
4) use pressing machine by surface layer fabric and nexine fabric melt bonded, described melt bonded temperature is 120 DEG C, and pressure is 120Pa, and the time is 12s;
5) fabric post processing, obtained suiting.
Embodiment 2:
A preparation method for wrinkle resistant suiting, comprises following method:
1) by wool fiber through low pressure plasma process, process conditions are argon plasma gas pressure is 60Pa, and glow discharge power is 35W, and the processing time is 3min;
2) by wool fiber, cotton fiber and the pearl fiber blending preparation table shell fabric after process, the mass ratio of described wool fiber, cotton fiber, pearl fiber is 100:25:8;
3) at surface layer fabric surface applying hot melt adhesives, the component of described wrinkle resistant PUR and weight portion are polytetramethylene ether diol 35 parts, butyl acrylate 22 parts, poly hexenoic acid 20 parts, two mercaptan butanedioic acid 18 parts, polyurethane 55 parts, dioctyl phthalate 6 parts;
4) use pressing machine by surface layer fabric and nexine fabric melt bonded, described melt bonded temperature is 130 DEG C, and pressure is 120Pa, and the time is 10s;
5) fabric post processing, obtained suiting.
Embodiment 3:
A preparation method for wrinkle resistant suiting, comprises following method:
1) by wool fiber through low pressure plasma process, process conditions are argon plasma gas pressure is 70Pa, and glow discharge power is 40W, and the processing time is 2min;
2) by wool fiber, cotton fiber and the pearl fiber blending preparation table shell fabric after process, the mass ratio of described wool fiber, cotton fiber, pearl fiber is 100:30:10;
3) at the wrinkle resistant PUR of surface layer fabric surface coating, the component of described wrinkle resistant PUR and weight portion are polytetramethylene ether diol 40 parts, butyl acrylate 25 parts, poly hexenoic acid 22 parts, two mercaptan butanedioic acid 20 parts, polyurethane 50 parts, dioctyl phthalate 5 parts;
4) use pressing machine by surface layer fabric and nexine fabric melt bonded, described melt bonded temperature is 140 DEG C, and pressure is 120Pa, and the time is 8s;
5) fabric post processing, obtained suiting.
The experimental data of the creasy recovery angle of suiting prepared by three groups of embodiments, breaking strength retention, washing size changing rate and dry-cleaning size changing rate is as shown in the table:
。
Claims (5)
1. a preparation method for wrinkle resistant suiting, is characterized in that: comprise following method:
1) by wool fiber through low pressure plasma process;
2) by wool fiber, cotton fiber and the pearl fiber blending preparation table shell fabric after process;
3) at the wrinkle resistant PUR of surface layer fabric surface coating, the component of described wrinkle resistant PUR and weight portion are polytetramethylene ether diol 30-40 part, butyl acrylate 20-25 part, poly hexenoic acid 18-22 part, two mercaptan butanedioic acid 15-20 parts, polyurethane 50-60 part, dioctyl phthalate 5-8 part;
4) use pressing machine by surface layer fabric and nexine fabric melt bonded;
5) fabric post processing;
In above-mentioned surface layer fabric, the mass ratio of wool fiber, cotton fiber, pearl fiber is 100 ︰ 20-30 ︰ 5-10;
The process conditions of above-mentioned low pressure plasma process are argon plasma gas pressure is 50-70Pa, and glow discharge power is 30-40W, and the processing time is 2-3min;
Above-mentioned melt bonded temperature is 120-140 DEG C, and pressure is 120-130Pa, and the time is 8-12s.
2. the preparation method of a kind of wrinkle resistant suiting according to claim 1, is characterized in that: the mass ratio of described wool fiber, cotton fiber, pearl fiber is 100 ︰ 25 ︰ 8.
3. the preparation method of a kind of wrinkle resistant suiting according to claim 1, is characterized in that: the process conditions of described low pressure plasma process are argon plasma gas pressure is 60Pa, and glow discharge power is 35W, and the processing time is 3min.
4. the preparation method of a kind of wrinkle resistant suiting according to claim 1, it is characterized in that: described melt bonded temperature is 130 DEG C, pressure is 120Pa, and the time is 10s.
5. the preparation method of a kind of wrinkle resistant suiting according to claim 1, is characterized in that: the component of described PUR and weight portion are polytetramethylene ether diol 35 parts, butyl acrylate 22 parts, poly hexenoic acid 20 parts, two mercaptan butanedioic acid 18 parts, polyurethane 55 parts, dioctyl phthalate 6 parts.